JP2013091807A - 架橋性ゴム組成物およびゴム架橋物 - Google Patents
架橋性ゴム組成物およびゴム架橋物 Download PDFInfo
- Publication number
- JP2013091807A JP2013091807A JP2013008371A JP2013008371A JP2013091807A JP 2013091807 A JP2013091807 A JP 2013091807A JP 2013008371 A JP2013008371 A JP 2013008371A JP 2013008371 A JP2013008371 A JP 2013008371A JP 2013091807 A JP2013091807 A JP 2013091807A
- Authority
- JP
- Japan
- Prior art keywords
- rubber
- rubber composition
- ethylenically unsaturated
- nitrile
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】α,β−エチレン性不飽和ニトリル単量体単位およびα,β−エチレン性不飽和ジカルボン酸モノエステル単量体単位を有し、ヨウ素価が120以下であるニトリルゴム100重量部に対し、アミノ基以外の極性基を有しない第一級モノアミン0.1〜20重量部、および、ポリアミン系架橋剤0.1〜20重量部を含有してなる架橋性ゴム組成物。
【選択図】 なし
Description
α,β−エチレン性不飽和ニトリル単量体単位およびα,β−エチレン性不飽和ジカルボン酸モノエステル単量体単位を有し、ヨウ素価が120以下であるニトリルゴム(A1)100重量部に対し、芳香族第二級アミン系老化防止剤(A2)0.2〜10重量部、および、ポリアミン系架橋剤(A3)0.2〜20重量部を含有してなる架橋性ゴム組成物が提供される。
第1の観点において、好ましくは、前記架橋性ゴム組成物のコンパウンドムーニー粘度ML1+4(100℃)が15〜200である。
第1の観点において、好ましくは、前記架橋性ゴム組成物が、25%圧縮した状態で150℃、504時間保持した後におけるO−リング圧縮永久ひずみが71%以下であるゴム架橋物を与えるものである。
α,β−エチレン性不飽和ニトリル単量体単位およびα,β−エチレン性不飽和ジカルボン酸モノエステル単量体単位を有し、ヨウ素価が120以下であるニトリルゴム(B1)100重量部に対し、アミノ基以外の極性基を有しない第一級モノアミン(B2)0.1〜20重量部、および、ポリアミン系架橋剤(B3)0.1〜20重量部を含有してなる架橋性ゴム組成物が提供される。
ニトリル基含有高飽和共重合体ゴム(C1)、ポリオキシアルキレンアルキルエーテルリン酸エステル(C2)およびポリアミン系架橋剤(C3)を含有してなる架橋性ゴム組成物が提供される。
α,β−エチレン性不飽和ジカルボン酸モノエステル単量体単位を有するニトリル基含有高飽和共重合体ゴム(D1)およびα,β−エチレン性不飽和ジカルボン酸モノエステル単量体単位を有するアクリルゴム(D2)の合計100重量部に対して、ポリアミン系架橋剤(D3)0.2〜20重量部を含有してなる架橋性ゴム組成物が提供される。
第4の観点において、好ましくは、前記ニトリル基含有高飽和共重合体ゴム(D1)および前記アクリルゴム(D2)の重量比が5/95〜95/5である。
第4の観点において、好ましくは、前記架橋性ゴム組成物が、25%圧縮した状態で150℃、168時間保持した後におけるO−リング圧縮永久ひずみが40%以下のゴム架橋物を与えるものである。
第4の観点において、好ましくは、前記架橋性ゴム組成物が、さらに塩基性架橋促進剤(D4)0.5〜10重量部を含有してなるものである。
まず、本発明の第1の観点に係る実施形態である第1実施形態について、説明する。
本発明の第1の観点に係る架橋性ゴム組成物は、α,β−エチレン性不飽和ニトリル単量体単位およびα,β−エチレン性不飽和ジカルボン酸モノエステル単量体単位を有し、ヨウ素価が120以下であるニトリルゴム(A1)100重量部に対し、芳香族第二級アミン系老化防止剤(A2)0.2〜10重量部、および、ポリアミン系架橋剤(A3)0.2〜20重量部を含有してなるものである。
以下、第1の観点(第1実施形態)においては、上記α,β−エチレン性不飽和ジカルボン酸モノエステル単量体単位を有し、ヨウ素価が120以下であるニトリルゴム(A1)を、「ニトリルゴム(A1)」と略記することがある。
ニトリルゴム(A1)のα,β−エチレン性不飽和ニトリル単量体単位を形成する単量体(α,β−エチレン性不飽和ニトリル単量体)は、ニトリル基を有するα,β−エチレン性不飽和化合物であれば限定されない。このような化合物としては、アクリロニトリル;α−クロロアクリロニトリル、α−ブロモアクリロニトリルなどのα−ハロゲノアクリロニトリル;メタクリロニトリルなどのα−アルキルアクリロニトリル;などが挙げられる。これらのなかでも、アクリロニトリルおよびメタクリロニトリルが好ましい。α,β−エチレン性不飽和ニトリルはこれらの複数種を併用してもよい。
ニトリルゴム(A1)に、α,β−エチレン性不飽和ジカルボン酸モノエステル単量体単位を含有させるための好ましい方法としては、上記α,β−エチレン性不飽和ニトリルにα,β−エチレン性不飽和ジカルボン酸モノエステルを共重合させる方法などが挙げられる。
共重合して得られた共重合体のヨウ素価が上記の範囲より高い場合は、共重合体の水素化(水素添加反応)を行うと良い。水素化の方法は特に限定されず、公知の方法を採用すればよい。
第1の観点に係る架橋性ゴム組成物は、上記ニトリルゴム(A1)に加えて、芳香族第二級アミン系老化防止剤(A2)を含有する。
