CN111118897B - Manufacturing process of anti-pilling fabric - Google Patents
Manufacturing process of anti-pilling fabric Download PDFInfo
- Publication number
- CN111118897B CN111118897B CN202010033103.3A CN202010033103A CN111118897B CN 111118897 B CN111118897 B CN 111118897B CN 202010033103 A CN202010033103 A CN 202010033103A CN 111118897 B CN111118897 B CN 111118897B
- Authority
- CN
- China
- Prior art keywords
- fabric
- shaping
- grey cloth
- agent
- desizing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a manufacturing process of anti-pilling fabric, which comprises the following steps: s1, weaving gray fabric, namely selecting an empty-packaged twisted yarn material, performing waxing treatment on the empty-packaged twisted yarn material by a pulp-free process, and weaving the gray fabric on a loom; s2, pre-setting the grey cloth once, drying the grey cloth at 170-180 ℃, and quickly cooling the baked grey cloth to below 40 ℃; s3, desizing, namely desizing the grey cloth by adopting a tension-free desizing process; s4, performing secondary pre-shaping on the grey cloth, namely soaking the desized grey cloth in a yellowing prevention agent, and then completing secondary pre-shaping at 190-200 ℃; s5, shaping and drying, namely soaking the grey cloth in a yarn fixing agent and then drying at a high temperature; s6, water splashing and shaping, namely absorbing the water splashing agent in the dried grey cloth through a rolling groove, and shaping at high temperature to enable the width of the fabric to reach the required width. The fabric prepared by the process has good water repellency, abrasion resistance and pilling resistance.
Description
Technical Field
The invention relates to the field of textile fabric production, in particular to a manufacturing process of anti-pilling fabric.
Background
The environment of outdoor exercises is more special, and outdoor exercises fan needs place such as jungle of cominging in and going out often, and the surface fabric on one's body is caught easily by thorn bush etc. and leads to the fluff balling-up. The tool is easy to have fluffing and pilling phenomena due to the special use environment, so that the problems are urgently needed to be solved.
Disclosure of Invention
In view of the above problems, the invention aims to provide a manufacturing process of a pilling resistant fabric, which can improve the pilling resistance of the fabric and can also improve the water repellency and the abrasion resistance of the fabric.
In order to achieve the purpose, the technical scheme adopted by the invention is as follows:
a manufacturing process of anti-pilling fabric comprises the following steps:
s1, weaving gray fabric, namely selecting an empty-packaged twisted yarn material, performing waxing treatment on the empty-packaged twisted yarn material by a pulp-free process, and weaving the gray fabric on a loom. The waxing treatment can protect the yarn from yarn binding and pilling, and helps the fabric to resist fluffing and pilling.
S2, pre-shaping the gray fabric once, drying the gray fabric at 175-185 ℃, and quickly cooling the dried gray fabric to below 40 ℃. The size stability of the fabric is kept, the width shrinkage of the grey cloth is reduced, and the width is more stable.
And S3, desizing, namely desizing the grey cloth obtained in the step S2 by adopting a tension-free desizing process. The tension is released to the maximum extent, the warp elasticity of the fabric is well recovered, the looseness of the fabric is kept, and the fabric is good in hand feeling and toughness.
And S4, carrying out secondary pre-shaping on the grey cloth, soaking the desized grey cloth in a yellowing prevention agent, and then finishing secondary pre-shaping at 190-200 ℃. The spandex can be prevented from being burnt by high temperature, the spandex is protected from being damaged by high temperature, and the dimensional stability of the fabric is facilitated. The width control is consistent with the width after dyeing, which is beneficial to stabilizing the shrinkage rate of boiling water and the shrinkage rate of steam ironing and keeping the washing shrinkage rate at 60 ℃ within 3 percent.
And S5, shaping and drying, namely, soaking the grey cloth in the yarn fixing agent, and drying at high temperature, so that the grey cloth is not hardened and not hard and brittle.
