CN105177749A - Polyamide yarn with anti-ultraviolet and anti-radiation functions - Google Patents
Polyamide yarn with anti-ultraviolet and anti-radiation functions Download PDFInfo
- Publication number
- CN105177749A CN105177749A CN201510585546.2A CN201510585546A CN105177749A CN 105177749 A CN105177749 A CN 105177749A CN 201510585546 A CN201510585546 A CN 201510585546A CN 105177749 A CN105177749 A CN 105177749A
- Authority
- CN
- China
- Prior art keywords
- weight portion
- agent
- radiation
- polystyrene
- polyamide yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a polyamide yarn with anti-ultraviolet and anti-radiation functions, and relates to the technical field of polyamide yarn spinning and manufacturing. The polyamide yarn is prepared from the following components: a PA6 slice, a carbon fiber, unsaturated polyester resin, polystyrene, epoxy resin, silicone powder, a silver fiber, a mulberry silk, nanosilicon dioxide, an alkali-free glass fiber, zinc oxide, a silica gel vulcanizing agent, titanium dioxide and an assistant; and the assistant is prepared from the following components: polyvinyl chloride, polystyrene, unsaturated polyester resin, polycarbonate, a coupling agent and a lubricating agent. According to the polyamide yarn, the radiation resistance of the polyamide yarn can be effectively improved; the anti-ultraviolet function of the polyamide yarn is improved; the wear-resisting property of the polyamide yarn can also be improved when the radiation protection capability and the anti-ultraviolet radiation ability are ensured; use by people is facilitated; and the safety performance is effectively improved.
Description
Technical field:
The present invention relates to POLYAMIDE YARNS textile manufacturing techniques field, be specifically related to a kind of POLYAMIDE YARNS with uvioresistant and radiation-resisting functional.
Background technology:
POLYAMIDE YARNS is a kind of weaving face fabric, has the polytypes such as monofilament, strand, special yarn, compared to the glossiness of silk broadcloth, POLYAMIDE YARNS fabric sheen is poor, as the sensation having coated one deck wax, rub back and forth with hand simultaneously, can feel friction sense between fabric.
In daily life, this fabric be mainly used at present make sportswear, scarf etc., still by people have an optimistic view of, in medical, be mainly used in making bandage, POLYAMIDE YARNS product is mainly for the production of trimming cloth.The advantage of POLYAMIDE YARNS is more well-pressed, and not balling-up is wrinkle resistant, convenient for cleaning.Because therefore some specific uses of POLYAMIDE YARNS require high to the radiation proof of POLYAMIDE YARNS and anti-uv-ray, especially some medical products are applied in even on clothes, excellent radiation protection ability and anti-uv-ray is needed to guarantee the result of use of product, but domestic market seldom can produce of fine quality and that shielding property is good POLYAMIDE YARNS in the manufacturing of POLYAMIDE YARNS, also or the good POLYAMIDE YARNS of anti-ultraviolet property, therefore this patent provides a kind of POLYAMIDE YARNS with uvioresistant and radiation-resisting functional, the shielding property that he effectively can improve POLYAMIDE YARNS can also improve anti-uv-ray simultaneously, break POLYAMIDE YARNS function singleness on market and even there is no the situation of function.
Summary of the invention:
Technical problem to be solved by this invention is to provide a kind of POLYAMIDE YARNS with uvioresistant and radiation-resisting functional, this product effectively can improve the capability of resistance to radiation of POLYAMIDE YARNS, improve the anti-ultraviolet function of POLYAMIDE YARNS, the anti-wear performance of POLYAMIDE YARNS can also be improved while ensureing radiation proof and anti-uv-ray.
