CN104448075A - 用于制备热稳定性聚偏氟乙烯的方法 - Google Patents

用于制备热稳定性聚偏氟乙烯的方法 Download PDF

Info

Publication number
CN104448075A
CN104448075A CN201410731738.5A CN201410731738A CN104448075A CN 104448075 A CN104448075 A CN 104448075A CN 201410731738 A CN201410731738 A CN 201410731738A CN 104448075 A CN104448075 A CN 104448075A
Authority
CN
China
Prior art keywords
weight
parts
preparation
weight part
polyvinylidene fluoride
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410731738.5A
Other languages
English (en)
Other versions
CN104448075B (zh
Inventor
徐建林
邹建良
宗建青
仇峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Changshu three Ai Fuzhenfu novel material company limited
Original Assignee
CHANGSHU LIYUAN MEMBRANE TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU LIYUAN MEMBRANE TECHNOLOGY Co Ltd filed Critical CHANGSHU LIYUAN MEMBRANE TECHNOLOGY Co Ltd
Priority to CN201410731738.5A priority Critical patent/CN104448075B/zh
Publication of CN104448075A publication Critical patent/CN104448075A/zh
Application granted granted Critical
Publication of CN104448075B publication Critical patent/CN104448075B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种用于制备热稳定性聚偏氟乙烯的方法，包括如下步骤：1）反应釜中投入0.9重量份双氧水、1.3重量份无机碱溶液，混合均匀，再投入17.4重量份三氟乙烷溶剂、1.7重量份异丁酰氯溶液，在-7.5℃搅拌反应38分钟；2）再通入5.2重量份聚丙烯酸钠溶液、83重量份偏氟乙烯单体、4.3重量份2,2,3-三甲基戊烷，在21℃搅拌反应，压力下降至0.18MPa以下时终止反应；3）过滤、洗涤、干燥，即得粉末状聚偏氟乙烯。本发明制备的偏氟乙烯具有良好的热稳定性和可加工性，可满足注塑、挤出和拉膜等生产工艺。

Description

用于制备热稳定性聚偏氟乙烯的方法
技术领域
本发明涉及用于制备热稳定性聚偏氟乙烯的方法。
背景技术
现有的偏氟乙烯材料，其热稳定性和可加工性有待提高，特别是不能很好的满足注塑、挤出和拉膜等生产工艺。
发明内容
本发明的目的在于提供一种用于制备热稳定性聚偏氟乙烯的方法，其制备的偏氟乙烯具有良好的热稳定性和可加工性，可满足注塑、挤出和拉膜等生产工艺。
为实现上述目的，本发明的技术方案是设计一种用于制备热稳定性聚偏氟乙烯的方法，包括如下步骤：
1）反应釜中投入0.9重量份双氧水、1.3重量份无机碱溶液，混合均匀，再投入17.4重量份三氟乙烷溶剂、1.7重量份异丁酰氯溶液，在-7.5℃搅拌反应38分钟；
2）再通入5.2重量份聚丙烯酸钠溶液、83重量份偏氟乙烯单体、4.3重量份2,2,3-三甲基戊烷，在21℃搅拌反应，压力下降至0.18MPa以下时终止反应；
3）过滤、洗涤、干燥，即得粉末状聚偏氟乙烯。
本发明的优点和有益效果在于：提供一种用于制备热稳定性聚偏氟乙烯的方法，其制备的偏氟乙烯具有良好的热稳定性和可加工性，可满足注塑、挤出和拉膜等生产工艺。
具体实施方式
下面结合实施例，对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是：
一种用于制备热稳定性聚偏氟乙烯的方法，包括如下步骤：
1）反应釜中投入0.9重量份双氧水、1.3重量份无机碱溶液，混合均匀，再投入17.4重量份三氟乙烷溶剂、1.7重量份异丁酰氯溶液，在-7.5℃搅拌反应38分钟；
2）再通入5.2重量份聚丙烯酸钠溶液、83重量份偏氟乙烯单体、4.3重量份2,2,3-三甲基戊烷，在21℃搅拌反应，压力下降至0.18MPa以下时终止反应；
3）过滤、洗涤、干燥，即得粉末状聚偏氟乙烯。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (1)

1.用于制备热稳定性聚偏氟乙烯的方法，其特征在于，包括如下步骤：
1）反应釜中投入0.9重量份双氧水、1.3重量份无机碱溶液，混合均匀，再投入17.4重量份三氟乙烷溶剂、1.7重量份异丁酰氯溶液，在-7.5℃搅拌反应38分钟；
2）再通入5.2重量份聚丙烯酸钠溶液、83重量份偏氟乙烯单体、4.3重量份2,2,3-三甲基戊烷，在21℃搅拌反应，压力下降至0.18MPa以下时终止反应；
3）过滤、洗涤、干燥，即得粉末状聚偏氟乙烯。
CN201410731738.5A 2014-12-06 2014-12-06 用于制备热稳定性聚偏氟乙烯的方法 Active CN104448075B (zh)