CN106480465A - 一种环保型脱脂剂及其制备方法 - Google Patents
一种环保型脱脂剂及其制备方法 Download PDFInfo
- Publication number
- CN106480465A CN106480465A CN201610950554.7A CN201610950554A CN106480465A CN 106480465 A CN106480465 A CN 106480465A CN 201610950554 A CN201610950554 A CN 201610950554A CN 106480465 A CN106480465 A CN 106480465A
- Authority
- CN
- China
- Prior art keywords
- sodium
- friedegreasing
- environmentally
- degreasing agent
- rotating speed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供了一种环保型脱脂剂及其制备方法。由以下步骤制备而成：（1）将五水偏硅酸钠、木质素磺酸钠、碳酸钠、氢氧化钠、柠檬酸钠和蒸馏水混合，用磁力搅拌机在室温下转速300‑500r/min下搅拌10‑20分钟；（2）加入海藻纤维、羧甲基纤维素、4A沸石、壬基酚聚氧乙烯醚、椰油酰胺丙基氧化胺、角鲨烷和聚氧乙烯山梨醇酐单硬脂酸酯，加热至40‑60℃，在转速200‑300r/min下搅拌20‑40分钟，冷却即得。本发明的一种环保型脱脂剂具有很好的脱脂效果，在室温和高温下脱脂率都很高，高温下相对更高，同时本材料不含磷，绿色环保。
Description
技术领域
本发明涉及精细化工技术领域，具体涉及一种环保型脱脂剂及其制备方法。
背景技术
在金属材料的表面处理工艺中，脱脂工序是其中一个非常重要的环节。金属材料表面上的各种油污不仅会阻碍磷化膜的形成，而且会影响涂层的结合力和耐蚀性，据统计，在表面处理中由于脱脂不彻底而导致镀层、转化膜不良的比例一般占60%-80%，因此选择一种合适的脱脂剂对于涂装前处理工艺来说非常重要。目前，多数脱脂剂的成分中仍以三聚磷酸钠为代表的聚磷酸盐为主，这是因为聚磷酸盐不仅能软化硬水，而且能捕捉污垢中所含的各种金属成分，使污垢在洗涤过程中得到解离，从而改善洗涤性能。但是聚磷酸盐类的脱脂剂也有其不可克服的缺点，就是富营养化，此类脱脂剂的废液排放中含有的大量磷会造成环境污染。因此，研究开发无磷的环保型脱脂剂对于环境保护具有重要的作用。
发明内容
要解决的技术问题：本发明的目的是提供一种环保型脱脂剂，具有很好的脱脂效果，在室温和高温下脱脂率都很高，高温下相对更高，同时本材料不含磷，绿色环保。
技术方案：一种环保型脱脂剂，由以下成分以重量份制备而成：五水偏硅酸钠5-10份、木质素磺酸钠2-5份、碳酸钠2-4份、海藻纤维1-3份、羧甲基纤维素1-2份、4A沸石2-4份、壬基酚聚氧乙烯醚0.5-1份、椰油酰胺丙基氧化胺0.5-1份、氢氧化钠15-20份、角鲨烷0.1-0.3份、聚氧乙烯山梨醇酐单硬脂酸酯0.5-1份、柠檬酸钠1-2份、蒸馏水75-100份。
进一步优选的，所述的一种环保型脱脂剂，由以下成分以重量份制备而成：五水偏硅酸钠6-9份、木质素磺酸钠3-4份、碳酸钠2.5-3.5份、海藻纤维1.5-2.5份、羧甲基纤维素1.2-1.8份、4A沸石2.5-3.5份、壬基酚聚氧乙烯醚0.6-0.9份、椰油酰胺丙基氧化胺0.6-0.9份、氢氧化钠16-19份、角鲨烷0.15-0.25份、聚氧乙烯山梨醇酐单硬脂酸酯0.6-0.9份、柠檬酸钠1.3-1.8份、蒸馏水80-90份。
上述易降解包装材料的制备方法包括以下步骤：
（1） 将五水偏硅酸钠、木质素磺酸钠、碳酸钠、氢氧化钠、柠檬酸钠和蒸馏水混合，用磁力搅拌机在室温下转速300-500r/min下搅拌10-20分钟；