There is a POLYAMIDE YARNS for uvioresistant and radiation-resisting functional, have following component to be prepared from:
PA6 section 50-60 weight portion
Carbon fiber 20-30 weight portion
Unsaturated-resin 20-30 weight portion
Polystyrene 20-30 weight portion
Epoxy resin 20-30 weight portion
Silicone powder 5-10 weight portion
Silver fiber 5-10 weight portion
Mulberry silk 5-10 weight portion
Nano silicon 5-10 weight portion
Alkali-free glass fibre 8-10 weight portion
Zinc oxide 1-3 weight portion
Silica gel vulcanizing agent 2-7 weight portion
Agent titanium dioxide 0.5-1.5 weight portion
Auxiliary agent 2-5 weight portion
Described auxiliary agent is prepared from by following component:
Polyvinyl chloride 15 weight portion
Polystyrene 15 weight portion
Unsaturated-resin 15 weight portion
Merlon 15 weight portion
Coupling agent 5 weight portion
Lubricant 5 weight portion
Above-mentioned a kind of POLYAMIDE YARNS with uvioresistant and radiation-resisting functional, its preparation method comprises the following steps:
(1) prepare auxiliary agent, polyvinyl chloride 15 weight portion, polystyrene 15 weight portion, unsaturated-resin 15 weight portion, Merlon 15 weight portion, coupling agent 5 weight portion, lubricant 5 weight portion are joined in high-speed mixer together and mix;
(2) raw material: PA6 section 50-60 weight portion, carbon fiber 20-30 weight portion, unsaturated-resin 20-30 weight portion, polystyrene 20-30 weight portion, epoxy resin 20-30 weight portion, silicone powder 5-10 weight portion, silver-colored fiber 5-10 weight portion, nano silicon 5-10 weight portion, alkali-free glass fibre 8-10 weight portion, zinc oxide 1-3 weight portion, silica gel vulcanizing agent 2-7 weight portion, agent titanium dioxide 0.5-1.5 weight portion, auxiliary agent 2-5 weight portion is prepared according to following proportioning;
(3) above-mentioned raw materials is carried out separately according to this drying process, use drying oven during process, temperature is arranged on 80-85 degree Celsius, continues 10 minutes;
(4) zinc oxide 1-3 weight portion, silica gel vulcanizing agent 2-7 weight portion, agent titanium dioxide 0.5-1.5 weight portion are joined according to this in masticator and carry out, for subsequent use after kneading 20-30 minute;
(5) spin fluid is prepared: utilize master batch to annotate pump and accurately add above each raw material, then mixed melting;
(6) spinning: mulberry silk is quantitatively pressed into filament spinning component through measuring pump together with above-mentioned spin fluid, is sprayed by spinnerets, forms tow in spinning window;
(7) aft-loaded airfoil: the fiber made is carried out successively draw-teisting, sizing, balance, dyeing grades and test package operation finally makes the POLYAMIDE YARNS with uvioresistant and radiation-resisting functional.
The product that the present invention obtains not only possesses the good feature of shielding property and also has good anti-ultraviolet property, in the formula of whole invention, utilize coupling agent, lubricant, polyvinyl chloride, polystyrene, unsaturated-resin, polycarbonate composition is prepared into auxiliary agent, utilize and add the performance that auxiliary agent can be whole raw material and product increase anti-ultraviolet property in the feed, and also add a large amount of silver-colored fibers in the feed, the compositions such as mulberry silk these can play shielding property under the adjustment of auxiliary agent, zinc oxide in addition, silica gel vulcanizing agent, agent titanium dioxide add the anti-wear performance that can increase POLYAMIDE YARNS, the finished product of the POLYAMIDE YARNS that whole like this processing step can be just in the process made is at antiultraviolet, there is the raising of high degree radiation proof and wear-resisting aspect.
Beneficial effect of the present invention is the capability of resistance to radiation that this product effectively can improve POLYAMIDE YARNS, improve the anti-ultraviolet function of POLYAMIDE YARNS, the anti-wear performance of POLYAMIDE YARNS can also be improved while ensureing radiation proof and anti-uv-ray, be convenient for people to use and effectively raise security performance, the anti-wear performance of POLYAMIDE YARNS can also be increased simultaneously, improve wilfulness and increase the service life.
