JP2014092645A - Forgery preventive structure, and label, transfer foil and forgery preventive sheet having the same - Google Patents
Forgery preventive structure, and label, transfer foil and forgery preventive sheet having the same Download PDFInfo
- Publication number
- JP2014092645A JP2014092645A JP2012242400A JP2012242400A JP2014092645A JP 2014092645 A JP2014092645 A JP 2014092645A JP 2012242400 A JP2012242400 A JP 2012242400A JP 2012242400 A JP2012242400 A JP 2012242400A JP 2014092645 A JP2014092645 A JP 2014092645A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- infrared
- hologram
- excitation
- light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、目視及び機械読取による真偽判定が可能な偽造防止構造に関し、さらに詳しくは、赤外線波長領域の励起光を照射された際の発光光が赤外波長領域の発光光である材料を含む赤外励起赤外発光層、ホログラム層と該ホログラム層に接した反射層とを含む偽造防止構造で、目視では前記偽造防止構造がホログラムとして観察でき、かつ前記赤外励起赤外発光層が機械読み取り可能で、該機械読取による真偽判定が可能な偽造防止構造並びにそれを有するラベル、転写箔及び偽造防止用紙に関するものである。 The present invention relates to an anti-counterfeit structure capable of determining authenticity by visual inspection and machine reading. More specifically, the present invention relates to a material in which emitted light when irradiated with excitation light in the infrared wavelength region is emitted light in the infrared wavelength region. Including an infrared excitation infrared emission layer, a forgery prevention structure including a hologram layer and a reflective layer in contact with the hologram layer, wherein the forgery prevention structure can be visually observed as a hologram, and the infrared excitation infrared emission layer is The present invention relates to an anti-counterfeit structure that is machine-readable and capable of authenticating by machine reading, and a label, transfer foil, and anti-counterfeit paper having the anti-counterfeit structure.
本明細書において、配合を示す「比」、「部」、「％」などは特に断わらない限り質量基準であり、「／」印は一体的に積層されていることを示す。また、「ＰＥＴ」は「ポリエチレンテレフタレート」、「ＵＶ」は「紫外線」及び「ＩＲ」は「赤外線」の略語、機能的表現、通称、又は業界用語である。 In the present specification, “ratio”, “part”, “%” and the like indicating the composition are based on mass unless otherwise specified, and the “/” mark indicates that they are integrally laminated. “PET” is an abbreviation, functional expression, common name, or industry term for “polyethylene terephthalate”, “UV” for “ultraviolet rays”, and “IR” for “infrared rays”.
（背景技術）従来、偽造防止方法には、複写防止画線、ホログラム、光学的変化材料、潜像模様などの複製や複写が困難なもの、彩紋や透かし等の視覚的に観察が容易なもの、凹凸や質感等の触覚によるものなどがある。また、商品に貼付されたラベルや印刷物の真偽を判定する際に、紫外線で発光する材料で認証用のマークを印刷し、紫外線ランプを照射して目視で判定したり、赤外光を吸収する材料で機械読取コード等を印刷して赤外線を照射して機械判定する、光を利用する真偽判定方法が多く利用されている。しかし、近年では、蛍光発光材料や、赤外光吸収材料の入手が比較的容易になり、これらの材料を偽造防止，偽造牽制手段として使用しても、専門知識を持っているものであれば光源を入手し、ラベルや印刷物に照射し、確認し、偽造することはそれほど難しいことではなくなってきている。 (Background Art) Conventionally, the anti-counterfeiting method has a copy-preventing image line, a hologram, an optically variable material, a latent image pattern and the like that are difficult to be copied or copied, and a visual observation such as a coloring pattern or a watermark is easy. And tactile sensations such as unevenness and texture. In addition, when judging the authenticity of labels and printed matter affixed to products, print a mark for authentication with a material that emits ultraviolet light, and determine it visually by irradiating an ultraviolet lamp, or absorb infrared light A true / false determination method using light, in which a machine reading code or the like is printed with a material to be used and machine determination is performed by irradiating infrared rays, is often used. However, in recent years, it has become relatively easy to obtain fluorescent materials and infrared light absorbing materials, and even if these materials are used as anti-counterfeiting and anti-counterfeiting means, Obtaining a light source, illuminating, verifying, and forging labels and prints has become less difficult.
（従来技術）従来、偽造防止印刷物は、赤外線反射性基材の上に、赤外領域に吸収ピークがある赤外線吸収性インキからなる検証用画像と、赤外領域に励起ピークがある励起光の照射により励起され、その励起光の励起ピーク波長よりも長波長側の赤外線を発光する蛍光インキからなる検証用画像とが設けられており、さらにはこれらの検証用画像を隠蔽するように隠蔽用画像が設けられていると共に、赤外線吸収性インキの吸収ピーク波長と蛍光インキの励起ピーク波長とが同じであることを特徴とする偽造防止印刷物が知られている（例えば、特許文献１参照。）。また、基材と、前記基材上に設けられた有色パターン印刷層とを有する偽造防止印刷物であって、前記有色パターン印刷層には、赤外線及び／又は紫外線に反応する不可視のセキュリティ材料が含有されていること、を特徴とする偽造防止印刷物が知られている（例えば、特許文献２参照。）。さらに、媒体基材と、前記媒体基材の上に設けられ、見る角度によって見える色彩が変化する色彩可変印刷層と、前記色彩可変印刷層の上に、前記色彩可変印刷層の少なくとも一部を表出するようにして設けられ、前記媒体基材と同色で形成され、特定の波長を有した光線の照射により蛍光発光する光反応印刷層と、を備える偽造防止印刷媒体が知られている（例えば、特許文献３参照。）。さらにまた、少なくとも一部に真偽判定のための情報領域を有する印刷物であって、前記真偽判定のための情報領域には、可視光波長域および赤外光波長域の光を照射することによって赤外光を発光する情報が形成されたことを特徴とする認証用印刷物が知られている（例えば、特許文献４参照。）。しかしながら、特許文献１〜４のいずれも、機械読取による真偽判定はできるものの、目視では機械読取できる情報を見え難くしており、目視での真偽判定はできず、機械読取と目視の両方での真偽判定ができないという欠点がある。また、特許文献２〜４は、本出願人による開示であり、これらの欠点を解消し、機械読取と目視の両方での真偽判定をできるようにするために、本発明の完成に至ったものである。 (Prior art) Conventionally, a forgery-preventing printed material is an image for verification consisting of an infrared-absorbing ink having an absorption peak in the infrared region on an infrared reflective substrate, and excitation light having an excitation peak in the infrared region. It is provided with a verification image made of fluorescent ink that is excited by irradiation and emits infrared light longer than the excitation peak wavelength of the excitation light, and further concealed so as to conceal these verification images An anti-counterfeit printed matter is known in which an image is provided and the absorption peak wavelength of the infrared absorbing ink is the same as the excitation peak wavelength of the fluorescent ink (see, for example, Patent Document 1). . Moreover, it is a forgery-preventing printed matter having a substrate and a colored pattern printing layer provided on the substrate, and the colored pattern printing layer contains an invisible security material that reacts to infrared rays and / or ultraviolet rays. A forgery-preventing printed matter characterized by the above is known (for example, see Patent Document 2). Furthermore, at least a part of the color variable printing layer is provided on the medium base material, the color variable printing layer provided on the medium base material, the color changing visible depending on the viewing angle, and the color variable printing layer. An anti-counterfeit printing medium provided with a photoreactive printing layer provided so as to be exposed, formed in the same color as the medium substrate, and emitting fluorescence by irradiation with light having a specific wavelength is known ( For example, see Patent Document 3.) Furthermore, the printed matter has an information region for authenticity determination at least partially, and the information region for authenticity determination is irradiated with light in a visible light wavelength region and an infrared light wavelength region. There is known a printed matter for authentication characterized in that information for emitting infrared light is formed by (see, for example, Patent Document 4). However, although all of Patent Documents 1 to 4 can make true / false judgments by machine reading, it makes it difficult to see information that can be read by machines visually, and cannot make true / false judgments by visual observation. There is a drawback that true / false judgments cannot be made. Further, Patent Documents 2 to 4 are disclosures by the present applicant, and the present invention has been completed in order to eliminate these drawbacks and enable true / false judgments by both machine reading and visual observation. Is.
従って、偽造防止構造並びにそれを有するラベル、転写箔及び偽造防止用紙は、目視では前記偽造防止構造がホログラムとして目視でも観察でき、かつ前記赤外励起赤外発光層が機械読取による真偽判定も可能なことが求められている。そこで、本発明は上記のような問題点を解消するために、本発明者らは鋭意研究を進め、本発明の完成に至ったものである。その目的は、機械読取と目視の両方での真偽判定をできるようにする偽造防止構造並びにそれを有するラベル、転写箔及び偽造防止用紙を提供することである。 Therefore, the anti-counterfeit structure and the label, transfer foil, and anti-counterfeit paper having the anti-counterfeit structure can be visually observed as the hologram as the anti-counterfeit structure, and the infrared excitation infrared light emitting layer can also be checked for authenticity by machine reading. What is possible is sought. In order to solve the above-described problems, the present inventors have made extensive studies and have completed the present invention. An object of the present invention is to provide a forgery prevention structure capable of performing authenticity determination by both machine reading and visual observation, and a label, transfer foil, and forgery prevention paper having the same.
