CN1608314A - 用于处理聚硅氮烷的溶剂和采用这种溶剂处理聚硅氮烷的方法 - Google Patents
用于处理聚硅氮烷的溶剂和采用这种溶剂处理聚硅氮烷的方法 Download PDFInfo
- Publication number
- CN1608314A CN1608314A CNA028259491A CN02825949A CN1608314A CN 1608314 A CN1608314 A CN 1608314A CN A028259491 A CNA028259491 A CN A028259491A CN 02825949 A CN02825949 A CN 02825949A CN 1608314 A CN1608314 A CN 1608314A
- Authority
- CN
- China
- Prior art keywords
- polysilazane
- solvent
- well
- handle
- perhydro
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
实施例&对比例 | 洗涤溶液 | 颗粒(数目/ml) | 水含量wt% | |
>0.5μm | >0.2μm | |||
实施例1 | Solvesso 100 | 5 | 30 | 0.002 |
实施例2 | Solvesso 150 | 2 | 10 | 0.003 |
实施例3 | Pegasol AN45 | 2 | 50 | 0.002 |
实施例4 | 萘烷 | 5 | 80 | 0.005 |
实施例5 | 环己烷 | 3 | 30 | 0.002 |
实施例6 | 环己烯 | 3 | 40 | 0.002 |
实施例7 | 甲基环己烷 | 8 | 40 | 0.002 |
实施例8 | 乙基环己烷 | 2 | 20 | 0.002 |
实施例9 | 苎烯 | 8 | 80 | 0.01 |
实施例10 | Solvesso 100(50%)+环己烷(50%) | 2 | 20 | 0.002 |
实施例11 | Pegasol AN45(50%)+萘烷(50%) | 3 | 80 | 0.002 |
实施例12 | 二甲苯 | 1 | 50 | 0.001 |
实施例13 | 二甲苯(50%)+正壬烷(50%) | 2 | 40 | 0.002 |
对比例1 | 二丁醚(未脱水,水含量:300ppm) | 3 | 40 | 0.002 |
实施例14 | 二丁醚(脱水,水含量:20ppm) | 3 | 40 | 0.005 |
实施例15 | 苯甲醚 | 5 | 30 | 0.05 |
对比例2 | 丙二醇单甲基醚 | 5 | 20 | 0.02 |
对比例3 | 丙二醇单甲基醚乙酸酯 | 1 | 20 | 0.01 |
实施例&对比例 | 胶凝天数 | 产生的气体(vol%) | 边缘切割性能 | ||
甲硅烷 | 氢 | 顶洗 | 背洗 | ||
实施例1 | 8 | 0.001 | 0.05 | 良好 | 良好 |
实施例2 | 9 | 0.001 | 0.03 | 良好 | 良好 |
实施例3 | 8 | 0.001 | 0.03 | 良好 | 良好 |
实施例4 | 6 | 0.003 | 0.1 | 良好 | 良好 |
实施例5 | 4 | 0.005 | 0.1 | 良好 | 良好 |
实施例6 | 4 | 0.005 | 0.1 | 良好 | 良好 |
实施例7 | 5 | 0.003 | 0.03 | 良好 | 良好 |
实施例8 | 4 | 0.003 | 0.02 | 良好 | 良好 |
实施例9 | 3 | 0.01 | 0.15 | 良好 | 良好 |
实施例10 | 7 | 0.001 | 0.03 | 良好 | 良好 |
实施例11 | 8 | 0.001 | 0.02 | 良好 | 良好 |
实施例12 | 8 | 0.001 | 0.01 | 良好 | 良好 |
实施例13 | 8 | 0.002 | 0.05 | 良好 | 良好 |
对比例1 | 0.5 | 0.04 | 1.2 | 良好 | 良好 |
实施例14 | 3 | 0.008 | 0.1 | 良好 | 良好 |
实施例15 | 4 | 0.08 | 0.2 | 良好 | 良好 |