第1の観点に係る架橋性ゴム組成物は、上記ニトリルゴム(A1)のカルボキシル基を架橋するために架橋剤として、ポリアミン系架橋剤(A3)をさらに含有する。ポリアミン系架橋剤(A3)は、(1)2つ以上のアミノ基を有する化合物、または、(2)架橋時に2つ以上のアミノ基を有する化合物の形態になるもの、であれば特に限定されないが、脂肪族炭化水素や芳香族炭化水素の複数の水素が、アミノ基またはヒドラジド構造(「−CONHNH2」で表される構造、COはカルボニル基を表す。)で置換された化合物が好ましい。ポリアミン系架橋剤(A3)の具体例としては、ヘキサメチレンジアミン、ヘキサメチレンジアミンカルバメート、テトラメチレンペンタミン、ヘキサメチレンジアミン−シンナムアルデヒド付加物、ヘキサメチレンジアミン−ジベンゾエート塩などの脂肪族多価アミン類;2,2−ビス{4−(4−アミノフェノキシ)フェニル}プロパン、4,4’−メチレンジアニリン、m−フェニレンジアミン、p−フェニレンジアミン、4,4’−メチレンビス(o−クロロアニリン)などの芳香族多価アミン類;イソフタル酸ジヒドラジド、アジピン酸ジヒドラジド、セバシン酸ジヒドラジドなどのヒドラジド構造を2つ以上有する化合物;などが挙げられる。このれらのなかでも、脂肪族多価アミン類が好ましく、ヘキサメチレンジアミンカルバメートが特に好ましい。
ポリアミン系架橋剤(A3)に代えて、他の架橋剤である多価エポキシ化合物、多価イソシアナート化合物、アジリジン化合物、塩基性金属酸化物、有機金属ハロゲン化物、および有機過酸化物などを用いた場合には、本発明(第1の観点に係る発明)の効果が得難くなる。
第1の観点に係る架橋性ゴム組成物には、上記ニトリルゴム(A1)、芳香族第二級アミン系老化防止剤(A2)およびポリアミン系架橋剤(A3)以外に、ゴム加工分野において通常使用される配合剤、例えば、カーボンブラックやシリカなどの補強性充填材、炭酸カルシウムやクレーなどの非補強性充填材、酸化防止剤、光安定剤、一級アミンなどのスコーチ防止剤、可塑剤、加工助剤、滑剤、粘着剤、潤滑剤、難燃剤、防黴剤、帯電防止剤、着色剤、硫黄架橋剤、有機過酸化物架橋剤、架橋促進剤、架橋助剤、架橋遅延剤などを配合することができる。これらの配合剤の配合量は、本発明の目的や効果を阻害しない範囲であれば特に限定されず、配合目的に応じた量を適宜配合することができる。
次に、本発明の第2の観点に係る実施形態である第2実施形態について、説明する。
本発明の第2の観点に係る架橋性ゴム組成物は、α,β−エチレン性不飽和ニトリル単量体単位およびα,β−エチレン性不飽和ジカルボン酸モノエステル単量体単位を有し、ヨウ素価が120以下であるニトリルゴム(B1)100重量部に対し、アミノ基以外の極性基を有しない第一級モノアミン(B2)0.1〜20重量部、および、ポリアミン系架橋剤(B3)0.1〜20重量部を含有してなるものである。
以下、第2の観点(第2実施形態)においては、上記α,β−エチレン性不飽和ジカルボン酸モノエステル単量体単位を有し、ヨウ素価が120以下であるニトリルゴム(B1)を、「ニトリルゴム(B1)」と略記することがある。
ニトリルゴム(B1)としては、上述の第1の観点におけるニトリルゴム(A1)と同様のものを使用することができる。
第2の観点に係る架橋性ゴム組成物に含有される、アミノ基以外の極性基を有しない第一級モノアミン(B2)〔以下、単に「第一級モノアミン(B2)」と記すことがある。〕は、一つの炭化水素残基と二つの水素原子とが窒素原子に結合してなるモノアミン化合物であって、該炭化水素残基が、たとえば、他のアミノ基、イミノ基、水酸基、アルコキシ基、カルボキシル基、エステル基、カルボニル基、ホルミル基、ニトロ基、ニトリル基、ハロゲン基などの極性基を有しないものである。炭化水素残基がアミノ基を二以上有したり、アミノ基以外の極性基を持つと本発明(第2の観点に係る発明)の効果が得難くなる。
第一級モノアミン(B2)の好適な具体例としては、ノナデシルアミン、オクタデシルアミン、ヘキサデシルアミン、トリデシルアミン、デシルアミン、オクチルアミンなどが挙げられるが、オクタデシルアミンが特に好ましい。
ポリアミン系架橋剤(B3)としては、上述の第1の観点におけるポリアミン系架橋剤(A3)と同様のものを使用することができる。
第2の観点においては、ポリアミン系架橋剤(B3)の含有量は、ニトリルゴム(B1)100重量部に対して、0.1〜20重量部、好ましくは0.3〜15重量部、より好ましくは0.5〜10重量部である。架橋性ゴム組成物における(B3)成分の含有量が少なすぎると、得られるゴム架橋物の圧縮永久ひずみが増加する傾向にある。逆に、多すぎると得られるゴム架橋物の耐疲労性が低下する可能性がある。
第2の観点に係る架橋性ゴム組成物には、上記ニトリルゴム(B1)、第一級モノアミン(B2)およびポリアミン系架橋剤(B3)以外に、ゴム加工分野において、通常使用される配合剤を適宜配合することができる。このような配合剤としては、上述の第1の観点と同様なものが使用できる。また、同様に、第2の観点に係る架橋性ゴム組成物には、本発明の目的や効果を阻害しない範囲であればニトリルゴム(B1)以外のゴムを配合してもよい。この場合の配合量も上述の第1の観点と同様とすれば良い。
特に、第2の観点によれば、繊維含浸体や金属複合体以外のバルクのゴム製品において、十分な引張強さ、引張応力などの機械的強度と伸びを有し、圧縮永久ひずみが小さい効果が活かされる。
次に、本発明の第3の観点に係る実施形態である第3実施形態について、説明する。
本発明の第3の観点に係る架橋性ゴム組成物は、ニトリル基含有高飽和共重合体ゴム(C1)、ポリオキシアルキレンアルキルエーテルリン酸エステル(C2)およびポリアミン系架橋剤(C3)を含有してなるものである。
以下、第3の観点(第3実施形態)においては、上記ニトリル基含有高飽和共重合体ゴム(C1)を、「高飽和ニトリルゴム(C1)」と略記することがある。
高飽和ニトリルゴム(C1)のニトリル基を形成するための好ましい態様としては、該ゴムがα,β−エチレン性不飽和ニトリル単量体単位を有する態様である。
α,β−エチレン性不飽和ニトリル単量体単位を形成する単量体としては、ニトリル基を有するα,β−エチレン性不飽和化合物であれば限定されないが、たとえば、上述の第1の観点におけるニトリルゴム(A1)と同様なものが使用できる。また、α,β−エチレン性不飽和ニトリル単量体単位の含有量も、上述の第1の観点と同様とすれば良い。
