CN108950786A - A kind of processing method of the soft bright fabric of cotton - Google Patents
A kind of processing method of the soft bright fabric of cotton Download PDFInfo
- Publication number
- CN108950786A CN108950786A CN201811001575.XA CN201811001575A CN108950786A CN 108950786 A CN108950786 A CN 108950786A CN 201811001575 A CN201811001575 A CN 201811001575A CN 108950786 A CN108950786 A CN 108950786A
- Authority
- CN
- China
- Prior art keywords
- yarn
- fabric
- processing method
- cotton
- cellulase
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of processing methods of the soft bright fabric of cotton, including the following process successively carried out: spinning → doubling plying → yarn singeing → yarn enzyme polishing → warping → sizing → weaving → cropping → fabric detects → turns over cloth margin to seam → singes → desizing → dyeing → cellulase polishing → light noniron finish → press polish → preshrunk.Warping process of the present invention in yarn road after yarn singeing, enzymatic treatment process are conducive to before weaving, sizing process and weft yarn waxing process are conducive to reduce weaving generation filoplume, the cellulase polishing process of printing and dyeing final finishing can further decrease the surface hairiness of fabric, and each process is all linked with one another to achieve the purpose that reducing fabric surface filoplume promotes cloth cover reflecting feel.
Description
Technical field
The invention belongs to household textiles technical fields, and in particular to a kind of processing method of the soft bright fabric of cotton.
Background technique
Pure-cotton high-count high-density fabric, fiber long by length, that uniformity is high are made, therefore the sense of touch of fabric is fine and smooth, moisture absorption
Permeability is good.Frequently with Warp Satin stitch technique in bed necessaries fabric, the main reason is that satin shell fabric gloss is soft bright, feel
It is soft and smooth, if the filoplume of weft yarn is more will to be revealed in fabric surface, influence the reflecting feel of fabric.Pure-cotton high-count high-density face
Material, due to through close larger, when weaving warp thread during up and down motion, between warp thread and warp thread, between warp thread and weft yarn, warp thread and steel
Frictional force between reed is big, is easy to produce filoplume, and cloth cover filoplume reduces the reflecting feel and quality sense of fabric.High-count high-density fabric
Mobilizable space is less in fabric construction, if generating folding line in use, yarn would become hard to mobile reinstatement, this
Also reduce the reflecting feel of fabric in use.With enriching for people's physical resources, have to the quality of product higher
Pursuit, do not require nothing more than bed necessaries fabric have pro-skin, softness, moisture absorption breathe freely equivalent comfort energy, also require the sense of cloth cover class high, use
Easily arrange.
Summary of the invention
The present invention in view of the shortcomings of the prior art, provide a kind of processing method of soft bright fabric of cotton, the fabric have it is bright and clean,
Soft bright appearance, and appearance after laundering shape-retaining ability is good.
To realize that above-mentioned beneficial effect, the present invention use following technological means:
A kind of processing method of the soft bright fabric of cotton, including the following process successively carried out: spinning → doubling plying → yarn is burnt
Hair → yarn enzyme polishing → warping → sizing → weaving → cropping → fabric detects → turns over cloth margin to seam → → desizing → dyeing of singing
→ cellulase polishing → light noniron finish → press polish → preshrunk；
Yarn singeing process is first to singe to yarn, and singeing fire hole temperature is 1000-1100 DEG C, then winder, in high temperature
Kiering, bleaching are carried out in dye vat, technological parameter is refining agent 8-10g/L, bleeding agent 4-6g/L, hydrogen peroxide 2-4g/L；
Yarn enzyme polishing process specifically comprises the processes of: pH value 4.0-4.5, cellulase 0.5-3g/L, 40-45 DEG C of temperature, processing
Time 45-60min；
Sizing operation is first starching after waxing, formula of size are as follows: starch 40-45Kg, converted starch 30-35 Kg, PVA slurry 10-
25 Kg, acrylic acid 25-30 Kg.
Preferably, the raw material of spinning process is Xinjiang Long staple cotton of the fibre length in 38-42mm, mic value 3.7-4.2,
It is spun into 120S-200S yarn.
Preferably, the strand that doubling roving process obtains is 120S/2-200S/2.
Preferably, weaving process use eight pieces of satin weaves, weaved in air-jet loom, denting technique be 6 reeds/
Enter.
Preferably, weaving process when being sent into weft yarn by weft yarn through Over emulsfication material device.
Preferably, the singeing step counter is singed using two positive two.
Preferably, the cellulase polishing process specifically comprises the processes of: pH value 4.0-4.5, cellulase 0.5-3g/L,
40-45 DEG C of temperature, handle time 45-60min.
Preferably, the light noniron finish process specifically comprises the processes of: LEC no-ironing resin 10-20g/L, SQ5 2-3g/L,
GN-01 6-8g/L, FFS 2-3g/L, PH-S 0.5-2g/L, speed 25-40m/min, 160-170 DEG C of temperature, pressure 1-3kg.
