CN1812944A - 磁性铁氧体和含有所述铁氧体的磁性装置 - Google Patents
磁性铁氧体和含有所述铁氧体的磁性装置 Download PDFInfo
- Publication number
- CN1812944A CN1812944A CNA2004800181711A CN200480018171A CN1812944A CN 1812944 A CN1812944 A CN 1812944A CN A2004800181711 A CNA2004800181711 A CN A2004800181711A CN 200480018171 A CN200480018171 A CN 200480018171A CN 1812944 A CN1812944 A CN 1812944A
- Authority
- CN
- China
- Prior art keywords
- magnetic
- ferrite
- sample
- conductor coils
- core
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及在GHz频带中操作良好的磁性铁氧体,和将所述磁性铁氧体用作磁芯的具有优良的高频特性的磁性装置。所述磁性铁氧体包括作为主组分的氧化铁、氧化钴与氧化锌和选自由钛、钽、铟、锆、锂、锡和钒组成的群组的至少一种的副组分。
Description
技术领域
本发明涉及用于各种电子设备的磁性铁氧体和含有所述磁性铁氧体的磁性装置。
背景技术
已使用氧化铁、氧化锌、氧化镍、氧化锰和氧化镁作为主组分来制造磁性铁氧体。也就是说,Mn-Zn铁氧体、Ni-Zn铁氧体和Mg铁氧体是铁氧体或尖晶石型铁氧体的基本组成。主组分间的比例与作为添加物添加的副组分的量视应用领域的不同而变化。已以上述方式制造磁性铁氧体,且其广泛用于在低频带上到约200MHz的高频带中操作的相当多的电子电路中。
利用芯铁氧体的下列基本运行规则,使用于电子电路中的磁性装置表现各种特性:
复磁导率μ=μ′-μ″xi(μ′:磁导率,μ″:损耗因数)。
最近,有人提出将含氧化铁、氧化钡和氧化锶作为主组分的六方晶铁氧体用于比200MHz更高的频带中。
日本未审查专利公开案第H5-36517号揭示含六方晶铁氧体的磁性材料的一实例。
然而,上述现有磁性铁氧体展示出在低于1GHz的频率下损耗因数μ″的突然增大。这意谓着包含现有磁性铁氧体的磁性装置只可用于低于1GHz的频带中。另一方面,在大量需要磁性装置的数字电子应用部分,高频技术取得显著进展。
为满足处理高速大容量信号的新兴需要,要求电路元件能够处理更高频率的信号。
本发明解决了上述问题并旨在提供损耗因数μ″只在比1GHz高的频带中才发生突然增大的磁性铁氧体。本发明还旨在通过利用所述磁性铁氧体来实现可用于高于1GHz的频带中的磁性装置。
发明内容
本发明涉及磁性铁氧体,其含有作为主组分的氧化铁、氧化钴与氧化锌和作为副组分选自由钛、钽、铟、锆、锂、锡及钒组成的群组的至少一种。本发明还提供含有磁性铁氧体的磁性装置。
附图说明
图1是根据本发明的第一实施例的磁性铁氧体的特性图。
图2是显示在第一实施例中作为添加物添加的副组分的数量与磁导率之间的关系的特性图。
图3是用于描述电感装置的绝缘体结构的透视图,所述装置为根据本发明第二实施例的磁性装置的一个实例。
图4是第二实施例中的磁性装置的一个实例的电感装置的部分剖开透视图。
图5示出阻抗装置的层状结构,所述装置为根据第三实施例的磁性装置的另一实例。
图6是一阻抗装置的透视图,所述装置为第三实施例中的磁性装置的另一实例。
图7是根据第四实施例的环形芯的透视图。
图8是共模干扰滤波器的部分剖开透视图,所述滤波器为第四实施例中的磁性装置的另一实例。
图9是天线装置的铁氧体芯的透视图,所述装置为第五实施例中的磁性装置的另一实例。