Detailed description of the invention:
The technological means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with concrete example, setting forth the present invention further.
Embodiment 1:
There is a POLYAMIDE YARNS for uvioresistant and radiation-resisting functional, have following component to be prepared from:
PA6 cuts into slices 50 weight portions
Carbon fiber 20 weight portion
Unsaturated-resin 20 weight portion
Polystyrene 20 weight portion
Epoxy resin 20 weight portion
Silicone powder 5 weight portion
Silver fiber 5 weight portion
Mulberry silk 5 weight portion
Nano silicon 5 weight portion
Alkali-free glass fibre 8 weight portion
Zinc oxide 1 weight portion
Silica gel vulcanizing agent 2 weight portion
Agent titanium dioxide 0.5 weight portion
Auxiliary agent 2 weight portion
Described auxiliary agent is prepared from by following component:
Polyvinyl chloride 15 weight portion
Polystyrene 15 weight portion
Unsaturated-resin 15 weight portion
Merlon 15 weight portion
Coupling agent 5 weight portion
Lubricant 5 weight portion
Above-mentioned a kind of POLYAMIDE YARNS with uvioresistant and radiation-resisting functional, its preparation method comprises the following steps:
(1) prepare auxiliary agent, polyvinyl chloride 15 weight portion, polystyrene 15 weight portion, unsaturated-resin 15 weight portion, Merlon 15 weight portion, coupling agent 5 weight portion, lubricant 5 weight portion are joined in high-speed mixer together and mix;
(2) prepare raw material: PA6 according to following proportioning to cut into slices 50 weight portions, carbon fiber 20 weight portion, unsaturated-resin 20 weight portion, polystyrene 20 weight portion, epoxy resin 20 weight portion, silicone powder 5 weight portion, silver-colored fiber 5 weight portion, nano silicon 5 weight portion, alkali-free glass fibre 8 weight portion, zinc oxide 1 weight portion, silica gel vulcanizing agent 2 weight portion, agent titanium dioxide 0.5 weight portion, auxiliary agent 2 weight portion;
(3) above-mentioned raw materials is carried out separately according to this drying process, use drying oven during process, temperature is arranged on 80 degrees Celsius, continues 10 minutes;
(4) zinc oxide 1 weight portion, silica gel vulcanizing agent 2 weight portion, agent titanium dioxide 0.5 weight portion are joined according to this in masticator and carried out, kneading is for subsequent use after 20 minutes;
(5) spin fluid is prepared: utilize master batch to annotate pump and accurately add above each raw material, then mixed melting;
(6) spinning: mulberry silk is quantitatively pressed into filament spinning component through measuring pump together with above-mentioned spin fluid, is sprayed by spinnerets, forms tow in spinning window;
(7) aft-loaded airfoil: the fiber made is carried out successively draw-teisting, sizing, balance, dyeing grades and test package operation finally makes the POLYAMIDE YARNS with uvioresistant and radiation-resisting functional.
