CN113201851A - 一种抗撕裂高分子瑜伽面料及其制备方法 - Google Patents

一种抗撕裂高分子瑜伽面料及其制备方法 Download PDF

Info

Publication number
CN113201851A
CN113201851A CN202110505003.0A CN202110505003A CN113201851A CN 113201851 A CN113201851 A CN 113201851A CN 202110505003 A CN202110505003 A CN 202110505003A CN 113201851 A CN113201851 A CN 113201851A
Authority
CN
China
Prior art keywords
fabric
yoga
tear
resistant polymer
following
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202110505003.0A
Other languages
English (en)
Inventor
蔡景润
谢若兰
刘雅玲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Demei New Material Technology Fujian Co ltd
Original Assignee
Demei New Material Technology Fujian Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Demei New Material Technology Fujian Co ltd filed Critical Demei New Material Technology Fujian Co ltd
Priority to CN202110505003.0A priority Critical patent/CN113201851A/zh
Publication of CN113201851A publication Critical patent/CN113201851A/zh
Pending legal-status Critical Current

Abstract

本发明属于高分子瑜伽面料领域，特别涉及一种抗撕裂高分子瑜伽面料及其制备方法，所述包括索罗娜、氨纶、涤棉和复合增强纱，本发明的索罗娜的手感柔软、弹性好，且吸水速度与棉织物相似，速度快、吸水干净；氨纶具有高弹性回复的效率，且进一步的提高了瑜伽面料的柔韧性；涤棉突出了涤纶的风格又有棉织物的长处，在干、湿情况下弹性和耐磨性都较好，尺寸稳定，缩水率小，具有挺拔、不易皱折、易洗、快干的特点，且复合增强纱内的聚苯硫醚和芳砜纶能够使得瑜伽面料具有阻燃的效果，复合增强纱内的高强尼龙长丝进一步的提高了弹性与耐磨性，且高强涤纶长丝的掺入提高了面料的强度，且弹性、耐磨性与吸水性皆有良好的表现。

Description

一种抗撕裂高分子瑜伽面料及其制备方法
技术领域
本发明涉及瑜伽面料及其制备方法相关领域，特别涉及一种抗撕裂高分子瑜伽面料及其制备方法。
背景技术
瑜伽是结合伸展和静心的运动，因此，瑜伽对服装面料的要求比较高，一方面，要求吸汗、排汗；另一方面，要求舒适、没有束缚感、贴肤感好，因此，瑜伽服对弹力要求高，此外，由于瑜伽服是贴身衣服，而人在进行瑜伽运动的过程中会产生大量的汗液，因此，如果瑜伽服不是采用绿色健康的面料，面料中的有害物质会随着人体毛孔的张开而进入皮肤、身体内，长期下去，会对人体造成很大的危害。
由于现有的瑜伽面料在使用的过程中，经纬向撕裂强度不均衡，通常经向撕裂强度远高于纬向，纬向撕裂强度低，所以大大降低了瑜伽产品的使用寿命，因此亟需研发一种抗撕裂高分子瑜伽面料及其制备方法。
发明内容
(一)要解决的技术问题
为了解决瑜伽产品在使用者长时间大浮动使用后，经纬撕裂的强度不均衡，从而降低瑜伽产品的使用寿命，本发明提供一种抗撕裂高分子瑜伽面料及其制备方法。
(二)技术方案
本发明通过如下技术方案实现：本发明提出了一种抗撕裂高分子瑜伽面料及其制备方法，所述一种抗撕裂高分子瑜伽面料包括以下原料：索罗娜、氨纶、涤棉和复合增强纱，其中涤棉和复合增强纱包括以下重量百分数的各组分：
涤棉按总质量分数100％计数：65％-67％涤纶、33％-35％棉花。
复合增强纱总质量分数100％计数：42％-46％高强尼龙长丝、44％-46％高强涤纶长丝、3％-7％聚苯硫醚、3％-5％芳砜纶。
作为进一步优选的，所述氨纶纱线的规格为70D。
作为进一步优选的，所述涤棉纱线的成分为T/C：65/35。
作为进一步优选的，所述在进行碱洗时，速度需要控制在42米/分。
一种抗撕裂高分子瑜伽面料及其制备方法，所述的生产工艺包括如下步骤：
(一)选材、整经，先选取所需要使用的所有材料，而后将纺织线进行整理；
(二)织造、、丝光、染色、物理摩擦、烘干，先将纱线进行织造成布料后，依次按照步骤进行，最后在对制造完成好的面料后，对面料进行烘干即可。
作为进一步优选的，所述在进行丝光过程中，PH值需要控制在6.5-7，且温度需要控制在40-60℃。
作为进一步优选的，所述在染色完成后，进行固色的温度需要控制在50-70℃，且时间需要控制在10-30分钟。
有益效果
本发明相对于现有技术，具有以下有益效果：
本发明的索罗娜的手感柔软、弹性好，且吸水速度与棉织物相似，速度快、吸水干净；氨纶具有高弹性回复的效率，且进一步的提高了瑜伽面料的柔韧性；涤棉突出了涤纶的风格又有棉织物的长处，在干、湿情况下弹性和耐磨性都较好，尺寸稳定，缩水率小，具有挺拔、不易皱折、易洗、快干的特点。
具体实施方式
本技术方案中：
为了使本发明的目的、技术方案及优点更加清楚明白，以下结合实施例，对本发明进行进一步详细说明。应当理解，此处所描述的具体实施例仅仅用以解释本发明，并不用于限定本发明。
实施例
一种抗撕裂高分子瑜伽面料包括以下原料：索罗娜、氨纶、涤棉和复合增强纱，涤棉组份为65-67份、33-35份，复合增强纱为42-46份高强尼龙长丝、44-46份高强涤纶长丝、3-7份聚苯硫醚、3-5份芳砜纶，随后先将所有的材料进行选取整理；
纺织：在进行纺织的过程中，六条纱路为一个基本循环，且每条纱路设有三个针路，一个基本循环为：第一条纱路的第一、二针路为平针，第一条纱路的第三针路为满针；第三条纱路的第一、三针路为平针，第三条纱路的第二针路为满针；第五条纱路的第二、三针路为平针，第五条纱路的第一针路为满针；第二、四、六条纱路的第一、二、三针路均为满针，且第一、第三纱路为索罗娜和氨纶；第二、第五纱路为涤棉；第四、第六纱路为复合增强纱。
丝光：可先将纺织好的面料放入烧碱溶液中进行丝光，且烧碱溶液的溶度为260～280g/L。
染色：随后将丝光好的面料放置入染缸内进行染色，且在染色处理完成后，需要对面料进行固定处理与速干整理，在固色是所需要的温度为50-70℃，且时间需要控制在10-30分钟，速干整理时，浴比为1：6-10，温度与时间均与固色的温度和时间相同。
物理摩擦：经过物理摩擦后，可以将染色完成的面料表面的毛进行磨除。
烘干：最后再次将面料放置烘干机内进行烘干，且烘干的时间只需要控制在20-30分钟，且烘干机内的温度为60℃。
本发明的索罗娜的手感柔软、弹性好，且吸水速度与棉织物相似，速度快、吸水干净；氨纶具有高弹性回复的效率，且进一步的提高了瑜伽面料的柔韧性；涤棉突出了涤纶的风格又有棉织物的长处，在干、湿情况下弹性和耐磨性都较好，尺寸稳定，缩水率小，具有挺拔、不易皱折、易洗、快干的特点，且复合增强纱内的聚苯硫醚和芳砜纶能够使得瑜伽面料具有阻燃的效果，复合增强纱内的高强尼龙长丝进一步的提高了弹性与耐磨性，且高强涤纶长丝的掺入提高了面料的强度，且弹性、耐磨性与吸水性皆有良好的表现。
以上所述仅为本发明的优选实施例而已，并不用于限制本发明，对于本领域的技术人员来说，本发明可以有各种更改和变化。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (7)