图10是天线装置的部分剖开透视图,所述装置为第五实施例中的磁性装置的另一实例。
具体实施方式
下文参考附图来描述根据本发明的磁性铁氧体和含有所述磁性铁氧体的磁性装置。
所述附图是本发明的示意图;应注意的是其并不展示组成部件的精确尺寸和定位。
第一实施例
参考图1和图2描述第一实施例。
以下列比率(以摩尔%计):Fe2O3∶ZnO∶CoO=48.0∶6.5∶45.5提供氧化铁粉末、氧化锌粉末和氧化钴粉末,其对于本发明的磁性铁氧体来说是容易购得的起始物质。
向所述粉末添加适量纯水并对其球磨,接着将其在120℃下干燥以产生混合粉末。在900℃煅烧所述混合粉末,将其用行星式球磨机粉碎直到最大颗粒直径减少到小于8μm。因此,提供经煅烧的铁氧体粉末。向所述经煅烧的铁氧体粉末添加1%重量百分比的SnO2并将其混合。添加适量的PVA(聚乙烯醇)水溶液并将其搅拌捏合以产生平均颗粒直径为约20μm的造粒粉末。
使所述造粒粉末形成环形并在特定温度下(例如在1200-1300℃下)将其烧结以使其致密。因此,提供环形芯(这个芯称为本发明的样本1)。为了达成比较的目的,还使用具有大体相同磁导率的六方晶铁氧体来提供另一个环形芯(这个芯称为对比样本1)。图1比较了两个圆环芯的特性。在图1中,曲线A和B分别表示本发明的样本1的μ′和μ″;而C和D分别表示对比样本1的μ′和μ″。如图1中所见,对比样本1展示在邻近0.8GHz处损耗因数μ″突然增大(曲线D)。
然而,样本1的突然增大频率移向高频率侧,直到邻近1.5GHz(曲线B)。
此外,曲线A指示其维持磁导率μ′为约3到接近6GHz。也就是说,根据本发明制造的磁性铁氧体所显示的磁性特性指示其可用于GHz频带。
还通过上述相同程序制造了更多的环状芯样本,其中作为主组分的氧化铁、氧化锌和氧化钴按照表1中所示的比例混合,添加2%重量百分比的SnO2作为副组分(本发明的样本1-12)。
因此提供的芯的磁性特性显示于表1中。
表1
E | F | G | H | μ′ | μ″ | |
摩尔% | 重量% | 在1GHz处 | ||||
样本1 | 48 | 45.5 | 6.5 | 2 | 3.1 | 0.05 |
样本2 | 50 | 47 | 3 | 2 | 2 | 0.15 |
样本3 | 50 | 42 | 8 | 2 | 3.5 | 0.15 |
样本4 | 45 | 52 | 3 | 2 | 2 | 0.06 |
样本5 | 44 | 42 | 14 | 2 | 2 | 0.14 |
样本6 | 42 | 52 | 6 | 2 | 2 | 0.07 |
样本7 | 42 | 44 | 14 | 2 | 2 | 0.15 |
样本8 | 51 | 44 | 5 | 2 | 1.8 | 0.2 |
样本9 | 48 | 50 | 2 | 2 | 1.6 | 0.04 |
样本10 | 48 | 41 | 11 | 2 | 1.8 | 0.2 |
样本11 | 42 | 55 | 3 | 2 | 1.5 | 0.05 |
样本12 | 42 | 42 | 16 | 2 | 1.8 | 0.2 |
对比样本2 | 41 | 49 | 10 | 1.8 | 0.26 |
E:Fe2O3 F:CoO G:SnO2
从表1中所示的结果来看,可了解本发明的磁性铁氧体样本1-12具有较高的磁导率μ′和较小的损耗因数μ″。更可了解在由表示样本2-7的组成比率的线所包围的区域内部内优势更显著。
上述结果指示根据本发明提供的高频率用的磁性铁氧体具有优良的用于GHz频带的特性。
