CN111777933A - 一种水性双组份白色弹性木器面漆及其制备方法 - Google Patents
一种水性双组份白色弹性木器面漆及其制备方法 Download PDFInfo
- Publication number
- CN111777933A CN111777933A CN202010522428.8A CN202010522428A CN111777933A CN 111777933 A CN111777933 A CN 111777933A CN 202010522428 A CN202010522428 A CN 202010522428A CN 111777933 A CN111777933 A CN 111777933A
- Authority
- CN
- China
- Prior art keywords
- water
- component
- aqueous
- acrylic resin
- wood finish
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种水性双组份白色弹性木器面漆及其制备方法,包括:组份A和组份B;所述组份A的原料重量比为:水性羟基丙烯酸树脂乳液60‑65%,水性分散剂0.3‑1%,弹性粉3‑5%,消光粉1‑2%,水性蜡乳液1‑3%,水性消泡剂0.2‑0.5%,水性润湿剂0.2‑0.5%,水性流平剂0.2‑0.5%,水性成膜助剂2‑6%,水性杀菌防霉剂0.1‑0.2%,水性钛白浆18‑25%,水性聚氨酯增稠剂0.5‑1%,去离子水1‑4%。所述组份B的原料重量比为:六亚甲基二异氰酯(HDI)的亲水性脂肪族聚异氰酸酯70‑80%,丙二醇甲醚醋酸酯20‑30%,除水剂0.5‑2%。本发明提供的涂料具有低光泽,高耐性,良好的肉厚感及爽滑性;漆膜与溶剂型底漆结合更致密,附着力更好;与油性漆相比更加环保、耐黄变,且硬度、耐水、耐化等性能较强;制备方法工艺简单、可操作性强。
Description
技术领域
本发明涉及涂料领域,尤其涉及一种高耐性、高肉厚感及爽滑性的水性双组份白色弹性木器面漆及其制备方法。
背景技术
随着全社会对环保意识的日益增强,用环保的水性涂料替代油性涂料已势在必行。水性涂料是一种以水为溶解介质的涂料,具有无毒环保、无气味、可挥发物极少、不燃不爆等优点,是不用有机溶剂作为稀释剂的绿色环保产品。所以越来越多的企业来采用水性涂料来满足客户以及自身的环保要求。然而市场上的现有水性双组份白色弹性木器面漆存在各种各样的缺点,比如耐性差,手感差,抗划伤差等,非常影响家具产品整体涂装效果。
因此,如何开发出一种高耐性、高肉厚感及爽滑性的水性双组份白色弹性木器面漆,解决现有的水性双组份白色弹性木器面漆存在的上述问题,已成为行业内具有前瞻意识的涂料厂家亟待解决的问题之一。
发明内容
本发明的目的在于提供一种低光泽,高耐性,具有良好的肉厚感及爽滑性的水性面漆。
为解决以上技术问题,本发明采用如下的技术方案:
一种水性双组份白色弹性木器面漆,包括:组份A和组份B;
所述组份A为:
所述组份B为:
六亚甲基二异氰酯(HDI)的亲水性脂肪族聚异氰酸酯 70-80%
丙二醇甲醚醋酸酯 20-30%
除水剂 0.5-2%
所述组份A与组份B的质量比为100:(10-20);
所述水性羟基丙烯酸树脂乳液包括高羟基丙烯酸树脂和/或中羟基丙烯酸树脂;所述高羟基丙烯酸树脂的羟基含量为3-4%,固含40-47%;中羟基丙烯酸树脂的羟基含量为2-2.5%,固含38-45%;
所述高羟基丙烯酸树脂的用量为10-18重量份;中羟基丙烯酸树脂的用量为42-55重量份;
所述水性分散剂包括BYK190和/或TEGO750W;
所述弹性粉为大日精化5070D;
所述消光粉为德固赛OK520;
所述水性蜡乳液包括为BYK513和/或龙海2558等高密度聚乙烯蜡乳液;
所述水性消泡剂包括TEGO902W、TEGO810、BYK028等聚醚类改性消泡剂中的一种或多种;
所述水性润湿剂包括TEGO270和/或TEGO4100和/或BYK346等有剂硅表面活性剂;