ジエン系単量体単位およびα−オレフィン単量体単位を形成するジエン系単量体およびα−オレフィン単量体としては、上述の第1の観点におけるニトリルゴム(A1)と同様なものが使用できる。また、これらの単量体単位の含有量も、上述の第1の観点と同様とすれば良い。
高飽和ニトリルゴム(C1)に、カルボキシル基を含有させるための好ましい態様としては、該ゴムの分子構造がα,β−エチレン性不飽和カルボン酸単量体単位、α,β−エチレン性不飽和ジカルボン酸モノエステル単量体単位またはα,β−エチレン性不飽和ジカルボン酸単量体単位を有する態様であり、より好ましくは、α,β−エチレン性不飽和ジカルボン酸モノエステル単量体単位を有する態様である。
そして、高飽和ニトリルゴム(C1)に、上述のより好ましい態様としてのα,β−エチレン性不飽和ジカルボン酸モノエステル単量体単位を含有させるための好ましい方法としては、上記α,β−エチレン性不飽和ニトリル単量体にα,β−エチレン性不飽和ジカルボン酸モノエステル単量体を共重合させる方法などが挙げられる。
上記α,β−エチレン性不飽和ジカルボン酸モノエステル単量体としては、たとえば、上述の第1の観点におけるニトリルゴム(A1)と同様なものが使用できる。また、α,β−エチレン性不飽和ジカルボン酸モノエステル単量体単位の含有量も、上述の第1の観点と同様とすれば良い。
第3の観点に係る架橋性ゴム組成物には、上述の高飽和ニトリルゴム(C1)に加えて、ポリオキシアルキレンアルキルエーテルリン酸エステル(C2)が含有される。ポリオキシアルキレンアルキルエーテルリン酸エステル(C2)は、ポリオキシアルキレンアルキルエーテル基を含有するリン酸モノエステル、ジエステルもしくはトリエステルであり、これらの混合物であっても良い。
これらの中でも、耐熱老化性の改善および圧縮永久ひずみ減少の観点から、下記一般式(1)で示される化学構造を有するものが好ましい。
第3の観点に係る架橋性ゴム組成物は、架橋物を形成するための架橋剤として、ポリアミン系架橋剤(C3)を含有することが好ましい。
ポリアミン系架橋剤(C3)としては、上述の第1の観点におけるポリアミン系架橋剤(A3)と同様のものが使用できる。また、ポリアミン系架橋剤(C3)の含有量は、高飽和ニトリルゴム(C1)100重量部に対して、好ましくは0.1〜20重量部、より好ましくは0.2〜15重量部、特に好ましくは0.3〜10重量部である。ポリアミン系架橋剤(C3)が少なすぎると、得られるゴム架橋物の架橋が不足して機械的強度の低下や圧縮永久ひずみの増大が起きるおそれがあり、逆に、多すぎると伸びが低下する可能性がある。
ジアルキルパーオキシド類としては、ジクミルパーオキシド、ジ−t−ブチルパーオキシド、2,5−ジメチル−2,5−ジ(t−ブチルパーオキシ)−3−ヘキシン、2,5−ジメチル−2,5−ジ(t−ブチルパーオキシ)ヘキサン、1,3−ビス(t−ブチルパーオキシイソプロピル)ベンゼンなどが挙げられる。ジアシルパーオキシド類としては、ベンゾイルパーオキシド、イソブチリルパーオキシドなどが挙げられる。パーオキシエステル類としては、2,5−ジメチル−2,5−ビス(ベンゾイルパーオキシ)ヘキサン、t−ブチルパーオキシイソプロピルカーボネートなどが挙げられる。
ジイソシアナート類の具体例としては、2,4−トリレンジイソシアナート(2,4−TDI)、2,6−トリレンジイソシアナート(2,6−TDI)、4,4’−ジフェニルメタンジイソシアナート(MDI)、ヘキサメチレンジイソシアナート、p−フェニレンジイソシアナート、m−フェニレンジイソシアナート、1,5−ナフチレンジイソシアナートなどが挙げられる。また、トリイソシアナート類の具体例としては、1,3,6−ヘキサメチレントリイソシアナート、1,6,11−ウンデカントリイソシアナート、ビシクロヘプタントリイソシアナートなどが挙げられる。これらは1種単独で、または2種以上併せて使用することができる。
第3の観点に係る架橋性ゴム組成物には、上記した各成分以外に、ゴム加工分野において、通常使用される配合剤を適宜配合することができる。このような配合剤としては、上述の第1の観点と同様なものが使用できる。また、同様に、第3の観点に係る架橋性ゴム組成物には、本発明の目的や効果を阻害しない範囲であれば高飽和ニトリルゴム(C1)以外のゴムを配合してもよい。この場合の配合量も上述の第1の観点と同様とすれば良い。
特に、第3の観点によれば、繊維含浸体や金属複合体以外のバルクのゴム製品において、引張強さ、引張応力などの機械的強度に優れ、かつ、圧縮永久ひずみが小さい効果が活かされる。
次に、本発明の第4の観点に係る実施形態である第4実施形態について、説明する。
本発明の第4の観点に係る架橋性ゴム組成物は、α,β−エチレン性不飽和ジカルボン酸モノエステル単量体単位を有するニトリル基含有高飽和共重合体ゴム(D1)およびα,β−エチレン性不飽和ジカルボン酸モノエステル単量体単位を有するアクリルゴム(D2)の合計100重量部に対して、ポリアミン系架橋剤(D3)0.2〜20重量部を含有してなるものである。
以下、第4の観点(第4実施形態)において上記ニトリル基含有高飽和共重合体ゴム(D1)を、「ニトリルゴム(D1)」と、また、α,β−エチレン性不飽和ジカルボン酸モノエステル単量体単位を有するアクリルゴム(D2)を、「アクリルゴム(D2)」と、それぞれ略記することがある。
ニトリルゴム(D1)のニトリル基を形成するための好ましい態様としては、該ゴムがα,β−エチレン性不飽和ニトリル単量体単位を有する態様である。
α,β−エチレン性不飽和ニトリル単量体単位を形成する単量体としては、ニトリル基を有するα,β−エチレン性不飽和化合物であれば限定されないが、たとえば、上述の第1の観点におけるニトリルゴム(A1)と同様なものが使用できる。また、α,β−エチレン性不飽和ニトリル単量体単位の含有量も、上述の第1の観点と同様とすれば良い。
ニトリルゴム(D1)に、α,β−エチレン性不飽和ジカルボン酸モノエステル単量体単位を含有させるための好ましい方法としては、上記α,β−エチレン性不飽和ニトリルにα,β−エチレン性不飽和ジカルボン酸モノエステルを共重合させる方法などが挙げられる。
