JP2002348552A - Pressure-sensitive adhesive sheet for removing solvent- containing material - Google Patents
Pressure-sensitive adhesive sheet for removing solvent- containing materialInfo
- Publication number
- JP2002348552A JP2002348552A JP2001155312A JP2001155312A JP2002348552A JP 2002348552 A JP2002348552 A JP 2002348552A JP 2001155312 A JP2001155312 A JP 2001155312A JP 2001155312 A JP2001155312 A JP 2001155312A JP 2002348552 A JP2002348552 A JP 2002348552A
- Authority
- JP
- Japan
- Prior art keywords
- pressure
- sensitive adhesive
- solvent
- adhesive sheet
- sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、例えば、スクリー
ン印刷の際にスクリーン印刷版の裏側に裏回りしたペー
スト（インキ）や、オフセット印刷、グラビア印刷、フ
レキソ印刷などの印刷機のロール類に付着したインキ、
その他、インクジェットプリンターのインキ、ペンキな
ど、溶剤含有物を除去するための粘着シートに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to, for example, a method of adhering a paste (ink) wrapped around the back side of a screen printing plate at the time of screen printing, or a roll of a printing machine such as offset printing, gravure printing, flexographic printing or the like. Ink,
In addition, the present invention relates to a pressure-sensitive adhesive sheet for removing solvent-containing substances such as ink and paint of an ink jet printer.
【０００２】[0002]
【従来の技術】溶剤含有物、例えば、ペースト、インキ
等の溶剤を含有して湿った状態にある半固形物は、印
刷、塗料、接着剤等の分野で広く使用されている。しか
し、このような溶剤含有物が、所定の部位に過剰に存在
したり、不要な部位に存在する場合には、機械や機器
類、手などを汚染したり、製品の品質を損なうなど種々
の不具合が発生しやすい。2. Description of the Related Art Solvent-containing substances, for example, semisolids in a wet state containing solvents such as pastes and inks, are widely used in the fields of printing, paints, adhesives and the like. However, when such a solvent-containing substance is excessively present in a predetermined part or is present in an unnecessary part, various kinds of substances, such as contaminating machines, equipment, hands, etc., and impairing the quality of products, etc. Failure is likely to occur.
【０００３】例えば、スクリーン印刷においては、一定
の印刷回数を経ると、スクリーン印刷版にペースト（イ
ンキ）が裏回りして被印刷物を汚染したり、印刷画像に
滲みが生じて、正確で美麗な印刷ができない状態とな
る。従来、このようなスクリーン印刷時の滲み等を防止
するために、版の裏側に裏回りしたペーストを粘着シー
トを用いて除去する方法が知られている。For example, in screen printing, after a certain number of printings, paste (ink) runs behind the screen printing plate, contaminating the printing material, and bleeding occurs in the printed image, resulting in an accurate and beautiful image. Printing cannot be performed. Conventionally, in order to prevent such bleeding at the time of screen printing, there is known a method of using an adhesive sheet to remove a paste wrapped around the back side of a plate.
【０００４】例えば、特開平３−７４８９３号公報に
は、プリント配線板のスクリーン印刷方法として、粘着
シートの粘着面にスクリーン印刷することにより版の裏
に回ったペーストを除去する方法が開示されている。ま
た、特開平６−２９７６８１号公報にも、粘着シートを
版に付着させるとともに、これを剥がすことにより、裏
回りしたペーストを除去する方法が記載されている。こ
の方法は溶剤を用いてウエスや紙で拭き取る方法に比
べ、ウエスや紙から発生するゴミやほこりなどの影響が
なく、ゴミやほこりによる印刷不良を防止できるとして
いる。For example, Japanese Patent Application Laid-Open No. 3-74893 discloses a method of screen printing a printed wiring board, in which a paste printed on the back side of a plate is removed by screen printing on an adhesive surface of an adhesive sheet. I have. Japanese Patent Application Laid-Open No. 6-297681 also discloses a method of attaching an adhesive sheet to a plate and peeling it off to remove the paste behind the plate. This method has no effect of dust and dirt generated from the waste and paper, and can prevent printing failure due to dirt and dust, as compared with a method of wiping with waste and paper using a solvent.
【０００５】[0005]
【発明が解決しようとする課題】そこで、本発明者ら
は、実際に粘着シートを使用してペーストやインキの除
去を試みたところ、粘着シートにおいて、同じ粘着剤を
使用していても、基材の種類（表面粗さ）が変わると、
ペーストやインキの除去性に差が生じることを見出し
た。The inventors of the present invention have attempted to remove paste and ink using an adhesive sheet, and have found that even if the same adhesive is used in the adhesive sheet, When the type of material (surface roughness) changes,
It has been found that there is a difference in the removability of paste and ink.
【０００６】従って、本発明の目的は、スクリーン印刷
版の裏側に裏回りしたペーストやオフセット印刷機の転
写胴に残存するインキ、インクジェットプリンターのイ
ンク噴射口付近のインク汚れなどの溶剤含有物を確実に
付着させて除去できる溶剤含有物除去効果の高い溶剤含
有物除去用粘着シートを提供することにある。本発明の
他の目的は、粘着シートの基材の材質によらずに、上記
のような溶剤含有物を確実に且つ速やかに付着させて除
去できる溶剤含有物除去用粘着シートを提供することに
ある。SUMMARY OF THE INVENTION Accordingly, an object of the present invention is to reliably remove solvent-containing substances such as a paste wrapped around the back side of a screen printing plate, ink remaining on a transfer cylinder of an offset printing machine, and ink stains near an ink ejection port of an ink jet printer. It is an object of the present invention to provide a solvent-containing material removing pressure-sensitive adhesive sheet having a high effect of removing a solvent-containing material that can be removed by adhering to a sheet. Another object of the present invention is to provide a solvent-containing material-removing pressure-sensitive adhesive sheet capable of securely and quickly adhering and removing the solvent-containing material as described above, regardless of the material of the base material of the pressure-sensitive adhesive sheet. is there.