图2显示由具有与样本1相同组成的经煅烧的铁氧体粉末因为添加各种副组分而引起的2GHz处的磁导率μ′变化。如从图2所了解,磁导率μ′随添加的副组分数量的增大而变得更高直到副组分数量达到2%重量百分比;特性上显示的最高提高可高达约60%。然而,当添加物的量为0.1%重量百分比时,磁导率μ′的增大仍很小;但是当添加2.5%重量百分比副组分时,磁导率μ′减小到比没有任何副组分添加物时更低。从上文显示的结果可知优选以以氧化物换算计为0.2-2.0%重量百分比的量添加由钛、钽、铟、锆、锂、锡和钒组成的群组中选出的至少一种作为副组分。
此外,通过与上述相同的程序使用与样本1中相同的经煅烧的铁氧体粉末作为基底材料、添加如表2中所示多种副组分,还可制造更多的环状芯样本(样本13-19)。为了达成比较的目的,使用样本1的经煅烧的铁氧体粉末而不添加任何副组分来制造另一环状芯样本(对比样本3)。
其磁性特性显示于表2中。
表2
添加物1 | 数量 | 添加物2 | 数量 | 添加物3 | 数量 | 磁导率 | |
重量% | 重量% | 重量% | 在2GHZ处 | ||||
样本13 | SnO2 | 1 | TiO2 | 1 | --- | 0 | 2.67 |
样本14 | SnO2 | 1 | In2O3 | 1 | --- | 0 | 2.76 |
样本15 | SnO2 | 1 | Ta2O5 | 1 | --- | 0 | 2.48 |
样本16 | V2O3 | 1 | ZrO2 | 1 | --- | 0 | 3.02 |
样本12 | V2O3 | 1 | LiO2 | 1 | --- | 0 | 3.25 |
样本12 | V2O3 | 1 | LiO2 | 0.5 | SnO2 | 0.5 | 3.10 |
样本12 | SnO2 | 1 | TiO2 | 0.5 | ZrO2 | 0.5 | 2.70 |
对比样本3 | --- | 0 | --- | 0 | --- | 0 | 2.26 |
参考表2,含有同时添加的两种或两种以上副组分的样本13-19在与其中未添加副组分的对比样本3相比较时也显示在2GHz下磁导率μ′增大。看来这些副组分用以促进主组分的烧结行为;即使是当其以复合形式投配时也没有引起对烧结过程的阻碍效应。同样地,副组分的复合用量在其中主组分的组成(即氧化铁、氧化锌和氧化钴)为在本发明的样本2-7的范围内的那些组分时可显示出相似结果。
也已确认当将不同化合价的氧化物或碳酸盐(例如CoO、Co2O3、Co2O4、CoCO3)用作主组分或添加物副组分的物质时产生相同优势。
第二实施例
参考图3和图4描述第二实施例。
在图3和图4中,绝缘体1是一个磁性铁氧体芯,其组成如表3所示。绝缘体1备有以铜、银或其类似的导体材料所形成的导体线圈2。导体线圈2的表面覆盖有由树脂或其它材料所制成的绝缘层3。在导体线圈2的各个末端提供两片外部电极4。因此提供一个完整的电感装置。
下文描述经上文配置的电感装置的制造方法以及结构和电子特性。
制备具有与本发明的样本1相同组成的经煅烧的铁氧体粉末。将列于表3中的一种氧化物作为副组分添加到所述经煅烧的铁氧体粉末,并将这些粉末以与第一实施例中相同的程序搅拌捏合在一起来提供造粒粉末。
以所述造粒粉末填充一个模具,并在特定的处理条件下对其进行处理以产生一特定的具体形状。并接着将其在一特定温度(例如1200-1300℃)下烧结以使其致密。因此提供绝缘体1。
通过将导线缠绕在绝缘体1上或其它方法形成导体线圈2,并接着使用绝缘树脂或绝缘无机材料提供绝缘层3。因此完成如图4所示的一个完整的电感装置(本发明的样本20-26)。
为了达成比较的目的,将氧化铝用于绝缘体1来制造另一电感装置(对比样本4),且将六方晶铁氧体用于绝缘体1来制造又一电感装置(对比样本5)。
这些电感装置的特性显示于表3中。
表3
添加物 | 在2GHz下的电感值(nH) | Q值为峰值的频率值(GHz) | ||
名称 | 数量重量% | |||
样本20 | TiO2 | 2 | 4.3 | 2.2 |