所述水性流平剂包括TEGO410、TEGO450、BYK333等聚醚硅烷类助剂中的一种或多种;
所述水性成膜助剂包括DPM、DPNB、丙二醇中的一种或多种;
所述水性杀菌防霉剂包括BEK100L、BEK560中的一种或多种;
所述水性钛白浆为科迪1008-SI水性钛白浆;
所述水性聚氨酯增稠剂包括RM-2020、RM-8W、TT615等聚氨酯缔合型流变助剂中的一种或多种;
所述除水剂包括Additive Ti、Additive OF中的一种或多种。
进一步,本发明还提供上述水性双组份白色弹性木器面漆的制备方法,包括以下步骤:
A组份制作方法:
5)将用300目过滤网将配方中高羟基丙烯酸树脂乳液,中羟基丙烯酸树脂乳液过滤到干净的容器中,分别按顺序投入水性分散剂,弹性粉,消光粉;将分散机调至800-1000r/min,分散20min以上;
6)取样刮板检验当细度≤20um时,添加水性消泡剂,将将分散机调至1500-1800r/min,分散25min以上;
7)取样滴两滴润湿剂喷涂观察涂膜外观是否缩孔,确认无缩孔以后将分散机转速调至800-1000r/min;
8)缓慢添加润湿剂、成膜助剂、水性杀菌防霉剂、水性流平剂、水性蜡乳液、水性钛白浆、水性聚氨酯增稠剂(用配方中去离子水开稀),搅拌30min,检验合格以后,用300目过滤网过滤得到A组份成品;
B组份制作方法:取干燥无水的容器,依次加入基于六亚甲基二异氰酯(HDI)的亲水性脂肪族聚异氰酸酯,丙二醇甲醚醋酸酯,除水剂混合搅拌均匀后分装到密闭的铁罐中。
使用时将A、B组份按比例调配均匀以后得到高耐性、高肉厚感及爽滑性的水性双组份白色弹性木器面漆。
本发明相比现有技术具有以下优点和有益效果:
1、本发明采用高羟基丙烯酸树脂乳液和中羟基丙烯酸树脂乳液搭配作为主要原材料,实现水性白色木器漆在涂料应用过程中在木材的润湿性非常好,与木材之间的结合程度非常高;
2、高羟基丙烯酸树脂乳液和中羟基丙烯酸树脂乳液搭配具有良好的成膜性能,漆膜与溶剂型底漆结合更致密,附着力更好;
3、本发明通过对各种助剂和辅料的特别选择和配比,最终得到的的水性面漆具有良好的肉厚及爽滑性的手感可以与油性漆相媲美,而且与油性漆相比更加环保、耐黄变,且硬度、耐水、耐化等性能较强;
4、本发明提供的水性双组份白色弹性木器面漆制备方法工艺简单、可操作性强、可连续化生产,适用于工业化规模生产的推广和应用。
具体实施方式
下面将结合具体实施例对本发明实施例中的技术方案进行清楚、完整地描述。
为了方便描述本发明的特征和优点,在下述实施例中:
所述的A组份中水性羟基丙烯酸树脂乳液选用拜耳公司的ACURE 2470(高羟)和广东花果山环保科技有限公司的2008(中羟);水性成膜助剂选用陶氏化学的DPM和DPNB;水性分散剂选用赢创公司的TEGO750W;弹性粉选用大日精化的5070D;消光粉选用德固赛OK520;水性蜡乳液选用毕克化学的BYK513;水性消泡剂选用赢创公司的TEGO902W和TEGO810;
水性润湿剂选用赢创公司的TEGO4100;水性流平剂选用赢创公司的TEGO410和毕克化学的BYK333;水性杀菌防霉剂选用广州冠志化工的BEK100L和BEK560;水性钛白浆选用广州科迪公司的1008-SI水性钛白浆;水性聚氨酯增稠剂选用陶氏化学RM-2020和RM-8W。
所述的B组份中六亚甲基二异氰酯(HDI)的亲水性脂肪族聚异氰酸酯选用拜耳公司的2655;丙二醇甲醚醋酸酯(PMA)选用陶氏化学生产的PMA;除水剂选用拜耳公司的Additive Ti。
实施例中所述材料均由市售购得,其牌号与厂家与说明书中所述的牌号与厂家相一致。
为使本发明的技术方案更加清楚、明确,以下列举实施例对本发明进一步详细说明。
实施例1
按下述配比制备一种水性双组份白色弹性木器面漆;
A组份:
B组份:
六亚甲基二异氰酯(HDI)的亲水性脂肪族聚异氰酸酯 80%
丙二醇甲醚醋酸酯 19%
除水剂 1%。
所述水性消泡剂由质量比为1:1的TEGO902W和TEGO810组成;水性流平剂由质量比为1:1的TEGO410和BYK333组成;水性成膜助剂由质量比为1:1的DPM和DPNB组成;水性杀菌防霉剂由质量比为1:1的BEK100L和BEK560组成;水性聚氨酯增稠剂由质量比为1:1的RM-2020和RM-8W组成。