【０００７】[0007]
【課題を解決するための手段】本発明者は前記目的を達
成するために鋭意検討した結果、粘着シートの背面にお
ける算術平均粗さ（Ｒａ）を特定の大きさに規定する
と、基材の種類又は材質によらずに、溶剤含有物を確実
に且つ速やかに付着させて除去できる溶剤含有物除去用
粘着シートが得られることを見出し、本発明を完成させ
た。Means for Solving the Problems As a result of intensive studies conducted by the present inventor to achieve the above object, if the arithmetic mean roughness (Ra) on the back surface of the pressure-sensitive adhesive sheet is specified to a specific size, the type of the base material is determined. Alternatively, they have found that a pressure-sensitive adhesive sheet for removing a solvent-containing substance that can reliably and quickly adhere and remove the solvent-containing substance regardless of the material is obtained, and completed the present invention.
【０００８】すなわち、本発明は、基材と、該基材の少
なくとも片方の面に形成された粘着剤層とで構成されて
いる溶剤含有物除去用粘着シートであって、シート背面
の算術平均粗さ（Ｒａ）が０．５μｍ以下であることを
特徴とする溶剤含有物除去用粘着シートを提供する。That is, the present invention relates to a pressure-sensitive adhesive sheet for removing a solvent-containing substance, comprising a substrate and a pressure-sensitive adhesive layer formed on at least one surface of the substrate, wherein an arithmetic average of the back surface of the sheet is provided. Provided is an adhesive sheet for removing a solvent-containing substance, which has a roughness (Ra) of 0.5 μm or less.
【０００９】前記粘着シートは、例えばスクリーン印刷
版の清浄用の粘着シートとして用いることができる。The pressure-sensitive adhesive sheet can be used as, for example, a pressure-sensitive adhesive sheet for cleaning a screen printing plate.
【００１０】本発明では、粘着シートの背面の算術平均
粗さ（Ｒａ）は、ＪＩＳ Ｂ ０６０１に準拠した方法
で測定することができる。In the present invention, the arithmetic average roughness (Ra) on the back surface of the pressure-sensitive adhesive sheet can be measured by a method according to JIS B0601.
【００１１】[0011]
【発明の実施の形態】本発明の溶剤含有物除去用粘着シ
ートでは、粘着シートの背面（シート背面）における算
術平均粗さ（相加平均粗さ）（Ｒａ）が０．５μｍ以下
となっていることが重要なポイントである。粘着シート
は、通常、粘着剤層の表面がシート背面と重ね合わされ
た状態、特にロール状に巻かれた状態で保存や運搬等が
行われており、粘着剤層の表面は、通常、シート背面と
接している。従って、シート背面の表面粗さが大きい
と、粘着剤層はシート背面の基材より粘弾性であるた
め、シート背面に接している粘着剤層の表面の表面粗さ
も同じ程度にまで大きくなるようになる。そのため、シ
ート背面の算術平均粗さ（Ｒａ）が０．５μｍを越えて
いると、これに伴い粘着剤層の表面の平均粗さ（算術平
均粗さ）も大きくなり、スクリーン印刷板との密着性が
低下し、ペーストやインキ等の除去性が低下すると思わ
れる。しかし、本発明では、シート背面の算術平均粗さ
（Ｒａ）が０．５μｍ以下となっているので、スクリー
ン印刷板等の被着体との密着性の低下が抑制又は防止さ
れており、ペーストやインキ等の除去性の低下を抑制又
は防止することができる。BEST MODE FOR CARRYING OUT THE INVENTION In the pressure-sensitive adhesive sheet for removing a solvent-containing substance according to the present invention, the arithmetic mean roughness (arithmetic mean roughness) (Ra) on the back surface (sheet back surface) of the pressure-sensitive adhesive sheet is 0.5 μm or less. Is an important point. The pressure-sensitive adhesive sheet is usually stored or transported in a state in which the surface of the pressure-sensitive adhesive layer is superimposed on the back surface of the sheet, particularly in a state of being wound in a roll shape, and the surface of the pressure-sensitive adhesive layer is usually in the back surface of the sheet. Is in contact with Therefore, when the surface roughness of the back surface of the sheet is large, the pressure-sensitive adhesive layer is more viscoelastic than the base material of the back surface of the sheet, so that the surface roughness of the surface of the pressure-sensitive adhesive layer in contact with the back surface of the sheet is also increased to the same extent. become. Therefore, if the arithmetic average roughness (Ra) of the back surface of the sheet exceeds 0.5 μm, the average roughness (arithmetic average roughness) of the surface of the pressure-sensitive adhesive layer also increases, and the adhesion to the screen printing plate increases. It is thought that the removability is reduced, and the removability of paste, ink, and the like is reduced. However, in the present invention, since the arithmetic mean roughness (Ra) of the back surface of the sheet is 0.5 μm or less, a decrease in adhesion to an adherend such as a screen printing plate is suppressed or prevented, and the paste is used. It is possible to suppress or prevent a decrease in removability of ink and ink.