样本21 | In2O3 | 2 | 4.5 | 2.0 |
样本22 | Ta2O5 | 2 | 4.5 | 1.9 |
样本23 | ZrO2 | 2 | 4.8 | 1.9 |
样本24 | LiO2 | 2 | 4.8 | 1.8 |
样本25 | SnO2 | 2 | 5.5 | 1.6 |
样本26 | V2O3 | 2 | 6.4 | 1.3 |
对比样本4 | --- | --- | 2.0 | 3.2 |
对比样本5 | --- | --- | 4.0 | 0.8 |
从表3中所示的结果可了解到与对比样本4相比较,样本20-26随着磁导率μ′的增大展示出更大的电感值。也就是说,本发明的样本对于用于高频率电路的电感装置所需的特性展示出显著改善。
另一方面,对比样本5(一电感装置)显示Q值为峰值处的频率值为邻近0.8GHz处。在高于1GHz的频率下,损耗变得过高以至于不能用于GHz频带。然而,本发明的各个样本20-26均显示Q值为峰值处的频率值在1-3GHz频带中。
也就是说,本发明的这些样本的每一者都是可用于GHz频带的电感装置。
作为通过压缩所述造粒粉末来提供绝缘体1的代替,所述绝缘体1可通过层压生胚薄片(green sheet)并接着将层压物切割或冲压特定的需要尺寸来制造。那些由后一种方法制造的绝缘体展示出相同效用。
作为通过缠绕导线来形成导体线圈2的代替,所述导体线圈2可通过首先利用镀覆法或薄膜技术在整个表面上形成一层并接着借助激光束或磨石等方法将所述层螺旋切割来提供。那些由后一种方法形成的导体线圈显示出相同效用。
此外,绝缘层3可包括混合其中的磁性材料。
此配置将进一步改善所述电感值。混合于绝缘层3中的优选磁性材料为本发明的磁性铁氧体粉末。
因为Q值随着磁性铁氧体粉末的颗粒直径增大而变得更高,所以最优选的颗粒直径为45μm或更大。
为了在特定的具体电感值、最大电感值下实现或以装置尺寸减少的方式实现电感装置,可在上述磁性铁氧体周围提供导体线圈。当磁性铁氧体具有较高的磁导率μ′时,可设计一装置来产生较高的电感值或达到较小的装置尺寸。
当所用磁性铁氧体具有较小的损耗因数μ″时,Q值可较大。因此,在一操作频率处的较大Q值表示其为一用于高频率应用的优良电感装置。
第三实施例
参考图5和图6描述第三实施例。
在图5和图6中,曲折的导体5由铂、钯等形成。通过层压磁性铁氧体生胚薄片来夹入所述导体5。以此方式提供磁性铁氧体6。磁性铁氧体6为绝缘构件。在磁性铁氧体6的两端有两个外部电极7,其与安置于其内部的导体5的各个端耦合。因此提供一个完整的阻抗装置。
如上所述,通过以磁性铁氧体6覆盖信号线(也就是导体5)来制造用作抗干扰组件的阻抗装置。将磁性铁氧体6的损耗因数μ″显示突然增大的特定频率定义为截止频率(cutoff frequency),阻抗装置的阻抗值在比所述截止频率高的频率处选择性地增加。结果,含有比所述截止频率高的频率组分的干扰被移除。当磁性铁氧体6具有较高的磁导率μ′时,可设计一装置来展示较高的阻抗值。因此,其实施一优良的阻抗装置。
下文书写一种制造经上文配置的阻抗装置的方法。
按照下列以摩尔%计的混合比率混合氧化铁、氧化锌和氧化钴:Fe2O3∶ZnO∶CoO=48.0∶6.5∶45.5。
添加适量纯水并对其进行球磨。将其在120℃下干燥以提供混合粉末。在900℃煅烧所述混合粉末,并将其用行星式球磨机粉碎直到最大颗粒直径减少到小于8μm。因此,产生经煅烧的铁氧体粉末。将向所述经煅烧的铁氧体粉末添加列于表4中的副组分作为添加物。
进一步添加适量缩丁醛树脂(butyral resin)和乙酸丁酯(butyl acetate),并将其球磨来使其很好地分散。因此产生一铁氧体浆料。