上記α,β−エチレン性不飽和ジカルボン酸モノエステル単量体としては、たとえば、上述の第1の観点におけるニトリルゴム(A1)と同様なものが使用できる。また、α,β−エチレン性不飽和ジカルボン酸モノエステル単量体単位の含有量も、上述の第1の観点と同様とすれば良い。
ジエン系単量体単位、α−オレフィン単量体単位を形成するジエン系単量体、α−オレフィン単量体としては、上述の第1の観点におけるニトリルゴム(A1)と同様なものが使用できる。また、これらの単量体単位の含有量も、上述の第1の観点と同様とすれば良い。
第4の観点で用いるα,β−エチレン性不飽和ジカルボン酸モノエステル単量体単位を有するアクリルゴム(D2)は、主構成単位であるアクリル酸エステル単量体単位と、α,β−エチレン性不飽和ジカルボン酸モノエステル単量体単位と、を含有するゴムである。
アクリルゴム(D2)中のアクリル酸エステル単量体単位とα,β−エチレン性不飽和ジカルボン酸モノエステル単量体単位との総量は、全単量体単位100重量%に対して、好ましくは70重量%以上、より好ましくは80重量%以上、特に好ましくは90重量%以上である。
一方、アクリルゴム(D2)中、アクリル酸エステル単量体単位とα,β−エチレン性不飽和ジカルボン酸モノエステル単量体単位との総量を100重量%とした場合に、α,β−エチレン性不飽和ジカルボン酸モノエステル単量体単位の割合は、好ましくは0.5〜10重量%、より好ましくは1〜5重量%である。
アクリル酸エステル単量体単位の割合が大きすぎると、本発明(第4の観点に係る発明)の効果が得られなくなるおそれがあり、逆に、アクリル酸エステル単量体単位の割合が小さすぎると、得られるゴム架橋物の機械的強度や伸びが低下する可能性がある。
(i)炭素数1〜8のアルキル基を有するアクリル酸アルキルエステル単量体単位のみを主構成単位として用いたアクリルゴム、または、
(ii)炭素数1〜8のアルキル基を有するアクリル酸アルキルエステル単量体単位と、アルキル基およびアルコキシ基の炭素数の和が1〜8のアクリル酸アルコキシアルキルエステル単量体単位と、を主構成単位として併用したアクリルゴム、
であることが好ましい。
このような 架橋性単量体としては、たとえば、活性塩素基含有不飽和単量体、エポキシ基含有単量体、カルボキシル基含有単量体、ジエン系単量体などが挙げられる。
このようなエチレン性不飽和単量体の具体例としては、エチレン、アクリロニトリル、酢酸ビニル、スチレン、α−メチルスチレン、アクリルアミド、ポリアルキレングリコールアクリル酸エステル、メタクリロニトリルなどがある。アクリルゴム(D2)中のその他の単量体の単位含有量は、全単量体単位100重量%に対して、好ましくは50重量%以下、より好ましくは40重量%以下、さらに好ましくは30重量%以下、特に好ましくは10重量%以下である。
ポリアミン系架橋剤(D3)としては、上述の第1の観点におけるポリアミン系架橋剤(A3)と同様のものを使用することができる。
第4の観点においては、ポリアミン系架橋剤(D3)の含有量は、ニトリルゴム(D1)およびアクリルゴム(D2)の合計100重量部に対して、0.2〜20重量部、好ましくは0.5〜15重量部、より好ましくは1〜10重量部である。架橋性ゴム組成物における(D3)成分の含有量が少なすぎると、本発明(第4の観点に係る発明)の効果が十分に得られないおそれがある。逆に、多すぎると架橋性ゴム組成物の貯蔵安定性が低下したり、架橋密度が高すぎて、得られるゴム架橋物が脆くなったりする可能性がある。
第4の観点に係る架橋性ゴム組成物は、塩基性架橋促進剤(D4)をさらに含有することが好ましい。塩基性架橋促進剤(D4)としては、テトラメチルグアニジン、テトラエチルグアニジン、ジフェニルグアニジン、ジ−o−トリルグアニジン、o−トリルビグアニド、ジカテコールホウ酸のジ−o−トリルグアジジン塩などのグアニジン系架橋促進剤;n−ブチルアルデヒドアニリン、アセトアルデヒドアンモニアなどのアルデヒドアミン系架橋促進剤;などが挙げられる。これらの中でも、グアニジン系架橋促進剤が好ましい。
第4の観点に係る架橋性ゴム組成物には、上記した各成分以外に、ゴム加工分野において、通常使用される配合剤を適宜配合することができる。このような配合剤としては、上述の第1の観点と同様なもの〔ただし、上記(D4)成分に相当するものを除く〕が使用できる。また、同様に、第4の観点に係る架橋性ゴム組成物には、本発明の目的や効果を阻害しない範囲であればニトリルゴム(D1)およびアクリルゴム(D2)以外のゴムを配合してもよい。この場合の配合量も上述の第1の観点と同様とすれば良い。
特に、第4の観点によれば、シール材として用いた場合に機械的強度および耐熱性に優れ、かつ、圧縮永久ひずみが顕著に小さい効果が活かされる。
まず、第1の観点に係る製造例(製造例1−1、1−2)、実施例(実施例1−1〜1−5)および比較例(比較例1−1〜1−7)について説明する。なお、第1の観点に係る実施例、比較例においては、下記の(1)〜(8)の各試験、評価を行った。
ニトリルゴムのカルボキシル基含有量は、水酸化カリウムの含水エタノール溶液(0.02N)を用いて、室温でチモールフタレインを指示薬とする滴定により、ゴム100グラムに対するカルボキシル基の数(モル数、単位はephr)を求めた。
ヨウ素価はJIS K6235に従って測定した。
ニトリルゴムのムーニー粘度(ポリマームーニー)および架橋性ゴム組成物のムーニー粘度(コンパウンドムーニー)は、JIS K6300に従って測定した。
架橋性ゴム組成物を170℃で20分間、プレス圧10MPaで架橋し、プレス架橋試験片を作製し、このプレス架橋試験片を用いて、JIS K6251に従い、架橋物の引張強さ、および伸びを測定した。
上記(4)と同様の条件で、JIS K6251に従い、架橋物の100%引張応力を測定した。
架橋性ゴム組成物を170℃で20分間、プレス圧10MPaで架橋し、次いでギヤー式オーブンにて170℃で4時間二次架橋を行う試験片を作製し、この試験片を用いて、JIS K6251に従い、二次架橋後のゴム架橋物の引張強さ、100%引張応力および伸びを測定した。
上記(6)と同様の条件で、JIS K6251に従い、二次架橋後のゴム架橋物の100%引張応力を測定した。
