CN1216360C - 隔声降噪的材料 - Google Patents
隔声降噪的材料 Download PDFInfo
- Publication number
- CN1216360C CN1216360C CN 02157781 CN02157781A CN1216360C CN 1216360 C CN1216360 C CN 1216360C CN 02157781 CN02157781 CN 02157781 CN 02157781 A CN02157781 A CN 02157781A CN 1216360 C CN1216360 C CN 1216360C
- Authority
- CN
- China
- Prior art keywords
- powder
- inorganic
- sound insulation
- sound
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种隔声降噪的材料属于高分子材料领域。本发明各组分及其重量百分比含量为:PVC:5%~45%,无机粉:30%~90%,无机粉为高比重金属粉、无机盐粉或两者的混合物,金属粉为钨、铋、铜、钴、钼、金、银、镍的一种或者多种,无机盐粉为重质碳酸钡或/和重晶石或/和硫酸钡,偶联剂:1%~10%,助剂:4%~15%。本发明除具有柔软和隔声性能外,还具有阻燃、防化学介质、防腐蚀、无毒、可施工性等特点,适合用于对声学要求严格的场所和环境,以铜粉为原料制备的材料为例,1mm厚度的隔声指数可达21.2分贝(100~1600Hz)。
Description
技术领域
本发明涉及的是一种复合材料,特别是一种隔声降噪的材料,属于高分子材料领域。
背景技术
关于隔声材料的研制和应用已有几十年的历史,已形成了比较成熟的研制和生产体系,但是目前市场上通常使用的隔声材料都存在一些缺点如产品成本高,多为硬质材料,不易二次加工和对不规则物体进行隔声处理。因此其应用范围有一定局限性。经文献检索发现,日本专利号为:JP56059857,名称为:SOUND-INSULATING COMPOSITION(隔声复合材料),该专利公布了一种隔声材料的制备,采用铅粉等无机金属为原料,制成具有一定隔声性能的软质材料。但由于铅对环境有害,同时隔声效果也不是太好。
发明内容
本发明的目的在于克服现有技术中的不足,提供一种隔声降噪的材料,使其更有效降低噪声,并改善工作和生活环境。本发明是通过以下技术方案实现的,本发明材料各组分及其重量百分比含量为:PVC:5%~45%,无机粉:30%~90%,无机粉为高比重金属粉、无机盐粉或两者的混合物,金属粉为钨、铋、铜、钴、钼、金、银、镍的一种或者多种,无机盐粉为重质碳酸钡或/和重晶石或/和硫酸钡,偶联剂:1%~10%,助剂:4%~15%;通过混炼后经注塑、模压或压延而成型。
偶联剂采用钛酸酯类偶联剂中的一种或几种,助剂选用普通稳定剂、增塑剂和抗老化剂中的一种或几种。
本发明具有实质性特点和显著进步,本发明材料除具有柔软性好和隔声性能高外,还具有阻燃、防化学介质、防腐蚀、无毒、可施工性好等特点,以铜粉为原料制备的材料为例,1mm厚度的隔声指数可达21.2分贝(100~1600Hz)。本发明适合于做都市高架轨道交通、航空和港口的隔声材料,以及建筑行业轻质墙板夹层的隔振处理,使用此种隔声复合材料可以有效地降低噪声,改善工作和生活环境。
具体实施方式
结合本发明的内容进一步提供以下实施例:
实施例一
将各组分以下列配比均匀混合,并在开炼机上混炼,制成1毫米的软质薄片,其平均隔声量在25分贝左右。
PVC:30%,钨粉:55%,单烷氧基三(二辛基磷酰氧基)钛酸酯:5%,邻苯二甲酸二丁酯:8%,硬脂酸钡:1%,三盐基硫酸铅:1%。
实施例二
将各组分以下列配比均匀混合,并在开炼机上混炼,制成1毫米的软质薄片,其平均隔声量在23.7分贝左右。
PVC:45%,超细硫酸钡:30%,单烷氧基三(二辛基磷酰氧基)钛酸酯:10%,邻苯二甲酸二丁酯:10%,硬脂酸钡:3%,三盐基硫酸铅:2%。
实施例三
将下列组分混合均匀后在开炼机上混炼,制成1毫米的软质薄片,其平均隔声量在21.2分贝左右(100~1600Hz)。
PVC:5%,铜粉:90%,单烷氧基三(二辛基磷酰氧基)钛酸酯:1%,邻苯二甲酸二丁酯:3%,硬脂酸钡:0.5%,三盐基硫酸铅:0.5%。
材料各项性能
实例一 | 实例二 | 实例三 | ||
抗拉强度MPa | 横向 | 10.067 | 9.038 | 7.276 |
纵向 | 9.875 | 8.779 | 7.12 | |
断裂伸长率% | 横向 | 239.6 | 276.37 | 320.3 |
纵向 | 223.87 | 263.53 | 216.83 | |
阻燃性 | 阻燃 | 阻燃 | 阻燃 |
Claims (3)
1、一种隔声降噪的材料,其特征在于:各组分及其重量百分比含量为:PVC:5%~45%,无机粉:30%~90%,无机粉为高比重金属粉、无机盐粉或两者的混合物,金属粉为钨、铋、铜、钴、钼、金、银、镍的一种或者多种,无机盐粉为重质碳酸钡或/和重晶石或/和硫酸钡,偶联剂:1%~10%,助剂:4%~15%。
2、根据权利要求1所述的这种隔声降噪的材料,其特征是所述的偶联剂,其采用钛酸酯类偶联剂中的一种或几种。
3、根据权利要求1所述的这种隔声降噪的材料,其特征是所述的助剂,是选用稳定剂、增塑剂和抗老化剂中的一种或几种。