CN107718831A - A kind of decorating film easy to use - Google Patents
A kind of decorating film easy to use Download PDFInfo
- Publication number
- CN107718831A CN107718831A CN201711090138.5A CN201711090138A CN107718831A CN 107718831 A CN107718831 A CN 107718831A CN 201711090138 A CN201711090138 A CN 201711090138A CN 107718831 A CN107718831 A CN 107718831A
- Authority
- CN
- China
- Prior art keywords
- layer
- decorating film
- another side
- connection corresponding
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of decorating film easy to use, the decorating film includes special media layer, the special media layer connection corresponding with glue layer, the connection corresponding with electrodeposited coating of the another side of the glue layer, the connection corresponding with embossing optical layer of the another side of the electrodeposited coating, the another side connection corresponding with printing layer of the embossing optical layer, the another side connection corresponding with PET film layer of the printing layer, the another side connection corresponding with stiffened coating of the PET film layer.Each functional layer of the present invention is got up by compoiste adhering from top to bottom.The present invention is used as a kind of decorating film with special media layer, heats and is attached to decorative aluminum plate, iron plate, on steel plate, you can is fabricated to out the products such as aluminium-plastic panel, ceiling, cut-off and furniture, execution conditions are more succinct, more efficient.
Description
Technical field
The present invention relates to a kind of decorating film, especially a kind of decorating film easy to use.
Background technology
Sheet metal surface coating technology is roughly divided into several techniques such as application, pad pasting, plating at present, and with film coating process
It is the most simple and environmentally-friendly, rich in color.
Generally there are two methods in film coating process, one kind is the applying hot melt adhesives on decorating film, heats and extrudes through hot-pressing roller,
PUR is penetrated into the pore interior of adherend, by mechanical bond, charge attraction, Van der Waals force, diffuse into one another, chemically react
Make to combine each other Deng active force, second method is before watch fob is compound, is coated with thermosetting glue on first in decorating film, leads to
Roller extruding is crossed, thermosetting glue is penetrated into the pore interior of adherend, then is handled through dry solidification, passes through mechanical bond, electric charge
Gravitation, Van der Waals force, the active force such as diffuse into one another, chemically react and make to combine each other.
If using first method, due to PUR uneven thickness or the spread deficiency of coating, bonding may be caused
Insufficient strength.If using second method, user must install automatic double surface gluer additional, and secondly steam bubble easily occurs in fitting process, paste
Enough cooking conditions environment are must assure that after conjunction, makes adhesive reaction complete, reaches solidification and complete, it is strong otherwise to influence bonding
Degree, while after gluing to before bonding, work cleannes must be high, the pollutant otherwise adhered in glue surface, plays buffer action,
Reduce adhesive effect.There is both of the above to require very high to bonding plane cleannes again, cleannes will not be high to be caused because of pollutant
Buffer action, reduces adhesive strength, it is necessary to physicomechanical processes or chemicals method by contaminant removal, until bonding plane
Expose metallic luster, then fully cleaned with trichloro ethylene steam, dry rear and can be used, such loaded down with trivial details process largely effects on production
Efficiency.Simultaneously because carrying solvent during gluing, final solvent can be discharged into air, because general producer will not be equipped with efficiently
Plant tail gas purified treatment, exist to environment and pollute.Therefore, it is necessary to design it is a kind of it is environmentally friendly, production cost is low, user
Just decorating film.
The content of the invention
For the defects of existing technology, there is provided a kind of decorating film easy to use.
The present invention is realized by following proposal：
A kind of decorating film easy to use, the decorating film include special media layer, the special media layer and glue layer pair
It should connect, the another side connection corresponding with electrodeposited coating of the glue layer, the another side of the electrodeposited coating is corresponding with embossing optical layer
Connection, the another side connection corresponding with printing layer of the embossing optical layer, the another side of the printing layer is corresponding with PET film layer to be connected
Connect, the another side connection corresponding with stiffened coating of the PET film layer.
The thickness of the stiffened coating is 1-10 microns, and the material of the stiffened coating includes UV resins.
The thickness of the PET film layer is 12-280 microns.
The thickness of the printing layer is 1-5 microns.
The thickness of the embossing optical layer is 1-20 microns, and the material of the embossing optical layer includes UV resins.
The thickness of the electrodeposited coating is 0.1-1 microns.
The thickness of the glue layer is 3-50 microns, and the material of the glue layer includes polyurethane adhesive.
The thickness of the special media layer is 30-200 microns, the material of the special media layer include ethylene-acetate and
Styrol copolymer.
Beneficial effects of the present invention are：
The present invention includes protection film layer, face mask layer, printed decoration layer, compound adhesive layer and special media bottom membrane, each work(
Ergosphere is got up by compoiste adhering from top to bottom.The present invention is attached to decoration as a kind of decorating film with special media layer, heating
Aluminium sheet, iron plate, on steel plate, you can be fabricated to out the products such as aluminium-plastic panel, ceiling, cut-off and furniture, execution conditions are more succinct, more
Efficiently.