上記の課題を解決するために、本発明の請求項１の発明に係わる偽造防止構造は、少なくとも、赤外励起赤外発光層、及びホログラム層と該ホログラム層に接した反射層とを含む偽造防止構造で、前記赤外励起赤外発光層が赤外線波長領域の励起光を照射された際の発光光が赤外波長領域の発光光であり、前記ホログラム層の前記反射層の面が微細な凹凸からなるレリーフホログラムであり、前記反射層が金属反射層又は透明反射層であり、前記偽造防止構造がホログラムとして目視でき、かつ前記赤外励起赤外発光層が機械読み取り可能であることを特徴とする偽造防止構造である。請求項２の発明に係わる偽造防止構造を有するラベルは、基材と、該基材の一方の面へ請求項１に記載の偽造防止構造及び粘着層をこの順に設けてなることを特徴とする偽造防止構造を有するラベルである。請求項３の発明に係わる偽造防止構造を有する転写箔は、転写基材と、該転写基材の一方の面へ剥離層、請求項１に記載の偽造防止構造及び接着層とをこの順に設けてなることを特徴とする偽造防止構造を有する転写箔である。請求項４の発明に係わる偽造防止構造を有する被転写体は、請求項３に記載の偽造防止構造を有する転写箔を用いて、被転写体へ前記偽造防止構造及び前記接着層を転写してなることを特徴とする偽造防止構造を有する被転写体である。請求項５の発明に係わる偽造防止構造を有する偽造防止用紙は、請求項１に記載の偽造防止構造を、基紙へ抄き込んでなることを特徴とする偽造防止構造を有する偽造防止用紙である。 In order to solve the above problems, a forgery prevention structure according to the invention of claim 1 of the present invention includes at least an infrared excitation infrared light emitting layer, a forgery layer, and a hologram layer and a reflection layer in contact with the hologram layer. In the prevention structure, when the infrared excitation infrared emission layer is irradiated with excitation light in the infrared wavelength region, the emission light is emission light in the infrared wavelength region, and the surface of the reflection layer of the hologram layer is fine It is a relief hologram composed of irregularities, wherein the reflection layer is a metal reflection layer or a transparent reflection layer, the anti-counterfeit structure is visible as a hologram, and the infrared excitation infrared emission layer is machine-readable. It is a forgery prevention structure. A label having an anti-counterfeit structure according to the invention of claim 2 is characterized in that the anti-counterfeit structure according to claim 1 and an adhesive layer are provided in this order on one surface of the base material and the base material. It is a label having a forgery prevention structure. A transfer foil having an anti-counterfeit structure according to the invention of claim 3 is provided with a transfer substrate, a release layer on one surface of the transfer substrate, and the anti-counterfeit structure and adhesive layer of claim 1 in this order. A transfer foil having an anti-counterfeit structure. A to-be-transferred body having a forgery prevention structure according to the invention of claim 4 uses the transfer foil having the forgery prevention structure according to claim 3 to transfer the forgery prevention structure and the adhesive layer to the transfer body. It is a to-be-transferred body which has the forgery prevention structure characterized by becoming. An anti-counterfeit paper having an anti-counterfeit structure according to the invention of claim 5 is an anti-counterfeit paper having an anti-counterfeit structure characterized in that the anti-counterfeit structure according to claim 1 is formed on a base paper. is there.
請求項１の本発明によれば、赤外励起赤外発光層を機械読取しての真偽判定と、ホログラムの目視による真偽判定とで、機械読取と目視の両方での真偽判定ができる効果を奏する偽造防止構造を提供する。請求項２の本発明によれば、赤外励起赤外発光層を機械読取しての真偽判定と、ホログラムの目視による真偽判定とで、機械読取と目視の両方での真偽判定ができる効果を奏する偽造防止構造を有するラベルを提供する。請求項３の本発明によれば、赤外励起赤外発光層を機械読取しての真偽判定と、ホログラムの目視による真偽判定とで、機械読取と目視の両方での真偽判定ができる効果を奏する偽造防止構造を有する転写箔を提供する。請求項４の本発明によれば、赤外励起赤外発光層を機械読取しての真偽判定と、ホログラムの目視による真偽判定とで、機械読取と目視の両方での真偽判定ができる効果を奏する偽造防止構造を有する被転写体を提供する。請求項５の本発明によれば、赤外励起赤外発光層を機械読取しての真偽判定と、ホログラムの目視による真偽判定とで、機械読取と目視の両方での真偽判定ができる効果を奏する偽造防止構造を有する偽造防止用紙を提供する。 According to the first aspect of the present invention, the true / false determination by mechanical reading of the infrared excitation infrared emission layer and the true / false determination by visual observation of the hologram can be performed by both the mechanical reading and visual inspection. An anti-counterfeit structure that provides an effect that can be achieved. According to the second aspect of the present invention, the true / false determination by mechanical reading of the infrared excitation infrared light emitting layer and the true / false determination by visual observation of the hologram can be performed by both mechanical reading and visual inspection. Provided is a label having an anti-counterfeit structure that exhibits an effect that can be achieved. According to the third aspect of the present invention, the true / false determination by mechanical reading of the infrared excitation infrared emission layer and the true / false determination by visual observation of the hologram can be performed by both the mechanical reading and visual inspection. Provided is a transfer foil having a forgery-preventing structure that exhibits an effect that can be achieved. According to the fourth aspect of the present invention, the true / false determination by mechanical reading of the infrared excitation infrared light emitting layer and the true / false determination by visual observation of the hologram can be performed by both mechanical reading and visual inspection. Provided is a transferred object having a forgery preventing structure that exhibits the effect that can be achieved. According to the present invention of claim 5, true / false determination by mechanical reading of the infrared excitation infrared emission layer and true / false determination by visual observation of the hologram can be performed by both mechanical reading and visual inspection. An anti-counterfeit paper having an anti-counterfeit structure that exhibits an effect that can be achieved is provided.
以下、本発明の実施形態について、図面を参照しながら、詳細に説明する。 Hereinafter, embodiments of the present invention will be described in detail with reference to the drawings.
（偽造防止構造）本発明の偽造防止構造１０は、図１に示すように、少なくとも、赤外励起赤外発光層１２、及びホログラム層１５と該ホログラム層１５に接した反射層１７とを含み、赤外励起赤外発光層１２が赤外線波長領域の励起光を照射された際の発光光が赤外波長領域の発光光であり、ホログラム層１５の反射層１７の面が微細な凹凸からなるレリーフホログラムであり、反射層１７が金属反射層又は透明反射層であり、偽造防止構造１０がホログラムとして目視でき、かつ赤外励起赤外発光層１２が機械読み取り可能であることを特徴とする。
(Anti-Counterfeit Structure) As shown in FIG. 1, the
（作用・効果）本発明の偽造防止構造１０によれば、赤外励起赤外発光層１２を機械読取しての真偽判定と、ホログラム層１５によって、ホログラムの目視による真偽判定とで、機械読取と目視の両方での真偽判定ができるという効果を奏することができる。また、ホログラムが観察されることで、機械読取用の赤外励起赤外発光層１２の存在が目視では判り難いという隠し効果もある。
(Operation / Effect) According to the
（赤外励起赤外発光層）赤外励起赤外発光層１２としては、少なくとも、赤外線波長領域の励起光を照射された際の発光光が赤外波長領域の発光光である赤外励起赤外発光剤とバインダとを含ませる。また、励起光の照射と発光光の発光に影響のない範囲で、必要に応じて、充填剤、可塑剤、着色剤、帯電防止剤などの添加剤を加えても良い。 (Infrared excitation infrared emission layer) As the infrared excitation infrared emission layer 12, at least infrared emission red when emitted light when irradiated with excitation light in the infrared wavelength region is emitted light in the infrared wavelength region. An external light-emitting agent and a binder are included. In addition, additives such as a filler, a plasticizer, a colorant, and an antistatic agent may be added as necessary within a range that does not affect the irradiation of excitation light and the emission of emitted light.
（バインダ）バインダとしては、従来公知の熱可塑性樹脂、熱硬化性樹脂、反応型樹脂、電子線硬化型樹脂、紫外線硬化型樹脂、可視光線硬化型樹脂やこれらの混合物が使用される。熱可塑性樹脂としては、例えば、塩化ビニル系共重合体、アクリル酸又はメタクリル酸系樹脂、ウレタン系樹脂、ポリアミド系樹脂、セルロース誘導体、ポリエステル樹脂、ポリカーボネート樹脂などの熱可塑性樹脂およびこれらの混合物等が使用される。熱硬化性樹脂または反応型樹脂としては、具体的には例えばエポキシ系樹脂、ポリウレタン系樹脂、ポリエステル系樹脂、アクリル系反応樹脂（電離放射線硬化性樹脂）等である。 (Binder) As the binder, conventionally known thermoplastic resins, thermosetting resins, reactive resins, electron beam curable resins, ultraviolet curable resins, visible light curable resins, and mixtures thereof are used. Examples of the thermoplastic resin include vinyl chloride copolymers, acrylic acid or methacrylic acid resins, urethane resins, polyamide resins, cellulose derivatives, polyester resins, polycarbonate resins, and the like, and mixtures thereof. used. Specific examples of the thermosetting resin or reactive resin include epoxy resins, polyurethane resins, polyester resins, and acrylic reaction resins (ionizing radiation curable resins).
