CN1291943C - Polished brick in porcelain texture, and production process - Google Patents
Polished brick in porcelain texture, and production process Download PDFInfo
- Publication number
- CN1291943C CN1291943C CN 200410050914 CN200410050914A CN1291943C CN 1291943 C CN1291943 C CN 1291943C CN 200410050914 CN200410050914 CN 200410050914 CN 200410050914 A CN200410050914 A CN 200410050914A CN 1291943 C CN1291943 C CN 1291943C
- Authority
- CN
- China
- Prior art keywords
- brick
- porcelain
- single crystal
- powder
- silicon single
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention discloses a ceramic polishing brick and a production process thereof. The ceramic polishing brick contains raw powdery materials used for preparing a ceramic brick, 2 to 60 meshes of single crystal silicon is mixed with the raw powdery materials of the ceramic brick, and the consumption of the single crystal silicon accounts for less than 10 wt% of the total weight. The powdery materials are proportionally and uniformly mixed, molded, dried and calcined at 1150 to 1250 DEG C., and the ceramic polishing brick is obtained by polishing and trimming. The surface of the ceramic polishing brick of the present invention has flash spot particles with metallic luster, the ceramic polishing brick has very favorable decorative effects, and a luxurious decorative ceramic polishing brick is provided for customers.
Description
Technical field
The present invention relates to a kind of Ceramic tiles and their production process.
Background technology
Improvement along with growth in the living standard and living environment, the human consumer more and more comes high to the requirement and the aesthetic conceptions of building and ornament materials, particularly to novel, high-grade and to have the demand of " humane, science and technology, environmental protection " hommization finishing material more and more, promoted the fast development of architectural pottery and building and ornament materials industry effectively, particularly various decoration techniques, technology and gimmick have been applied in the decoration of ceramic, have promoted the development and application of architectural pottery again.Especially various, the thousand strange different expressions metalluster effects of occurring in nature have caused architectural pottery circle personage's extensive concern and consumers in general's favor with its noble quality, novelty, gorgeous characteristic, and insider's exploratory development always expectation can form flash metal luster spot effect on the polished brick in porcelain character surface.
Summary of the invention
The Ceramic tiles and their production process that the purpose of this invention is to provide a kind of surface particles shape flash metal luster spot.
Another order of the present invention provides a kind of production technique of polished brick in porcelain character of surface particles shape flash metal luster spot
The object of the present invention is achieved like this, and it contains porcelain brick proportioning base powder, is mixed with 2-60 purpose silicon single crystal in porcelain adobe powder, and it is that (weight percent) is below 10% that the usage quantity of 2-60 purpose silicon single crystal accounts for gross weight.
The preferred amount ranges of 2-60 purpose silicon single crystal of the present invention is (weight percent) 0.08-2%.
The optimum quantum of utilization of 2-60 purpose silicon single crystal of the present invention is (weight percent) 0.15%.
Another object of the present invention is achieved in that its production craft step is as follows:
1), the preparation of ceramic polished adobe powder: mud, sand, stone, colorant, water are by the weighing of porcelain brick proportioning, and ball milling becomes mud, and it is standby to be spray dried to one or more pigment base substrate powders after deironing;
2), standby polished brick in porcelain character base substrate powder and 2-60 purpose silicon single crystal particle are mixed;
3), with the impact briquetting behind cloth of press or secondary material distributing of above-mentioned mixed powder;
4), drying;
5), burn till in 1150-1250 ℃;
6) polishing, deburring.
The present invention is through experimental study, filter out with the good silicon single crystal of porcelain adobe powder affinity, be used for porcelain brick first and make ornamental raw materials.
The present invention sneaks into 2-60 purpose silicon single crystal in above-mentioned porcelain adobe powder after, there is the flash of light speckle granule of metalluster on the polished brick in porcelain character surface of adopting polished brick in porcelain character production technique of the present invention to make, has extraordinary decorative effect, for the human consumer provides a kind of luxurious decoration polished brick in porcelain character.Be more suitable for beautifying the luxurious decoration of household and large public building.
Embodiment
Embodiment 1 (is example with white polished brick in porcelain character)
The preparation of ceramic polished adobe powder: get raw material by weight percentage, mud 25%, porcelain sand 50%, porcelain stone powder 25%, goal abrading-ball are worn into 250 mesh screen residue 0.8-1.0%, are processed into the ultrawhite powder by spraying drying;
The silicon single crystal of the ultrawhite powder of weight percent 99.92% and 20-30 order weight percent 0.08% mixes; Mixed powder is through cloth of press, drying, in 1210 ℃ burn till, polishing, deburring, the white products surface forms flash of light stippled finish effect.
Embodiment 2 (is example with the black porcelain polished tile)
The preparation of ceramic polished adobe powder (weight percent): mud 20%, porcelain sand 55%, porcelain stone powder 25%, add black pigment 4%, the goal abrading-ball is worn into 250 mesh screen residue 0.8-1.0%, is processed into the black powder by spraying drying;
Black porcelain brick powder (weight percent) 98% mixes with 40-50 order silicon single crystal particle (weight percent) 2%; Mixed powder is through the press secondary material distributing, drying, in 1170 ℃ of temperature burn till, polishing, deburring, the black product surface forms flash of light stippled finish effect.