借助用流延法(doctor blade process)涂覆所述铁氧体浆料以产生铁氧体生胚薄片。在所述铁氧体生胚薄片上,用Pt膏印刷导体5的图案。将具有经印刷的导体5的铁氧体生胚薄片和没有导体5图案的铁氧体生胚薄片层压多次直到将其制成一特定的所要厚度。并接着将所述层压片切割成模制小片的个别片。在1200-1300℃烧结所述模制小片以产生一经烧结的磁性铁氧体,其在内层含有导体5。在所述经烧结的磁性铁氧体的两端提供两个与导体5的各个端耦合的外部电极7。
因此制造如图6中所示的完整的阻抗装置(本发明的样本27-33)。
为了达成比较的目的,使用六方晶铁氧体来制造另一阻抗装置(对比样本6)。这些阻抗装置的电子特性在表4中比较。
从表4中所示的结果可了解到与对比样本6相比较,本发明的样本27-33显示出更高的截止频率(阻抗变为10Ω时的频率)。这意谓着所述样本表示在GHz频带中可用作干扰滤波器的阻抗装置。
因为所用的磁性铁氧体具有较高的磁导率μ′,所以阻抗值变得更高,使所述装置成为一优良的阻抗装置。
在内部形成的导体5的Pt图案形状并不限于曲折形状。举例来说,可通过层压铁氧体生胚薄片并使用它们的通孔来提供一螺旋形线圈形状。
表4
添加物 | 截止频率GHz | 2GHz处的阻抗值(Ω) | ||
名称 | 数量重量% | |||
样本27 | TiO2 | 2 | 1.0 | 98 |
样本28 | In2O3 | 2 | 1.0 | 104 |
样本29 | Ta2O5 | 2 | 1.0 | 104 |
样本30 | ZrO2 | 2 | 1.0 | 110 |
样本31 | LiO2 | 2 | 1.O | 111 |
样本32 | SnO2 | 2 | 1.3 | 127 |
样本33 | V2O3 | 2 | 1.0 | 147 |
对比样本6 | --- | --- | O.5 | 30 |
在这种状况下,如果导体5的螺旋线圈的末端与外部电极7之间的距离很短,那么阻抗值降低。
因此,所述距离应足够长;优选为200μm或更长。
导体5可以用Pd或Pt与Pd的合金来形成。然而,考虑到导电率,优选使用Pt或Pd。
第四实施例
参考图7和图8描述第四实施例。
在图7和图8中,环状芯9以磁性铁氧体形成,并在表面上提供两个由铜、银等制成的导体线圈10。
在两个导体线圈10的表面上形成由树脂或其类似材料制成的绝缘层11。提供四个外部电极12以与两个导体线圈10的各个终端耦合。一个完整的共模干扰滤波器具有所述结构。
在标准电子电路中用于差动传输线的共模干扰滤波器中,两个导体线圈10以相同方向绕环形磁性铁氧体芯9缠绕。
所述滤波器通过利用两个差速传输线之间归因于磁性铁氧体的磁导率μ′而增强的磁性耦合来移除共模组分。磁性铁氧体的损耗因数μ″越小,差速模式的损耗或传输的信号水平的损耗越小。因此,其制成一优良的共模干扰滤波器。由于上述结构,在GHz频带中操作的优良共模干扰滤波器可通过将根据本发明的磁性铁氧体用于环状芯9来实现。
下文描述一种制造经上文配置的共模干扰滤波器的方法。
向样本1的主组分添加列于表5中的副组分作为添加物并通过与第一实施例中相同的程序对其进行处理以提供造粒粉末。
使所述造粒粉末成型为环形,并在1200-1300℃下将其烧结以产生环状芯9。将双导线绕环状芯9同一方向缠绕以产生两个导体线圈10。
用树脂材料对其进行模制以形成绝缘层11,并提供外部电极12与两个导体线圈10的终端耦合。
以此方式制造如图8中所说明的共模干扰滤波器(本发明的样本34-40)。也制造一用于比较研究的共模干扰滤波器(对比样本7),其将六方晶铁氧体用于环形芯9。
表5比较了这些共模干扰滤波器的特性。
表5
添加物 | 耦合系数 | ||
名称 | 数量重量% |
样本34 | TiO2 | 2 | 0.83 |
样本35 | In2O3 | 2 | 0.88 |
样本36 | Ta2O5 | 2 | 0.88 |
样本37 | ZrO2 | 2 | 0.89 |
样本38 | LiO2 | 2 | 0.91 |