The present invention is to use high polymer material as special media layer, and is directly bonded using special adhesive with decorating film
Together, making turns into a kind of decorating film with special media layer, and film in use, directly ironed stock by user with high temperature
On, decorating film will be bonded firmly on the substrate.
Brief description of the drawings
Fig. 1 is a kind of decorative film configuration schematic diagram easy to use of the present invention；
Embodiment
The preferred embodiment of the invention is further illustrated with reference to Fig. 1：
A kind of decorating film easy to use, the decorating film include special media layer 7, the special media layer 7 and glue layer 6
Corresponding connection, the another side connection corresponding with electrodeposited coating 5 of the glue layer 6, another side and the embossing optical layer of the electrodeposited coating 5
4 corresponding connections, the another side connection corresponding with printing layer 3 of the embossing optical layer 4, the another side and PET film of the printing layer 3
The corresponding connection of layer 2, the another side connection corresponding with stiffened coating 1 of the PET film layer 2.
The thickness of the stiffened coating 1 is 1-10 microns.The material of stiffened coating 1 preferentially selects UV resins, can make decoration
Film surface reaches 2H or more hardness, have it is anti-scratch, wearability, effectively protect membrane material.Stiffened coating is realized with coating method and applied
Cloth, coating process include the decorating films such as anilox roll coating, scraper for coating, multiple roll coating, the accurate coating of nick and are applied hardening liquid
Afterwards, by drying tunnel levelling, then irradiate by UV, realize ultraviolet curing, reach design hardness.Product hardness is higher, wear-resisting resistance to
It is better to scrape performance.
The thickness of the PET film layer 2 is 12-280 microns.Important carrier of the PET film layer 2 as decorating film, ink are printed
Its surface is brushed, to carry out step process.Preferably pet layer is same from sided corona treatment, immersion coating processing or both
When the polyester film that uses.
The thickness of the printing layer 3 is 1-5 microns.The material of printing layer 3 includes printing-ink.Printing layer is using print
Brush ink is directly printed on PET, and to show abundant pattern, printing layer is typically completed by multiple chromatograph double exposures, color ink bag
Color ink and metal color ink are included, the typography of printing layer has gravure, anilox printing, cylinder printing, flexographic printing etc., and pattern leads to
Color separation, engraving are crossed, roller is made, then ink is transferred in PET film by roller ink cell.
The thickness of the embossing optical layer 4 is 1-20 microns.The material of embossing optical layer 4 includes UV resins, embosses optics
Layer 4 is used as a kind of special optical dioptric layer, is to be printed onto using UV resins on material in practical application, then pass through mould or mould
Mould system and excessively ultraviolet lamp realize that UV solidifies, and allow UV resin beds grain texture occur, realize the refraction to light, so as to show
Go out optical effect, and mold membrane, mould will not be brought into decorating film, this coating only makees information transfer.The optical effect
Including 3D stereoeffects, optically focused astigmatism and other effects, typography has gravure, anilox printing, cylinder printing etc..
The thickness of the electrodeposited coating 5 is 0.1-1 microns.In the present embodiment, electrodeposited coating 5 preferentially selects vacuum plated aluminum film.It is logical
Vacuum plating, or water plating are crossed, aluminium atom is plated on material, realizes mirror-like silver effect.Puted forth effort by early stage, other gold can be achieved
Belong to color mirror effect.It can in advance be printed before plating and wash aluminium lamination, can be by washing aluminium technique the anti-of pattern after the completion of plating
As washing away, parcel plating effect is finally realized.Washing aluminium pre-treatment printing layer can use gravure, anilox printing, cylinder to print
Printing is realized etc. technique.
The thickness of the glue layer 6 is 3-50 microns.Glue layer is polyurethane adhesive, cured, will reach by 12 hours
To highest stripping and water-fast function.Solvent-based adhesive, solventless adhesive, aqueous adhesive etc. can be used in glue layer, applies
The technique of cloth adhesive includes net roll coating, scraper for coating, multiple roll coating, extrusion coated etc..
The thickness of the special media layer 7 is 30-200 microns.Using high polymer material as special media layer, and make
Directly it is bonded together with special adhesive with decorating film, making turns into a kind of decorating film with special media layer, and user makes
Used time, directly film is ironed on metallic plate with high temperature, decorating film will be bonded firmly on a metal plate.Preferably, by the gold of hot pressure
Category plate refers to the metallic plate such as aluminium sheet, galvanized sheet, steel, copper.It is as long as hot when user is using a kind of decorating film with special media layer
Scald film is multiple to reaching set adhesive strength after plate, it is not necessary to any maturing process, have viscosity stabilized, stronger initial stage glues
Connect intensity and later stage adhesive strength.