（2） 加入海藻纤维、羧甲基纤维素、4A沸石、壬基酚聚氧乙烯醚、椰油酰胺丙基氧化胺、角鲨烷和聚氧乙烯山梨醇酐单硬脂酸酯，加热至40-60℃，在转速200-300r/min下搅拌20-40分钟，冷却即得。
进一步优选的，步骤（1）中转速为350-450r/min，搅拌时间为15分钟。
进一步优选的，步骤（2）中加热至45-55℃，转速为250r/min，搅拌时间为25-35分钟。
有益效果：本发明的一种环保型脱脂剂，具有很好的脱脂效果，其在30℃下的脱脂率在98.6%-99.2%之间，而在60℃下的脱脂率在99.2%-99.4%之间，在室温和高温下脱脂率都很高，高温下相对更高，同时本材料不含磷，绿色环保。
具体实施方式
实施例1
一种环保型脱脂剂，由以下成分以重量份制备而成：五水偏硅酸钠5份、木质素磺酸钠2份、碳酸钠2份、海藻纤维1份、羧甲基纤维素1份、4A沸石2份、壬基酚聚氧乙烯醚0.5份、椰油酰胺丙基氧化胺0.5份、氢氧化钠15份、角鲨烷0.1份、聚氧乙烯山梨醇酐单硬脂酸酯0.5份、柠檬酸钠1份、蒸馏水75份。
上述易降解包装材料的制备方法为：
（1） 将五水偏硅酸钠、木质素磺酸钠、碳酸钠、氢氧化钠、柠檬酸钠和蒸馏水混合，用磁力搅拌机在室温下转速300r/min下搅拌10分钟；
（2） 加入海藻纤维、羧甲基纤维素、4A沸石、壬基酚聚氧乙烯醚、椰油酰胺丙基氧化胺、角鲨烷和聚氧乙烯山梨醇酐单硬脂酸酯，加热至40℃，在转速200r/min下搅拌20分钟，冷却即得。
实施例2
一种环保型脱脂剂，由以下成分以重量份制备而成：五水偏硅酸钠6份、木质素磺酸钠3份、碳酸钠2.5份、海藻纤维1.5份、羧甲基纤维素1.2份、4A沸石2.5份、壬基酚聚氧乙烯醚0.6份、椰油酰胺丙基氧化胺0.6份、氢氧化钠16份、角鲨烷0.15份、聚氧乙烯山梨醇酐单硬脂酸酯0.6份、柠檬酸钠1.3份、蒸馏水80份。
上述易降解包装材料的制备方法为：
（1） 将五水偏硅酸钠、木质素磺酸钠、碳酸钠、氢氧化钠、柠檬酸钠和蒸馏水混合，用磁力搅拌机在室温下转速350r/min下搅拌15分钟；
（2） 加入海藻纤维、羧甲基纤维素、4A沸石、壬基酚聚氧乙烯醚、椰油酰胺丙基氧化胺、角鲨烷和聚氧乙烯山梨醇酐单硬脂酸酯，加热至45℃，在转速250r/min下搅拌25分钟，冷却即得。
实施例3
一种环保型脱脂剂，由以下成分以重量份制备而成：五水偏硅酸钠7.5份、木质素磺酸钠3.5份、碳酸钠3份、海藻纤维2份、羧甲基纤维素1.5份、4A沸石3份、壬基酚聚氧乙烯醚0.75份、椰油酰胺丙基氧化胺0.75份、氢氧化钠17.5份、角鲨烷0.2份、聚氧乙烯山梨醇酐单硬脂酸酯0.75份、柠檬酸钠1.5份、蒸馏水87.5份。
上述易降解包装材料的制备方法为：
（1） 将五水偏硅酸钠、木质素磺酸钠、碳酸钠、氢氧化钠、柠檬酸钠和蒸馏水混合，用磁力搅拌机在室温下转速400r/min下搅拌15分钟；
（2） 加入海藻纤维、羧甲基纤维素、4A沸石、壬基酚聚氧乙烯醚、椰油酰胺丙基氧化胺、角鲨烷和聚氧乙烯山梨醇酐单硬脂酸酯，加热至50℃，在转速250r/min下搅拌30分钟，冷却即得。
实施例4
一种环保型脱脂剂，由以下成分以重量份制备而成：五水偏硅酸钠9份、木质素磺酸钠4份、碳酸钠3.5份、海藻纤维2.5份、羧甲基纤维素1.8份、4A沸石3.5份、壬基酚聚氧乙烯醚0.9份、椰油酰胺丙基氧化胺0.9份、氢氧化钠19份、角鲨烷0.25份、聚氧乙烯山梨醇酐单硬脂酸酯0.9份、柠檬酸钠1.8份、蒸馏水90份。
上述易降解包装材料的制备方法为：
（1） 将五水偏硅酸钠、木质素磺酸钠、碳酸钠、氢氧化钠、柠檬酸钠和蒸馏水混合，用磁力搅拌机在室温下转速450r/min下搅拌15分钟；
（2） 加入海藻纤维、羧甲基纤维素、4A沸石、壬基酚聚氧乙烯醚、椰油酰胺丙基氧化胺、角鲨烷和聚氧乙烯山梨醇酐单硬脂酸酯，加热至55℃，在转速250r/min下搅拌35分钟，冷却即得。
实施例5
一种环保型脱脂剂，由以下成分以重量份制备而成：五水偏硅酸钠10份、木质素磺酸钠5份、碳酸钠4份、海藻纤维3份、羧甲基纤维素2份、4A沸石4份、壬基酚聚氧乙烯醚1份、椰油酰胺丙基氧化胺1份、氢氧化钠20份、角鲨烷0.3份、聚氧乙烯山梨醇酐单硬脂酸酯1份、柠檬酸钠2份、蒸馏水100份。