内径30mm、リング径3mmの金型を用いて、架橋性ゴム組成物を170℃でプレス圧10MPaにて20分間架橋した後、170℃で4時間二次架橋を行ってO−リングセット試験用の試験片を得た。そして、O−リング圧縮永久ひずみを、O−リングを挟んだ二つの平面の距離をリング厚み方向に25%圧縮した状態で150℃にて504時間保持する条件でJIS K6262に従って測定した。
金属製ボトルに、イオン交換水180部、濃度10重量%のドデシルベンゼンスルホン酸ナトリウム(乳化剤)水溶液25部、アクリロニトリル37部、フマル酸モノn−ブチル8部、t−ドデシルメルカプタン(分子量調整剤)0.5部の順に仕込み、内部の気体を窒素で3回置換した後、1,3−ブタジエン55部を仕込んだ。金属製ボトルを5℃に保ち、クメンハイドロパーオキサイド(重合触媒)0.1部を仕込み、次いで、金属製ボトルを回転させながら16時間重合反応を行った。そして、濃度10重量%のハイドロキノン(重合停止剤)水溶液0.1部を加えて重合反応を停止した後、水温60℃のロータリーエバポレータを用いて残留単量体を除去し、アクリロニトリル単位34重量%、ブタジエン単位59重量%、フマル酸モノn−ブチル単位7重量%のアクリロニトリル−ブタジエン−α,β−エチレン性不飽和ジカルボン酸モノアルキルエステル共重合体ゴムのラテックス(固形分濃度約30重量%)を得た。
製造例1−1において、フマル酸モノn−ブチルを用いず、アクリロニトリルを37部、ブタジエンを63部とする以外は製造例1−1と同様な操作を行って、アクリロニトリル単位37重量%、ブタジエン単位63重量%のアクリロニトリル−ブタジエン共重合体ゴムのラテックスを得た。そして、得られたゴムについて、製造例1−1と同様に水素添加反応を行い、ニトリルゴム(A1’−2)を調製した。ニトリルゴム(A1’−2)のヨウ素価は10、ムーニー粘度〔ML1+4(100℃)〕は65であった。
バンバリーミキサを用いてニトリルゴム(A1−1)100部に、ステアリン酸1部、FEFカーボンブラック(旭60、旭カーボン社製)40部、可塑剤(アデカサイザーC−8、旭電化社製)5部およびN−イソプロピル−N’−フェニル−p−フェニレンジアミン(ノクラック810NA、大内新興化学工業社製、芳香族第二級アミン系老化防止剤(A2−1))2部を添加して混合した。次いで、得られた混合物をロールに移して3−ジ−o−トリルグアニジン(ノクセラーDT、大内新興化学工業社製、架橋促進剤)2部およびヘキサメチレンジアミンカルバメート(Diak#1、デュポン・ダウエラストマー社製、ポリアミン系架橋剤(A3−1))3.4部を添加して混練し、コンパウンドムーニー粘度96である架橋性ゴム組成物を調製した。
上記にて調製した架橋性ゴム組成物を架橋して得たゴム架橋物について常態物性、二次架橋後の物性およびO−リングセット試験(150℃、504時間)の各試験、評価を行った。結果を表1に記す。
実施例1−1において、表1に示すように、老化防止剤としてのN−イソプロピル−N’−フェニル−p−フェニレンジアミン(A2−1)に代えて、表1に示す各老化防止剤を使用した以外は、実施例1−1と同様に行って、それぞれ架橋性ゴム組成物を調製した。
すなわち、実施例1−2においては、オクチル化ジフェニルアミン〔ノクラックAD−F、大内新興化学工業社製、芳香族第二級アミン系老化防止剤(A2−2)成分〕を、
実施例1−3においては、4,4’−ビス(α,α’−ジメチルベンジル)ジフェニルアミン〔ノクラックCD,大内新興化学工業社製、芳香族第二級アミン系老化防止剤(A2−3)成分〕を、
実施例1−4においては、スチレン化ジフェニルアミン〔ノンフレックスLAS、精工化学社製、芳香族第二級アミン系老化防止剤(A2−4)成分〕を、
それぞれ使用した。
実施例1−1において、表1に示すように、架橋剤としてのヘキサメチレンジアミンカルバメート(A3−1)に代えて、架橋剤としての2,2−ビス{4−(4−アミノフェノキシ)フェニル}プロパン〔BAPP、和歌山精化工業社製、ポリアミン系架橋剤(A3−2)成分〕8.6部を使用した以外は、実施例1−1と同様に行って架橋性ゴム組成物を調製した。
実施例1−1において、老化防止剤としてのN−イソプロピル−N’−フェニル−p−フェニレンジアミン(A2−1)を使用しなかった以外は、実施例1−1と同様に行って架橋性ゴム組成物を調製した。
実施例1−1において、表1に示すように、老化防止剤としてのN−イソプロピル−N’−フェニル−p−フェニレンジアミン(A2−1)に代えて、表1に示す各老化防止剤を使用した以外は、実施例1−1と同様に行って、それぞれ架橋性ゴム組成物を調製した。
すなわち、比較例1−2においては、2,2,4−トリメチル−1,2−ジハイドロキノリン〔ノクラック224、大内新興化学工業社製 (A2’−5)成分〕を、
比較例1−3においては、2−メルカプトベンゾイミダゾール〔ノクラックMB、大内新興化学工業社製 (A2’−6)成分〕を、
比較例1−4においては、トリス(ノニルフェニル)ホスファイト〔ノクラックTNP、大内新興化学工業社製 (A2’−7)成分〕を、
比較例1−5においては、4,4’−チオビス(3−メチル−6−t−ブチルフェノール)〔ノクラック300、大内新興化学工業社製 (A2’−8)成分〕を、
それぞれ使用した。
実施例1−1において、架橋剤としてのヘキサメチレンジアミンカルバメート(A3−1)に代えて、1,3−ビス(t−ブチルペルオキシイソプロピル)ベンゼン〔Vulcup40KE、ハーキュレス社製 (A3’−3)成分〕8部を添加し、3−ジ−o−トリルグアニジンを添加しない他は実施例1−1と同様に行って、架橋性ゴム組成物を調製した。
実施例1−1において、ニトリルゴム(A1−1)に代えて、上記にて製造したニトリルゴム(A1’−2)を用いた他は実施例1−1と同様に行って架橋性ゴム組成物を調製した。
(A2−1):N−イソプロピル−N’−フェニル−p−フェニレンジアミン(ノクラック810NA、大内新興化学工業社製)
(A2−2):オクチル化ジフェニルアミン(ノクラックAD−F、大内新興化学工業社製)
(A2−3):4,4’−ビス(α,α’−ジメチルベンジル)ジフェニルアミン(ノクラックCD、大内新興化学工業社製)