A、B组份的重量比为100:15。
制备方法包括以下步骤:
A组份制作方法:
1)将用300目过滤网将配方中高羟基丙烯酸树脂乳液,中羟基丙烯酸树脂乳液过滤到干净的容器中,分别按顺序投入水性分散剂,弹性粉,消光粉;将分散机调至800-1000r/min,分散20min以上;
2)取样刮板检验当细度≤20um时,添加水性消泡剂,将将分散机调至1500-1800r/min,分散25min以上;
3)取样滴两滴润湿剂喷涂观察涂膜外观是否缩孔,确认无缩孔以后将分散机转速调至800-1000r/min;
4)缓慢添加润湿剂、成膜助剂、水性杀菌防霉剂、水性流平剂、水性蜡乳液、水性钛白浆、水性聚氨酯增稠剂(用配方中去离子水开稀),搅拌30min,检验合格以后,用300目过滤网过滤得到A组份成品。
B组份制作方法:取干燥无水的容器,依次加入基于六亚甲基二异氰酯(HDI)的亲水性脂肪族聚异氰酸酯,丙二醇甲醚醋酸酯,除水剂混合搅拌均匀后分装到密闭的铁罐中。
使用时将A、B组份按比例调配均匀以后制到水性双组份白色弹性木器面漆。
实施例2
按下述配比制备一种水性双组份白色弹性木器面漆;
A组份:
B组份:
六亚甲基二异氰酯(HDI)的亲水性脂肪族聚异氰酸酯 80%
丙二醇甲醚醋酸酯 19%
除水剂 1%。
所述水性消泡剂由质量比为1:1的TEGO902W和TEGO810组成;水性流平剂由质量比为1:1的TEGO410和BYK333组成;水性成膜助剂由质量比为1:1的DPM和DPNB组成;水性杀菌防霉剂由质量比为1:1的BEK100L和BEK560组成;水性聚氨酯增稠剂由质量比为1:1的RM-2020和RM-8W组成。A、B组份的重量比为100:15。
制备方法包括以下步骤:
A组份制作方法:
1)将用300目过滤网将配方中高羟基丙烯酸树脂乳液,中羟基丙烯酸树脂乳液过滤到干净的容器中,分别按顺序投入水性分散剂,弹性粉,消光粉;将分散机调至800-1000r/min,分散20min以上;
2)取样刮板检验当细度≤20um时,添加水性消泡剂,将将分散机调至1500-1800r/min,分散25min以上;
3)取样滴两滴润湿剂喷涂观察涂膜外观是否缩孔,确认无缩孔以后将分散机转速调至800-1000r/min;
4)缓慢添加润湿剂、成膜助剂、水性杀菌防霉剂、水性流平剂、水性蜡乳液、水性钛白浆、水性聚氨酯增稠剂(用配方中去离子水开稀),搅拌30min,检验合格以后,用300目过滤网过滤得到A组份成品。
B组份制作方法:取干燥无水的容器,依次加入基于六亚甲基二异氰酯(HDI)的亲水性脂肪族聚异氰酸酯,丙二醇甲醚醋酸酯,除水剂混合搅拌均匀后分装到密闭的铁罐中。
使用时将A、B组份按比例调配均匀以后制到水性双组份白色弹性木器面漆。
实施例3
按下述配比制备一种水性双组份白色弹性木器面漆;
A组份:
B组份:
六亚甲基二异氰酯(HDI)的亲水性脂肪族聚异氰酸酯 80%
丙二醇甲醚醋酸酯 19%
除水剂 1%。
所述水性消泡剂由质量比为1:1的TEGO902W和TEGO810组成;水性流平剂由质量比为1:1的TEGO410和BYK333组成;水性成膜助剂由质量比为1:1的DPM和DPNB组成;水性杀菌防霉剂由质量比为1:1的BEK100L和BEK560组成;水性聚氨酯增稠剂由质量比为1:1的RM-2020和RM-8W组成。A、B组份的重量比为100:15。
制备方法包括以下步骤:
A组份制作方法:
1)将用300目过滤网将配方中高羟基丙烯酸树脂乳液,中羟基丙烯酸树脂乳液过滤到干净的容器中,分别按顺序投入水性分散剂,弹性粉,消光粉;将分散机调至800-1000r/min,分散20min以上;
2)取样刮板检验当细度≤20um时,添加水性消泡剂,将将分散机调至1500-1800r/min,分散25min以上;
3)取样滴两滴润湿剂喷涂观察涂膜外观是否缩孔,确认无缩孔以后将分散机转速调至800-1000r/min;
