JP2009013052A - 強化ガラス基板及びその製造方法 - Google Patents
強化ガラス基板及びその製造方法 Download PDFInfo
- Publication number
- JP2009013052A JP2009013052A JP2008148998A JP2008148998A JP2009013052A JP 2009013052 A JP2009013052 A JP 2009013052A JP 2008148998 A JP2008148998 A JP 2008148998A JP 2008148998 A JP2008148998 A JP 2008148998A JP 2009013052 A JP2009013052 A JP 2009013052A
- Authority
- JP
- Japan
- Prior art keywords
- glass
- glass substrate
- zno
- zro
- mgo
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】 表面に圧縮応力層を有する強化ガラス基板であって、ガラス組成として、質量%でSiO2 40〜70%、Al2O3 12〜25%、B2O3 0〜10%、Li2O 0〜8%、Na2O 6〜15%、K2O 0〜10%、Li2O+Na2O+K2O 13〜20%、MgO 0〜3.9%、CaO 0〜5%、ZnO 0〜5%、ZrO2 0〜6%、SrO+BaO 0〜5%含有し、且つ質量分率で(MgO+ZrO2+ZnO)/(MgO+ZrO2+ZnO+Al2O3)の値が0.25〜0.45であることに特徴とする。上記強化ガラスは、所定のガラス組成となるように調合したガラス原料を溶融し、オーバーフローダウンドロー法にて板状に成形した後、イオン交換処理を行ってガラス板表面に圧縮応力層を形成することにより作製できる。
【選択図】なし
Description
強化処理は、イオン交換処理にて行うことが望ましい。イオン交換処理は、例えば400〜550℃の硝酸カリウム溶液中にガラス板を1〜8時間浸漬することによって行うことができる。イオン交換条件は、ガラスの粘度特性等を考慮して最適な条件を選択すればよい。
Claims (15)
- 表面に圧縮応力層を有する強化ガラス基板であって、ガラス組成として、質量%でSiO2 40〜70%、Al2O3 12〜25%、B2O3 0〜10%、Li2O 0〜8%、Na2O 6〜15%、K2O 0〜10%、Li2O+Na2O+K2O 13〜20%、MgO 0〜3.9%、CaO 0〜5%、ZnO 0〜5%、ZrO2 0〜6%、SrO+BaO 0〜5%含有し、且つ質量分率で(MgO+ZrO2+ZnO)/(MgO+ZrO2+ZnO+Al2O3)の値が0.25〜0.45であることを特徴とする強化ガラス基板。
- 表面に圧縮応力層を有する強化ガラス基板であって、ガラス組成として、質量%でSiO2 40〜70%、Al2O3 12〜25%、B2O3 0〜10%、Li2O 0〜8%、Na2O 6〜15%、K2O 0〜10%、Li2O+Na2O+K2O 13〜20%、MgO 0〜3.9%、CaO 0〜5%、ZnO 0〜5%、ZrO2 0〜5.5%、SrO+BaO 0〜5%含有し、且つ質量分率で(MgO+ZrO2+ZnO)/(MgO+ZrO2+ZnO+Al2O3)の値が0.25〜0.45であることを特徴とする請求項1の強化ガラス基板。
- 化学的に強化されてなることを特徴とする請求項1又は2の強化ガラス基板。
- 表面の圧縮応力が100MPa以上、且つ圧縮応力層の厚みが1μm以上であることを特徴とする請求項1〜3の何れかの強化ガラス基板。
- 未研磨の表面を有することを特徴とする請求項1〜4のいずれかの強化ガラス基板。
- 液相温度が1050℃以下のガラスからなることを特徴とする請求項1〜5のいずれかの強化ガラス基板。
- 液相粘度が104.0dPa・s以上のガラスからなることを特徴とする請求項1〜6のいずれかの強化ガラス基板。
- タッチパネルディスプレイに用いられることを特徴とする請求項1〜7のいずれかの強化ガラス基板。
- 携帯電話のカバーガラスに用いられることを特徴とする請求項1〜7のいずれかの強化ガラス基板。
- 太陽電池のカバーガラスに用いられること特徴とする請求項1〜7のいずれかの強化ガラス基板。
- ディスプレイの保護部材として用いられることを特徴とする請求項1〜7のいずれかの強化ガラス基板。
- ガラス組成として、質量%でSiO2 40〜70%、Al2O3 12〜25%、B2O3 0〜10%、Li2O 0〜8%、Na2O 6〜15%、K2O 0〜10%、Li2O+Na2O+K2O 13〜20%、MgO 0〜3.9%、CaO 0〜5%、ZnO 0〜5%、ZrO2 0〜6%、SrO+BaO 0〜5%含有し、且つ質量分率で(MgO+ZrO2+ZnO)/(MgO+ZrO2+ZnO+Al2O3)の値が0.25〜0.45であることを特徴とするガラス。
- ガラス組成として、質量%でSiO2 40〜70%、Al2O3 12〜25%、B2O3 0〜10%、Li2O 0〜8%、Na2O 6〜15%、K2O 0〜10%、Li2O+Na2O+K2O 13〜20%、MgO 0〜3.9%、CaO 0〜5%、ZnO 0〜5%、ZrO2 0〜6%、SrO+BaO 0〜5%含有し、且つ質量分率で(MgO+ZrO2+ZnO)/(MgO+ZrO2+ZnO+Al2O3)の値が0.25〜0.45の範囲のガラス組成となるように調合したガラス原料を溶融し、板状に成形した後、イオン交換処理を行ってガラス表面に圧縮応力層を形成することを特徴とする強化ガラスの製造方法。
- ダウンドロー法にて板状に成形することを特徴とする請求項13の強化ガラス基板の製造方法。
- オーバーフローダウンドロー法にて板状に成形することを特徴とする請求項13又は14の強化ガラス基板の製造方法。