CN104448094A - 用于生产热稳定性聚偏氟乙烯的工艺 - Google Patents

用于生产热稳定性聚偏氟乙烯的工艺 Download PDF

Info

Publication number
CN104448094A
CN104448094A CN201410731743.6A CN201410731743A CN104448094A CN 104448094 A CN104448094 A CN 104448094A CN 201410731743 A CN201410731743 A CN 201410731743A CN 104448094 A CN104448094 A CN 104448094A
Authority
CN
China
Prior art keywords
weight
parts
weight part
production process
polyvinylidene fluoride
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410731743.6A
Other languages
English (en)
Inventor
徐建林
邹建良
宗建青
仇峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU LIYUAN MEMBRANE TECHNOLOGY Co Ltd
Original Assignee
CHANGSHU LIYUAN MEMBRANE TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU LIYUAN MEMBRANE TECHNOLOGY Co Ltd filed Critical CHANGSHU LIYUAN MEMBRANE TECHNOLOGY Co Ltd
Priority to CN201410731743.6A priority Critical patent/CN104448094A/zh
Publication of CN104448094A publication Critical patent/CN104448094A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种用于生产热稳定性聚偏氟乙烯的工艺，包括如下步骤：1）反应釜中投入1.7重量份双氧水、3.6重量份无机碱溶液，混合均匀，再投入8.2重量份氟利昂溶剂、1.9重量份丙酰氯溶液，在-6.5℃搅拌反应42分钟；2）再通入2.5重量份聚乙烯吡咯烷酮溶液、81重量份偏氟乙烯单体、1.4重量份二溴环戊烷，在13℃搅拌反应，压力下降至0.19MPa以下时终止反应；3）过滤、洗涤、干燥，即得粉末状聚偏氟乙烯。本发明制备的偏氟乙烯具有良好的热稳定性和可加工性，可满足注塑、挤出和拉膜等生产工艺。

Description

用于生产热稳定性聚偏氟乙烯的工艺
技术领域
本发明涉及用于生产热稳定性聚偏氟乙烯的工艺。
背景技术
现有的偏氟乙烯材料，其热稳定性和可加工性有待提高，特别是不能很好的满足注塑、挤出和拉膜等生产工艺。 
发明内容
本发明的目的在于提供一种用于生产热稳定性聚偏氟乙烯的工艺，其制备的偏氟乙烯具有良好的热稳定性和可加工性，可满足注塑、挤出和拉膜等生产工艺。
为实现上述目的，本发明的技术方案是设计一种用于生产热稳定性聚偏氟乙烯的工艺，包括如下步骤：
1）反应釜中投入1.7重量份双氧水、3.6重量份无机碱溶液，混合均匀，再投入8.2重量份氟利昂溶剂、1.9重量份丙酰氯溶液，在-6.5℃搅拌反应42分钟；
2）再通入2.5重量份聚乙烯吡咯烷酮溶液、81重量份偏氟乙烯单体、1.4重量份二溴环戊烷，在13℃搅拌反应，压力下降至0.19MPa以下时终止反应；
3）过滤、洗涤、干燥，即得粉末状聚偏氟乙烯。
本发明的优点和有益效果在于：提供一种用于生产热稳定性聚偏氟乙烯的工艺，其制备的偏氟乙烯具有良好的热稳定性和可加工性，可满足注塑、挤出和拉膜等生产工艺。
具体实施方式
下面结合实施例，对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是：
一种用于生产热稳定性聚偏氟乙烯的工艺，包括如下步骤：
1）反应釜中投入1.7重量份双氧水、3.6重量份无机碱溶液，混合均匀，再投入8.2重量份氟利昂溶剂、1.9重量份丙酰氯溶液，在-6.5℃搅拌反应42分钟；
2）再通入2.5重量份聚乙烯吡咯烷酮溶液、81重量份偏氟乙烯单体、1.4重量份二溴环戊烷，在13℃搅拌反应，压力下降至0.19MPa以下时终止反应；
3）过滤、洗涤、干燥，即得粉末状聚偏氟乙烯。
 
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (1)

1.用于生产热稳定性聚偏氟乙烯的工艺，其特征在于，包括如下步骤：
1）反应釜中投入1.7重量份双氧水、3.6重量份无机碱溶液，混合均匀，再投入8.2重量份氟利昂溶剂、1.9重量份丙酰氯溶液，在-6.5℃搅拌反应42分钟；
2）再通入2.5重量份聚乙烯吡咯烷酮溶液、81重量份偏氟乙烯单体、1.4重量份二溴环戊烷，在13℃搅拌反应，压力下降至0.19MPa以下时终止反应；
3）过滤、洗涤、干燥，即得粉末状聚偏氟乙烯。
CN201410731743.6A 2014-12-06 2014-12-06 用于生产热稳定性聚偏氟乙烯的工艺 Pending CN104448094A (zh)