对比例2 | >20 | 1.5 | 30 | 良好 | 良好 |
对比例3 | 0.5 | 0.5 | 25 | 良好 | 良好 |
实施例&对比例 | 洗涤溶液 | 颗粒(数目/ml) | 水含量wt% | |
>0.5μm | >0.2μm | |||
实施例16 | Solvesso 100 | 5 | 30 | 0.002 |
实施例17 | Solvesso 150 | 2 | 10 | 0.003 |
实施例18 | Pegasol AN45 | 2 | 50 | 0.002 |
实施例19 | 萘烷 | 5 | 80 | 0.005 |
实施例20 | 环己烷 | 3 | 30 | 0.002 |
实施例21 | 环己烯 | 3 | 40 | 0.002 |
实施例22 | 甲基环己烷 | 8 | 40 | 0.002 |
实施例23 | 乙基环己烷 | 2 | 20 | 0.002 |
实施例24 | 苎烯 | 8 | 80 | 0.01 |
实施例25 | Solvesso 100(50%)+环己烷(50%) | 2 | 20 | 0.002 |
实施例26 | Pegasol AN45(50%)+萘烷(50%) | 3 | 80 | 0.002 |
实施例27 | 二甲苯 | 1 | 50 | 0.001 |
实施例28 | 二甲苯(50%)+正壬烷(50%) | 2 | 40 | 0.002 |
对比例4 | 二丁醚(未脱水,水含量:300ppm) | 3 | 40 | 0.002 |
实施例29 | 二丁醚(脱水,水含量:20ppm) | 3 | 40 | 0.005 |
实施例30 | 苯甲醚 | 5 | 30 | 0.05 |
对比例5 | 丙二醇单甲基醚 | 5 | 20 | 0.02 |
对比例6 | 丙二醇单甲基醚乙酸酯 | 1 | 20 | 0.01 |
实施例&对比例 | 胶凝天数 | 产生的气体(vol%) | 边缘切割性能 | ||
甲硅烷 | 氢 | 顶洗 | 背洗 | ||
实施例16 | 9 | 0.002 | 0.1 | 良好 | 良好 |
实施例17 | 9 | 0.001 | 0.1 | 良好 | 良好 |
实施例18 | 9 | 0.002 | 0.05 | 良好 | 良好 |
实施例19 | 6 | 0.002 | 0.05 | 良好 | 良好 |
实施例20 | 5 | 0.005 | 0.05 | 良好 | 良好 |
实施例21 | 4 | 0.001 | 0.1 | 良好 | 良好 |
实施例22 | 5 | 0.005 | 0.03 | 良好 | 良好 |
实施例23 | 7 | 0.01 | 0.08 | 良好 | 良好 |
实施例24 | 3 | 0.01 | 0.08 | 良好 | 良好 |
实施例25 | 7 | 0.002 | 0.05 | 良好 | 良好 |
实施例26 | 8 | 0.002 | 0.05 | 良好 | 良好 |
实施例27 | 10 | 0.002 | 0.03 | 良好 | 良好 |
实施例28 | 12 | 0.003 | 0.07 | 良好 | 良好 |
对比例4 | 1 | 0.08 | 0.9 | 良好 | 良好 |
实施例29 | 4 | 0.01 | 0.08 | 良好 | 良好 |
实施例30 | 7 | 0.02 | 0.2 | 良好 | 良好 |
对比例5 | >20 | 2.2 | 45 | 良好 | 良好 |
对比例6 | 1 | 1.2 | 30 | 良好 | 良好 |
实施例&对比例 | 洗涤溶液 | 颗粒(数目/ml) | 水含量wt% | |
>0.5μm | >0.2μm | |||
实施例31 | Solvesso 100 | 5 | 30 | 0.002 |
实施例32 | Solvesso 150 | 2 | 10 | 0.003 |
实施例33 | Pegasol AN45 | 2 | 50 | 0.002 |
实施例34 | 萘烷 | 2 | 20 | 0.001 |
实施例35 | 环己烷 | 3 | 30 | 0.002 |
实施例36 | 环己烯 | 3 | 40 | 0.002 |
实施例37 | 甲基环己烷 | 8 | 40 | 0.002 |