【００１２】本発明では、シート背面（すなわち算術平
均粗さ（Ｒａ）が０．５μｍ以下である背面）は、基材
の表面であってもよい。そのため、本発明では、表面の
算術平均粗さ（Ｒａ）が０．５μｍ以下である基材を用
いることにより、粘着シートの背面における算術平均粗
さを前記範囲となるようにコントロールすることができ
る。粘着シートの背面における算術平均粗さ（Ｒａ）と
しては、０．５μｍ以下であれば特に制限されないが、
０．３μｍ以下であることが好ましく、さらに０．１μ
ｍ以下であることが最適である。なお、粘着シートの背
面における算術平均粗さ（Ｒａ）の下限は特にないが、
一般には０．０１μｍ（好ましくは０．０２μｍ、さら
に好ましくは０．０３μｍ）程度である。In the present invention, the back surface of the sheet (that is, the back surface having an arithmetic average roughness (Ra) of 0.5 μm or less) may be the surface of the substrate. Therefore, in the present invention, the arithmetic average roughness on the back surface of the pressure-sensitive adhesive sheet can be controlled to be in the above range by using a substrate having an arithmetic average roughness (Ra) of 0.5 μm or less on the surface. . The arithmetic average roughness (Ra) on the back surface of the adhesive sheet is not particularly limited as long as it is 0.5 μm or less.
0.3 μm or less, preferably 0.1 μm
Most preferably, it is less than m. There is no particular lower limit for the arithmetic average roughness (Ra) on the back surface of the adhesive sheet,
Generally, it is about 0.01 μm (preferably 0.02 μm, more preferably 0.03 μm).
【００１３】本発明の粘着シートの基材としては特に制
限はないが、ゴミや異物の混入を避けたい場合は、ポリ
エチレンフィルム、ポリプロピレンフィルム等のポリオ
レフィン系フィルム；ポリエチレンテレフタレートフィ
ルム等のポリエステルフィルムなどのプラスチックフィ
ルムが紙粉の発生のおそれがなく好適に使用される。単
にロールの清掃に使用する場合などは、基材として紙な
ども使用できる。また、凹凸面上のペーストやインキを
除去する用途には、ポリウレタン、ポリエチレン、ＥＰ
ＤＭ（エチレン−プロピレン−ジエンゴム）などの発泡
体も基材として好適に使用される。さらに、用途によっ
ては、基材として、不織布、布、金属箔などを用いるこ
ともできる。The base material of the pressure-sensitive adhesive sheet of the present invention is not particularly limited. However, when it is desired to prevent dust and foreign matter from being mixed, a polyolefin film such as a polyethylene film or a polypropylene film; a polyester film such as a polyethylene terephthalate film; A plastic film is preferably used without fear of generating paper dust. In the case where the roll is simply used for cleaning the roll, paper can be used as the base material. Applications for removing paste and ink on uneven surfaces include polyurethane, polyethylene, EP
A foam such as DM (ethylene-propylene-diene rubber) is also suitably used as the base material. Furthermore, depending on the application, a nonwoven fabric, cloth, metal foil, or the like can be used as the base material.
【００１４】本発明では、基材としては、その表面の算
術平均粗さ（Ｒａ）が０．５μｍ以下のものを好適に用
いることができる。そのため、基材としては、プラスチ
ックフィルムが好適である。In the present invention, a substrate having an arithmetic average roughness (Ra) of 0.5 μm or less can be suitably used as the substrate. Therefore, a plastic film is suitable as the substrate.
【００１５】基材の厚みも特に制限されず、強度や作業
性などを考慮して適宜設定できるが、一般には１０〜５
００μｍ、好ましくは１２〜２００μｍ、更に好ましく
は１５〜１００μｍ程度である。基材が発泡体の場合に
は、数ｍｍから数十ｍｍの厚さが一般的である。The thickness of the substrate is not particularly limited and can be appropriately set in consideration of strength, workability, and the like.
It is about 00 μm, preferably about 12 to 200 μm, and more preferably about 15 to 100 μm. When the substrate is a foam, a thickness of several mm to several tens mm is generally used.
【００１６】なお、基材は単層の形態を有していてもよ
く、また、複層の形態を有していてもよい。さらにま
た、前記基材の表面における算術平均粗さ（Ｒａ）が
０．５μｍを越えている場合、粘着シートの背面側とな
る方に、表面の算術平均粗さ（Ｒａ）が０．５μｍ以下
の基材を積層することにより、シート背面の算術平均粗
さ（Ｒａ）が０．５μｍ以下となるように、シート背面
の算術平均粗さ（Ｒａ）をコントロールすることができ
る。The substrate may have a single-layer form or a multi-layer form. Furthermore, when the arithmetic average roughness (Ra) on the surface of the base material exceeds 0.5 μm, the arithmetic average roughness (Ra) on the surface is 0.5 μm or less toward the back side of the adhesive sheet. By laminating the base material, the arithmetic average roughness (Ra) of the back surface of the sheet can be controlled so that the arithmetic average roughness (Ra) of the back surface of the sheet is 0.5 μm or less.
【００１７】本発明の粘着シートの粘着剤層を構成する
粘着剤としては、特に制限はなく、例えば、ゴム系粘着
剤（例えば、天然ゴム系、スチレン−ブタジエン共重合
体系、ポリイソブチレン系、スチレン−イソプレン−ス
チレン共重合体系など）、アクリル系粘着剤など、任意
の粘着剤が使用できる。これらの粘着剤の中でも、アク
リル系粘着剤が好ましい。The pressure-sensitive adhesive constituting the pressure-sensitive adhesive layer of the pressure-sensitive adhesive sheet of the present invention is not particularly limited, and examples thereof include rubber-based pressure-sensitive adhesives (for example, natural rubber-based, styrene-butadiene copolymer-based, polyisobutylene-based, and styrene-based pressure-sensitive adhesives). Any adhesive such as an isoprene-styrene copolymer system) and an acrylic adhesive can be used. Among these adhesives, an acrylic adhesive is preferable.
