DE1567860B2 - Zeolithisch« Molekularsiebe, die Lignosulfonat enthalten Ausscheidung aus 1213392 - Google Patents
Zeolithisch« Molekularsiebe, die Lignosulfonat enthalten Ausscheidung aus 1213392Info
- Publication number
- DE1567860B2 DE1567860B2 DE1567860A DE1567860A DE1567860B2 DE 1567860 B2 DE1567860 B2 DE 1567860B2 DE 1567860 A DE1567860 A DE 1567860A DE 1567860 A DE1567860 A DE 1567860A DE 1567860 B2 DE1567860 B2 DE 1567860B2
- Authority
- DE
- Germany
- Prior art keywords
- molecular sieves
- lignosulfonate
- weight
- percent
- sodium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
Aus der deutschen Patentschrift 1040 005 sind gebundene zeolithische Molekularsiebe bekannt, die
als Bindemittel 1 bis 40 Gewichtsprozent Tonmineral, z. B. feinteilige Kaoline, enthalten. Die Bruch- und;
Abriebfestigkeit dieser geformten Molekularsiebe genügt bei längerer Verwendung, höheren Temperaturen
und mehrfacher Regenerierung nicht allen Ansprüchen.
Der Erfindung liegt die Aufgabe zugrunde, ein geformtes Molekularsieb zu schaffen, das sich durch
hohe Bruch- und Abriebfestigkeit und gleichbleibend gute Adsorptionseigenschaften auszeichnet.
Gegenstand der Erfindung sind geformte Molekularsiebe
aus kristallinen Zeolithen und 1 bis 40 Gewichtsprozent kaolinischem Ton als Bindemittel, die dadurch
gekennzeichnet sind, daß sie 55 bis 97 Gewichtsprozent kristalline Zeolithe und 2 bis 5 Gewichtsprozent eines
Lignosulfonats enthalten.
Die erfindungsgemäßen Molekularsiebe haben besonders gute Eigenschaften, wenn sie 10 bis 25 Gewichtsprozent
eines kaolinischen Tons.nnd als kristallinen Zeolith; Natrium-Zeolith X oder Natrium- oder
Calcium-Zeoiith A enthalten.
Als kaolinische Tone im Sinne der Erfindung kommen beispielsweise in Betracht: Kaolin, Kaolinit,
Halloysit, Andellit, Dickit, Kugelton, Averyton, Porzellanton. Alle ■ diese Tone haben ■ die Formel
Al2O3 · ZSiO2 · 2 bis 4 H2O, wobei ζ etwa zwischen
1,8 und 2,3, üblicherweise bei ungefähr 2 liegt. Tone anderer Struktur, z. B. Attapulgit und Bentonit, sind
nicht so gut verwendbar und ergeben Siebe von geringerer Adsorptionsfähigkeit. ' ... - . : . ! '
Die genannten Grenzen für den Zusatz des Lignosulfonats sind in einem gewissen Ausmaße kritisch.
Bei einem Gehalt unter 2 Gewichtsprozent haben die Molekularsiebe eine Bruchfestigkeit, die praktisch
nicht über der Bruchfestigkeit von solchen Sieben liegt, welche kein Lignosulfonat enthalten. Bei einem
Gehalt über 5 Gewichtsprozent nimmt die Adsorptionsfähigkeit ab.
Es wurde ferner gefunden, daß ausgezeichnete Molekularsiebe ein kristallines zeolithisches Molekularsieb
A, z. B. ein Natrium- oder Calziumzeolith A, oder ein kristallines zeolithisches Molekularsieb X,
z. B. einen Natrium- oder Galziumzeolith X, ent
halten. Auch Gemische dieser beiden Typen sind
'■■■.'•brauchbar.'·'-·.'.·'. '· '■':■ '.'..'■'■. ■■""■; \;\.;;;
Der Gehalt an kaolinischem Ton kann innerhalb recht weiter Grenzen schwanken. Gute Ergebnisse
werden bei Gehalten von 10 bis 25 Gewichtsprozent erhalten.