(A2−4):スチレン化ジフェニルアミン(ノンフレックスLAS、精工化学社製)
(A2’−5):2,2,4−トリメチル−1,2−ジハイドロキノリン(ノクラック224、大内新興化学工業社製)
(A2’−6):2−メルカプトベンゾイミダゾール(ノクラックMB、大内新興化学工業社製)
(A2’−7):トリス(ノニルフェニル)ホスファイト(ノクラックTNP、大内新興化学工業社製)
(A2’−8):4,4’−チオビス(3−メチル−6−t−ブチルフェノール)(ノクラック300、大内新興化学工業社製)
(A3−1):ヘキサメチレンジアミンカルバメート(Diak#1、デュポン・ダウエラストマー社製)
(A3−2):2,2−ビス{4−(4−アミノフェノキシ)フェニル}プロパン(BAPP、和歌山精化工業社製)
(A3’−3):1,3−ビス(t−ブチルペルオキシイソプロピル)ベンゼン(Vulcup40KE、ハーキュレス社製)
表1に示すように、アクリロニトリル単量体単位およびフマル酸モノn−ブチル単量体単位を有し、ヨウ素価10であるニトリルゴム(A1−1)に、芳香族第二級アミン系老化防止剤(A2−1)〜(A2−4)のいずれかと、ポリアミン系架橋剤(A3−1)および(A3−2)のいずれかと、を含有してなる架橋性ゴム組成物は、いずれもコンパウンドムーニー粘度が120以下と低くて扱い易く、引張強さ、引張応力などの機械的強度と伸びのバランスに優れ、かつ、O−リング圧縮永久ひずみが特に小さい(70%以下)ゴム架橋物を与えた(実施例1−1〜1−5)。
(ii)ニトリルゴム(A1−1)に対して老化防止剤として芳香族第二級アミン系(A2−1)を用い、有機過酸化物系(A3’−3)の架橋剤を使用した場合(比較例1−6)、
においては、得られるゴム架橋物はいずれも大きなO−リング圧縮永久ひずみ(76%以上)を示し、圧縮永久ひずみが悪化した。
次に、第2の観点に係る実施例(実施例2−1〜2−2)および比較例(比較例2−1〜2−4)について説明する。なお、第2の観点に係る実施例、比較例においては、上記第1の観点における(1)〜(4)の各試験、評価、および下記の(9)〜(11)の各試験、評価を行った。
L形ロータを用いて、温度125℃にて、JIS K6300−1に準じて測定し、この測定結果よりムーニースコーチ時間t5(分)およびムーニー粘度〔ML1+4(100℃)〕の最低値Vminを求めた。t5(分)の値が大きいほどスコーチ安定性に優れる。また。Vminが低いほど成形時の加工性に優れると判断される。
架橋性ゴム組成物を170℃で20分間、プレス圧10MPaで架橋し、プレス架橋試験片を作製し、170℃で4時間二次架橋を行った後、JIS K6253に従い、デュロメータ硬さ試験機タイプAを用いてゴム架橋物の硬さを測定した。
内径30mm、リング径3mmの金型を用いて、架橋性ゴム組成物を170℃でプレス圧10MPaにて20分間架橋した後、170℃で4時間二次架橋を行ってO−リングセット試験用の試験片を得た。そして、O−リング圧縮永久ひずみを、O−リングを挟んだ二つの平面の距離をリング厚み方向に25%圧縮した状態で150℃にて168時間保持する条件でJIS K6262に従って測定した。
まず、上記製造例1−1における、ニトリルゴム(A1−1)と同様の方法により製造されたニトリルゴム(B1−1)を準備した。
次いで、バンバリーミキサを用いてニトリルゴム(B1−1)100部に、ステアリン酸1部、カーボンブラック(N550、東海カーボン社製)40部、オクタデシルアミン(ファーミン80、花王社製、アミノ基以外の極性基を有しない第一級モノアミン)0.5部、トリメリット酸エステル(アデカサイザーC−8、旭電化社製,可塑剤)5部、4,4’−ジ−(α,α’−ジメチルベンジル)ジフェニルアミン(ナウガード445、ユニロイヤル社製、老化防止剤)1.5部および2−メルカプトベンズイミダゾール(ノクラックMB、大内新興化学工業社製、老化防止剤)1.5部を添加して混合した。次いで、得られた混合物をロールに移して1,3−ジ−o−トリルグアニジン(ノクセラーDT、大内新興化学工業社製、架橋促進剤)2部およびヘキサメチレンジアミンカルバメート(Diak#1、デュポン・ダウエラストマー社製、ポリアミン系架橋剤)3部を添加して混練し、コンパウンドムーニー粘度92である架橋性ゴム組成物を調製した。
上記にて調製した架橋性ゴム組成物のムーニースコーチ試験、ならびに、該組成物を架橋して得たゴム架橋物の常態物性およびO−リングセット試験(150℃、168時間)の各試験、評価を行った。結果を表2に記す。
実施例2−1において、オクタデシルアミン0.5部を1部(実施例2−2)または無添加(比較例2−1)に変更した他は実施例2−1と同様に行って、それぞれ架橋性ゴム組成物を調製し、実施例2−1と同様の試験、評価を行った。結果を表2に記す。
実施例2−1において、オクタデシルアミン0.5部に代えてジアルキルアミン(アーミン2C、ライオン・アクゾ社製、アルキル基の炭素数8〜18)2部(比較例2−2)、または、n−ブチルアルデヒドアニリン1部(比較例2−3)に変更した他は実施例2−1と同様に行って、それぞれ架橋性ゴム組成物を調製し、実施例2−1と同様の試験、評価を行った。結果を表2に記す。
まず、上記製造例1−2における、ニトリルゴム(A1’−2)と同様の方法により製造されたニトリルゴム(B1’−2)を準備した。
表2に示すように、アクリロニトリル単位およびフマル酸モノn−ブチル単位を有し、ヨウ素価10であるニトリルゴム(B1−1)、本発明(第2の観点に係る発明)所定の第一級モノアミン(B2)およびポリアミン系架橋剤(B3)を含有してなる架橋性ゴム組成物は、いずれもコンパウンドムーニー粘度が100以下と低く、スコーチタイムt5は十分に長く、かつ、Vminは低くて扱い易く、しかも十分な引張強さと伸びを有し、O−リング圧縮永久ひずみが60%以下と小さいゴム架橋物を与えた(実施例2−1,2−2)。
次に、第3の観点に係る製造例(製造例3−1)、実施例(実施例3−1〜3−2)および比較例(比較例3−1〜3−4)について説明する。なお、第3の観点に係る実施例、比較例においては、上記第1の観点における(1)〜(3)、(6)の各試験、評価、および下記の(12)〜(15)の各試験、評価を行った。
