CN1075731A - 快干腻子 - Google Patents
快干腻子 Download PDFInfo
- Publication number
- CN1075731A CN1075731A CN 93101647 CN93101647A CN1075731A CN 1075731 A CN1075731 A CN 1075731A CN 93101647 CN93101647 CN 93101647 CN 93101647 A CN93101647 A CN 93101647A CN 1075731 A CN1075731 A CN 1075731A
- Authority
- CN
- China
- Prior art keywords
- parts
- resins
- component
- putty
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种快干腻子由两种组分组成,其特征在于:第
一组分腻子基料组成为(重量份数):
聚酯粘合剂:337树脂 23—27份
196树脂 23—27份
182树脂 23—27份
3301树脂 23—27份
促进剂:环烷酸钻液 0.4—0.8份
填料:滑石粉 27—29份
轻钙 13—15份
钛白粉 9—11份
重晶石粉 7—11份
硅藻上 6—9份
白炭黑粉 0.5—2份
铁黑粉 0.5—2份
玻璃微珠 13—17份
(天津合成材料厂提供)
双飞粉(重质碳酸钙) 3—5份
第二组分固化剂组成(重量份数):过氧化环己酮
40—60份
白炭黑粉 40—60份。
Description
本发明涉及一种快干腻子,特别是一种常温快干双组份腻子。IPC E04B1/66。
众所周知,腻子有许多种,如目前一般油漆家具用于打底的腻子,建筑上用于嵌固门窗玻璃的腻子,漆机床或汽车外壳时刮嵌打底用的腻子,还有油腻子,水腻子等,这类腻子制作方法虽然简单,但存在的缺点较多,例如干固时间较长,易开裂,与作业面的结合力差,易剥落等等。中国专利CN86101069A专利申请公开了一种交联型乳胶烘烤腻子,虽然克服了一些上述腻子的缺点,但是其生产工艺极其复杂,在批量生产时,在设备和技术上都有较高要求,成本也较高,且因其固化时需要烘烤,所以其使用范围狭窄。而目前生产销售的多种新型腻子,如日本关西99腻子、合肥工业大学研制的“ARC常温快速固化腻子”、上海造漆厂生产的“聚脂腻子”以及上海前卫造漆厂生产的“H07-5环氧自干腻子”等等,尽管这类腻子均具有工艺性较好,涂补质量较高等特点,但其制取工艺复杂、冷却,耗能较多,因而产品成本较高。
本发明的目的是提供一种生产工艺简易,耗能少,所用的生产设备要求低,生产过程无三废排放,实际使用方便,涂层固化时间短,易打磨,不开裂,结合力强,可广泛用于金属或非金属表面涂补或装修的常温固化速效腻子,特别是一种双组份腻子。
本发明采用第一组份腻子基料和第二组份固化剂分别制取并分别包装,在使用时再按一定配比拌匀制得即可供使用的技术手段,来实现本发明目的。
所制的第一组份腻子基料,含有聚酯粘合剂、促进剂和填料,按配比经拌匀而制取。
所制的第二组份固化剂,含有引发剂、白炭黑,按配比经拌匀而制取。
本发明的进一步特征在于:所用的促进剂是环烷酸钴液,所用的引发剂是过氧化环己酮,所用的填料是含有滑石粉、钛白粉、硅藻土、重晶石粉、白炭黑粉、双飞粉、铁黑粉和玻璃微珠的混合物。
第一组份腻子基料组成为(重量份数):
聚酯粘合剂:
337树脂 23-27份
196树脂 23-27份
182树脂 23-27份