（赤外励起赤外発光剤）赤外励起赤外発光剤としては、赤外光（８００ｎｍ）で励起し、より長波長（９８０〜１０２０ｎｍ）に発光するものであればよく、例えば、ＬｉＮｄ0.9Ｙｂ0.1Ｐ4Ｏ12、ＬｉＢｉ0.2Ｎｄ0.7Ｙｂ0.1Ｐ4Ｏ12、Ｎｄ0.9Ｙｂ0.1Ｎｄ5（ＭｏＯ4）4、ＮａＮｄ0.9Ｙｂ0.1Ｐ4Ｏ12、Ｎｄ0.8Ｙｂ0.2Ｎａ5（ＷＯ4）4、Ｎｄ0.8Ｙｂ0.2Ｎａ5（Ｍｏ0.5Ｗ0.5Ｏ4）4、Ｃｅ0.05Ｇｄ0.05Ｎｄ0.75Ｙｂ0.15Ｎａ5（Ｗ0.7Ｍｏ0.3Ｏ4）4、Ｎｄ0.9Ｙｂ0.1Ａｌ3（ＢＯ3）4、Ｎｄ0.9Ｙｂ0.1Ａｌ2.7Ｃｒ0.3（ＢＯ3）4、Ｎｄ0.6Ｙｂ0.4Ｐ5Ｏ14、Ｎｄ0.8Ｙｂ0.2Ｋ3（ＰＯ4）2などが例示できる。具体的には、蛍光顔料ＩＲＳ−Ｆ（根本特殊化学社製）などが例示できる。 (Infrared excited infrared luminescent agent) The infrared excited infrared luminescent agent may be any one that is excited by infrared light (800 nm) and emits light at a longer wavelength (980 to 1020 nm). For example, LiNd 0.9 Yb 0.1 P 4 O 12 , LiBi 0.2 Nd 0.7 Yb 0.1 P 4 O 12 , Nd 0.9 Yb 0.1 Nd 5 (MoO 4 ) 4 , NaNd 0.9 Yb 0.1 P 4 O 12 , Nd 0.8 Yb 0.2 Na 5 (WO 4 ) 4 Nd 0.8 Yb 0.2 Na 5 (Mo 0.5 W 0.5 O 4 ) 4 , Ce 0.05 Gd 0.05 Nd 0.75 Yb 0.15 Na 5 (W 0.7 Mo 0.3 O 4 ) 4 , Nd 0.9 Yb 0.1 Al 3 (BO 3 ) 4 , Nd Examples include 0.9 Yb 0.1 Al 2.7 Cr 0.3 (BO 3 ) 4 , Nd 0.6 Yb 0.4 P 5 O 14 , Nd 0.8 Yb 0.2 K 3 (PO 4 ) 2 and the like. Specifically, fluorescent pigment IRS-F (manufactured by Nemoto Special Chemical Co., Ltd.) can be exemplified.
（ホログラム）ホログラム層１５／反射層１７が積層され、意匠性及び／又はセキュリティ性の著しく優れるホログラムが観察される。しかも、その製造についても、真空成膜装置による薄膜による反射層１７以外については、既存設備での印刷法により形成可能で、小ロット生産にも対応でき、低コストで生産することができる。 (Hologram) Hologram layer 15 / reflective layer 17 is laminated, and a hologram with extremely excellent design and / or security is observed. In addition, the manufacturing process can be performed by a printing method using existing equipment except for the reflective layer 17 formed of a thin film by a vacuum film forming apparatus, can be produced in a small lot, and can be produced at low cost.
（ホログラム層）ホログラム層１５には該ホログラム層１５の反射層１７の面に微細な凹凸からなるレリーフホログラムが賦形されている。ホログラム層１５は下記の電離放射線硬化性樹脂を含む組成物を電離放射線で硬化させてなる層とする。 (Hologram Layer) The hologram layer 15 is formed with a relief hologram made of fine irregularities on the surface of the reflection layer 17 of the hologram layer 15. The hologram layer 15 is a layer formed by curing a composition containing the following ionizing radiation curable resin with ionizing radiation.
（電離放射線硬化性樹脂）電離放射線硬化性樹脂は（イ）分子中にイソシアネート基を３個以上有するイソシアネート類、（ロ）分子中に水酸基を少なくとも１個と（メタ）アクリロイルオキシ基を少なくとも２個有する多官能（メタ）アクリレート類、又は（ハ）分子中に水酸基を少なくとも２個有する多価アルコール類の反応生成物であるウレタン（メタ）アクリレートオリゴマーで、電離放射線硬化性を有するウレタン変性アクリレート樹脂である。好ましいウレタン（メタ）アクリレートオリゴマーとしては、詳細は特開２００１−３２９０３１号公報で開示されている光硬化性樹脂が好ましい。具体的には、ＭＨＸ４０５ニス（ザ・インクテック（株）製、電離放射線硬化性樹脂商品名）、ユピマーＵＶ・Ｖ３０３１（三菱化学（株）製、電離放射線硬化性樹脂商品名）が例示できる。 (Ionizing radiation curable resin) The ionizing radiation curable resin is (i) an isocyanate having three or more isocyanate groups in the molecule, (b) at least one hydroxyl group and at least two (meth) acryloyloxy groups in the molecule. Polyurethane (meth) acrylates which are polyfunctional (meth) acrylates having a number of units, or (c) urethane (meth) acrylate oligomers which are reaction products of polyhydric alcohols having at least two hydroxyl groups in the molecule, and are urethane-modified acrylates having ionizing radiation curability. Resin. As a preferable urethane (meth) acrylate oligomer, a photocurable resin disclosed in detail in JP-A No. 2001-329031 is preferable. Specific examples include MHX405 varnish (made by The Inktec Co., Ltd., ionizing radiation curable resin product name) and Iupimer UV · V3031 (manufactured by Mitsubishi Chemical Co., Ltd., product name of ionizing radiation curable resin).
（ホログラム層の形成）ホログラム層１５の形成は、上記の電離放射線硬化性樹脂と、必要に応じて、光重合開始剤、可塑剤、安定剤、界面活性剤等を加え、溶媒へ分散または溶解して、ロールコート、グラビアコート、コンマコート、ダイコートなどの公知のコーティング方法で塗布し乾燥して、レリーフを賦型した後に、電離放射線で反応（硬化）させればよい。ホログラム層１５の厚さとしては、通常は１μｍ〜３０μｍ程度、好ましくは２μｍ〜２０μｍ程度である。複数回の塗布でもよい。 (Hologram layer formation) The hologram layer 15 is formed by adding the above-mentioned ionizing radiation curable resin and, if necessary, a photopolymerization initiator, a plasticizer, a stabilizer, a surfactant, etc., and dispersing or dissolving in a solvent. Then, after applying a relief by a known coating method such as roll coating, gravure coating, comma coating, and die coating, and shaping a relief, it may be reacted (cured) with ionizing radiation. The thickness of the hologram layer 15 is usually about 1 μm to 30 μm, preferably about 2 μm to 20 μm. It may be applied several times.
（レリーフホログラム）次に、ホログラム層１５の表面には、ホログラムなどの光回折効果の発現する所定のレリーフ構造を賦型し、硬化させる。ホログラムは物体光と参照光との光の干渉による干渉縞を凹凸のレリーフ形状で記録されたもので、例えば、フレネルホログラム等のレーザ再生ホログラム、及びレインボーホログラム等の白色光再生ホログラム、さらに、それらの原理を利用したカラーホログラム、コンピュータジェネレーティッドホログラム（ＣＧＨ）、ホログラフィック回折格子などがある。レリーフ形状は凹凸形状であり、特に限定されるものではなく、微細な凹凸形状を有する光拡散、光散乱、光反射、光回折などの機能を発現するものでもよく、例えば、フーリエ変換やレンチキュラーレンズ、光回折パターン、モスアイ、が形成されたものである。また、光回折機能はないが、特異な光輝性を発現するヘアライン柄、マット柄、万線柄、干渉パターンなどでもよい。 (Relief Hologram) Next, on the surface of the hologram layer 15, a predetermined relief structure such as a hologram that exhibits a light diffraction effect is formed and cured. A hologram is a recording of interference fringes due to the interference of light between object light and reference light in an uneven relief shape, such as a laser reproduction hologram such as a Fresnel hologram, a white light reproduction hologram such as a rainbow hologram, There are color holograms utilizing the above principle, computer generated holograms (CGH), holographic diffraction gratings and the like. The relief shape is a concavo-convex shape, and is not particularly limited, and may have a fine concavo-convex shape such as light diffusion, light scattering, light reflection, light diffraction, etc., such as Fourier transform or lenticular lens. , A light diffraction pattern, and a moth eye. Further, although it does not have a light diffraction function, it may be a hairline pattern, a mat pattern, a line pattern, an interference pattern, or the like that expresses a unique glitter.
これらのレリーフ形状の作製方法としてはホログラム撮影記録手段を利用して作製されたホログラムや回折格子の他に、干渉や回折という光学計算に基づいて電子線描画装置等を用いて作製されたホログラムや回折格子をあげることもできる。また、ヘアライン柄や万線柄のような比較的大きなパターンなどは機械切削法でもよい。これらのホログラム及び／又は回折格子の単一若しくは多重に記録しても、組み合わせて記録しても良い。これらの原版は公知の材料、方法で作成することができ、通常、感光性材料を塗布したガラス板を用いたレーザ光干渉法、電子線レジスト材料を塗布したガラス板に電子線描画装置を用いてパターン作製する電子線描画法をなどが適用できる。 As a method for producing these relief shapes, in addition to holograms and diffraction gratings produced using hologram photographing and recording means, holograms produced using an electron beam drawing device based on optical calculations such as interference and diffraction, A diffraction grating can also be mentioned. Also, a relatively large pattern such as a hairline pattern or a line pattern may be a machine cutting method. These holograms and / or diffraction gratings may be recorded single or multiple, or may be recorded in combination. These original plates can be prepared by known materials and methods, and usually, laser beam interference using a glass plate coated with a photosensitive material, using an electron beam drawing apparatus on a glass plate coated with an electron beam resist material. An electron beam drawing method for patterning can be applied.