样本39 | SnO2 | 2 | 0.90 |
样本40 | V2O3 | 2 | 0.92 |
对比样本7 | --- | --- | 0.50 |
从表5所示的结果可了解到与对比样本7相比较,样本34-40由于在1GHz下的较高磁导率μ′和较小的损耗因数μ″而展示出较高的耦合系数。
虽然已用绝缘层11模制缠绕有线圈的环形芯9以促进表面安装操作,但是在消除树脂模制的情况下可将两个导体线圈10直接连接于基板上来产生相同效果。
第五实施例
参考图9和图10描述第五实施例。
在图9和图10中,铁氧体芯13以磁性铁氧体制造。在铁氧体芯13的表面上提供由铜、银等所形成的导体线圈14。用树脂或类似材料的绝缘层15覆盖导体线圈14的表面。完整的天线装置具有所述结构。
下文描述一种制造经上文配置的天线装置的方法。
向与样本1相同的主组分添加列于表6的副组分作为添加物,以通过与第一实施例中相同的程序来提供造粒粉末。
使所述造粒粉末形成为棒状,并将其在1200-1300℃下烧结。且接着将其研磨切削加工成如图9中所说明的形状以产生天线装置的铁氧体芯13。通过镀覆法或其它方法,以诸如铜、银等的低欧姆值的金属覆盖铁氧体芯13的整个表面。以激光束将所述经镀覆的表面螺旋切割以形成导体线圈14。
以树脂来模制在表面上提供有导体线圈14的铁氧体芯13以提供绝缘层15。以此方式,完成如图10中所说明的完整的天线装置(本发明的样本41-47)。
为了比较研究,使用类似外形的树脂芯制造天线装置(对比样本8),和将六方晶铁氧体用于铁氧体芯13的天线装置(对比样本9)。
表6比较其放射损耗以及使树脂芯制造天线装置(对比样本8)的尺寸为100时的尺寸的优势。
从图6中所示的结果可了解到在本发明的天线装置中,磁性铁氧体的磁导率μ′越大,天线装置的尺寸与具有树脂制成的芯的天线装置尺寸相比越小。
将六方晶铁氧体用于铁氧体芯13的天线装置具有太大的放射损耗以至于无法精确测定其尺寸。
表6
添加物 | 天线尺寸相对值(%) | 放射损耗-dB | ||
名称 | 数量重量% | |||
样本41 | TiO2 | 2 | 83 | -1.7 |
样本42 | In2O3 | 2 | 81 | -1.9 |
样本43 | Ta2O5 | 2 | 81 | -1.8 |
样本44 | ZrO2 | 2 | 79 | -1.6 |
样本45 | LiO2 | 2 | 79 | -1.8 |
样本46 | SnO2 | 2 | 73 | -1.6 |
样本47 | V2O3 | 2 | 71 | -1.7 |
对比样本8 | --- | --- | 100 | -0.52 |
对比样本9 | --- | --- | --- | -8.8 |
也可了解含有六方晶铁氧体的天线装置展示较大的放射损耗,而根据本发明的天线装置的放射损耗足够小以可用于2GHz频带中。
天线装置可借助焊接或铆接(calking)连接于一电路上。然而,优选使所述装置具有用于安装的螺纹部分,以确保足够的安装强度。
所述螺纹部分可借助使用独立型模具的粉末压制法代替切割法(切削加工)来提供。
至于用于镀覆的材料,可使用Ag、Cu、Au、Al、Ni、Pt、Pd等。然而,考虑到电导率,优选使用Ag或Cu。
导体线圈14可通过将导线缠绕或将一金属板冲压成线圈形状来提供。两种方法产生相同效果。
可在铁氧体芯13的表面与导体线圈14之间形成一非磁性材料薄膜。
天线装置可以树脂材料模制或以树脂模制盖覆盖。
因为其基于归因于磁导率μ′的波长缩短效应,所以除上文的螺旋型天线装置以外,在平板天线或其它类型天线上当然可产生相同优势。
本发明的磁性铁氧体包括作为主组分的氧化铁、氧化钴与氧化锌和作为副组分选自由钛、钽、铟、锆、锂、锡和钒组成的群组的至少一种。这种磁性铁氧体在高于1GHz的频率处展示损耗因数μ″突然增大,且1GHz以上处的损耗因数μ″较小而磁导率μ′较高。