上述易降解包装材料的制备方法为：
（1） 将五水偏硅酸钠、木质素磺酸钠、碳酸钠、氢氧化钠、柠檬酸钠和蒸馏水混合，用磁力搅拌机在室温下转速500r/min下搅拌20分钟；
（2） 加入海藻纤维、羧甲基纤维素、4A沸石、壬基酚聚氧乙烯醚、椰油酰胺丙基氧化胺、角鲨烷和聚氧乙烯山梨醇酐单硬脂酸酯，加热至60℃，在转速300r/min下搅拌40分钟，冷却即得。
对比例1
本实施例与实施例5的区别在于不含有海藻纤维和羧甲基纤维素。具体地说是：
一种环保型脱脂剂，由以下成分以重量份制备而成：五水偏硅酸钠10份、木质素磺酸钠5份、碳酸钠4份、4A沸石4份、壬基酚聚氧乙烯醚1份、椰油酰胺丙基氧化胺1份、氢氧化钠20份、角鲨烷0.3份、聚氧乙烯山梨醇酐单硬脂酸酯1份、柠檬酸钠2份、蒸馏水100份。
上述易降解包装材料的制备方法为：
（1） 将五水偏硅酸钠、木质素磺酸钠、碳酸钠、氢氧化钠、柠檬酸钠和蒸馏水混合，用磁力搅拌机在室温下转速500r/min下搅拌20分钟；
（2） 加入4A沸石、壬基酚聚氧乙烯醚、椰油酰胺丙基氧化胺、角鲨烷和聚氧乙烯山梨醇酐单硬脂酸酯，加热至60℃，在转速300r/min下搅拌40分钟，冷却即得。
本发明的环保型脱脂剂的脱脂率见下表1，我们可以看到其在30℃下的脱脂率在98.6%-99.2%之间，而在60℃下的脱脂率在99.2%-99.4%之间，在室温和高温下脱脂率都很高，高温下相对更高，同时本材料不含磷，绿色环保。对比例1中不含有海藻纤维和羧甲基纤维素，其脱脂率有明显的下降，说明海藻纤维和羧甲基纤维素的加入对于提高脱脂除油效果有较大的影响。
表1 环保型脱脂剂的脱脂率
| 产品名称 | 30℃脱脂率（%） | 60℃脱脂率（%） |
| 实施例1 | 98.6 | 99.2 |
| 实施例2 | 98.8 | 99.3 |
| 实施例3 | 98.9 | 99.3 |
| 实施例4 | 99.2 | 99.4 |
| 实施例5 | 99.1 | 99.2 |
| 对比例1 | 95.3 | 97.1 |
Claims (5)
1.一种环保型脱脂剂，其特征在于：由以下成分以重量份制备而成：五水偏硅酸钠5-10份、木质素磺酸钠2-5份、碳酸钠2-4份、海藻纤维1-3份、羧甲基纤维素1-2份、4A沸石2-4份、壬基酚聚氧乙烯醚0.5-1份、椰油酰胺丙基氧化胺0.5-1份、氢氧化钠15-20份、角鲨烷0.1-0.3份、聚氧乙烯山梨醇酐单硬脂酸酯0.5-1份、柠檬酸钠1-2份、蒸馏水75-100份。
2.根据权利要求1所述的一种环保型脱脂剂，其特征在于：由以下成分以重量份制备而成：五水偏硅酸钠6-9份、木质素磺酸钠3-4份、碳酸钠2.5-3.5份、海藻纤维1.5-2.5份、羧甲基纤维素1.2-1.8份、4A沸石2.5-3.5份、壬基酚聚氧乙烯醚0.6-0.9份、椰油酰胺丙基氧化胺0.6-0.9份、氢氧化钠16-19份、角鲨烷0.15-0.25份、聚氧乙烯山梨醇酐单硬脂酸酯0.6-0.9份、柠檬酸钠1.3-1.8份、蒸馏水80-90份。
3.权利要求1至2任一项所述的一种环保型脱脂剂的制备方法，其特征在于：包括以下步骤：
（1） 将五水偏硅酸钠、木质素磺酸钠、碳酸钠、氢氧化钠、柠檬酸钠和蒸馏水混合，用磁力搅拌机在室温下转速300-500r/min下搅拌10-20分钟；
（2） 加入海藻纤维、羧甲基纤维素、4A沸石、壬基酚聚氧乙烯醚、椰油酰胺丙基氧化胺、角鲨烷和聚氧乙烯山梨醇酐单硬脂酸酯，加热至40-60℃，在转速200-300r/min下搅拌20-40分钟，冷却即得。
4.根据权利要求3所述的一种环保型脱脂剂的制备方法，其特征在于：所述步骤（1）中转速为350-450r/min，搅拌时间为15分钟。
5.根据权利要求3所述的一种环保型脱脂剂的制备方法，其特征在于：所述步骤（2）中加热至45-55℃，转速为250r/min，搅拌时间为25-35分钟。