By the above effective technology means, the present invention realize it is following the utility model has the advantages that
The warping process in yarn road after yarn singeing and enzymatic treatment process are conducive to before weaving, on sizing process and weft yarn
Wax process is conducive to reduce weaving generation filoplume, and the cellulase polishing process for final finishing of printing and dyeing can further decrease the surface of fabric
Filoplume, each process is all linked with one another to achieve the purpose that reducing fabric surface filoplume promotes cloth cover reflecting feel.Fabric passes through light non-ironing work
Skill promotes the wrinkle resistance of fabric, and fabric is not allowed to crease easily and generate filoplume in use, to make fabric persistently as new.
Detailed description of the invention
Fig. 1 is the fabric structure figure of embodiment 1, and Fig. 2 is the fabric structure figure of embodiment 2, wherein longitudinal
Yarn indicates that warp thread, lateral yarn indicate that weft yarn, ■ indicate that, through interlacing point, indicates latitude interlacing point.
Specific embodiment
The present invention provides a kind of manufacturing method of pure-cotton high-count high-density fabric.The fabric not only has soft bright reflecting feel,
And it is not wrinkled in fabric use process, appearance after laundering shape-retaining ability is good.The technical process of the fabric are as follows: spinning → doubling is closed
Stock → yarn singeing → yarn enzyme polishing → warping → sizing → weaving → cropping → fabric detects → turns over cloth margin to seam → singes →
Desizing → dyeing → cellulase polishing → light noniron finish → press polish → preshrunk.The specific process is as follows:
The preferred fibre length of fabric is in 38-42mm, and the Xinjiang Long staple cotton of mic value 3.7-4.2, thus cotton fiber passes through
Combing process, and using have the Spinning Frame of compact spinning apparatus at 120S-200S yarn.
In order to improve yarn strength and reduce filoplume, the fabric warp and weft is strand, specially 120S/2-200S/
2。
Filoplume is generated in warping process in order to reduce, the present invention singes to yarn and the pre-treatment work of enzyme polishing.
Gas singeing machine is specifically used, is singed to yarn, singeing fire hole temperature is 1000-1100 DEG C.Yarn network after singing
Cylinder, and kiering, bleaching are carried out in high temperature dye vat, technological parameter is refining agent 8-10g/L, bleeding agent 4-6g/L, hydrogen peroxide
2-4g/L.Enzyme polishing specifically comprises the processes of: pH value 4.0-4.5, handles the time by 40-45 DEG C of temperature, cellulase 0.5-3g/L
45-60min。
The sizing technique uses based on starch size, supplemented by PVA slurry, after waxing technique, principle of sizing mixing be in it is dense
Degree, medium viscosity.Formula of size starch 40-45Kg, converted starch 30-35 Kg, PVA slurry 10-25 Kg, acrylic acid 25-30
Kg.It is finally waxed with emulsifying wax to yarn, improves the flatness of yarn.
The fabric uses eight pieces of satin weaves, and specific eight piece of three winged Warp Satin and eight piece five fly through face satin weave,
It is weaved in air-jet loom.Wherein woven denting technique is 6 reeds/enter.
Through Over emulsfication material device when the weft weaving, makes weft yarn surface layer with wax, yarn smoothness is promoted, to subtract
Filoplume is weaved less.
The fabric using two positive two it is counter singe, the removal long filoplume of fabric, fabric generates after desizing and dyeing process
Slight filoplume, polished in overflow cylinder using cellulase, concrete technology is pH value 4.0-4.5,40-45 DEG C of temperature,
Cellulase 0.5-3g/L handles time 45-60min.
Fabric uses light ironing-free technology in softness sizing.Specially LEC no-ironing resin: 10-20g/L；SQ5:2-3g/L；
GN-01:6-8g/L；FFS:2-3g/L；PH-S:0.5-2g/L；Speed 25-40m/min, 160-170 DEG C of temperature, pressure 1-3kg.
Embodiment 1
The fabric warp and weft is all made of 120S/2 strand, specification 120S/2*120S/2/230*110, and fabric tissue is
Eight piece three is flown through face satin weave.
The present invention needs to handle yarn.It using gas singeing machine, singes to yarn, singeing fire hole temperature is
1100℃.Yarn carries out kiering, bleaching in high temperature dye vat, and technological parameter is refining agent 10g/L, bleeding agent 6g/L, dioxygen
Water 4g/L.Yarn enzyme polishing technological parameter be are as follows: pH value 4.5, temperature 45 C, cellulase 3g/L, handle time 60min.
The formula of size starch 45Kg of sizing technique, 35 Kg of converted starch, 25 Kg of PVA slurry, 30 Kg of acrylic acid.Most
It is waxed afterwards with emulsifying wax to warp thread, improves the flatness of yarn.