S6, water is splashed for shaping, the dried grey cloth is subjected to rolling tank to absorb a shaping agent, and then high-temperature shaping is carried out, so that the width of the fabric reaches the required width, wherein the shaping agent comprises the following raw materials in percentage by weight:
3-9 g/L of resin
0.5-1 g/L of penetrating agent
20-100 g/L of water splashing agent
10-60 g/L of yarn cracking resistant agent.
Further, a step S41 is further included between the step S4 and the step S5, the gray fabric after the secondary pre-shaping is dyed, and the dyeing temperature is 90-95 ℃.
Further, in the step S1, the draft ratio of the empty twisted yarn is 2.8 to 3.6, and the twist number is 800 to 1200 turns/m.
Further, the tension-free desizing process in the step S3 is an ultrasonic high-frequency vibration desizing process, and the desizing time is 8-10 min. The contact time with the medicament is long, the desizing refining effect is better, and the good desizing effect is kept while the fiber is not damaged.
Further, the yellowing prevention agent in the step S4 is an alkyl sulfonate yellowing prevention agent, the code is 72406, and the using amount is 1-6g/L.
Furthermore, the yarn fixing agent in the step S5 is an organic silicon yarn fixing agent, and the using amount is 20-40 g/L.
Further, the setting conditions in step S5 are: the setting temperature is 155-165 ℃, the overfeeding is 3-20%, the speed is 30-60 m/min, and the breadth is 52-58'.
Further, the setting conditions in step S6 are: the setting temperature is 155-165 ℃, the overfeeding is 3-20%, the speed is 30-60 m/min, and the breadth is 52-58'.
The invention has the following beneficial effects: the process for manufacturing the anti-pilling fabric is provided, and the manufactured fabric has good water repellency, abrasion resistance and anti-pilling performance. The water repellency can reach ISO 4920 grade, the abrasion resistance can reach ISO 12947-2 (12 KPA/woven wood fabric) 2016 (5 ten thousand times), and the pilling resistance can reach GB/T4802.1 (1500 pilling) grade 4.
Detailed Description
The present invention will be further described with reference to the following embodiments.
Example one
The manufacturing process of the anti-pilling fabric comprises the following steps:
firstly, nylon 70D is selected for empty package twisting yarns, the twist number is 800 twist number/m, the Asahi formation spandex yarns, the package yarn draft ratio is 2.8, and the finished product warp and weft density: 145*120. The spandex yarns are waxed by a paddle-free process, and grey cloth is woven on a rapier loom.
And secondly, drying the grey cloth at 175 ℃, and quickly cooling the dried grey cloth to be below 40 ℃ to finish primary presetting.
And thirdly, desizing the grey cloth by adopting an ultrasonic high-frequency vibration desizing process, wherein the desizing time is 8min.
And step four, dipping the desized grey cloth into a yellowing preventing agent, and then finishing secondary pre-shaping at 190 ℃, wherein the yellowing preventing agent is an alkyl sulfonate yellowing preventing agent, the code is 72406, and the using amount is 1-6%.
Fifthly, dyeing the gray fabric subjected to secondary pre-shaping at the dyeing temperature of 90 DEG C
And fifthly, the grey cloth is dried at high temperature after being dipped in the yarn fixing agent. The yarn fixing agent is organic silicon yarn fixing agent, the using amount is 20g/L, and the setting conditions are as follows: the setting temperature is 155 ℃, the overfeeding is 3 percent, the speed is 30m/min, and the breadth is 52'.
Sixthly, absorbing a water-splashing medicament by the dried grey cloth through a rolling groove, and shaping at a high temperature, wherein the shaping conditions are as follows: the setting temperature is 155 ℃, the overfeeding is 3 percent, the speed is 30m/min, and the breadth is 52'. The water repellent medicament comprises resin and a water repellent agent, wherein the dosage of the resin is 3g/L, and the water repellent agent is prepared from the following raw materials in percentage by weight:
G01AY 0.5g/L
L75QG 20g/L
V17CS 10g/L。
the grey cloth prepared in the first embodiment is subjected to physical tests, the water repellency can reach ISO 4920 grade, the abrasion resistance can reach ISO 12947-2 2016 (12 KPA/woven wood fabric) >5 ten thousand times, and the fuzzing and pilling resistance can reach GB/T4802.1 (1500 fuzzing and 1500 pilling) grade 4.