【００１８】アクリル系粘着剤は、一般に、粘着性を与
える主モノマー、凝集性を与えるコモノマー、及び粘着
性を向上させたり架橋点を形成するための官能基含有モ
ノマーより形成される。前記主モノマーとしては、例え
ば、アクリル酸エチル、アクリル酸プロピル、アクリル
酸イソプロピル、アクリル酸ブチル、アクリル酸イソブ
チル、アクリル酸ペンチル、アクリル酸ヘキシル、アク
リル酸ヘプチル、アクリル酸オクチル、アクリル酸２−
エチルヘキシル、アクリル酸ノニル、アクリル酸デシル
などのアクリル酸Ｃ2-10アルキルエステルなどが挙げら
れる。The acrylic pressure-sensitive adhesive is generally formed of a main monomer for providing tackiness, a comonomer for providing cohesion, and a monomer having a functional group for improving tackiness or forming a crosslinking point. Examples of the main monomer include ethyl acrylate, propyl acrylate, isopropyl acrylate, butyl acrylate, isobutyl acrylate, pentyl acrylate, hexyl acrylate, heptyl acrylate, octyl acrylate, and acrylate 2-
Examples include C 2-10 alkyl acrylates such as ethylhexyl, nonyl acrylate, and decyl acrylate.
【００１９】前記凝集性を与えるコモノマーとしては、
例えば、アクリル酸メチル；メタクリル酸メチル、メタ
クリル酸エチル、メタクリル酸イソプロピルなどのメタ
クリル酸アルキルエステル；酢酸ビニル等のビニルエス
テル類；スチレン、α−メチルスチレン、ビニルトルエ
ンなどのスチレン系モノマー；アクリロニトリルなどが
挙げられる。これらの中でも、ビニルエステル類、アク
リロニトリルなどが好ましい。Examples of the comonomers providing the cohesiveness include:
For example, methyl acrylate; alkyl methacrylates such as methyl methacrylate, ethyl methacrylate, and isopropyl methacrylate; vinyl esters such as vinyl acetate; styrene monomers such as styrene, α-methyl styrene, and vinyl toluene; acrylonitrile; No. Among these, vinyl esters and acrylonitrile are preferred.
【００２０】前記官能基含有モノマーとしては、例え
ば、アクリル酸、メタクリル酸、イタコン酸、無水マレ
イン酸などのカルボキシル基又は酸無水物基含有モノマ
ー；アクリル酸２−ヒドロキシエチル、メタクリル酸２
−ヒドロキシエチル、メタクリル酸ヒドロキシプロピル
などのヒドロキシル基含有モノマー；アクリル酸グリシ
ジル、メタクリル酸グリシジルなどのエポキシ基含有モ
ノマー；Ｎ−メチロールアクリルアミド、Ｎ−メチロー
ルメタクリルアミドなどのアミド基含有モノマー；メタ
クリル酸ジメチルアミノエチル、メタクリル酸ｔ−ブチ
ルアミノエチルなどのアミノ基含有モノマーなどが挙げ
られる。これらの中でも、官能基含有モノマーとして、
アクリル酸などのカルボキシル基又は酸無水物基含有モ
ノマーなどが好ましい。Examples of the functional group-containing monomer include carboxyl group or acid anhydride group-containing monomers such as acrylic acid, methacrylic acid, itaconic acid and maleic anhydride; 2-hydroxyethyl acrylate, methacrylic acid 2
-Hydroxyl group-containing monomers such as hydroxyethyl and hydroxypropyl methacrylate; epoxy group-containing monomers such as glycidyl acrylate and glycidyl methacrylate; amide group-containing monomers such as N-methylol acrylamide and N-methylol methacrylamide; dimethylamino methacrylate Amino group-containing monomers such as ethyl and t-butylaminoethyl methacrylate are exemplified. Among these, as a functional group-containing monomer,
Carboxyl group or acid anhydride group-containing monomers such as acrylic acid are preferred.
【００２１】アクリル系粘着剤を形成する前記主モノマ
ー、コモノマー及び官能基含有モノマーの割合は、除去
対象となる溶剤含有物の種類（固形分の種類及び溶剤の
種類）等により適宜選択できるが、例えば、全モノマー
成分に対する割合として、前記主モノマーは、４０〜９
８重量％程度、好ましくは５０〜９５重量％程度であ
り、前記コモノマーは、０〜５０重量％程度、好ましく
は２〜４０重量％程度であり、前記官能基含有モノマー
は０．５〜１５重量％、好ましくは１〜１０重量％程度
である。The proportions of the main monomer, comonomer and functional group-containing monomer forming the acrylic pressure-sensitive adhesive can be appropriately selected depending on the type of the solvent-containing substance to be removed (the type of the solid content and the type of the solvent). For example, as a ratio to the total monomer components, the main monomer is 40 to 9
About 8% by weight, preferably about 50 to 95% by weight, the comonomer is about 0 to 50% by weight, preferably about 2 to 40% by weight, and the functional group-containing monomer is 0.5 to 15% by weight. %, Preferably about 1 to 10% by weight.