实施例38 | 乙基环己烷 | 2 | 20 | 0.002 |
实施例39 | 苎烯 | 8 | 80 | 0.01 |
实施例40 | 正己烷 | 3 | 20 | 0.001 |
实施例41 | 异己烷 | 2 | 20 | 0.002 |
实施例42 | 正庚烷 | 2 | 20 | 0.001 |
实施例43 | 异庚烷 | 5 | 30 | 0.001 |
实施例44 | 正辛烷 | 5 | 70 | 0.003 |
实施例45 | 异辛烷 | 2 | 20 | 0.002 |
实施例46 | 正壬烷 | 3 | 20 | 0.002 |
实施例47 | 异壬烷 | 3 | 80 | 0.001 |
实施例48 | 正癸烷 | 5 | 100 | 0.002 |
实施例49 | 异癸烷 | 3 | 20 | 0.001 |
实施例50 | 二甲苯 | 1 | 50 | 0.001 |
实施例51 | 二甲苯(50%)+正壬烷(50%) | 2 | 40 | 0.002 |
实施例52 | Solvesso 100(50%)+环己烷(50%) | 2 | 10 | 0.001 |
实施例53 | Pegasol AN45(50%)+异壬烷(50%) | 2 | 30 | 0.001 |
对比例7 | 二丁醚(未脱水,水含量:300ppm) | 3 | 40 | 0.002 |
实施例54 | 二丁醚(脱水,水含量:20ppm) | 3 | 40 | 0.005 |
实施例55 | 苯甲醚 | 5 | 30 | 0.05 |
对比例8 | 丙二醇单甲基醚 | 5 | 20 | 0.02 |
对比例9 | 丙二醇单甲基醚乙酸酯 | 1 | 20 | 0.01 |
实施例&对比例 | 胶凝天数 | 产生的气体(vol%) | 边缘切割性能 | ||
甲硅烷 | 氢 | 顶洗 | 背洗 | ||
实施例31 | 10 | 0.001 | 0.1 | 良好 | 良好 |
实施例32 | 10 | 0.001 | 0.02 | 良好 | 良好 |
实施例33 | 9 | 0.002 | 0.03 | 良好 | 良好 |
实施例34 | 13 | 0.001 | 0.04 | 良好 | 良好 |
实施例35 | 12 | 0.01 | 0.05 | 良好 | 良好 |
实施例36 | 12 | 0.003 | 0.05 | 良好 | 良好 |
实施例37 | 9 | 0.001 | 0.02 | 良好 | 良好 |
实施例38 | 9 | 0.001 | 0.1 | 良好 | 良好 |
实施例39 | 7 | 0.001 | 0.1 | 良好 | 良好 |
实施例40 | 12 | 0.002 | 0.1 | 良好 | 良好 |
实施例41 | 12 | 0.002 | 0.05 | 良好 | 良好 |
实施例42 | 15 | 0.003 | 0.03 | 良好 | 良好 |
实施例43 | 15 | 0.005 | 0.04 | 良好 | 良好 |
实施例44 | 12 | 0.001 | 0.04 | 良好 | 良好 |
实施例45 | 10 | 0.005 | 0.01 | 良好 | 良好 |
实施例46 | 12 | 0.008 | 0.05 | 良好 | 良好 |
实施例47 | 12 | 0.003 | 0.05 | 良好 | 良好 |
实施例48 | 12 | 0.002 | 0.06 | 良好 | 良好 |
实施例49 | 14 | 0.002 | 0.01 | 良好 | 良好 |
实施例50 | 15 | 0.001 | 0.03 | 良好 | 良好 |
实施例51 | 12 | 0.001 | 0.03 | 良好 | 良好 |
实施例52 | 12 | 0.002 | 0.1 | 良好 | 良好 |
实施例53 | 12 | 0.001 | 0.02 | 良好 | 良好 |
对比例7 | 1 | 0.06 | 0.7 | 良好 | 良好 |
实施例54 | 4 | 0.008 | 0.03 | 良好 | 良好 |
实施例55 | 9 | 0.02 | 0.2 | 良好 | 良好 |
对比例8 | >20 | 1.1 | 28 | 良好 | 良好 |
对比例9 | 1 | 0.9 | 15 | 良好 | 良好 |
Claims (7)