根据本发明的磁性铁氧体的组成在由成分线所包围的区域内,所述成分线表示下列以Fe2O3、CoO和ZnO摩尔%换算计的氧化铁、氧化钴和氧化锌的混合比率:50∶47∶3、50∶42∶8、45∶52∶3、44∶42∶14、42∶52∶6和42∶44∶14。根据本发明的磁性铁氧体在高频带展示出优良的特性。
本发明的磁性铁氧体含有以氧化物换算计为0.2-2.0重量%的选自由钛、钽、铟、锆、锂、锡和钒组成的群组的至少一种作为副组分。通过按照具体比例混合组成组分,在权利要求1中所述的磁性铁氧体实现了较高磁导率μ′的磁性铁氧体。
本发明的磁性装置包括一棒状绝缘体、螺旋形成于所述绝缘体上的导体线圈、覆盖所述导体线圈的绝缘层和两个与所述导体线圈耦合的外部电极。将在权利要求1至3中任一权利要求所述的磁性铁氧体用于所述绝缘体,使所述磁性装置成为电感装置。所述电感装置甚至在1GHz或更高时展示出高Q值,且能够使内部导体线变短。
本发明的磁性装置包括磁性绝缘构件、提供于所述磁性绝缘构件内部的曲折导体线圈和两个与所述导体线圈耦合的外部电极。将在权利要求1至3中任一权利要求所述的磁性铁氧体用于所述磁性绝缘构件,使所述磁性装置成为阻抗装置。因为其低通滤波器(low-pass filter)的截止频率可确定在高于1GHz的频带中并具有较大的阻抗值,所以其为有效阻断干扰的阻抗装置。
本发明的磁性装置包括一环状芯、两个以相同方向缠绕于所述环形芯上的导体线圈、一覆盖所述导体线圈的绝缘层和四个与所述导体线圈耦合的外部电极。将在权利要求1至3中任一权利要求所述的磁性铁氧体用于所述环形芯,使所述磁性装置成为共模干扰滤波器。根据本发明,传输信号频率带可设计于1GHz或更高,并且所述共模干扰滤波器可在所述GHz频带中显示高耦合系数。
本发明的磁性装置包括一铁氧体芯、螺旋缠绕于所述芯上的导体线圈和覆盖所述导体线圈的绝缘层。将在权利要求1至3中任一权利要求所述的磁性铁氧体用于所述铁氧体芯,使所述磁性装置成为一天线装置。这实现了用于1-3GHz频带中的内置天线(compact antenna)装置。
工业适用性
本发明中的磁性铁氧体可用于安装于在GHz频带中操作的电子电路上的磁性装置中。
Claims (7)
1.磁性铁氧体,其包括作为主组分的氧化铁、氧化钴与氧化锌和选自由钛、钽、铟、锆、锂、锡和钒组成的群组的至少一种的副组分。
2.根据权利要求1所述的磁性铁氧体,其中
以经摩尔%换算的Fe2O3、CoO和ZnO计的氧化铁、氧化钴和氧化锌的混合比例在由表示下列比率的成分线所包围的区域内:50∶47∶3、50∶42∶8、45∶52∶3、44∶42∶14、42∶52∶6和42∶44∶14。
3.根据权利要求1所述的磁性铁氧体,其中
含有以氧化物换算计为0.2-2.0%重量百分比的选自由钛、钽、铟、锆、锂、锡和钒组成的群组的至少一种作为副组分。
4.电感装置,其是包含棒状绝缘体、螺旋形成于所述绝缘体周围的导体线圈、覆盖所述导体线圈的绝缘层和与所述导体线圈耦合的两个外部电极的磁性装置,其中
所述绝缘体为根据权利要求1至3中任一权利要求所述的磁性铁氧体。
5.阻抗装置,其是包含磁性绝缘构件、提供于所述磁性绝缘构件内部的曲折导体线圈和与所述导体线圈耦合的两个外部电极的磁性装置,其中
所述磁性绝缘构件为根据权利要求1至3中任一权利要求所述的磁性铁氧体。
6.共模噪声滤波器,其包含环状磁芯、两个以相同方向缠绕于所述环形磁芯上的导体线圈、覆盖所述导体线圈的绝缘层和与所述导体线圈耦合的四个外部电极的磁性装置,其中
所述环形磁芯为根据权利要求1至3中任一权利要求所述的磁性铁氧体。
7.天线装置,其包含铁氧体磁芯、螺旋缠绕于所述铁氧体磁芯周围的导体线圈和覆盖所述导体线圈的绝缘层的磁性装置,其中
所述铁氧体芯为根据权利要求1至3中任一权利要求所述的磁性铁氧体。