ロール粘着性は、ロール混練作業での状況から下記の二水準の間に1〜4の段階を加えた6水準で評価した。
0:ロール粘着性が激しく混練が不可能
5:ロール粘着性がなく容易に混練が可能
架橋性ゴム組成物を縦15cm、横15cm、深さ0.2cmの金型に入れ、170℃で20分間、プレス圧10MPaで架橋し、次いでギヤー式オーブンにて170℃で4時間二次架橋を行って試験片を作製し、JIS K6253に従い、デュロメータ硬さ試験機タイプAを用いて二次架橋後のゴム架橋物の硬さを測定した。
内径30mm、リング径3mm、深さ3mmの金型を用いて、架橋性ゴム組成物を170℃でプレス圧10MPaにて20分間架橋した後、170℃で4時間二次架橋を行ってO−リングセット試験用の試験片を得た。そして、O−リング圧縮永久ひずみを、O−リングを挟んだ二つの平面の距離をリング厚み方向に25%圧縮した状態で170℃にて70時間保持する条件でJIS K6262に従って測定した。
上記(13)と同様に一次および二次架橋して作成した試験片をJIS K6257(ノーマルオーブン法)に従い、170℃において168時間後の引張強さおよびその変化率(%)ならびに伸びおよびその変化率(%)を求めた。
製造例1−1において、t−ドデシルメルカプタン(分子量調整剤)の添加量を0.5部から0.7部に変更し、クメンハイドロパーオキシド(重合触媒)の添加量を0.1部から0.06部に変更した以外は、製造例1−1と同様にして、アクリロニトリル単位35重量%、ブタジエン単位57.8重量%、フマル酸モノn−ブチル単位7.2重量%のアクリロニトリル−ブタジエン−α,β−エチレン性不飽和ジカルボン酸モノアルキルエステル共重合体ゴムのラテックス(固形分濃度約25重量%)を得た。
バンバリーミキサを用いて高飽和ニトリルゴム(C1−1)100部に、ポリオキシエチレンアルキルエーテルリン酸エステル(製品名「フォスファノールRL―210」、東邦化学工業社製;モノエステル41.6重量%、ジエステル38.4重量%、ポリオキシエチレンアルキルエーテル約20重量%混入)1部、4,4’−ジ−(α,α’−ジメチルベンジル)ジフェニルアミン(ナウガード445、ユニロイヤル社製、老化防止剤)1.5部およびFEFカーボンブラック(旭60、旭カーボン社製、補強性充填剤)40部を添加して混合した。次いで、得られた混合物をロールに移して3−ジ−o−トリルグアニジン(ノクセラーDT、大内新興化学工業社製、架橋促進剤)2部およびヘキサメチレンジアミンカルバメート〔Diak#1、デュポン・ダウエラストマー社製、ポリアミン系架橋剤〕3.4部を添加し、混練して架橋性ゴム組成物を調製した。
上記にて調製した架橋性ゴム組成物の調製時のロール粘着性、架橋性ゴム組成物を架橋して得たゴム架橋物の常態物性、O−リングセット試験(170℃、70時間)および耐熱老化性(170℃、168時間)の各試験、評価を行った。結果を表3に記す。
実施例3−1において、ポリオキシエチレンアルキルエーテルリン酸エステル1部に代えて、ポリオキシエチレンオクタデシルエーテルリン酸エステル(製品名「VAMFRE VAM」、R.T.Vanderbilt社製)1部を用いた他は実施例3−1と同様に操作して架橋性ゴム組成物を調製し、実施例3−1と同様の試験、評価を行った。結果を表3に記す。
実施例3−1において、ポリオキシエチレンアルキルエーテルリン酸エステルを添加しなかった他は実施例3−1と同様に操作して架橋性ゴム組成物を調製し、実施例3−1と同様の試験、評価を行った。結果を表3に記す。
実施例3−1において、ポリオキシエチレンアルキルエーテルリン酸エステル1部に代えて、ステアリン酸(比較例3−2)、脂肪酸エステル(比較例3−3)またはリン酸トリ(2−エチルヘキシル)エステル(比較例3−4)各1部を用いた他は実施例3−1と同様に操作してそれぞれ架橋性ゴム組成物を調製した。なお、脂肪酸エステル(比較例3−3)としてはストラクトール社製の製品名「ストラクトールWB222」を、リン酸トリ(2−エチルヘキシル)エステル(比較例3−4)としては大八化学社製の製品名「TOP」を、それぞれ使用した。
それぞれにつき実施例3−1と同様の試験、評価を行った。結果を表3に記す。
表3に示すように、本発明(第3の観点に係る発明)所定の架橋性ゴム組成物は、いずれもロール粘着性が小さくて扱い易く、ゴム架橋物の引張強さ、伸びおよび硬さが良好であり、O−リング圧縮永久ひずみが35%以下と顕著に小さく、しかも、耐熱老化性に優れるゴム架橋物を与えた(実施例3−1,3−2)。
次に、第4の観点に係る製造例(製造例4−1〜4−2)、実施例(実施例4−1〜4−3)および比較例(比較例4−1〜4−3)について説明する。なお、第4の観点に係る実施例、比較例においては、上記第1の観点における(1)〜(3)、(6)、上記第2の観点における(11)の各試験、評価、および下記の(16)の試験、評価を行った。
架橋性ゴム組成物を、縦15cm、横15cm、深さ0.2cmの金型に入れ、170℃で20分間、プレス圧10MPaで架橋し、次いでギヤー式オーブンにて170℃で4時間二次架橋を行って試験片を作製し、作製した試験片をJIS K6257(ノーマルオーブン法)に従い、150℃において504時間後の引張強さおよびその変化率(%)ならびに伸びおよびその変化率(%)を求めた。
温度計、攪拌装置を備えた重合反応器に、イオン交換水200部、ラウリル硫酸ナトリウム(乳化剤)3部、アクリル酸エチル70部、アクリル酸n−ブチル28部およびマレイン酸モノメチル2部を仕込み、減圧脱気および窒素置換を2度行って酸素を十分除去した後、クメンハイドロパーオキサイド0.005部およびホルムアルデヒドスルホキシル酸ナトリウム0.002部を加えて常圧下、温度30℃で乳化重合を開始し、重合転化率が95%に達するまで反応させた。得られた乳化重合液を塩化カルシウム水溶液で凝固し、脱水、水洗、乾燥してアクリルゴム(D2−1)を得た。
アクリルゴム(D2−1)の組成は、アクリル酸エチル単位70重量%、アクリル酸n−ブチル単位28重量%およびマレイン酸モノメチル単位2重量%(カルボキシル基含有量1.3×10−2ephr)であり、ムーニー粘度〔ML1+4(100℃)〕は45であった。