Special media layer 7 forms deielectric-coating by high polymer material, coupling molecule, its structure be ethene-vinyl acetate polymer,
The copolymers such as styrene, coupling molecule, tackifier, antioxidant, plasticizer.Using coextrusion process, high polymer material co-extrusion film forming,
The thickness of film is visibly homogeneous, error range 0.5~2%.Its ratio and effect are as shown in table 1：
The composition and ratio of the special media layer of table 1
Ethene-vinyl acetate polymer, formed it is characterized in that being rolled through high temperature, precision equipment.After solidification with PET and aluminium
Piece has the features such as stronger cementability, superior weatherability, light transmittance and ultraviolet resistance.Coupling molecule, increase is played in material
The metal materials such as organic resin ethylene-vinyl acetate copolymer in special media layer, styrene and aluminium sheet are bonded intensity, because
The effect of coupling agent is mainly modified to organic-inorganic product surface, makes adhesion stronger.Plasticizer increases when being rolled into sheet material
Add its plasticity, improve extrusion efficiency, while soak filler, improve cause because adding filler gelation degree reduction because
Element.
In the present embodiment, technical indicator is as shown in table 2 when special media layer is applied.
Technical indicator when the special media layer of table 2 is applied
| Project | Adhesive film technical indicator 0.05mm |
| Density (gram/cm) | 0.93-0.95 |
| Tensile strength (Mpa) | 11-20 |
| Elongation at break (%) | 280-350 |
| Fusing point (degree Celsius) | 95-130 |
In the present embodiment, special media layer 7 is made up of ethene-vinyl acetate modified copolymer, it is preferable that by ethene-
Acetate ethylene copolymer as special media layer, ethene-vinyl acetate modified copolymer have superior weatherability, light transmittance and
The characteristics such as ultraviolet resistance, through high temperature, precision equipment roll special media layer solidification after with glass, PET, TPT and silicon chip have compared with
Strong cementability.Due to making special media layer using coextrusion process, the thickness error of special media layer is relatively few, ensures final
When user scalds plate, overall uniformity.Due to without solvent, so being not likely to produce steam bubble, making heat posted scald the more reliable property of plate.Special Jie
When matter layer is heated boiling hot plate as end user, melting is used as adhesive, the film that upper strata supports is bonded with aluminium sheet and through supercooling
But after, bonding strength is effectively reached, its intensity is by mechanical bond, is diffused into one another, charge attraction, Van der Waals force, and chemistry is anti-
Multiple bonding forces should be waited to combine.
The present invention is in the case of without using second glue spreading water, and directly heating can just fit together with aluminium sheet, easy construction,
Environmental protection is had a positive effect, adhesive force is very good, and the overall structure of film is more resistant to time, more stable.Using to human body parent
Made with, environment friendly material, can avoid utilizing PVC, it is nontoxic, more environmentally friendly.Its material includes PET, macromolecule, PU bondings
Agent.The present invention is because multiple technique chromatographs are completed on the intensive printing production line to specialty, printing brush decorating film one of the present invention
As take effective purification of air technique, more favorably to environmental protection.
Although more detailed elaboration is done to technical scheme and has been enumerated, it will be appreciated that for ability
For field technique personnel, modification is made to above-described embodiment or uses equivalent alternative solution, this is to those skilled in the art
It is it is clear that these modifications or improvements without departing from theon the basis of the spirit of the present invention, belong to the present invention for member
Claimed scope.
Claims (8)
- A kind of 1. decorating film easy to use, it is characterised in that：The decorating film includes special media layer (7), the special media Layer (7) connection corresponding with glue layer (6), the another side connection corresponding with electrodeposited coating (5) of the glue layer (6), the electrodeposited coating (5) connection corresponding with embossing optical layer (4) of another side, the another side of the embossing optical layer (4) is corresponding with printing layer (3) to be connected Connect, the another side connection corresponding with PET film layer (2) of the printing layer (3), another side and the stiffened coating of the PET film layer (2) (1) corresponding connection.
- A kind of 2. decorating film easy to use according to claim 1, it is characterised in that：The thickness of the stiffened coating (1) Spend includes UV resins for 1-10 microns, the material of the stiffened coating (1).
- A kind of 3. decorating film easy to use according to claim 1, it is characterised in that：The thickness of the PET film layer (2) For 12-280 microns.
- A kind of 4. decorating film easy to use according to claim 1, it is characterised in that：The thickness of the printing layer (3) For 1-5 microns.
- A kind of 5. decorating film easy to use according to claim 1, it is characterised in that：The embossing optical layer (4) Thickness is 1-20 microns, and the material of the embossing optical layer (4) includes UV resins.
- A kind of 6. decorating film easy to use according to claim 1, it is characterised in that：The thickness of the electrodeposited coating (5) For 0.1-1 microns.
- A kind of 7. decorating film easy to use according to claim 1, it is characterised in that：The thickness of the glue layer (6) For 3-50 microns, the material of the glue layer (6) includes polyurethane adhesive.
- A kind of 8. decorating film easy to use according to claim 1, it is characterised in that：The special media layer (7) Thickness is 30-200 microns, and the material of the special media layer (7) includes ethylene-acetate and styrol copolymer.