Embodiment 2:
There is a POLYAMIDE YARNS for uvioresistant and radiation-resisting functional, have following component to be prepared from:
PA6 cuts into slices 55 weight portions
Carbon fiber 25 weight portion
Unsaturated-resin 25 weight portion
Polystyrene 25 weight portion
Epoxy resin 25 weight portion
Silicone powder 8 weight portion
Silver fiber 8 weight portion
Mulberry silk 8 weight portion
Nano silicon 8 weight portion
Alkali-free glass fibre 9 weight portion
Zinc oxide 2 weight portion
Silica gel vulcanizing agent 5 weight portion
Agent titanium dioxide 1 weight portion
Auxiliary agent 3 weight portion
Described auxiliary agent is prepared from by following component:
Polyvinyl chloride 15 weight portion
Polystyrene 15 weight portion
Unsaturated-resin 15 weight portion
Merlon 15 weight portion
Coupling agent 5 weight portion
Lubricant 5 weight portion
Above-mentioned a kind of POLYAMIDE YARNS with uvioresistant and radiation-resisting functional, its preparation method comprises the following steps:
(1) prepare auxiliary agent, polyvinyl chloride 15 weight portion, polystyrene 15 weight portion, unsaturated-resin 15 weight portion, Merlon 15 weight portion, coupling agent 5 weight portion, lubricant 5 weight portion are joined in high-speed mixer together and mix;
(2) prepare raw material: PA6 according to following proportioning to cut into slices 55 weight portions, carbon fiber 25 weight portion, unsaturated-resin 25 weight portion, polystyrene 25 weight portion, epoxy resin 25 weight portion, silicone powder 8 weight portion, silver-colored fiber 8 weight portion, nano silicon 8 weight portion, alkali-free glass fibre 9 weight portion, zinc oxide 2 weight portion, silica gel vulcanizing agent 5 weight portion, agent titanium dioxide 1 weight portion, auxiliary agent 3 weight portion;
(3) above-mentioned raw materials is carried out separately according to this drying process, use drying oven during process, temperature is arranged on 80 degrees Celsius, continues 10 minutes;
(4) zinc oxide 2 weight portion, silica gel vulcanizing agent 5 weight portion, agent titanium dioxide 1 weight portion are joined according to this in masticator and carried out, kneading is for subsequent use after 25 minutes;
(5) spin fluid is prepared: utilize master batch to annotate pump and accurately add above each raw material, then mixed melting;
(6) spinning: mulberry silk is quantitatively pressed into filament spinning component through measuring pump together with above-mentioned spin fluid, is sprayed by spinnerets, forms tow in spinning window;
(7) aft-loaded airfoil: the fiber made is carried out successively draw-teisting, sizing, balance, dyeing grades and test package operation finally makes the POLYAMIDE YARNS with uvioresistant and radiation-resisting functional.
Embodiment 3
There is a POLYAMIDE YARNS for uvioresistant and radiation-resisting functional, have following component to be prepared from:
PA6 cuts into slices 60 weight portions
Carbon fiber 30 weight portion
Unsaturated-resin 30 weight portion
Polystyrene 30 weight portion
Epoxy resin 30 weight portion
Silicone powder 10 weight portion
Silver fiber 10 weight portion
Mulberry silk 10 weight portion
Nano silicon 10 weight portion
Alkali-free glass fibre 10 weight portion
Zinc oxide 3 weight portion
Silica gel vulcanizing agent 7 weight portion
Agent titanium dioxide 1.5 weight portion
Auxiliary agent 5 weight portion
Described auxiliary agent is prepared from by following component:
Polyvinyl chloride 15 weight portion
Polystyrene 15 weight portion
Unsaturated-resin 15 weight portion
Merlon 15 weight portion
Coupling agent 5 weight portion
Lubricant 5 weight portion
Above-mentioned a kind of POLYAMIDE YARNS with uvioresistant and radiation-resisting functional, its preparation method comprises the following steps:
(1) prepare auxiliary agent, polyvinyl chloride 15 weight portion, polystyrene 15 weight portion, unsaturated-resin 15 weight portion, Merlon 15 weight portion, coupling agent 5 weight portion, lubricant 5 weight portion are joined in high-speed mixer together and mix;
(2) prepare raw material: PA6 according to following proportioning to cut into slices 60 weight portions, carbon fiber 30 weight portion, unsaturated-resin 30 weight portion, polystyrene 30 weight portion, epoxy resin 30 weight portion, silicone powder 10 weight portion, silver-colored fiber 10 weight portion, nano silicon 10 weight portion, alkali-free glass fibre 10 weight portion, zinc oxide 3 weight portion, silica gel vulcanizing agent 7 weight portion, agent titanium dioxide 1.5 weight portion, auxiliary agent 5 weight portion;
(3) above-mentioned raw materials is carried out separately according to this drying process, use drying oven during process, temperature is arranged on 80-85 degree Celsius, continues 10 minutes;
(4) zinc oxide 3 weight portion, silica gel vulcanizing agent 7 weight portion, agent titanium dioxide 1.5 weight portion are joined according to this in masticator and carried out, kneading is for subsequent use after 30 minutes;
(5) spin fluid is prepared: utilize master batch to annotate pump and accurately add above each raw material, then mixed melting;
(6) spinning: mulberry silk is quantitatively pressed into filament spinning component through measuring pump together with above-mentioned spin fluid, is sprayed by spinnerets, forms tow in spinning window;
(7) aft-loaded airfoil: the fiber made is carried out successively draw-teisting, sizing, balance, dyeing grades and test package operation finally makes the POLYAMIDE YARNS with uvioresistant and radiation-resisting functional.