【００２２】粘着剤層には、粘着剤ポリマー（ベースポ
リマー）に加えて、種々の添加剤、例えば、架橋剤（例
えば、イソシアネート系架橋剤、エポキシ系架橋剤、ウ
レア系架橋剤、メラミン系架橋剤、カルボン酸又は酸無
水物系架橋剤、金属化合物系架橋剤など）、粘着付与剤
［例えば、テルペン系樹脂（テルペン樹脂、テルペンフ
ェノール樹脂、芳香族変性テルペン樹脂、水添テルペン
樹脂など）、石油樹脂（脂肪族系、芳香族系、脂環式
系）、ロジン系樹脂（ロジン、水添ロジンエステルな
ど）、クマロン・インデン樹脂、スチレン系樹脂等］、
界面活性剤（リン酸エステル系、硫酸エステル系、スル
ホン酸系、カルボン酸系などのアニオン系界面活性剤；
アミン塩系、第４級アンモニウム塩系などのカチオン系
界面活性剤；エステル系、エーテル系、エステルエーテ
ル系、アルカノールアミド系などのノニオン系界面活性
剤；カルボキシベタイン系、グリシン系などの両性界面
活性剤）、可塑剤、酸化防止剤、着色剤、帯電防止剤、
充填剤、発泡剤などが含まれていてもよい。好ましい架
橋剤には、イソシアネート系架橋剤などが含まれ、好ま
しい粘着付与剤には、テルペンフェノール樹脂などのテ
ルペン系樹脂等が含まれる。In the pressure-sensitive adhesive layer, in addition to the pressure-sensitive adhesive polymer (base polymer), various additives such as a crosslinking agent (for example, an isocyanate-based crosslinking agent, an epoxy-based crosslinking agent, a urea-based crosslinking agent, and a melamine-based crosslinking agent) Agents, carboxylic acid or acid anhydride crosslinking agents, metal compound crosslinking agents, etc.), tackifiers [for example, terpene resins (terpene resins, terpene phenol resins, aromatic modified terpene resins, hydrogenated terpene resins, etc.), Petroleum resin (aliphatic, aromatic, alicyclic), rosin resin (rosin, hydrogenated rosin ester, etc.), cumarone / indene resin, styrene resin, etc.],
Surfactants (anionic surfactants such as phosphate esters, sulfate esters, sulfonic acids, and carboxylic acids);
Cationic surfactants such as amine salts and quaternary ammonium salts; Nonionic surfactants such as ester, ether, ester ether and alkanolamide; amphoteric surfactants such as carboxybetaine and glycine Agents), plasticizers, antioxidants, coloring agents, antistatic agents,
A filler, a foaming agent, and the like may be included. Preferred crosslinking agents include isocyanate-based crosslinking agents, and preferred tackifiers include terpene-based resins such as terpene-phenol resins.
【００２３】これらの添加剤の使用量は、粘着性等を損
なわない範囲で適宜選択できる。例えば、架橋剤の使用
量は、粘着剤ポリマー（ベースポリマー）１００重量部
に対して、例えば１〜３０重量部程度、好ましくは２〜
１５重量部程度である。The amount of these additives can be appropriately selected within a range that does not impair the adhesiveness and the like. For example, the amount of the crosslinking agent used is, for example, about 1 to 30 parts by weight, preferably 2 to 30 parts by weight, based on 100 parts by weight of the pressure-sensitive adhesive polymer (base polymer).
It is about 15 parts by weight.
【００２４】なお、本発明では、粘着剤層を構成する粘
着剤が、除去対象物に含まれる溶剤に対して不溶性の成
分のみで構成されていてもよい。例えば、架橋剤以外の
添加剤、特に可塑剤や界面活性剤などは、例えばスクリ
ーン印刷用ペースト等に含まれる溶剤に溶出しやすいの
で、必要最小量にとどめるのが好ましく、さらにはその
ような除去対象物に含まれる溶剤に対して可溶性のもの
（該溶剤により溶出されうるもの）は添加しないのが良
い。In the present invention, the pressure-sensitive adhesive constituting the pressure-sensitive adhesive layer may be composed of only a component insoluble in a solvent contained in the object to be removed. For example, additives other than the cross-linking agent, particularly plasticizers and surfactants, are easily eluted in a solvent contained in, for example, a screen printing paste or the like. It is preferable not to add a solvent that is soluble in the solvent contained in the object (that can be eluted by the solvent).
【００２５】粘着剤層の厚みは、本発明の上記特性が得
られる範囲で任意に設定でき、例えば５〜５０００μｍ
程度、好ましくは１０〜２０００μｍ程度である。The thickness of the pressure-sensitive adhesive layer can be arbitrarily set as long as the above-mentioned characteristics of the present invention can be obtained.
Degree, preferably about 10 to 2000 μm.
【００２６】除去対象となる溶剤含有物としては、特に
限定されず、溶剤を含有して湿った状態にある半固形
物、例えば、ペースト、インキ、糊、接着剤、塗料など
が挙げられる。The solvent-containing substance to be removed is not particularly limited, and includes a semi-solid substance containing a solvent and being wet, for example, paste, ink, paste, adhesive, paint, and the like.
