CN1570324A - Method of making colored sand for construction decoration - Google Patents
Method of making colored sand for construction decoration Download PDFInfo
- Publication number
- CN1570324A CN1570324A CN 03149577 CN03149577A CN1570324A CN 1570324 A CN1570324 A CN 1570324A CN 03149577 CN03149577 CN 03149577 CN 03149577 A CN03149577 A CN 03149577A CN 1570324 A CN1570324 A CN 1570324A
- Authority
- CN
- China
- Prior art keywords
- resin
- adhesive
- colored
- organic
- sandstone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
This invention provides one building for decorative or ornamental purpos colored sand and crushed stone manufacture method, its characteristic lies in, after uses two kind of either two kind of above organic gummy (resin) the medicinal preparation or organic gummy (resin) the medicinal preparation and the inorganic adhesive intensive mixing forms compound gummy matches again by is organic or the inorganic pigment and the supplementary material helps the medicinal preparation, the mix forms the compound adhesive coating color thick liquid, to the tint or the white natural grit which selects carry on the surface treatment, causes the sand and crushed stone pellet evenly to wrap up the compound colored coating, again passes through certain temperature processing, forms has the reliable colored coating the colored sand and crushed stone. This invention craft simple, production cost inexpensive, simultaneously may through to compound be gummy (resin) the medicinal preparation to carry on the suitable combination to match with the proportion adjustment, facilitates nimbly improves the colored coating performance, entrusts with the colored sand and crushed stone different color and the performance characteristic. This invention manufacture colored sand and crushed stone color even, color bright-colored, the soil layer reliable is hard, has bears the aging, water resistant, bears the chemical reagent and so on the outstanding performance.
Description
The invention provides a kind of manufacture method of architectural decoration coloured sandstone.
The method of existing manufacturing coloured sandstone, mainly contain two kinds of technology paths: a kind of is the Ceramic glaze method, promptly adopt cryogenic glass glaze or ceramic glaze to make coloured coating, be characterized in that coating is firm, the surface is bright, but its manufacturing process is complicated, needs high temperature furnace to carry out sintering processes, not only manufacturing cost height, and control device complexity.Another kind method is the organic coating method, promptly makes coloured coating with a certain organic resin, is characterized in that technology is easy, but coating easily fades loss of properties on aging inadequately firmly with hard.
The invention provides a kind of new manufacture method---compound adhesive adhesive coating layer method, promptly adopt two or more organic gluing (resin) agent, or organic gluing (resin) agent and inorganic adhesive fully mix the back and form composite adhesive, be equipped with organic or inorganic pigment and auxiliary material auxiliary agent again, mix and form compound adhesive adhesive coating layer mill base, thereafter, selected light or white natural sandstone and compound gluing mill base to be dyed are fully mixed by a certain percentage, wrap composite coloured coating with making the sandstone uniform particles, form color grains, at last these color grains are carried out Low Temperature Heat Treatment, coloured coating is combined securely with particle, thereby produce the coloured sandstone of function admirable.
Technology of the present invention is easy, low production cost can improve the coloured coating performance easily and flexibly by suitable combination collocation and ratio adjustment are carried out in compound gluing (resin) agent simultaneously, give different color of coloured sandstone and performance characteristics, satisfy actual instructions for use.The colored sand and crushed stone color even that the present invention makes, color is bright and beautiful, and coating is firmly hard, has excellent properties such as ageing-resistant, water-fast, chemical-resistant reagent.
According to process characteristic of the present invention, taking environmental conservation into consideration characteristics again, can select water-based gluing (resin) agent for use as far as possible, as easily purchasing on the markets such as acrylic resin (emulsion) class, Lauxite class, water glass class, phosphoric acid salt and cheap product is made the sticking mill base material of compound adhesive, its industrial water (mainly being slurry) is after simple precipitation, can directly discharge, environment not polluted.
Process materials of the present invention is formed by 4 kinds, can use following equation expression:
A+B+C+D＝100％
A is compound gluing (resin) agent, A=A
1+ A
2+ A
3+ A
4A
1, A
2, A
3, A
4Deng being different single organic or inorganic gluing (resin) agent.It is 0.5～20% that A uses total amount.
B is the auxiliary material auxiliary agent, mainly contains talcum, titanium dioxide, kaolin, zinc oxide, prodan etc., and use amount is 0～30%.