4)缓慢添加润湿剂、成膜助剂、水性杀菌防霉剂、水性流平剂、水性蜡乳液、水性钛白浆、水性聚氨酯增稠剂(用配方中去离子水开稀),搅拌30min,检验合格以后,用300目过滤网过滤得到A组份成品。
B组份制作方法:取干燥无水的容器,依次加入基于六亚甲基二异氰酯(HDI)的亲水性脂肪族聚异氰酸酯,丙二醇甲醚醋酸酯,除水剂混合搅拌均匀后分装到密闭的铁罐中。
使用时将A、B组份按比例调配均匀以后制到水性双组份白色弹性木器面漆。
性能测试
对该水性双组份白色弹性木器面漆实施例1-3及市面普通乳液白色漆的漆膜外观、干燥时间、附着力、硬度、各种耐化性等性能进行检测。测试结果如下表所示:
由测试结果可知:
(1)本发明通过对高羟基丙烯酸树脂乳液和中羟基丙烯酸树脂乳液的搭配相对于普通羟基丙烯酸树脂乳液,表干时间缩短为≤30min,实干时间缩短为≤48h,必现有技术均缩短50%以上,显著优于现有技术。
(2)本发明通过对高羟基丙烯酸树脂乳液和中羟基丙烯酸树脂乳液的搭配使用,于六亚甲基二异氰酯(HDI)的亲水性脂肪族聚异氰酸酯反应后该面漆漆膜非常致密,表面硬度高;因此漆膜与木材及UV底漆、PU底漆底漆等溶剂型底漆结合更致密,附着力更好;对耐水性、耐汽油性、耐10%NaOH、耐10%HCL等各种物化性测试有更加优异的表现。
(3)本发明通过对弹性粉,消光粉以及各类助剂的选择使该面漆表面漆膜效果显著优于现有技术。
上述实施例为本发明较佳的实施方式,但应当理解的是,本发明的应用不限于上述的举例,对本领域普通技术人员来说,可以根据上述说明加以改进或变换,所有这些改进和变换都应属于本发明所附权利要求的保护范围。
Claims (10)
2.根据权利要求1所述的水性双组份白色弹性木器面漆,其特征在于,所述组份A与组份B的质量比为100:(10-20)。
3.根据权利要求1所述的水性双组份白色弹性木器面漆,其特征在于,
所述水性羟基丙烯酸树脂乳液包括高羟基丙烯酸树脂和中羟基丙烯酸树脂;
所述高羟基丙烯酸树脂的羟基含量为3-4%,固含40-47%;中羟基丙烯酸树脂的羟基含量为2-2.5%,固含38-45%;
所述高羟基丙烯酸树脂的用量为10-18重量份;中羟基丙烯酸树脂的用量为42-55重量份。
4.根据权利要求1所述的水性双组份白色弹性木器面漆,其特征在于:所述水性消泡剂包括TEGO902W、TEGO810、BYK028中的一种或多种。
5.根据权利要求1所述的水性双组份白色弹性木器面漆,其特征在于:所述水性流平剂包括TEGO410、TEGO450、BYK333中的一种或多种。
6.根据权利要求1所述的水性双组份白色弹性木器面漆,其特征在于:水性成膜助剂包括DPM、DPNB、丙二醇中的一种或多种。
7.根据权利要求1所述的水性双组份白色弹性木器面漆,其特征在于:所述水性杀菌防霉剂包括BEK100L、BEK560中的一种或多种。
8.根据权利要求1所述的水性双组份白色弹性木器面漆,其特征在于:所述水性聚氨酯增稠剂包括RM-2020、RM-8W、TT615中的一种或多种。
9.根据权利要求1所述的水性双组份白色弹性木器面漆,其特征在于:除水剂包括Additive Ti、Additive OF中的一种或多种。
10.一种制备如权利要求1-9任一项所述的水性双组份白色弹性木器面漆的方法,其特征在于,包括以下步骤:
A组份制作方法:
1)将用300目过滤网将配方中高羟基丙烯酸树脂乳液,中羟基丙烯酸树脂乳液过滤到干净的容器中,分别按顺序投入水性分散剂,弹性粉,消光粉;将分散机调至800-1000r/min,分散20min以上;
2)取样刮板检验当细度≤20um时,添加水性消泡剂,将将分散机调至1500-1800r/min,分散25min以上;
3)取样滴两滴润湿剂喷涂观察涂膜外观是否缩孔,确认无缩孔以后将分散机转速调至800-1000r/min;
4)缓慢添加润湿剂、成膜助剂、水性杀菌防霉剂、水性流平剂、水性蜡乳液、水性钛白浆、水性聚氨酯增稠剂(用配方中去离子水开稀),搅拌30min,检验合格以后,用300目过滤网过滤得到A组份成品;
B组份制作方法:取干燥无水的容器,依次加入基于六亚甲基二异氰酯(HDI)的亲水性脂肪族聚异氰酸酯,丙二醇甲醚醋酸酯,除水剂混合搅拌均匀后分装到密闭的铁罐中。