【００２７】前記溶剤含有物に含まれる溶剤としては、
例えば、ヘキサン、ヘプタン、ミネラルスピリットなど
の脂肪族炭化水素；シクロヘキサンなどの脂環式炭化水
素；トルエン、キシレン、ソルベントナフサ、テトラリ
ン、ジペンテンなどの芳香族炭化水素；メチルアルコー
ル、エチルアルコール、イソプロピルアルコール、ブチ
ルアルコール、イソブチルアルコール、ｓ−ブチルアル
コール、シクロヘキシルアルコール、２−メチルシクロ
ヘキシルアルコール、トリデシルアルコールなどのアル
コール；酢酸メチル、酢酸エチル、酢酸イソプロピル、
酢酸ブチルなどのエステル；アセトン、メチルエチルケ
トン、メチルイソブチルケトン、シクロヘキサノン、メ
チルシクロヘキサノン、ジアセトンアルコール、イソホ
ロンなどのケトン；エチレングリコール、プロピレング
リコール、ジエチレングリコール、トリエチレングリコ
ール、ジプロピレングリコールなどのグリコール；ブチ
ルセロソルブ、プロピレングリコールモノメチルエーテ
ル、プロピレングリコールモノエチルエーテル、プロピ
レングリコールモノブチルエーテル、ジエチレングリコ
ールモノブチルエーテルなどのグリコールエーテル；ブ
チルセロソルブアセテート、プロピレングリコールモノ
メチルエーテルアセテート、プロピレングリコールモノ
エチルエーテルアセテート、ジエチレングリコールモノ
ブチルエーテルアセテートなどのグリコールエーテルエ
ステル；水などが挙げられる。スクリーン印刷インキの
場合には、中沸点溶剤（沸点：約１２０〜２３０℃）や
高沸点溶剤（沸点：約２３０〜３２０℃）が多く用いら
れており、例えば、ジエチレングリコールモノブチルエ
ーテルアセテート、ジエチレングリコールモノブチルエ
ーテルなど（例えば、ジエチレングリコールモノブチル
エーテルアセテート／ジエチレングリコールモノブチル
エーテル［９／１（重量比）］）などが挙げられる。The solvent contained in the solvent-containing material includes:
For example, aliphatic hydrocarbons such as hexane, heptane and mineral spirit; alicyclic hydrocarbons such as cyclohexane; aromatic hydrocarbons such as toluene, xylene, solvent naphtha, tetralin, and dipentene; methyl alcohol, ethyl alcohol, isopropyl alcohol; Alcohols such as butyl alcohol, isobutyl alcohol, s-butyl alcohol, cyclohexyl alcohol, 2-methylcyclohexyl alcohol, and tridecyl alcohol; methyl acetate, ethyl acetate, isopropyl acetate;
Esters such as butyl acetate; ketones such as acetone, methyl ethyl ketone, methyl isobutyl ketone, cyclohexanone, methyl cyclohexanone, diacetone alcohol, and isophorone; glycols such as ethylene glycol, propylene glycol, diethylene glycol, triethylene glycol, and dipropylene glycol; butyl cellosolve, propylene Glycol ethers such as glycol monomethyl ether, propylene glycol monoethyl ether, propylene glycol monobutyl ether, and diethylene glycol monobutyl ether; butyl cellosolve acetate, propylene glycol monomethyl ether acetate, propylene glycol monoethyl ether acetate, diethylene glycol monobutyl ether acetate Glycol ether esters such as Tate; and water. In the case of screen printing inks, medium-boiling solvents (boiling point: about 120 to 230 ° C.) and high-boiling solvents (boiling point: about 230 to 320 ° C.) are often used. For example, diethylene glycol monobutyl ether acetate, diethylene glycol monobutyl ether And the like (for example, diethylene glycol monobutyl ether acetate / diethylene glycol monobutyl ether [9/1 (weight ratio)]).
【００２８】本発明において、溶剤含有物除去用粘着シ
ートの使用前の粘着力としては、ＪＩＳ Ｚ ０２３７
に準拠した方法（試験板としてＳＵＳ４３０ＢＡを用
い、粘着シートを試験板に圧着して１分後に測定）で、
４Ｎ／２５ｍｍ（４００ｇｆ／２５ｍｍ）以下（例え
ば、０．０１〜４Ｎ／２５ｍｍ程度）が好ましく、より
好ましくは３Ｎ／２５ｍｍ（３００ｇｆ／２５ｍｍ）以
下（例えば、０．０３〜３Ｎ／２５ｍｍ程度）である。In the present invention, the adhesive strength before use of the pressure-sensitive adhesive sheet for removing a solvent-containing substance is determined according to JIS Z 0237.
(Measured 1 minute after pressing the pressure-sensitive adhesive sheet on the test plate using SUS430BA as the test plate)
It is preferably 4 N / 25 mm (400 gf / 25 mm) or less (for example, about 0.01 to 4 N / 25 mm), and more preferably 3 N / 25 mm (300 gf / 25 mm) or less (for example, about 0.03 to 3 N / 25 mm). .
【００２９】本発明の粘着シートは、コーティング法な
どの慣用の方法を用いて、基材上に粘着剤層を形成する
ことにより製造できる。粘着剤層は、通常、基材の片面
に形成されている。The pressure-sensitive adhesive sheet of the present invention can be produced by forming a pressure-sensitive adhesive layer on a substrate by a conventional method such as a coating method. The pressure-sensitive adhesive layer is usually formed on one side of the substrate.