製造例4−1において、重合反応器に仕込むアクリル酸エチルの量を70部から30部に、アクリル酸n−ブチルの量を28部から35部に、マレイン酸モノメチル2部をアクリル酸2−メトキシエチル33部およびメタクリル酸2部にそれぞれ変更する他は製造例4−1と同様に行って、アクリルゴム(D2’−2)を得た。
アクリルゴム(D2’−2)の組成は、アクリル酸エチル30重量%、アクリル酸n−ブチル35重量%、アクリル酸2−メトキシエチル33重量%およびメタクリル酸2重量%であり、ムーニー粘度〔ML1+4、(100℃)〕は35であった。
まず、上記製造例1−1における、ニトリルゴム(A1−1)と同様の方法により製造されたニトリルゴム(D1−1)を準備した。
次いで、バンバリーミキサを用いてニトリルゴム(D1−1)75部および上記にて製造したアクリルゴム(D2−1)25部に、ステアリン酸1部、FEFカーボンブラック(旭60、旭カーボン社製)40部、可塑剤(アデカサイザーC−8、旭電化社製)5部、有機酸樹脂複合系滑剤(モールドウイズ21G、巴工業社製)0.5部、エステル系ワックス(グレッグG−8205、大日本インキ化学工業社製)1部、アミン系老化防止剤(ナウガード445、ユニロイヤル社製)1.5部および2−メルカプトベンゾイミダゾール(ノクラックMB,大内新興化学工業社製、老化防止剤)1.5部を添加して混合した。次いで、得られた混合物をロールに移して1,3−ジ−o−トリルグアニジン(ノクセラーDT、大内新興化学工業社製、塩基性架橋促進剤)2部およびヘキサメチレンジアミンカルバメート(Diak#1、デュポン・ダウエラストマー社製、ポリアミン系架橋剤)2.7部を添加して混練し、コンパウンドムーニー粘度72である架橋性ゴム組成物を調製した。
上記にて調製した架橋性ゴム組成物を架橋して得たゴム架橋物について二次架橋後の物性、熱老化試験(150℃、504時間)およびO−リングセット試験(150℃、168時間)の各試験、評価を行った。結果を表4に記す。
実施例4−1において、表4に示すようにニトリルゴム(D1−1)およびアクリルゴム(D2−1)の配合比およびヘキサメチレンジアミンカルバメートの量を変えた他は、実施例4−1と同様に行って架橋性ゴム組成物を調製し、実施例4−1と同様の試験、評価を行った。結果を表4に記す。
実施例4−1において、ニトリルゴム(D1−1)の添加量を75部から50部に変更し、アクリルゴム(D2−1)25部に代えてアクリルゴム(D2’−2)50部を用い、ヘキサメチレンジアミンカルバメートの添加量を2.7部を2.1部に変更した他は、実施例4−1と同様に行って架橋性ゴム組成物を調製し、実施例4−1と同様の試験、評価を行った。結果を表4に記す。
実施例4−1において、ニトリルゴム(D1−1)およびアクリルゴム(D2−1)を共に50部に変え、1,3−ジ−o−トリルグアニジンおよびヘキサメチレンジアミンカルバメートに代えて1,3−ビス(t−ブチルパーオキシイソプロピル)ベンゼン40%品(バルカップ40KE、GEO Specialty Chemicals Inc製、有機過酸化物)8部(有機過酸化物純分で3.2部)を用いた他は、実施例4−1と同様に行って架橋性ゴム組成物を調製し、実施例4−1と同様の試験、評価を行った。結果を表4に記す。
表4に示すように、本発明(第4の観点に係る発明)所定の架橋性ゴム組成物は、いずれもコンパウンドムーニー粘度が80以下と低くて扱い易く、引張強さは10MPa以上あって十分大きく、熱老化試験では伸びの低下が見られるくらいで特に異常はなく、O−リング圧縮永久ひずみが40%以下と顕著に小さいゴム架橋物を与えた(実施例4−1〜4−3)。
Claims (13)
- α,β−エチレン性不飽和ニトリル単量体単位およびα,β−エチレン性不飽和ジカルボン酸モノエステル単量体単位を有し、ヨウ素価が120以下であるニトリルゴム100重量部に対し、アミノ基以外の極性基を有しない第一級モノアミン0.1〜20重量部、および、ポリアミン系架橋剤0.1〜20重量部を含有してなる架橋性ゴム組成物。
- 前記アミノ基以外の極性基を有しない第一級モノアミンが、脂肪族第一級モノアミンである請求項1記載の架橋性ゴム組成物。
- ニトリル基含有高飽和共重合体ゴム、ポリオキシアルキレンアルキルエーテルリン酸エステルおよびポリアミン系架橋剤を含有してなる架橋性ゴム組成物。
- 前記ニトリル基含有高飽和共重合体ゴムが、α,β−エチレン性不飽和ニトリル単量体単位含有量が10〜60重量%でヨウ素価が100以下のニトリルゴムである請求項3に記載の架橋性ゴム組成物。
- α,β−エチレン性不飽和ジカルボン酸モノエステル単量体単位を有するニトリル基含有高飽和共重合体ゴムおよびα,β−エチレン性不飽和ジカルボン酸モノエステル単量体単位を有するアクリルゴムの合計100重量部に対して、ポリアミン系架橋剤0.2〜20重量部を含有してなる架橋性ゴム組成物。
- 前記α,β−エチレン性不飽和ジカルボン酸モノエステル単量体単位を形成する単量体が、α,β−エチレン性不飽和結合を形成する二つの炭素原子の各々にカルボキシル基を有するジカルボン酸のモノエステル単量体である請求項5に記載の架橋性ゴム組成物。
- 前記α,β−エチレン性不飽和ジカルボン酸モノエステル単量体単位を形成する単量体のアルコキシ基の炭素数が3〜8である請求項5または6に記載の架橋性ゴム組成物。
- 前記ニトリル基含有高飽和共重合体ゴムおよび前記アクリルゴムの重量比が5/95〜95/5である請求項5〜7のいずれか1項に記載の架橋性ゴム組成物。
- 25%圧縮した状態で150℃、168時間保持した後におけるO−リング圧縮永久ひずみが40%以下のゴム架橋物を与える請求項5〜8のいずれか1項に記載の架橋性ゴム組成物。
- さらに塩基性架橋促進剤0.5〜10重量部を含有してなる請求項5〜9のいずれか1項に記載の架橋性ゴム組成物。
- 請求項1〜10のいずれか1項に記載の架橋性ゴム組成物を架橋してなるゴム架橋物。
- シール材である請求項11に記載のゴム架橋物。
- ベルト材である請求項11に記載のゴム架橋物。