CN104402407A - Preparation method of teapot made of purple sand and volcano slime - Google Patents
Preparation method of teapot made of purple sand and volcano slime Download PDFInfo
- Publication number
- CN104402407A CN104402407A CN201410620693.4A CN201410620693A CN104402407A CN 104402407 A CN104402407 A CN 104402407A CN 201410620693 A CN201410620693 A CN 201410620693A CN 104402407 A CN104402407 A CN 104402407A
- Authority
- CN
- China
- Prior art keywords
- boccaro
- teapot
- volcanic
- volcanic slurry
- slurry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses preparation methods of a teapot made of purple sand and volcano slime, and relates to a preparation method of a teapot. The invention aims to solve the problem that the conventional teapots do not have a healthcare function. The preparation method one comprises the following steps: taking purple sand and volcano slime as the raw materials, and then making the raw materials into a teapot through a wholly-artificial method, a semi-artificial method, a slime pouring method, or an artificial blank pulling method. The preparation method two comprises the following steps: preparing a purple sand mud-strip at first, then coating a mixture of purple sand and volcano slime onto the purple sand mud-strip, and finally manufacturing a teapot. The preparation method three comprises the following steps: preparing purple a sand blank from purple sand through a wholly-artificial method, a semi-artificial method, a slime pouring method, or an artificial blank pulling method, then coating a mixture of purple sand and volcano slime on the internal surface of the purple sand blank, and finally manufacturing the teapot. The provided teapot can supplement a plurality of trace elements, which are required by human body, and thus has a healthcare function. The provided teapot can be used as a part of a tea set.
Description
Technical field
The present invention relates to a kind of preparation method of teapot.
Background technology
Dark-red enameled pottery is the one of tea set, for soaking tealeaves; Because dark-red enameled pottery has two pore ventilating structure, therefore millet paste is overnight undergoes no deterioration, long-time use, two pore ventilating structure makes dark-red enameled pottery easily form tea hill (tea stain) when soaking, cause dark-red enameled pottery can retain the tea perfume of tealeaves, and dark-red enameled pottery is handsome in appearance, it is the first-selected tea set that numerous tea lover samples tea.But existing dark-red enameled pottery does not possess the function of health care, it is only a kind of instrument soaking tealeaves.
Summary of the invention
The object of the invention is to solve the problem that existing dark-red enameled pottery does not possess the function of health care, and the preparation method of boccaro-volcanic slurry teapot is provided.
The preparation method of boccaro-volcanic slurry teapot, specifically complete according to the following steps: first volcanic slurry and boccaro are mixed, obtain boccaro-volcanic slurry mixture, with boccaro-volcanic slurry mixture for raw material, adopt full manual method, semi-hand method, grouting kettle method or pull embryo method and boccaro-volcanic slurry mixture is prepared boccaro-volcanic slurry teapot green compact, at temperature is 1100 DEG C ~ 1200 DEG C, boccaro-volcanic slurry teapot green compact are fired, namely obtain boccaro-volcanic slurry teapot; In described boccaro-volcanic slurry mixture, the massfraction of volcanic slurry is 30% ~ 50%.
The preparation method of boccaro-volcanic slurry teapot, specifically completes according to the following steps: one, first adopt full manual method or semi-hand method that boccaro is played slice process, obtain purple clay bar; Two, volcanic slurry and boccaro are mixed, obtain boccaro-volcanic slurry mixture; Three, boccaro-volcanic slurry mixture is coated on purple clay bar, thickness is 1mm ~ 2mm, employing is beaten body cylinder method and is connected into cylinder with boccaro-volcanic slurry mixture in interior, boccaro form outside, then full manual method is continued or semi-hand method is prepared into boccaro-volcanic slurry teapot green compact, at temperature is 1100 DEG C ~ 1200 DEG C, boccaro-volcanic slurry teapot green compact are fired, namely obtain boccaro-volcanic slurry teapot; In boccaro described in step 2-volcanic slurry mixture, the massfraction of volcanic slurry is 45% ~ 55%.
The preparation method of boccaro-volcanic slurry teapot, specifically completes according to the following steps: one, adopt full manual method, semi-hand method, grouting kettle method or pull embryo method and boccaro is prepared boccaro green compact; Two, volcanic slurry and boccaro are mixed, obtain boccaro-volcanic slurry mixture; Three, boccaro-volcanic slurry mixture is dipped, boccaro-volcanic slurry mixture is coated to boccaro green compact inner, apply 2 ~ 3 times, obtain boccaro-volcanic slurry teapot green compact, at temperature is 1100 DEG C ~ 1200 DEG C, boccaro-volcanic slurry teapot green compact are fired, namely obtain boccaro-volcanic slurry teapot; In boccaro described in step 2-volcanic slurry mixture, the massfraction of volcanic slurry is 45% ~ 55%.