Die Molekularsiebe - nach "dem Verfahren der Erfindung zeichnen sich durchweine ausgezeichnete
Adsorptionsfähigkeit für viele Stoffe, durch eine hohe
ίο Bruchfestigkeit und durch eine gute Abriebfestigkeit
aus, auch bei längerer Verwendung bei höheren Temperaturen. und mehrfacher Regenerierung.,
Es wurde festgestellt, daß die erfindungsgemäßen Molekularsiebe trotz ihres Gehaltes an Lignosulfonat
auch bei hohen Temperaturen in einem Sauerstoff strom sich weder entzünden noch explodieren.
Um den Einfluß des Lignosulfonats auf die Bruchfestigkeit
und die Dichte zu prüfen, wurden aus 80 Gewichtsteilen pulverförmigem Natriumzeolith X und
ao 20 Gewichtsteilen Kaolinton mit wechselnden Zusätzen
von Natriumlignosulfonat Kugeln von 0,33 cm Durchmesser hergestellt. Die mittlere Bruchfestigkeit
wurde auf einem Amboß mit einem Durchmesser von 0,68 cm geprüft. Die Ergebnisse sind in der nachstehenden
Tabelle enthalten:
Natrium lignosulfonat |
Bruchfestigkeit | Dichte |
(%) | (kg) | |
0,0 | 4,54 | — 0,945 |
0,5 | 6,43 | 0,994 |
1,0 | 8,19 | 0,962' |
1,5 | 8,67 | 0,962 |
2,0 | 17,24 | 1,010 |
3,0 | 17,78 | 1,042 |
5,0 | 11,70 | 0,978. |
Um den Einfluß des Lignosulfonats auf weitere Eigenschaften der Molekularsiebe zu prüfen, wurden
Kugeln von 0,33 cm Durchmesser aus folgenden Mischungen hergestellt:
Gewichtsprozent
A Calziumzeolith A 77,7
Natriumlignosulfonat 2,9
Averyton ...........;..... 19,6
B Calziumzeolith A 80,0
Averyton 20,0
C Natriumzeolith X 77,7
Natriumlignosulfonat 2,9
Averyton ...........;::'. 19,6
D Natriumzeolith X 80,0
Averyton 20,0
Geprüft wurden die mittlere Bruchfestigkeit in kg, die Dichte, die Adsorptionsfähigkeit für Sauerstoff bei
-1830C und einem Druck von 100 mm Hg in frisch
hergestelltem Zustand und nach 24stündigem Behandeln mit Dampf in Gewichtsprozent und der Abriebverlust
in Gewichtsprozent. Die Ergebnisse sind in der nachstehenden Tabelle enthalten:
Muster
Bruchfestigkeit (kg)
Dichte
(^-Adsorption (Gewichtsprozent) frisch I gedämpft
Abrieb (Gewichtsprozent)
A
B
C
D
B
C
D
22,7 bis 27,2
5,44
17,69
4,54
1,187 1,122 1,042 0,945
21,8 21,3 24,3 25,0
18,8 13,7
0,07 0,17
Die Ergebnisse zeigen deutlich die Überlegenheit von Molekularsieben, die Lignosulfonat enthalten.
Claims (2)
1. Geformte Molekularsiebe aus kristallinen Zeolithen und 1 bis 40 Gewichtsprozent kaolinischem
' Ton als Bindemittel, dadurch gekennzeichnet, daß sie 55 bis 97 Gewichtsprozent
kristalline Zeolithe und 2 bis 5 Gewichtsprozent eines Lignosulfonats enthalten.
2. Molekularsiebe nach Anspruch 1, dadurch gekennzeichnet, daß sie als kristallinen Zeolith
Natrium-Zeolith X oder Natrium- oder Calcium-Zeolith
A enthalten.