3301树脂 23-27份
促进剂:
环烷酸钴液 0.4-0.8份
填料:
滑石粉 27-29份
轻钙 13-15份
钛白粉 9-11份
重晶石粉 7-11份
硅藻土 6-9份
白炭黑粉 0.5-2份
铁黑粉 0.5-2份
玻璃微珠 13-17份
(天津合成材料厂提供)
双飞粉(重质碳酸钙) 3-5份
第二组份固化剂组成(重量份数):
过氧化环己酮 40-60份
白炭黑粉 40-60份
在实际使用时,第一、二双组份的配比为:第一组份腻子基料100(重量份数)加配第二组份固化剂0.5-10(重量份数),经拌匀制得即可供使用。
本发明腻子的制备方法如下:
1.第一组份的制备:
A.聚酯粘合剂的配制:将337树脂、196树脂、182树脂、3301树脂按上述配比在不锈钢搅拌槽中搅拌均匀,然后加促进剂,混匀。
B.填料:按上述配比将各种填料混合均匀。
C.将填料加到聚酯粘合剂中,搅拌均匀,并用三辊研磨机研磨两遍以上,灌筒包装,第一组份制备完毕;
2.第二组份制备:按前述配比将过氧化环己酮和白炭黑一起搅拌,研磨均匀,灌袋即成。
本发明具有生产工艺简单,节约能源,所用的生产设备要求低,生产过程无三废排放,产品成本低,使用方便,固化时间短可广泛适用于金属非金属表面涂补与装修。
以下用实施例对本发明作进一步说明。
实施例
取337树脂、196树脂、182树脂、3301树脂各25公斤,混拌均匀,然后加入0.5公斤环烷酸钴,继续混拌均匀。
在上面得到的聚酯粘合剂混合物中,添加滑石粉29公斤,轻钙15公斤,钛白份11公斤,双飞粉5公斤,硅藻土9公斤,玻璃微珠16公斤,重晶石粉11公斤,铁黑粉2公斤,白炭黑粉2公斤,然后将上述混合物搅拌均匀,并用三辊研磨机研磨三遍,灌筒包装,至此第一组份制备完毕。
取过氧化环己酮50公斤,白炭黑50公斤,将二者混合,并研磨均匀,灌袋包装,即成为第二种组份。
在实际使用时,取第一组份腻子基料100粉,第二组份固化剂三份,混合均匀后即可进行使用。
本发明的快干腻子经河北省合成材料质量监督检验测试站检验其使用性能如下:
腻子外观:浅黄,细腻,无结块膏状物。
涂层外观:干后不裂,不鼓包。
固含量:82%。
干燥时间:25分钟。
打磨性:易打磨,不沾砂纸。
耐冲击性:800(牛顿.厘米)
附着力:250(牛顿.平方厘米)
本领域技术人员应该明白,任何不超出本发明范围的改进,都在本发明的范围之内。
Claims (2)
1、一种快干腻子由两种组份组成,其特征在于:
第一组份腻子基料组成为(重量份数):
聚酯粘合剂:
337树脂 23--27份
196树脂 23--27份
182树脂 23--27份
3301树脂 23--27份
促进剂:
环烷酸钴液 0.4--0.8份
填料:
滑石粉 27--29份
轻钙 13--15份
钛白粉 9--11份
重晶石粉 7--11份
硅藻土 6--9份
白炭黑粉 0.5--2份
铁黑粉 0.5--2份
玻璃微珠 13--17份
(天津合成材料厂提供)
双飞粉(重质碳酸钙) 3--5份
第二组份固化剂组成(重量份数):
过氧化环己酮 40--60份
白炭黑粉 40--60份。
2、一种快干腻子制备方法,其特征在于:
1.第一组份的制备:
A.聚酯粘合剂的配制:将337树脂、196树脂、182树脂、3301树脂按上述配比在不锈钢搅拌槽中搅拌均匀,然后加促进剂,混匀;
B.填料:按上述配比将各种填料混合均匀;
C.将填料加到聚酯粘合剂中,搅拌均匀,并用三辊研磨机研磨两遍以上,灌筒包装,第一组份制备完毕;
2.第二组份制备:按前述配比将过氧化环己酮和白炭黑一起搅拌,研磨均匀,灌袋即成。