Example two
The first step, selecting nylon 70D empty package twisting yarn, the twist is 900 twist number/m, the Asahi is formed into spandex yarn, the package yarn draft ratio is 3.2, the finished product warp and weft density: 145*120. The spandex yarns are waxed by a paddle-free process, and grey cloth is woven on a rapier loom.
And secondly, drying the grey cloth at 180 ℃, and quickly cooling the dried grey cloth to below 40 ℃ to finish primary pre-shaping.
And thirdly, desizing the grey cloth by adopting an ultrasonic high-frequency vibration desizing process, wherein the desizing time is 9min.
And step four, dipping the desized grey cloth into a yellowing preventing agent, and then finishing secondary pre-shaping at 195 ℃, wherein the yellowing preventing agent is an alkyl sulfonate yellowing preventing agent, the code is 72406, and the using amount is 1-6%.
Fifthly, dyeing the gray fabric subjected to secondary pre-shaping at the dyeing temperature of 95 DEG C
And fifthly, the grey cloth is dried at high temperature after being dipped in the yarn fixing agent. The yarn fixing agent is organic silicon yarn fixing agent, the using amount is 30g/L, and the setting conditions are as follows: setting temperature is 160 ℃, overfeeding is 15%, speed is 40m/min, and breadth is 54'.
Sixthly, absorbing the water repellent agent by the dried grey cloth through a rolling groove, and shaping at high temperature, wherein the shaping conditions are as follows: the setting temperature is 160 ℃, the overfeeding is 15%, the speed is 40m/min, and the breadth is 54'. The water splashing medicament comprises resin and a water splashing agent, the dosage of the resin is 6g/L, and the water splashing agent comprises the following raw materials:
G01AY 1g/L
L75QG 40g/L
V17CS 20g/L。
the grey cloth prepared in the second embodiment is subjected to physical tests, the water repellency can reach ISO 4920 grade, the abrasion resistance can reach ISO 12947-2 2016 (12 KPA/woven wood fabric) >5 ten thousand times, and the pilling resistance can reach GB/T4802.1 (1500 pilling times) 4 grade.
EXAMPLE III
Firstly, nylon 70D is selected for empty package twisting yarns, the twist number is 1200 twist number/m, the Asahi formation spandex yarns, the package yarn draft ratio is 3.6, and the warp and weft density of finished products are as follows: 145*120. The spandex yarns are subjected to a non-sizing process and a waxing treatment, and are woven into grey cloth on a rapier loom.
And secondly, drying the grey cloth at 185 ℃, and quickly cooling the dried grey cloth to below 40 ℃ to finish primary pre-shaping.
And thirdly, desizing the grey cloth by adopting an ultrasonic high-frequency vibration desizing process, wherein the desizing time is 10min.
And step four, dipping the desized grey cloth in a yellowing preventing agent, and then finishing secondary pre-shaping at 200 ℃, wherein the yellowing preventing agent is an alkyl sulfonate yellowing preventing agent with the code of 72406 and the using amount of 1-6%.
Fifthly, dyeing the gray fabric subjected to secondary pre-shaping at the dyeing temperature of 95 DEG C
And fifthly, the grey cloth is dried at high temperature after being dipped in the yarn fixing agent. The yarn fixing agent is organic silicon yarn fixing agent, the using amount is 40g/L, and the setting conditions are as follows: the setting temperature is 165 ℃, the overfeeding is 20%, the speed is 60m/min, and the breadth is 58'.
