CN1879897A - 包括在表面上交联的粉末聚合物的吸液吸收层 - Google Patents
包括在表面上交联的粉末聚合物的吸液吸收层 Download PDFInfo
- Publication number
- CN1879897A CN1879897A CNA2006100898528A CN200610089852A CN1879897A CN 1879897 A CN1879897 A CN 1879897A CN A2006100898528 A CNA2006100898528 A CN A2006100898528A CN 200610089852 A CN200610089852 A CN 200610089852A CN 1879897 A CN1879897 A CN 1879897A
- Authority
- CN
- China
- Prior art keywords
- polymer
- layer
- polymer powder
- powder
- preferred
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
实施例 | Al2(SO4)3 */H2O | FeCl3 +/H2O | MgCl2 #/H2O | AAP | TB | SFC |
V1V2B1B2B3B4B5V3V4 | 0,1/0,50,1/3,01,0/1,0 | 0,25/0,50,75/3,0 | 0,25/3,00,25/1,0 | 23,223,522,521,621,121,620,622,122,3 | 242424232423232323 | 52695360105981204837 |
产品处理 | 水分吸收性[%] | 筛分通过量[%] |
不用Al2(SO4)3用Al2(SO4)3 | 10.28.1 | 33.099.8 |
wt%Al2(SO4)3溶液 | 0 | 0.4 | 1.0 | 2.0 | 4.0 |
不分离150μm以下的细级分的SFC分离150μm以下的细级分的SFC球磨机后的SFC | 447120 | 52 | 67 | 89 | 8779 |
实施例 | Al2(SO4)3 */H2O | FeCl3 +/H2O | AAP | TB | SFC |
V6V7B10B11B12B13 | 0,5/0,51,0/3,0 | 0,25/0,50,5/3,0 | 2323,521,5222121 | 2423,724,5242423,5 | 456993727660 |
实施例 | 处理前细级分 | Al2(SO4)3 */H2O | AAP | TB | SFC | 处理后细级分 |
V8B14B15V9B16B17V10B18B19 | 555101010151515 | 0,5/0,50,5/3,00,5/0,50,5/3,00,5/0,50,5/3,0 | 2221,320,221,420,82021,519,619,8 | 2424,724,424,324,323,723,223,723,8 | 265245295345255340 | 2,53,54,5 |
实施例 | Al2(SO4)3 */H2O | FFC | AAP | TB | SFC |
B20V11 | 0,15/0,15无 | 145,7 | 22,523 | 2726,5 | 4744 |
B21V12 | 0,15/0,5无 | 116,2 | 22,823,3 | 2626,7 | 4137 |
B22V13 | 0,15/1,0无 | 10,46,2 | 22,823,5 | 26,527 | 4837 |
B23V14 | 0,15/2,0无 | 8,66,2 | 22,324 | 26,826,3 | 4538 |
B24V15 | 0,15/3,0无 | 8,36,8 | 2223,8 | 2626,5 | 6346 |
Claims (11)