（レリーフの賦型）ホログラム層１５面へ、上記のレリーフ形状を賦形（複製ともいう）する。ホログラムの賦型は、公知の方法によって形成でき、例えば、回折格子やホログラムの干渉縞を表面凹凸のレリーフとして記録する場合には、回折格子や干渉縞が凹凸の形で記録された原版をプレス型（スタンパという）として用い、上記樹脂層上に前記原版を重ねて加熱ロールなどの適宜手段により、両者を加熱圧着することにより、原版の凹凸模様を複製することができる。 (Relief shaping) The relief shape is shaped (also referred to as replication) on the surface of the hologram layer 15. Hologram shaping can be formed by a known method. For example, when recording diffraction gratings or interference fringes of holograms as reliefs of surface irregularities, a master on which the diffraction gratings or interference fringes are recorded in irregularities is pressed. The concave / convex pattern of the original can be duplicated by using it as a mold (referred to as a stamper) and by superimposing the original on the resin layer and heat-pressing both of them with an appropriate means such as a heating roll.
（レリーフの硬化）ホログラム層１５は、スタンパでエンボス中、又はエンボス後に、電離放射線を照射して、電離放射線硬化性樹脂を硬化させる。上記の電離放射線硬化性樹脂は、レリーフを形成後に、電離放射線を照射して硬化（反応）させると電離放射線硬化樹脂（ホログラム層１５）となる。電離放射線としては、電磁波が有する量子エネルギーで区分する場合もあるが、本明細書では、すべての紫外線（ＵＶ−Ａ、ＵＶ−Ｂ、ＵＶ−Ｃ）、可視光線、ガンマー線、Ｘ線、電子線を包含するものと定義する。従って、電離放射線としては、紫外線（ＵＶ）、可視光線、ガンマー線、Ｘ線、または電子線などが適用できるが、紫外線（ＵＶ）が好適である。電離放射線で硬化する電離放射線硬化性樹脂は、紫外線硬化の場合は光重合開始剤、及び／又は光重合促進剤を添加し、エネルギーの高い電子線硬化の場合は添加しないで良く、また、適正な触媒が存在すれば、熱エネルギーでも硬化できる。 (Relief Curing) The hologram layer 15 is irradiated with ionizing radiation during or after embossing with a stamper to cure the ionizing radiation curable resin. The ionizing radiation curable resin becomes an ionizing radiation curable resin (hologram layer 15) when cured (reacted) by irradiation with ionizing radiation after the relief is formed. The ionizing radiation may be classified according to the quantum energy of the electromagnetic wave, but in this specification, all ultraviolet rays (UV-A, UV-B, UV-C), visible light, gamma rays, X-rays, electrons It is defined as including a line. Accordingly, ultraviolet (UV), visible light, gamma rays, X-rays, or electron beams can be applied as ionizing radiation, but ultraviolet (UV) is preferred. An ionizing radiation curable resin that is cured by ionizing radiation may contain a photopolymerization initiator and / or a photopolymerization accelerator in the case of ultraviolet curing, and may not be added in the case of high energy electron beam curing. Can be cured even with thermal energy.
（レリーフの絵柄）ホログラム層１５の絵柄を擬似連続絵柄とすることが好ましい。擬似連続絵柄はプレス型（スタンパという）を作成する際に、小さなレリーフ版の複数を、精度よく突合せてつなぎ目を目立たなくしたり、つなぎ目を樹脂で埋めたりすればよい。このように、擬似連続絵柄とすることで、できるだけ大きな面積、又は好ましくは全面とすることもできる。大面積又は全面のホログラム絵柄を背景とし他の任意な印刷絵柄と、同調させたり、合わせたりして、さらなる特異な意匠性を向上させることができる。 (Relief pattern) The pattern of the hologram layer 15 is preferably a quasi-continuous pattern. When creating a press mold (referred to as a stamper) for the pseudo continuous pattern, it is only necessary to match a plurality of small relief plates with high accuracy to make the joints inconspicuous, or to fill the joints with resin. In this way, by using a quasi-continuous pattern, the area can be as large as possible, or preferably the entire surface. Further unique design can be improved by synchronizing or matching with any other printed pattern against a large area or entire surface of the hologram pattern.
（反射層）反射層１７は、所定のレリーフ構造を設けたホログラム層１５面のレリーフ面へ、反射層１７へ設けることにより、レリーフの反射及び／又は回折効果を高めるので、ホログラム層１５の反射率がより高れば、特に限定されない。該反射層１７としては、真空薄膜法などによる金属薄膜などの金属光沢反射層、又は透明反射層のいずれでもよい
（金属反射層）反射層１７に用いる金属としては、金属光沢を有し光を反射する金属元素の薄膜で、Ｃｒ、Ｎｉ、Ａｇ、Ａｕ、Ａｌ等の金属、及びその酸化物、硫化物、窒化物等の薄膜を単独又は複数を組み合わせてもよい。上記の光反射性の金属薄膜の形成は、いずれも１０ｎｍ〜２０００ｎｍ程度、好ましくは２０ｎｍ〜１０００ｎｍの厚さになるよう、真空蒸着法、スパッタリング法、イオンプレーティング法などの真空薄膜法で得られるが、その他、メッキなどによっても形成できる。反射層１７の厚さがこの範囲未満では、光がある程度透過して効果が減じ、また、それ以上では、反射効果は変わらないので、コスト的に無駄である。
(Reflection layer) Since the reflection layer 17 is provided on the reflection layer 17 on the relief surface of the hologram layer 15 provided with a predetermined relief structure, the reflection reflection and / or diffraction effect is enhanced. If a rate is higher, it will not specifically limit. The reflective layer 17 may be a metallic glossy reflective layer such as a metal thin film by a vacuum thin film method or a transparent reflective layer. (Metal reflective layer) The metal used for the reflective layer 17 has a metallic luster and emits light. The reflective metal element thin film may be a metal such as Cr, Ni, Ag, Au, or Al, and thin films such as oxides, sulfides, and nitrides thereof, or a combination thereof. The light-reflective metal thin film can be formed by a vacuum thin film method such as a vacuum deposition method, a sputtering method, or an ion plating method so as to have a thickness of about 10 nm to 2000 nm, preferably 20 nm to 1000 nm. However, it can also be formed by plating. If the thickness of the reflective layer 17 is less than this range, the light is transmitted to some extent and the effect is reduced, and if it is more than that, the reflective effect is not changed, which is wasteful in cost.
（透明反射層）反射層１７に用いる透明反射層は、所定のレリーフ構造を設けたホログラム層１５面のレリーフ面へ、透明反射層へ設けることにより、レリーフの反射及び／又は回折効果を高めるので、ほぼ無色透明な色相で、その光学的な屈折率がホログラム層のそれとは異なることにより、金属光沢が無いにもかかわらず、ホログラムなどの光輝性を視認できるから、透明なホログラムを作製することができる。 (Transparent Reflective Layer) Since the transparent reflective layer used for the reflective layer 17 is provided on the transparent reflective layer on the relief surface of the hologram layer 15 provided with a predetermined relief structure, the relief reflection and / or diffraction effect is enhanced. Because it has almost colorless and transparent hue and its optical refractive index is different from that of the hologram layer, it is possible to visually recognize the glitter of the hologram, etc., even though there is no metallic luster, so that a transparent hologram is produced. Can do.
透明反射層１７としては、例えば、ホログラム層１５よりも光屈折率の高い薄膜、および光屈折率の低い薄膜とがあり、前者の例としては、ＺｎＳ、ＴｉＯ2、Ａｌ2Ｏ3、Ｓｂ2Ｓ3、ＳｉＯ、ＳｎＯ2、ＩＴＯ等があり、後者の例としては、ＬｉＦ、ＭｇＦ2、ＡｌＦ3がある。好ましくは、金属酸化物又は窒化物であり、具体的には、Ｂｅ、Ｍｇ、Ｃａ、Ｃｒ、Ｍｎ、Ｃｕ、Ａｇ、Ａｌ、Ｓｎ、Ｉｎ、Ｔｅ、Ｆｅ、Ｃｏ、Ｚｎ、Ｇｅ、Ｐｂ、Ｃｄ、Ｂｉ、Ｓｅ、Ｇａ、Ｒｂ、Ｓｂ、Ｐｂ、Ｎｉ、Ｓｒ、Ｂａ、Ｌａ、Ｃｅ、Ａｕ等の酸化物又は窒化物他はそれらを２種以上を混合したもの等が例示できる。またアルミニウム等の一般的な光反射性の金属薄膜も、厚みが２００Å以下になると、透明性が出て使用できる。透明金属化合物の形成は、金属の薄膜と同様、ホログラム層１５のレリーフ面に、１０〜２０００ｎｍ程度、好ましくは２０〜１０００ｎｍの厚さになるよう、蒸着、スパッタリング、イオンプレーティング、ＣＶＤなどの真空薄膜法などにより設ければよい。 Examples of the transparent reflection layer 17 include a thin film having a higher refractive index than that of the hologram layer 15 and a thin film having a lower refractive index. Examples of the former include ZnS, TiO 2 , Al 2 O 3 , and Sb 2. There are S 3 , SiO, SnO 2 , ITO, etc., and examples of the latter include LiF, MgF 2 , and AlF 3 . Preferably, it is a metal oxide or nitride, specifically, Be, Mg, Ca, Cr, Mn, Cu, Ag, Al, Sn, In, Te, Fe, Co, Zn, Ge, Pb, Cd , Bi, Se, Ga, Rb, Sb, Pb, Ni, Sr, Ba, La, Ce, Au, and other oxides or nitrides, and the like can be exemplified by a mixture of two or more thereof. Also, a general light-reflective metal thin film such as aluminum can be used when it has a thickness of 200 mm or less. The transparent metal compound is formed on the relief surface of the hologram layer 15 by vacuum such as vapor deposition, sputtering, ion plating, and CVD so that the thickness of the relief layer of the hologram layer 15 is about 10 to 2000 nm, preferably 20 to 1000 nm. It may be provided by a thin film method or the like.