Embodiment 3 (is example with white polished brick in porcelain character)
The preparation of ceramic polished adobe powder: get raw material by weight percentage, mud 25%, porcelain sand 50%, porcelain stone powder 25%, goal abrading-ball are worn into 250 mesh screen residue 0.8%-1.0%, are processed into the ultrawhite powder by spraying drying;
The silicon single crystal of the ultrawhite powder of weight percent 97% and 8-20 order weight percent 3% mixes; Mixed powder is through cloth of press, drying, in 1210 ℃ burn till, polishing, deburring, the white products surface forms flash of light stippled finish effect.
Embodiment 4 (is example with the spot polished brick in porcelain character)
The preparation of ceramic polished adobe powder: get raw material by weight percentage, mud 30%, porcelain sand 45%, porcelain stone powder 25%, the goal abrading-ball is worn into 250 mesh screen residue 0.8%-1.0%, be processed into white powder by spraying drying, above white powder proportioning adds 3% yellow colorant and makes yellow toner, adds 4% red colorant with proportioning on the white powder and makes red toner;
The preparation of high temperature frit; Get raw material by weight percentage, quartz 57%, calcite 24%, aluminum oxide 7%, zinc oxide 6%, soda ash 1%, boric acid 3%, barium carbonate 1%, magnesium oxide 1%; The raw material of said ratio mixes the back and founds for 1500 ℃ in the high temperature calcar; Shrend becomes particle; Sieve after the drying and make 2-60 order particle;
More than (weight percent) (yellow: redness: white=20: 30: 50) mix totally 98.85% of several color powders with silicon single crystal 8-20 order weight percentage 0.15% and high temperature frit 2-60 order weight percent 1%, the press secondary material distributing, drying, in 1220 ℃ burn till, polishing, deburring, the brindled brick surface forms mottled metal lustre decorative effect.
Embodiment 5 (is example with the spot polished brick in porcelain character)
The preparation of ceramic polished adobe powder: get raw material by weight percentage, mud 30%, porcelain sand 45%, porcelain stone powder 25%, the goal abrading-ball is worn into 250 mesh screen residue 0.8%-1.0%, be processed into white powder by spraying drying, above white powder proportioning adds 3% yellow colorant and makes yellow toner, adds 4% red toner with proportioning on the white powder;
The preparation of high temperature frit; Get raw material by weight percentage, quartz 57%, calcite 24%, aluminum oxide 7%, zinc oxide 6%, soda ash 1%, boric acid 3%, barium carbonate 1%, magnesium oxide 1%; The raw material of said ratio mixes the back and founds for 1500 ℃ in the high temperature calcar; Shrend becomes particle; Sieve after the drying and make 2-60 order particle;
More than several color powders (weight percent) 89% (yellow: redness: white=20: 30: 50) mix altogether with silicon single crystal 8-20 order weight percentage 10% and high temperature frit 2-6 order weight percent 1%, the press secondary material distributing, drying, in 1220 ℃ burn till, polishing, deburring, the brindled brick surface forms mottled metal lustre decorative effect.
Claims (7)
1, a kind of polished brick in porcelain character, it contains porcelain brick proportioning base powder, it is characterized in that: be mixed with 2-60 purpose silicon single crystal in porcelain adobe powder, the usage quantity of 2-60 purpose silicon single crystal accounts for below 10% of gross weight.
2, polished brick in porcelain character according to claim 1 is characterized in that: the weight percent of described 2-60 purpose silicon single crystal consumption is 0.08-2%.
3, polished brick in porcelain character according to claim 1 is characterized in that: the weight percent of described 2-60 purpose silicon single crystal consumption is 0.15%.
4, according to the production technique of claim 1 or 2 or 3 described polished brick in porcelain character, it is characterized in that:
1), the preparation of ceramic polished adobe powder: mud, sand, stone, colorant, water are by the weighing of porcelain brick proportioning, and ball milling becomes mud, and it is standby to be spray dried to one or more pigment base substrate powders after deironing;
2), standby base substrate powder and 2-60 order silicon single crystal silicon grain are mixed by proportioning;
3), mixed powder impact briquetting behind cloth of press or secondary material distributing;
4), drying;
5) burn till in 1150-1250 ℃;
6), polishing, deburring.
5, polished brick in porcelain character according to claim 1 is characterized in that: it also contains 2-60 purpose high temperature frit, and the weight percent of its add-on is 1%.
6, polished brick in porcelain character according to claim 5 is characterized in that: the batching of high temperature frit is formed weight percent and is: quartz 57%, calcite 24%, aluminum oxide 7%, zinc oxide 6%, soda ash 1%, boric acid 3%, barium carbonate 1%, magnesium oxide 1%.
7, according to the production technique of claim 5 or 6 described polished brick in porcelain character, it is characterized in that: the preparation method of high temperature frit: get raw material quartz, calcite, aluminum oxide, zinc oxide, soda ash, boric acid, barium carbonate, magnesium oxide by proportioning, above raw material is mixed the back found for 1500 ℃ in the high temperature calcar; Found after shrend becomes particle; Particle sieves and makes 2-60 order particle after drying.