Through Over emulsfication material device when weft weaving, make weft yarn surface layer with wax.
The critical process of final finishing of the present invention is enzyme polishing and light ironing-free technology.It is carried out in overflow cylinder using cellulase
Polishing, concrete technology are pH value 4.5, temperature 45 C, cellulase 3g/L, processing time 60min.Fabric is adopted in softness sizing
With light ironing-free technology.Specially LEC no-ironing resin: 20g/L；SQ5:3g/L；GN-01:8g/L；FFS:3g/L；PH-S:2g/L；
Speed 40m/min, 170 DEG C of temperature, pressure 3kg.
Embodiment 2
The fabric warp and weft is all made of 200S/2 strand, specification 200S/2*200S/2/320*160, and fabric tissue is
Eight piece five is flown through face satin weave.
The present invention needs to handle yarn.It using gas singeing machine, singes to yarn, singeing fire hole temperature is
1000℃.Yarn carries out kiering, bleaching in high temperature dye vat, and technological parameter is refining agent 8g/L, bleeding agent 4g/L, hydrogen peroxide
2g/L.Yarn enzyme polishing technological parameter be are as follows: pH value 4.0,40 DEG C of temperature, cellulase 0.5g/L, handle time 45min.
The formula of size starch 40Kg of sizing technique, converted starch 30Kg, PVA slurry 10Kg, acrylic acid 25Kg.Finally use
Emulsifying wax waxes to warp thread, improves the flatness of yarn.
Through Over emulsfication material device when weft weaving, make weft yarn surface layer with wax.
The critical process of final finishing of the present invention is enzyme polishing and light ironing-free technology.It is carried out in overflow cylinder using cellulase
Polishing, concrete technology are pH value 4.0,40 DEG C of temperature, cellulase 0.5g/L, handle time 45min.Fabric is in softness sizing
Using light ironing-free technology.Specially LEC no-ironing resin: 10g/L；SQ5:2g/L；GN-01:6g/L；FFS:2g/L；PH-S:
0.5g/L；Speed 25m/min, 160 DEG C of temperature, pressure 1kg.
Claims (8)
1. a kind of processing method of the soft bright fabric of cotton, it is characterised in that: including the following process successively carried out: spinning → doubling
Plying → yarn singeing → yarn enzyme polishing → warping → sizing → weaving → cropping → fabric detects → turns over cloth margin to seam → is singed
→ desizing → dyeing → cellulase polishing → light noniron finish → press polish → preshrunk；
Yarn singeing process is first to singe to yarn, and singeing fire hole temperature is 1000-1100 DEG C, then winder, in high temperature
Kiering, bleaching are carried out in dye vat, technological parameter is refining agent 8-10g/L, bleeding agent 4-6g/L, hydrogen peroxide 2-4g/L；
Yarn enzyme polishing process specifically comprises the processes of: pH value 4.0-4.5, cellulase 0.5-3g/L, 40-45 DEG C of temperature, processing
Time 45-60min；
Sizing operation is first starching after waxing, formula of size are as follows: starch 40-45Kg, converted starch 30-35 Kg, PVA slurry 10-
25 Kg, acrylic acid 25-30 Kg.
2. the processing method of the soft bright fabric of cotton according to claim 1, it is characterised in that: the raw material of spinning process is fibre
Length is tieed up in the Xinjiang Long staple cotton of 38-42mm, mic value 3.7-4.2, is spun into 120S-200S yarn.
3. the processing method of the soft bright fabric of cotton according to claim 1, it is characterised in that: doubling roving process obtains
Strand is 120S/2-200S/2.
4. the processing method of the soft bright fabric of cotton according to claim 1, it is characterised in that: weaving process uses eight pieces of satin
Line tissue, is weaved in air-jet loom, and denting technique is 6 reeds/enter.
5. the processing method of the soft bright fabric of cotton according to claim 1, it is characterised in that: weaving process is being sent into weft yarn
When by weft yarn through Over emulsfication material device.
6. the processing method of the soft bright fabric of cotton according to claim 1, it is characterised in that: the singeing step uses two
Positive two counter singe.
7. the processing method of the soft bright fabric of cotton according to claim 1, it is characterised in that: the cellulase buffer
Sequence specifically comprises the processes of: pH value 4.0-4.5, cellulase 0.5-3g/L, handle time 45-60min by 40-45 DEG C of temperature.
8. the processing method of the soft bright fabric of cotton according to claim 1, it is characterised in that: the light noniron finish process
Specifically comprises the processes of: LEC no-ironing resin 10-20g/L, SQ5 2-3g/L, GN-01 6-8g/L, FFS 2-3g/L, PH-S 0.5-
2g/L, speed 25-40m/min, 160-170 DEG C of temperature, pressure 1-3kg.