（機械読取）機械読取については、赤外線照射装置から、必要に応じて、ハーフミラーを通して、偽造防止構造を有するラベル、偽造防止構造を有する転写箔、転写された偽造防止構造を有する被転写体、偽造防止構造を有する偽造防止用紙の偽造防止構造１０へ、赤外励起赤外発光層１２に含まれる赤外励起赤外発光剤の励起波長に近似した特定波長の赤外線を照射し、赤外線受光センサーにおいて赤外線励起赤外線発光剤の発光波長を検知すればよい。偽造防止構造１０は、目視による観察では、ホログラムが観察されるので、機械読取用の赤外励起赤外発光層１２の存在が目視では判り難い。しかしながら、偽造防止構造１０に対して、例えば８００ｎｍの波長の近辺にシャープな発光特性を持つＬＥＤを用いて近赤外線を、必要に応じてレンズで集光して、照射することによって得られる発光光を９５０ｎｍ前後に透過特性のあるバンドパスフィルターを通して赤外線カメラで撮影したところ、赤外励起赤外発光層１２の部分が白く撮影され、他の部分は黒く撮影され、情報を読み取ることができる。
(Machine reading) For machine reading, from an infrared irradiation device, if necessary, through a half mirror, a label having a forgery prevention structure, a transfer foil having a forgery prevention structure, a transferred object having a transferred forgery prevention structure, Infrared receiving sensor that irradiates
また、赤外線発光光の読取方法としては、ラインでも、面でも読み取ってもよい。面での読取では、発光光源から照射された光が券面を面状に照射し、受光部のフォトトランジスタがデジタルカメラに組み込まれたＣＣＤのように面で読み取れる。この場合には、赤外励起赤外発光層１２が、数字やバーコードであれば、その情報も読み取れる。ラインでの読取では、例えば、偽造防止構造１０を有する商品券を読取装置に読み込ませ、商品券を動かせば、発光部を読み取れる。具体的には、例えば、デパートの店頭などにおいて、商品券が使用されたら、赤外励起赤外発光層１２に赤外光（約８００〜９００ｎｍ）を照射する（照射工程）。照射して、赤外励起赤外発光層１２で形成された、例えば文字列（「○○デパート」及び「￥１，０００」など）が、赤外線発光光した場合には、その商品券が、本物であると判定することができる（判定工程）。仮に、偽造された商品券の場合は、赤外励起赤外発光層１２で形成されているべき文字列が赤外線発光光しないので、容易に偽物であることを判定することができる。
In addition, as a method for reading infrared light emission, line or surface reading may be used. In surface reading, the light emitted from the light emitting light source illuminates the face of the bill, and the phototransistor of the light receiving unit can be read on the surface like a CCD incorporated in a digital camera. In this case, if the infrared excitation infrared emission layer 12 is a number or a barcode, the information can also be read. In reading on the line, for example, if the gift certificate having the
（ラベル）図２に示すように、基材１１と、該基材１１の一方の面へ偽造防止構造１０及び粘着層２９をこの順に設け、基材１１／赤外励起赤外発光層１２／ホログラム層１５／反射層１７／粘着層２９の層構成となる偽造防止構造１０を有する粘着ラベルである。該粘着ラベルによれば、赤外励起赤外発光層１２を機械読取しての真偽判定と、ホログラム層１５によってホログラムの目視による真偽判定とで、機械読取と目視の両方での真偽判定をすることができる。
(Label) As shown in FIG. 2, a base material 11 and an
（基材）基材１１としては、透明又は半透明であれば、用途に応じて種々の材料が適用できる。例えば、ポリエチレンテレフタレート、ポリエチレンナフタレートなどのポリエステル系樹脂、ナイロン６などのポリアミド系樹脂、ポリエチレン、ポリプロピレン、ポリメチルペンテンなどのポリオレフィン系樹脂、ポリ塩化ビニルなどのビニル系樹脂、ポリメチルメタアクリレートなどのアクリル系樹脂、ポリカーボネート、セロファン、セルロースアセテートなどのセルロース系フィルムなどが例示できる。該基材１１は、これら樹脂を主成分とする共重合樹脂、または、混合体（アロイを含む）、若しくは複数層からなる積層体であっても良い。また、該基材は、延伸フィルムでも、未延伸フィルムでも良いが、強度を向上させる目的で、一軸方向または二軸方向に延伸したフィルムが好ましい。該基材は、これら樹脂の少なくとも１層からなるフィルム、シート、ボード状として使用する。該基材は、塗布に先立って塗布面へ、コロナ放電処理、プラズマ処理、オゾン処理、フレーム処理、プライマー（アンカーコート、接着促進剤、易接着剤とも呼ばれる）塗布処理、予熱処理、除塵埃処理、蒸着処理、アルカリ処理、などの易接着処理を行ってもよい。また、必要に応じて、充填剤、可塑剤、着色剤、帯電防止剤などの添加剤を加えても良い。 (Substrate) As the substrate 11, various materials can be applied depending on the use as long as it is transparent or translucent. For example, polyester resins such as polyethylene terephthalate and polyethylene naphthalate, polyamide resins such as nylon 6, polyolefin resins such as polyethylene, polypropylene and polymethylpentene, vinyl resins such as polyvinyl chloride, polymethyl methacrylate, etc. Examples thereof include cellulose films such as acrylic resin, polycarbonate, cellophane, and cellulose acetate. The substrate 11 may be a copolymer resin containing these resins as a main component, a mixture (including an alloy), or a laminate including a plurality of layers. The substrate may be a stretched film or an unstretched film, but a film stretched in a uniaxial direction or a biaxial direction is preferable for the purpose of improving the strength. The substrate is used as a film, sheet or board formed of at least one layer of these resins. Prior to application, the substrate is subjected to corona discharge treatment, plasma treatment, ozone treatment, flame treatment, primer (also called an anchor coat, adhesion promoter, or easy adhesive) application treatment, pre-heat treatment, dust removal treatment. Alternatively, easy adhesion treatment such as vapor deposition treatment or alkali treatment may be performed. Moreover, you may add additives, such as a filler, a plasticizer, a coloring agent, and an antistatic agent, as needed.
（粘着層）粘着層２９としては、公知の感圧で接着する粘着剤が適用できる。粘着剤としては、特に限定されるものではなく、例えば、天然ゴム系、合成ゴム系樹脂、シリコーン系樹脂、アクリル系樹脂、酢酸ビニール系樹脂、ウレタン系樹脂、アクリロニトリル、炭化水素樹脂、アルキルフェノール樹脂、ロジン系樹脂が適用できる。 (Adhesive layer) As the adhesive layer 29, a pressure-sensitive adhesive that adheres with a known pressure sensitivity can be applied. The adhesive is not particularly limited. For example, natural rubber, synthetic rubber resin, silicone resin, acrylic resin, vinyl acetate resin, urethane resin, acrylonitrile, hydrocarbon resin, alkylphenol resin, A rosin resin is applicable.
（粘着層の形成）これらの樹脂、またはこれらの混合物を、ラテックス、水分散液、または有機溶媒液として、スクリーン印刷またはコンマコートなどの、公知の印刷またはコーティング法で、印刷または塗布し乾燥すれば良い。また、粘着層２９は、全面でなく一部分に形成しても良い。また、粘着剤の粘着力や凝集力は、用途や対象に合わせて適宜選定することができる。必要に応じて、粘着層２９面へ、上質紙・コート紙・含浸紙・プラスチックフィルムなどの基材の片面に離型層を有して剥離紙（セパレート紙、セパ紙とも呼ばれる）を剥離可能に積層してもよい。 (Formation of adhesive layer) These resins, or a mixture thereof, can be printed, applied or dried as a latex, aqueous dispersion, or organic solvent by a known printing or coating method such as screen printing or comma coating. It ’s fine. Further, the adhesive layer 29 may be formed on a part rather than the entire surface. Moreover, the adhesive force and cohesive force of an adhesive can be suitably selected according to a use and object. If necessary, release paper (also called separate paper or separate paper) can be peeled off by having a release layer on one side of the base material such as high-quality paper, coated paper, impregnated paper, and plastic film on the adhesive layer 29 May be laminated.