【００３０】本発明の粘着シートでは、粘着剤層がシー
ト背面と重ねられていても、シート背面の算術平均粗さ
（Ｒａ）が小さいので、使用時（スクリーン印刷板等の
被着体に貼り付ける際）の粘着剤層における表面の算術
平均粗さ（Ｒａ）が小さくなっており、スクリーン印刷
板等の被着体との密着性が高めることができる。そのた
め、例えば、スクリーン印刷に使用するペースト（イン
キ）や、オフセット印刷機などの印刷機のロール類に付
着したインキ等の溶剤含有物中に含まれる溶剤を粘着剤
層により効率よく吸収することができるので、粘着シー
トをスクリーン版の裏側やロール類等に貼り付けること
により、スクリーン版の裏側に裏回りしたペーストやロ
ール類に付着したインキなどに含まれている溶剤をほと
んど吸収して、該ペースト等を固形物化できる。従っ
て、本発明の溶剤含有物除去用粘着シートは、例えば、
スクリーン印刷版の裏側に裏回りしたペースト（イン
キ）や、オフセット印刷等の印刷機のロール類に付着し
たインキ、インクジェットプリンターのインク噴射口付
近のインク汚れなどを除去するのに適している。In the pressure-sensitive adhesive sheet of the present invention, even when the pressure-sensitive adhesive layer is superimposed on the back surface of the sheet, the arithmetic mean roughness (Ra) of the back surface of the sheet is small, so that the pressure-sensitive adhesive layer can be used at the time of use. The arithmetic average roughness (Ra) of the surface of the pressure-sensitive adhesive layer at the time of attachment) is small, and the adhesion to an adherend such as a screen printing plate can be increased. Therefore, for example, the solvent contained in solvent-containing materials such as paste (ink) used for screen printing and ink attached to rolls of a printing machine such as an offset printing machine can be efficiently absorbed by the adhesive layer. Since the adhesive sheet can be adhered to the back side of the screen plate or rolls, etc., the solvent contained in the ink or the like attached to the paste or rolls wrapped around the back side of the screen plate is almost absorbed. A paste or the like can be solidified. Therefore, the pressure-sensitive adhesive sheet for removing a solvent-containing substance of the present invention includes, for example,
It is suitable for removing paste (ink) wrapped around the back side of a screen printing plate, ink adhered to rolls of a printing machine such as offset printing, ink stain near an ink ejection port of an inkjet printer, and the like.
【００３１】[0031]
【発明の効果】本発明の溶剤含有物除去用粘着シートに
よれば、シート背面の算術平均粗さが小さいため、使用
時における粘着剤層の表面の算術平均粗さが小さくなっ
ているので、スクリーン印刷板との密着性が向上し、ス
クリーン版の裏側に裏回りしたペーストなどの被処理体
に付着した溶剤含有物を確実に付着させて除去できる。
そのため、スクリーン印刷の場合は滲みによる印刷不良
を軽減することができ、オフセット印刷、グラビア印
刷、フレキソ印刷の場合は各ロール類の清掃時間を短縮
でき、生産性を向上できる。According to the pressure-sensitive adhesive sheet for removing a solvent-containing substance of the present invention, the arithmetic average roughness of the back surface of the sheet is small, and the arithmetic average roughness of the surface of the pressure-sensitive adhesive layer during use is small. The adhesion to the screen printing plate is improved, and the solvent-containing substances such as the paste wrapped around the back side of the screen plate and adhered to the object to be processed can be reliably adhered and removed.
Therefore, in the case of screen printing, printing defects due to bleeding can be reduced, and in the case of offset printing, gravure printing, or flexographic printing, the cleaning time for each roll can be reduced, and productivity can be improved.
【００３２】[0032]
【実施例】以下に、実施例に基づいて本発明をより詳細
に説明するが、本発明はこれらの実施例により限定され
るものではない。EXAMPLES The present invention will be described below in more detail with reference to Examples, but the present invention is not limited to these Examples.
【００３３】実施例１ 厚さ０．０６ｍｍのポリエチレンフィルム（基材）の片
面に、アクリル系粘着剤［ブチルアクリレート／アクリ
ル酸（重量比：９６／４）の共重合体１００重量部＋イ
ソシアネート系架橋剤１５重量部］を、乾燥後の厚みが
１０μｍとなるように塗布し、乾燥して、粘着シートを
作製した。この粘着シートの使用前の粘着力を、ＪＩＳ
Ｚ ０２３７に準拠した測定法（但し、試験板として
ＳＵＳ４３０ＢＡを用い、粘着シートを試験板に圧着し
て１分後に測定）により測定したところ、１４０ｃＮ／
２５ｍｍであった。また、この粘着シートの背面の算術
平均粗さ（Ｒａ）を、ＪＩＳ Ｂ ０６０１に準拠した
方法で測定したところ、０．０４μｍであった。Example 1 One side of a polyethylene film (substrate) having a thickness of 0.06 mm was coated on one side with an acrylic pressure-sensitive adhesive [100 parts by weight of a copolymer of butyl acrylate / acrylic acid (weight ratio: 96/4) + isocyanate type] 15 parts by weight of a crosslinking agent] was applied so that the thickness after drying was 10 μm, and dried to prepare an adhesive sheet. The adhesive strength of this adhesive sheet before use is measured according to JIS
When measured by a measuring method in accordance with Z0237 (using SUS430BA as a test plate and pressing the pressure-sensitive adhesive sheet against the test plate and measuring one minute later), 140 cN /
It was 25 mm. The arithmetic mean roughness (Ra) of the back surface of the pressure-sensitive adhesive sheet was measured by a method in accordance with JIS B0601, and was found to be 0.04 μm.
【００３４】実施例１により得られた粘着シートを、ロ
ール状に巻き取った状態で、温度：２３℃、湿度：６５
％ＲＨの条件で、１０日間保管した後、実際のスクリー
ン印刷工程で、スクリーン印刷版の裏側に貼り付けたと
ころ、ペーストの除去性は良好であった。The pressure-sensitive adhesive sheet obtained in Example 1 was wound into a roll, and was subjected to a temperature of 23 ° C. and a humidity of 65.