Sixthly, absorbing the water repellent agent by the dried grey cloth through a rolling groove, and shaping at high temperature, wherein the shaping conditions are as follows: the setting temperature is 165 ℃, the overfeeding is 20%, the speed is 60m/min, and the breadth is 58'. The water splashing medicament comprises resin and a water splashing agent, the dosage of the resin is 9g/L, and the water splashing agent comprises the following raw materials:
G01AY 1g/L
L75QG 100g/L
V17CS 60g/L。
physical tests are carried out on the grey cloth prepared in the third embodiment, the water repellency can reach ISO 4920 grade, the abrasion resistance can reach ISO 12947-2 2016 (12 KPA/woven wood fabric) >5 ten thousand times, and the pilling resistance can reach GB/T4802.1 (1500 pilling) 4 grade.
While the invention has been particularly shown and described with reference to a preferred embodiment, it will be understood by those skilled in the art that various changes in form and detail may be made therein without departing from the spirit and scope of the invention as defined by the appended claims.
Claims (8)
1. The manufacturing process of the anti-pilling fabric is characterized by comprising the following steps of:
s1, weaving gray fabric, namely selecting an empty-packaged twisted yarn material, performing waxing treatment on the empty-packaged twisted yarn material by a pulp-free process, and weaving the gray fabric on a loom;
s2, pre-shaping the gray fabric once, drying the gray fabric at 175-185 ℃, and quickly cooling the dried gray fabric to below 40 ℃;
s3, desizing, namely desizing the grey cloth obtained in the step S2 by adopting a tension-free desizing process;
s4, performing secondary pre-shaping on the grey cloth, namely soaking the desized grey cloth in a yellowing prevention agent, and then completing secondary pre-shaping at 190-200 ℃;
s5, shaping and drying, namely soaking the grey cloth in a yarn fixing agent and then drying at a high temperature;
s6, water is poured for shaping, the dried grey cloth is subjected to rolling groove absorption shaping agent, and high-temperature shaping is performed, so that the width of the fabric reaches the required width, and the shaping agent comprises the following raw materials in parts by weight:
3-9 g/L of resin
0.5-1 g/L of penetrating agent
20-100 g/L of water splashing agent
10-60 g/L of yarn cracking prevention agent.
2. The process for manufacturing the anti-pilling fabric as claimed in claim 1, wherein the process comprises the following steps: and a step S41 of dyeing the gray fabric subjected to secondary pre-shaping at the dyeing temperature of 90-95 ℃ is further included between the step S4 and the step S5.
3. The process for manufacturing the anti-pilling fabric as claimed in claim 1, wherein the process comprises the following steps: in the step S1, the draft ratio of the empty package twisted yarn is 2.8-3.6, and the twisting twist is 800-1200 turns/m.
4. The process for manufacturing the anti-pilling fabric as claimed in claim 1, wherein the process comprises the following steps: the tension-free desizing process in the step S3 is an ultrasonic high-frequency vibration desizing process, and the desizing time is 8-10 min.
5. The process for manufacturing the anti-pilling fabric as claimed in claim 1, wherein the process comprises the following steps: the yellowing inhibitor in the step S4 is alkyl sulfonate yellowing inhibitor, and the dosage is 1-6g/L.
6. The process for manufacturing the anti-pilling fabric as claimed in claim 1, wherein the process comprises the following steps: the yarn fixing agent in the step S5 is an organic silicon yarn fixing agent, and the using amount is 20-40 g/L.
7. The process for manufacturing the anti-pilling fabric as claimed in claim 1, wherein the process comprises the following steps: the setting conditions in the step S5 are as follows: the setting temperature is 155-165 ℃, the overfeeding is 3-20%, the speed is 30-60 m/min, and the breadth is 52-58'.
8. The process for manufacturing the anti-pilling fabric as claimed in claim 1, wherein the process comprises the following steps: the setting conditions in the step S6 are as follows: the setting temperature is 155-165 ℃, the overfeeding is 3-20%, the speed is 30-60 m/min, and the breadth is 52-58'.