（変形形態）また、粘着ラベル形状では、図３に示すように、基材１１を、赤外励起赤外発光層１２と、ホログラム層１５及び反射層１７との間に積層して、赤外励起赤外発光層１２／基材１１／ホログラム層１５／反射層１７／粘着層２９の層構成としてもよい。また、粘着層２９を設けず単なるラベルでもよく、現物に添付したり、貼着したり、包装内へ封入すればよい。該ラベルでも、赤外励起赤外発光層１２を機械読取しての真偽判定と、ホログラム層１５によって、ホログラムの目視による真偽判定とで、機械読取と目視の両方での真偽判定をすることができる。 (Modification) In the adhesive label shape, as shown in FIG. 3, the base 11 is laminated between the infrared excitation infrared emission layer 12, the hologram layer 15 and the reflection layer 17. It is good also as a layer structure of excitation infrared light emitting layer 12 / base material 11 / hologram layer 15 / reflection layer 17 / adhesion layer 29. Moreover, a simple label may be used without providing the adhesive layer 29, and it may be attached to the actual product, adhered, or enclosed in a package. Even for the label, the true / false determination by mechanical reading of the infrared excitation infrared light emitting layer 12 and the true / false determination by visual observation of the hologram by the hologram layer 15 can be performed by both the mechanical reading and visual verification. can do.
（転写箔）図４に示すように、転写基材２１と、該転写基材２１の一方の面へ剥離層１３、偽造防止構造１０及び接着層１９とをこの順に設けると、偽造防止構造１０を有する転写箔となる。該転写箔を用いて、被転写体へ転写すれば、赤外励起赤外発光層１２を機械読取しての真偽判定と、ホログラム層１５によって、ホログラムの目視による真偽判定とで、機械読取と目視の両方での真偽判定をすることができる被転写体となる。
(Transfer foil) As shown in FIG. 4, when a transfer base 21 and a release layer 13, an
（転写基材）転写基材２１としては、耐熱性、機械的強度、製造に耐える機械的強度、耐溶剤性などがあれば、用途に応じて種々の材料が適用できる。例えば、ポリエチレンテレフタレート、ポリエチレンナフタレートなどのポリエステル系樹脂、ナイロン６などのポリアミド系樹脂、ポリエチレン、ポリプロピレン、ポリメチルペンテンなどのポリオレフィン系樹脂、ポリ塩化ビニルなどのビニル系樹脂、ポリメチルメタアクリレートなどのアクリル系樹脂、ポリカーボネート、セロファン、セルロースアセテートなどのセルロース系フィルム、などがある。好ましくは、耐熱性、機械的強度の点で、ポリエチレンテレフタレート、ポリエチレンナフタレートなどのポリエステル系樹脂のフィルムで、ポリエチレンテレフタレートが最適である。該基材の厚さは、通常、２．５μｍ〜１００μｍ程度が適用できるが、４μｍ〜５０μｍが転写性の点で好ましい。 (Transfer Base Material) As the transfer base material 21, various materials can be applied depending on the use as long as they have heat resistance, mechanical strength, mechanical strength to withstand manufacturing, and solvent resistance. For example, polyester resins such as polyethylene terephthalate and polyethylene naphthalate, polyamide resins such as nylon 6, polyolefin resins such as polyethylene, polypropylene and polymethylpentene, vinyl resins such as polyvinyl chloride, polymethyl methacrylate, etc. Examples include acrylic resins, polycarbonate, cellophane, and cellulose films such as cellulose acetate. Preferably, in terms of heat resistance and mechanical strength, polyethylene terephthalate is the most suitable for polyester resin films such as polyethylene terephthalate and polyethylene naphthalate. The thickness of the substrate is usually about 2.5 μm to 100 μm, but 4 μm to 50 μm is preferable in terms of transferability.
該転写基材２１は、これら樹脂を主成分とする共重合樹脂、または、混合体（アロイを含む）、若しくは複数層からなる積層体であっても良い。また、該基材は、延伸フィルムでも、未延伸フィルムでも良いが、強度を向上させる目的で、一軸方向または二軸方向に延伸したフィルムが好ましい。該基材は、これら樹脂の少なくとも１層からなるフィルム、シート、ボード状として使用する。該基材は、塗布に先立って塗布面へ、コロナ放電処理、プラズマ処理、オゾン処理、フレーム処理、プライマー（アンカーコート、接着促進剤、易接着剤とも呼ばれる）塗布処理、予熱処理、除塵埃処理、蒸着処理、アルカリ処理、などの易接着処理を行ってもよい。また、必要に応じて、充填剤、可塑剤、着色剤、帯電防止剤などの添加剤を加えても良い。 The transfer substrate 21 may be a copolymer resin containing these resins as a main component, a mixture (including an alloy), or a laminate composed of a plurality of layers. The substrate may be a stretched film or an unstretched film, but a film stretched in a uniaxial direction or a biaxial direction is preferable for the purpose of improving the strength. The substrate is used as a film, sheet or board formed of at least one layer of these resins. Prior to application, the substrate is subjected to corona discharge treatment, plasma treatment, ozone treatment, flame treatment, primer (also called an anchor coat, adhesion promoter, or easy adhesive) application treatment, pre-heat treatment, dust removal treatment. Alternatively, easy adhesion treatment such as vapor deposition treatment or alkali treatment may be performed. Moreover, you may add additives, such as a filler, a plasticizer, a coloring agent, and an antistatic agent, as needed.
（剥離層）剥離層１３としては、離型性樹脂、離型剤を含んだ樹脂、電離放射線で架橋する硬化性樹脂などがあるが、好ましくはメラミン系樹脂を用いる。該メラミン系樹脂を用いることで、後述するホログラム層１５との組合わせで安定した剥離性を発揮する。 (Peeling layer) The peeling layer 13 includes a release resin, a resin containing a release agent, and a curable resin that is cross-linked by ionizing radiation. Preferably, a melamine resin is used. By using the melamine resin, stable releasability is exhibited in combination with the hologram layer 15 described later.
剥離層１３の形成は、該樹脂を溶媒へ分散又は溶解して、ロールコート、グラビアコート、コンマコート、プレーコートなどの印刷又はコーティング方法で、少なくとも１部に塗布し乾燥して塗膜を形成する。また、要すれば、温度３０℃〜１２０℃で加熱乾燥、あるいはエージングしてもよい。離型層１３の厚さとしては、通常は０．０１μｍ〜５μｍ程度、好ましくは０．５μｍ〜３μｍ程度である。該厚さは薄ければ薄い程良いが、０．１μｍ以上であればより良い成膜が得られて剥離力が安定する。 The release layer 13 is formed by dispersing or dissolving the resin in a solvent and applying it to at least one part by a printing or coating method such as roll coating, gravure coating, comma coating, play coating, etc., and drying to form a coating film. To do. Further, if necessary, it may be heat-dried or aged at a temperature of 30 ° C. to 120 ° C. The thickness of the release layer 13 is usually about 0.01 μm to 5 μm, preferably about 0.5 μm to 3 μm. The thinner the thickness is, the better. However, when the thickness is 0.1 μm or more, better film formation is obtained and the peeling force is stabilized.
（接着層）接着層１９としては、公知の加熱されると溶融または軟化して接着効果を発揮する感熱接着剤が適用でき、具体的には、ポリオレフィン系樹脂、塩化ビニル系樹脂、酢酸ビニル系樹脂、塩化ビニル酢酸ビニル共重合樹脂、アクリル系樹脂、ポリエステル系樹脂などが挙げられる。該接着層１９には、マイクロシリカなどのフィラーを含むことが、箔切れ性の点で好ましい。また、接着層１９の樹脂としては、９５℃程度の低温で溶融接着し、６０℃程度になると固化して接着する融点が６０〜９５℃ものが好ましい。融点が上記範囲未満であると、支持体との接着性が不十分であり、形成された画像を使用する温度が制限される。また、融点が上記範囲を越えるとサーマルヘッドによる加熱では転写性が不十分となり、又、ハードコート層の箔切れ性が低下し、解像性の良い転写が困難となる。該材料樹脂を溶剤に溶解または分散させて、適宜顔料などの添加剤を添加して、公知のロールコーティング、グラビアコーティング、コンマコーティングなどの方法で塗布し乾燥させて、厚さ１〜３０μｍの層を得る。 (Adhesive layer) As the adhesive layer 19, a heat-sensitive adhesive which melts or softens when heated and exhibits an adhesive effect can be applied. Specifically, polyolefin resin, vinyl chloride resin, vinyl acetate Examples thereof include resins, vinyl chloride vinyl acetate copolymer resins, acrylic resins, polyester resins, and the like. The adhesive layer 19 preferably contains a filler such as microsilica in terms of the ability to break the foil. Further, the resin of the adhesive layer 19 is preferably one having a melting point of 60 to 95 ° C. which melts and adheres at a low temperature of about 95 ° C. and solidifies and adheres at about 60 ° C. When the melting point is less than the above range, the adhesion to the support is insufficient, and the temperature at which the formed image is used is limited. On the other hand, if the melting point exceeds the above range, the transferability becomes insufficient by heating with a thermal head, the foil breakability of the hard coat layer is lowered, and transfer with good resolution becomes difficult. The material resin is dissolved or dispersed in a solvent, an additive such as a pigment is added as appropriate, and the layer is applied and dried by a known method such as roll coating, gravure coating, comma coating, etc. Get.