After storage for 10 days under the condition of% RH, the paste was attached to the back side of the screen printing plate in an actual screen printing step, and the removability of the paste was good.
【００３５】実施例２ 厚さ０．０４ｍｍのポリプロピレン／ポリエチレン（重
量比：９０／１０）ブレンドフィルム（基材）の片面
に、アクリル系粘着剤［ブチルアクリレート／アクリル
酸（重量比：９６／４）の共重合体１００重量部＋テル
ペンフェノール系粘着付与剤７重量部＋イソシアネート
系架橋剤１５重量部］を、乾燥後の厚みが１０μｍとな
るように塗布し、乾燥して、粘着シートを作製した。こ
の粘着シートの使用前の粘着力、およびシート背面の算
術平均粗さ（Ｒａ）を実施例１と同様にして測定したと
ころ、１４０ｃＮ／２５ｍｍ、０．３６μｍであった。Example 2 An acrylic adhesive [butyl acrylate / acrylic acid (weight ratio: 96/4) was applied to one surface of a polypropylene / polyethylene (weight ratio: 90/10) blend film (base material) having a thickness of 0.04 mm. 100 parts by weight of the copolymer) +7 parts by weight of a terpene phenol-based tackifier + 15 parts by weight of an isocyanate-based cross-linking agent], and dried to form a pressure-sensitive adhesive sheet. did. The adhesive strength before use of this adhesive sheet and the arithmetic average roughness (Ra) of the back surface of the sheet were measured in the same manner as in Example 1, and were 140 cN / 25 mm and 0.36 μm.
【００３６】また、実施例２により得られた粘着シート
を、実施例１と同様にして、ロール状に巻き取った状態
で、温度：２３℃、湿度：６５％ＲＨの条件で、１０日
間保管した後、実施例１と同様の実際のスクリーン印刷
工程で、スクリーン印刷版の裏側に貼り付けたところ、
ペーストの除去性は良好であった。Further, the pressure-sensitive adhesive sheet obtained in Example 2 was stored for 10 days under the conditions of a temperature of 23 ° C. and a humidity of 65% RH in a state of being wound into a roll in the same manner as in Example 1. After that, in the actual screen printing process similar to that of Example 1, when pasted on the back side of the screen printing plate,
The removability of the paste was good.
【００３７】比較例１ 坪量７０ｇ／ｍ2のポリエチレンラミネート紙の片面
に、アクリル系粘着剤［ブチルアクリレート／アクリル
酸（重量比：９６／４）の共重合体１００重量部＋イソ
シアネート系架橋剤１５重量部］を、乾燥後の厚みが２
０μｍとなるように塗布し、乾燥して、粘着シートを作
製した。この粘着シートの使用前の粘着力、およびシー
ト背面の算術平均粗さ（Ｒａ）を実施例１と同様にして
測定したところ、１００ｃＮ／２５ｍｍ、０．７４μｍ
であった。Comparative Example 1 An acrylic adhesive [100 parts by weight of a copolymer of butyl acrylate / acrylic acid (weight ratio: 96/4) +100 parts by weight of an isocyanate-based crosslinking agent] was applied to one side of a polyethylene laminated paper having a basis weight of 70 g / m 2. 15 parts by weight] when the thickness after drying is 2
The composition was applied so as to have a thickness of 0 μm and dried to prepare an adhesive sheet. The adhesive strength before use of this adhesive sheet and the arithmetic average roughness (Ra) of the back surface of the sheet were measured in the same manner as in Example 1. As a result, 100 cN / 25 mm, 0.74 μm
Met.
【００３８】また、比較例１により得られた粘着シート
を、実施例１と同様にして、ロール状に巻き取った状態
で、温度：２３℃、湿度：６５％ＲＨの条件で、１０日
間保管した後、実施例１と同様の実際のスクリーン印刷
工程で、スクリーン印刷版の裏側に貼り付けたところ、
ペーストの除去性が不十分であり、印刷不良（にじみ）
が発生した。Further, the pressure-sensitive adhesive sheet obtained in Comparative Example 1 was stored for 10 days at a temperature of 23 ° C. and a humidity of 65% RH in a state wound up in a roll in the same manner as in Example 1. After that, in the actual screen printing process similar to that of Example 1, when pasted on the back side of the screen printing plate,
Poor removability of paste, poor printing (bleeding)
There has occurred.
───────────────────────────────────────────────────── フロントページの続き Ｆターム(参考） 2C035 FD29 2C250 FA05 FB11 4J004 AA04 AA05 AA07 AA10 AB01 CA04 CA06 CC02 EA06 FA10 ──────────────────────────────────────────────────続 き Continued on the front page F term (reference) 2C035 FD29 2C250 FA05 FB11 4J004 AA04 AA05 AA07 AA10 AB01 CA04 CA06 CC02 EA06 FA10
Claims (2)
形成された粘着剤層とで構成されている溶剤含有物除去
用粘着シートであって、シート背面の算術平均粗さ（Ｒ
ａ）が０．５μｍ以下であることを特徴とする溶剤含有
物除去用粘着シート。1. A pressure-sensitive adhesive sheet for removing a solvent-containing substance, comprising a substrate and a pressure-sensitive adhesive layer formed on at least one surface of the substrate, wherein an arithmetic average roughness (R
a) The adhesive sheet for removing a solvent-containing substance, wherein a) is 0.5 μm or less.
れる請求項１記載の溶剤含有物除去用粘着シート。2. The pressure-sensitive adhesive sheet according to claim 1, which is used for cleaning a screen printing plate.