1.一种抗撕裂高分子瑜伽面料及其制备方法，其特征在于：所述一种抗撕裂高分子瑜伽面料包括以下原料：索罗娜、氨纶、涤棉和复合增强纱，其中涤棉和复合增强纱包括以下重量百分数的各组分
涤棉按总质量分数100％计数：65％-67％涤纶、33％-35％棉花。
复合增强纱总质量分数100％计数：42％-46％高强尼龙长丝、44％-46％高强涤纶长丝、3％-7％聚苯硫醚、3％-5％芳砜纶。
2.根据权利要求1所述一种抗撕裂高分子瑜伽面料及其制备方法，其特征在于：所述氨纶纱线的规格为70D。
3.根据权利要求1所述一种抗撕裂高分子瑜伽面料及其制备方法，其特征在于：所述涤棉纱线的成分为T/C：65/35。
4.根据权利要求1所述一种抗撕裂高分子瑜伽面料及其制备方法，其特征在于：所述在进行碱洗时，速度需要控制在42米/分。
5.根据权利要求1-4任一项所述的一种抗撕裂高分子瑜伽面料及其制备方法，其特征在于：所述的生产工艺包括如下步骤：
(一)选材、整经，先选取所需要使用的所有材料，而后将纺织线进行整理；
(二)织造、、丝光、染色、物理摩擦、烘干，先将纱线进行织造成布料后，依次按照步骤进行，最后在对制造完成好的面料后，对面料进行烘干即可。
6.根据权利要求5所述一种抗撕裂高分子瑜伽面料及其制备方法，其特征在于：所述在进行丝光过程中，PH值需要控制在6.5-7，且温度需要控制在40-60℃。
7.根据权利要求5所述一种抗撕裂高分子瑜伽面料及其制备方法，其特征在于：所述在染色完成后，进行固色的温度需要控制在50-70℃，且时间需要控制在10-30分钟。
CN202110505003.0A 2021-05-10 2021-05-10 一种抗撕裂高分子瑜伽面料及其制备方法 Pending CN113201851A (zh)