（被転写体）上記の偽造防止構造１０を有する転写箔を用いて、被転写体へ前記偽造防止構造１０及び前記接着層１９を転写すれば、偽造防止構造１０を有する被転写体となる。該偽造防止構造１０を有する被転写体によれば、赤外励起赤外発光層１２を機械読取しての真偽判定と、ホログラム層１５によって、ホログラムの目視による真偽判定とで、機械読取と目視の両方での真偽判定をすることができる。
(Transfer To be Transferred) If the transfer
（被転写体）被転写体としては特に限定されず、例えば天燃繊維紙、コート紙、トレーシングペーパー、転写時の熱で変形しないプラスチックフイルム、ガラス、金属、セラミックス、木材、布あるいは染料受容性のある媒体等いずれのものでもよい。また、被転写体の媒体はその少なくとも１部が着色、印刷、その他の加飾が施されていてもよく、印刷、その他の加飾を施してもよい。 (Transfer material) The transfer material is not particularly limited, for example, natural fiber paper, coated paper, tracing paper, plastic film that does not deform by heat during transfer, glass, metal, ceramics, wood, cloth or dye acceptance Any medium may be used. Further, at least a part of the medium of the transfer medium may be colored, printed, or other decoration, or may be subjected to printing or other decoration.
（転写）被転写体への転写は、公知の転写法でよく、例えば、熱刻印によるホットスタンプ（箔押）、熱ロールによる全面又はストライプ転写、サーマルヘッド（感熱印画ヘッド）による熱転写プリンタなどの公知の方法が適用できる。スポット状、文字、数字、イラストなどの任意の形状を転写してもよい。 (Transfer) The transfer to the transfer object may be performed by a known transfer method, such as hot stamping by hot stamping (foil stamping), whole surface or stripe transfer by a heat roll, thermal transfer printer by a thermal head (thermal printing head), etc. Known methods can be applied. Any shape such as a spot shape, letters, numbers, and illustrations may be transferred.
（偽造防止用紙）図５に示すように、偽造防止構造１０を、基紙へ抄き込んでなることを特徴とする偽造防止構造１０を有する偽造防止用紙となる。該偽造防止構造１０を有する用紙によれば、赤外励起赤外発光層１２を機械読取しての真偽判定と、ホログラム層１５によって、ホログラムの目視による真偽判定とで、機械読取と目視の両方での真偽判定ができる効果を奏する偽造防止構造を有する偽造防止用紙を提供する。
(Counterfeit Prevention Paper) As shown in FIG. 5, the
（基紙）本発明の偽造防止構造を有する偽造防止用紙の基紙としては、表面平滑性および耐熱性に優れ、適当な強度、厚さを有するものであれば、特に制限はないが、上質紙等の洋紙、薄手の板紙、カード紙等の紙が適用できる。１００〜２００ｇ／ｍ2の坪量で、印字、転写適性に優れる上質紙、コート紙が好ましい。 (Base paper) The base paper of the anti-counterfeit paper having the anti-counterfeit structure of the present invention is not particularly limited as long as it is excellent in surface smoothness and heat resistance and has appropriate strength and thickness. Paper such as paper, thin paperboard, card paper, etc. can be applied. High-quality paper and coated paper having a basis weight of 100 to 200 g / m 2 and excellent printability and transferability are preferred.
（抄紙）基紙へ、スレッドを抄き込んで製造する。即ち、針葉樹晒クラフトパルプ（ＮＢＫＰ）、広葉樹晒クラフトパルプ（ＬＢＫＰ）、針葉樹晒サルファィトパルプ（ＮＢＳＰ）、サーモメカニカルパルプ（ＴＭＰ）等の木材パルプや麻、綿、藁を原料とした非木材パルプ等を適宜混合して叩解し、これに填料、乾燥紙力増強剤、湿潤紙力増強剤、サイズ剤、定着剤、歩留り向上剤、濾水性向上剤、消泡剤、染料、着色顔料、蛍光剤などを適宜添加し、通常フリーネス４００〜２５０ｍｌＣ．Ｓ．Ｆ．に調整した紙料を調製する。該紙料へ、狭い幅のスレッドを繰り出しながら、長網抄紙機や円網抄紙機などの公知の抄紙機を使用して抄き込んで製造し、必要に応じてマシンカレンダー、スーパーカレンダー処理をする。前述のように、スレッドは、必要に応じて、基紙中へ埋没、半分埋め込み、表面上でもよく、また、基紙の表面に部分的に露出させた窓開きでもよい。 (Paper making) Manufactured by making threads on base paper. In other words, wood pulp such as softwood bleached kraft pulp (NBKP), hardwood bleached kraft pulp (LBKP), softwood bleached sulfite pulp (NBSP), thermomechanical pulp (TMP), etc. and non-wood pulp made from hemp, cotton, and straw Etc. are mixed and beaten appropriately, and this is filled with filler, dry paper strength enhancer, wet paper strength enhancer, sizing agent, fixing agent, yield improver, freeness improver, antifoaming agent, dye, coloring pigment, fluorescent A suitable freeness is usually added to 400 to 250 ml C.I. S. F. Prepare a paper stock adjusted to. The paper stock is manufactured by using a well-known paper machine such as a long paper machine or a circular paper machine while feeding a narrow-width thread, and machine calendar and super calendar processing is performed as necessary. To do. As described above, the thread may be embedded in the base paper, half-embedded, on the surface, or may be a window opening partially exposed on the surface of the base paper, as necessary.
（スレッド）上記の抄紙に用いるスレッドは、接着層１９又は粘着層２９を有しない層構成の偽造防止構造１０からなり、基紙へ抄き込めるように、細い幅にスリットしたものである。該スレッドの層構成は、例えば、基材１１／赤外励起赤外発光層１２／ホログラム層１５／反射層１７、赤外励起赤外発光層１２／基材１１／ホログラム層１５／反射層１７、赤外励起赤外発光層１２／反射層１／ホログラム層１５７／基材１１、の層構成が例示できる。
(Thread) The thread used for the paper making is composed of the
また、スレッドには、必要に応じて他の層を層間及び／又は表裏面に設けてもよい。また、図示しないが、スレッドの表面及び／又は裏面には、紙層との接着を向上させるため、接着剤層が積層されていてもよい。スレッドは、幅が０．３ｍｍ〜３０ｍｍ程度、好ましくは１ｍｍ〜１０ｍｍの幅のごく狭い糸状とも見えるテープ状の装飾片を意味し、基本的には紙層どうしが積層された間に適当な間隔で挿入される。 Moreover, you may provide another layer in an interlayer and / or front and back, as needed. Although not shown, an adhesive layer may be laminated on the front surface and / or back surface of the thread in order to improve the adhesion with the paper layer. The thread means a tape-like decorative piece that can be seen as a very narrow thread shape having a width of about 0.3 mm to 30 mm, preferably 1 mm to 10 mm. Basically, an appropriate interval between the paper layers is laminated. Is inserted.
（変形形態）前述した、偽造防止構造１０はもとより、ラベル、転写箔、スレッドなどのどの形態においても、反射層１７を円形や矩形などの幾何学模様、イラストなどの模様を有する部分反射層や、着色反射層としてもよい。
(Deformation) In addition to the
部分反射層とする方法は、エッチング加工、パスター加工などの公知の方法でよい。また、着色反射層とする方法は、薄膜金属として着色した金属、例えば、アンバー色の珪素、赤っぽい色の銅、金色の銅アルミニウム合金などを用いればよい。また、着色反射層を部分反射層とする場合には、着色反射層のない部分に透明反射層を設けてもよく、着色反射層のない部分は透明ホログラムが観察され、着色反射層の部分は着色ホログラムが観察される。 The method for forming the partially reflective layer may be a known method such as etching or paster. As a method for forming a colored reflective layer, a metal colored as a thin film metal, for example, amber silicon, reddish copper, gold copper aluminum alloy, or the like may be used. In addition, when the colored reflective layer is a partially reflective layer, a transparent reflective layer may be provided in a portion without the colored reflective layer, a transparent hologram is observed in the portion without the colored reflective layer, and the colored reflective layer portion is A colored hologram is observed.
以下、実施例及び比較例により、本発明を更に詳細に説明するが、これに限定されるものではない。なお、溶媒を除き、各層の各組成物は固形分換算の質量部である。 EXAMPLES Hereinafter, although an Example and a comparative example demonstrate this invention further in detail, it is not limited to this. In addition, except a solvent, each composition of each layer is a mass part of solid content conversion.