More than show and describe general principle of the present invention and principal character and advantage of the present invention.The technical staff of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and description just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (2)
1. one kind has the POLYAMIDE YARNS of uvioresistant and radiation-resisting functional, it is characterized in that: have following component to be prepared from: PA6 section 50-60 weight portion, carbon fiber 20-30 weight portion, unsaturated-resin 20-30 weight portion, polystyrene 20-30 weight portion, epoxy resin 20-30 weight portion, silicone powder 5-10 weight portion, silver fiber 5-10 weight portion, mulberry silk 5-10 weight portion, nano silicon 5-10 weight portion, alkali-free glass fibre 8-10 weight portion, zinc oxide 1-3 weight portion, silica gel vulcanizing agent 2-7 weight portion, agent titanium dioxide 0.5-1.5 weight portion, auxiliary agent 2-5 weight portion, described auxiliary agent is prepared from by following component: polyvinyl chloride 15 weight portion polystyrene 15 weight portion, unsaturated-resin 15 weight portion, Merlon 15 weight portion, coupling agent 5 weight portion, lubricant 5 weight portion.
2. there is a preparation method for the POLYAMIDE YARNS of uvioresistant and radiation-resisting functional, it is characterized in that: comprise the following steps:
(1) prepare auxiliary agent, polyvinyl chloride 15 weight portion, polystyrene 15 weight portion, unsaturated-resin 15 weight portion, Merlon 15 weight portion, coupling agent 5 weight portion, lubricant 5 weight portion are joined in high-speed mixer together and mix;
(2) raw material: PA6 section 50-60 weight portion, carbon fiber 20-30 weight portion, unsaturated-resin 20-30 weight portion, polystyrene 20-30 weight portion, epoxy resin 20-30 weight portion, silicone powder 5-10 weight portion, silver-colored fiber 5-10 weight portion, nano silicon 5-10 weight portion, alkali-free glass fibre 8-10 weight portion, zinc oxide 1-3 weight portion, silica gel vulcanizing agent 2-7 weight portion, agent titanium dioxide 0.5-1.5 weight portion, auxiliary agent 2-5 weight portion is prepared according to following proportioning;
(3) above-mentioned raw materials is carried out separately according to this drying process, use drying oven during process, temperature is arranged on 80-85 degree Celsius, continues 10 minutes;
(4) zinc oxide 1-3 weight portion, silica gel vulcanizing agent 2-7 weight portion, agent titanium dioxide 0.5-1.5 weight portion are joined according to this in masticator and carry out, for subsequent use after kneading 20-30 minute;
(5) spin fluid is prepared: utilize master batch to annotate pump and accurately add above each raw material, then mixed melting;
(6) spinning: mulberry silk is quantitatively pressed into filament spinning component through measuring pump together with above-mentioned spin fluid, is sprayed by spinnerets, forms tow in spinning window;
(7) aft-loaded airfoil: the fiber made is carried out successively draw-teisting, sizing, balance, dyeing grades and test package operation finally makes the POLYAMIDE YARNS with uvioresistant and radiation-resisting functional.