C is inorganic or organic pigment, according to pigmenting power and being of different shades, takes the circumstances into consideration to select for use, and use amount is 0.1～6%.
D is white or light natural sandstone, as quartz sand, and calcite, wollastonite etc., the granularity scope is generally 0.08～12mm, and different with the shade requirement according to granularity difference (specific area difference), its usage ratio is generally 65～98%.
For A, the present invention recommends following compound gluing (resin) agent combination collocation:
Combination 1, A=A
1+ A
2
That is crylic acid resin (as pure-acrylic emulsion, benzene emulsion etc.)+Lauxite class (as Lauxite, melmac etc.).
This combination coating is ageing-resistant, water resistance good.
Combination 2, A=A
1+ A
2+ A
3
That is crylic acid resin+Lauxite class+polyvinyl acetate resin,
After this combination coating adds polyvinyl acetate resin, can increase coating brightness and hardness.
Combination 3, A=A
1+ A
4
Crylic acid resin (as pure-acrylic emulsion, benzene emulsion etc.)+water glass class (or phosphoric acid salt).
This combination coating hardness is higher, ageing-resistant, water resistance is good.
Combination 4, A=A
1+ A
2+ A
4
Crylic acid resin (as pure-acrylic emulsion, benzene emulsion etc.)+water glass class+Lauxite class
This combination coating adhesion strength height, hardness is also higher, and is ageing-resistant, chemical-resistance good.
Above process materials combination and production method actual process production testing, respond well.Lifting an example below is illustrated.
Embodiment 1: manufacturing 100kg, granularity are the green colorful quartz sands of 0.6～1.0mm.
1) at first prepares A-compound gluing (resin) agent, A=A
1+ A
2+ A
3,
Select for use: crylic acid resin+Lauxite class+polyvinyl acetate resin
Weighing A, cinnamic acid emulsion/Lauxite/polyvinyl acetate resin=0.4/0.5/0.1,
Total amount 2.8kg, mixing and stirring gets compound gluing (resin) agent A.
2) weighing B, talcum, kaolin, zinc oxide is 1.7kg altogether, ratio 7: 2: 1.
Weighing C, chrome oxide green pigment 0.5kg.
B, C two material mix stirring with compound gluing (resin) agent A, get green compound adhesive adhesive coating layer mill base.
3) take by weighing the common 95kg of refining quartz sand that granularity is 0.6～1.0mm, mix stirring, make quartz sand particle wrap coloured coating equably, get coloured coating quartz sand with green composite coating mill base.
4) coloured coating quartz sand is put into electric furnace, heat-treat under 170 ℃ of temperature, come out of the stove after 0.5 hour, cooling, and sorting process naturally promptly gets green quartz sand finished product.
Claims (6)
1, a kind of architectural decoration coloured sandstone manufacture method, it is characterized in that, it comprises: adopt two or more organic gluing (resin) agent or organic gluing (resin) agent and inorganic adhesive fully to mix the back and form composite adhesive, be equipped with organic or inorganic pigment and auxiliary material auxiliary agent again, mix forming compound adhesive adhesive coating layer mill base; , selected to be dyed light or white natural sandstone and compound gluing mill base by a certain percentage fully mixed, wrap composite coloured coating with making the sandstone uniform particles, form color grains thereafter; At last these color grains are carried out Low Temperature Heat Treatment, coloured coating is combined securely with particle, thereby produce the coloured sandstone of function admirable.
2, a kind of architectural decoration coloured sandstone manufacture method, it is characterized in that in the described process materials that the composite adhesive consumption is 0.5～20%, the auxiliary material auxiliary dosage is 0～30%, inorganic or organic pigment consumption is 0.1～6%, and white or light natural sandstone consumption is 65～98%.
3, method according to claim 1 and 2 is characterized in that described composite adhesive is combined as crylic acid resin+Lauxite class.
4, method according to claim 1 and 2 is characterized in that described composite adhesive is combined as crylic acid resin and Lauxite class and polyvinyl acetate resin.
5, method according to claim 1 and 2 is characterized in that described composite adhesive is combined as crylic acid resin+water glass class.
6, method according to claim 1 and 2 is characterized in that described composite adhesive is combined as crylic acid resin+water glass class+Lauxite class.