（実施例１）基材１１として厚さ２５μｍのＰＥＴフィルムを用い、該基材１１の一方の面へ、下記の赤外励起赤外発光インキを用いて、シルクスクリーン印刷法で、番号及びイラストを印刷し乾燥して、赤外励起赤外発光層１２とした。
・＜赤外励起赤外発光インキ＞
蛍光顔料 ＩＲＳ−Ｆ（根本特殊化学製） ０．５部
酢酸ビニル塩化ビニル共重合樹脂 １０部
ポリエステル系樹脂 １０部
溶媒（トルエン：酢酸エチル＝１：１） ８０部
次に、該赤外励起赤外発光層１２の面へ、下記の電離放射線硬化性樹脂組成物をグラビアリバースコーターで乾燥後の厚さが２μｍになるように、塗工し１００℃で乾燥させた。
・＜ホログラム層の電離放射線硬化性樹脂組成物＞
ＭＨＸ４０５ニス（ザ・インクテック社製、商品名） ８０部
紫光ＵＶ３５２０ＥＡ（日本合成化学社製、エステル単位含有、商品名）２０部
反応性シリコーン（信越化学社製、商品名Ｘ−２２−２４４５） ０．１５部
光重合開始剤（チバ社製、商品名イルガキュア１８４） ５部
溶媒（メチルイソブチルケトン：トルエン＝１：１） ３００部
次に、該層は電離放射線硬化前であり、塗膜は指乾状態であった。該層面へ、２光束干渉法による回折格子から２Ｐ法で複製した擬似連続絵柄としたプレス型を複製装置のエンボスローラーに貼着して、相対するローラーとの間で加熱プレス（エンボス）して、微細な凹凸パターンからなるレリーフを賦形させた。賦形後直ちに、高圧水銀灯を用いて紫外線を照射して硬化させて、ホログラム層１５を形成した。該ホログラム層１５のレリーフ面へ、厚さ２０ｎｍの酸化チタンをスパッタリング法で形成して透明な反射層１７とした。次に、透明な反射層１７の面へ、下記のプライマ層組成物をグラビアコーターで乾燥後の厚さが０．５μｍになるように、塗工し１００℃で乾燥させて、プライマ層とした。
・＜プライマ層の組成物＞
酢酸ビニル塩化ビニル共重合樹脂 １０部
ポリエステル系樹脂 １０部
溶媒（トルエン：酢酸エチル＝１：１） ８０部
次に、プライマ層面へ、粘着剤（ニッセツＰＥ−１１８＋ＣＫ１０１、日本カーバイド製）を、乾燥膜厚が２５ｇ／ｍ2になるようにロールコートで塗布し、１００℃で乾燥して溶剤を揮散させた後、剥離紙としてシリコーン処理ＰＥＴフイルム（ＳＰＯ５、東京セロファン紙社製）を貼合し、必要に応じて半抜きして、基材１１／赤外励起赤外発光層１２／ホログラム層１５／反射層１７／粘着層２９の層構成からなる偽造防止構造を有するラベルを得た。該偽造防止構造を有するラベルは、目視ではホログラムが観察されて真正であることが判り、かつ、赤外励起赤外発光層１２の番号とイラストを機械で読み取りすることができて、真正であることが判った。
Example 1 Using a PET film having a thickness of 25 μm as the base material 11, and using the following infrared excitation infrared light-emitting ink on one surface of the base material 11, numbers and illustrations were obtained by silk screen printing. Was printed and dried to obtain an infrared excitation infrared emission layer 12.
・ <Infrared excitation infrared emission ink>
Fluorescent pigment IRS-F (manufactured by Nemoto Special Chemical) 0.5 part Vinyl acetate vinyl
・ <Ionizing radiation curable resin composition of hologram layer>
MHX405 varnish (trade name, manufactured by The Inktec Co., Ltd.) 80 parts Purple light UV3520EA (manufactured by Nippon Synthetic Chemical Co., Ltd., containing ester units, product name) 20 parts reactive silicone (trade name: X-22-2445, manufactured by Shin-Etsu Chemical Co., Ltd.) 0.15 parts Photopolymerization initiator (trade name Irgacure 184, manufactured by Ciba) 5 parts Solvent (methyl isobutyl ketone: toluene = 1: 1) 300 parts Next, the layer is before ionizing radiation curing, and the coating film is The finger was dry. A press die having a pseudo continuous pattern duplicated by a 2P method from a diffraction grating by a two-beam interference method is attached to the layer surface on an embossing roller of a duplicating apparatus, and is heated and pressed (embossed) with an opposing roller. Then, a relief composed of a fine uneven pattern was formed. Immediately after the shaping, the hologram layer 15 was formed by irradiating and curing with ultraviolet rays using a high-pressure mercury lamp. Titanium oxide with a thickness of 20 nm was formed on the relief surface of the hologram layer 15 by a sputtering method to form a transparent reflective layer 17. Next, the following primer layer composition was applied to the surface of the transparent reflective layer 17 with a gravure coater so that the thickness after drying was 0.5 μm and dried at 100 ° C. to form a primer layer. .
・ <Primer layer composition>
Vinyl acetate Vinyl
（実施例２）基材１１として厚さ５０μｍのＰＥＴフィルムを用い、該基材１１の一方の面へ、グラビアコート法で、ＴＣＭ０１メジューム（大日本インキ社製、メラミン樹脂商品名）塗工液を乾燥後２μｍになるように塗布し乾燥して、１８０℃２０秒間焼き付けて、離型層１３を形成した。該離型層１３面へ、実施例１と同様に赤外励起赤外発光層１２を設け、さらに、電離放射線硬化性樹脂組成物の層を設け、該層面へ、２光束干渉法による回折格子から２Ｐ法で複製した擬似連続絵柄としたプレス型を複製装置のエンボスローラーに貼着して、相対するローラーとの間で加熱プレス（エンボス）して、微細な凹凸パターンからなるレリーフを賦形させた。賦形後直ちに、高圧水銀灯を用いて紫外線を照射して硬化させて、ホログラム層１５を形成した。該ホログラム層１５のレリーフ面へ、厚さ１００ｎｍのアルミニウムをスパッタリング法で形成して金属薄膜からなる反射層１７とした。次に、反射層１７の面へ、下記のプライマ層組成物をグラビアコーターで乾燥後の厚さが０．５μｍになるように、塗工し１００℃で乾燥させて、プライマ層とした。
・＜プライマ層の組成物＞
酢酸ビニル塩化ビニル共重合樹脂 １０部
ポリエステル系樹脂 １０部
溶媒（トルエン：酢酸エチル＝１：１） ８０部
次に、プライマ層の面へ、接着層組成物としてＴＭ−Ａ１ＨＳ（大日精化社製、商品名）をグラビアコーターで乾燥後の塗布量が１μｍになるように、塗工し１００℃で乾燥させて、接着層１９を形成して、基材１１／剥離層１３／赤外励起赤外発光層１２／ホログラム層１５／反射層１７／プライマ層／接着層１９の層構成からなる実施例２の偽造防止構造を有する転写箔を得た。該偽造防止構造を有する転写箔は、目視ではホログラムが観察されて真正であることが判り、かつ、赤外励起赤外発光層１２の番号とイラストを機械で読み取りすることができて、真正であることが判った。
Example 2 Using a PET film having a thickness of 50 μm as the base material 11, a TCM01 medium (Dainippon Ink Co., Ltd., melamine resin product name) coating solution is applied to one surface of the base material 11 by a gravure coating method. After being dried, it was applied to a thickness of 2 μm, dried, and baked at 180 ° C. for 20 seconds to form a release layer 13. An infrared excitation infrared light emitting layer 12 is provided on the surface of the release layer 13 in the same manner as in Example 1, and a layer of ionizing radiation curable resin composition is further provided on the surface of the release layer. 2P method is applied to the embossing roller of the duplicating machine, and a press die that is a quasi-continuous pattern is heat-pressed (embossed) with the opposite roller to form a relief with a fine uneven pattern. I let you. Immediately after the shaping, the hologram layer 15 was formed by irradiating and curing with ultraviolet rays using a high-pressure mercury lamp. On the relief surface of the hologram layer 15, aluminum having a thickness of 100 nm was formed by sputtering to form a reflective layer 17 made of a metal thin film. Next, the following primer layer composition was applied to the surface of the reflective layer 17 with a gravure coater so that the thickness after drying was 0.5 μm, and dried at 100 ° C. to obtain a primer layer.
・ <Primer layer composition>
Vinyl acetate vinyl
（実施例３）被転写体とした上質紙からなる商品券へ、実施例２の偽造防止構造を有する転写箔を用いて、偽造防止構造１０及び前記接着層１９を転写して偽造防止構造を有する被転写体（商品券）を得た。該商品券も、目視ではホログラムが観察されて真正であることが判り、かつ、赤外励起赤外発光層１２の番号とイラストを機械で読み取りすることができて、真正であることが判った。
(Example 3) A
本発明は、クレジットカード、キャッシュカードなどのカード類、株券、債券、小切手、商品券、宝くじ、定期券等の証券類に利用できる。しかしながら、セキュリティ性が高く、機械読取と目視の両方での真偽判定を必要とする用途であれば、特に限定されるものではない。 The present invention can be used for cards such as credit cards and cash cards, stock certificates, bonds, checks, gift certificates, lotteries, commuter passes, and other securities. However, it is not particularly limited as long as it has high security and requires an authenticity determination both by machine reading and visual observation.
１０：偽造防止構造
１１：基材
１２：赤外励起赤外発光層
１３：剥離層
１５：ホログラム層
１７：反射層
１９：接着層
２１：転写基材
２９：粘着層
10: Anti-counterfeit structure 11: Base material 12: Infrared excitation infrared light emitting layer 13: Release layer 15: Hologram layer 17: Reflective layer 19: Adhesive layer 21: Transfer base material 29: Adhesive layer
Claims (5)
前記赤外励起赤外発光層が赤外線波長領域の励起光を照射された際の発光光が赤外波長領域の発光光であり、
前記ホログラム層の前記反射層の面が微細な凹凸からなるレリーフホログラムであり、
前記反射層が金属反射層又は透明反射層であり、
前記偽造防止構造がホログラムとして目視でき、かつ前記赤外励起赤外発光層が機械読み取り可能であることを特徴とする偽造防止構造。 At least an anti-counterfeit structure including an infrared excitation infrared emission layer, and a hologram layer and a reflective layer in contact with the hologram layer,
The emitted light when the infrared excitation infrared emission layer is irradiated with excitation light in the infrared wavelength region is emitted light in the infrared wavelength region,
A relief hologram comprising a surface of the reflection layer of the hologram layer having fine irregularities;
The reflective layer is a metal reflective layer or a transparent reflective layer;
An anti-counterfeit structure, wherein the anti-counterfeit structure is visible as a hologram, and the infrared excitation infrared emission layer is machine-readable.