Advantage of the present invention: compared with existing dark-red enameled pottery, volcanic slurry is with the addition of in boccaro prepared by the present invention-volcanic slurry teapot, owing to being rich in multiple hydrocarbonate and potassium, sodium, calcium, magnesium four kinds of macroelements and barium in volcanic slurry, tin, fluorine, silicon, strontium, iron, chromium, zinc, cobalt, molybdenum, selenium, nickel more than ten plants trace element, boccaro-volcanic slurry teapot in use, the mineral composition having trace in volcanic slurry is exuded in millet paste, supplement the various trace elements that human body needs, reach the object of health care.
Embodiment
Embodiment one: present embodiment is the preparation method of boccaro-volcanic slurry teapot, specifically complete according to the following steps: first volcanic slurry and boccaro are mixed, obtain boccaro-volcanic slurry mixture, with boccaro-volcanic slurry mixture for raw material, adopt full manual method, semi-hand method, grouting kettle method or pull embryo method and boccaro-volcanic slurry mixture is prepared boccaro-volcanic slurry teapot green compact, at temperature is 1100 DEG C ~ 1200 DEG C, boccaro-volcanic slurry teapot green compact are fired, namely obtain boccaro-volcanic slurry teapot; In described boccaro-volcanic slurry mixture, the massfraction of volcanic slurry is 30% ~ 50%.
Embodiment two: the difference of present embodiment and embodiment one is: described volcanic slurry is Wudalianchi Volcanic sludge.
Embodiment three: the difference of present embodiment and embodiment one is: described boccaro is yixing purple sand.
Embodiment four: the preparation method of boccaro-volcanic slurry teapot, specifically completes according to the following steps: one, first adopt full manual method or semi-hand method that boccaro is played slice process, obtain purple clay bar; Two, volcanic slurry and boccaro are mixed, obtain boccaro-volcanic slurry mixture; Three, boccaro-volcanic slurry mixture is coated on purple clay bar, thickness is 1mm ~ 2mm, employing is beaten body cylinder method and is connected into cylinder with boccaro-volcanic slurry mixture in interior, boccaro form outside, then full manual method is continued or semi-hand method is prepared into boccaro-volcanic slurry teapot green compact, at temperature is 1100 DEG C ~ 1200 DEG C, boccaro-volcanic slurry teapot green compact are fired, namely obtain boccaro-volcanic slurry teapot; In boccaro described in step 2-volcanic slurry mixture, the massfraction of volcanic slurry is 45% ~ 55%.
Embodiment five: the difference of present embodiment and embodiment four is: the boccaro described in step one is yixing purple sand.
Embodiment six: one of present embodiment and embodiment four or five difference is: the boccaro described in step 2 is yixing purple sand.
Embodiment seven: one of present embodiment and embodiment four to six difference is: the volcanic slurry described in step 2 is Wudalianchi Volcanic sludge.
Embodiment eight: the preparation method of boccaro-volcanic slurry teapot, specifically completes according to the following steps: one, adopt full manual method, semi-hand method, grouting kettle method or pull embryo method and boccaro is prepared boccaro green compact; Two, volcanic slurry and boccaro are mixed, obtain boccaro-volcanic slurry mixture; Three, boccaro-volcanic slurry mixture is dipped, boccaro-volcanic slurry mixture is coated to boccaro green compact inner, apply 2 ~ 3 times, obtain boccaro-volcanic slurry teapot green compact, at temperature is 1100 DEG C ~ 1200 DEG C, boccaro-volcanic slurry teapot green compact are fired, namely obtain boccaro-volcanic slurry teapot; In boccaro described in step 2-volcanic slurry mixture, the massfraction of volcanic slurry is 45% ~ 55%.
Embodiment nine: the difference of present embodiment and embodiment eight is: the boccaro described in step one is yixing purple sand.
Embodiment ten: one of present embodiment and embodiment eight or nine difference is: the boccaro described in step 2 is yixing purple sand.
Embodiment 11: one of present embodiment and embodiment eight to ten difference is: the volcanic slurry described in step 2 is Wudalianchi Volcanic sludge.
Adopt following verification experimental verification effect of the present invention
Test one: the preparation method of boccaro-volcanic slurry teapot, specifically complete according to the following steps: first volcanic slurry and boccaro are mixed, obtain boccaro-volcanic slurry mixture, with boccaro-volcanic slurry mixture for raw material, adopt full manual method that boccaro-volcanic slurry mixture is prepared boccaro-volcanic slurry teapot green compact, at temperature is 1100 DEG C ~ 1200 DEG C, boccaro-volcanic slurry teapot green compact are fired, namely obtain boccaro-volcanic slurry teapot; In described boccaro-volcanic slurry mixture, the massfraction of volcanic slurry is 40%.
Boiling water is poured in boccaro-volcanic slurry teapot prepared by test one, place 30min, detect, hardly containing potassium and sodium in initial boiling water, in initial boiling water, calcium concn is 12.5mg/L, place after 30min, in boiling water, potassium concn is 9.2mg/L, na concn is 7.5mg/L, calcium concn is 23.6mg/L.
Test two: the preparation method of boccaro-volcanic slurry teapot, specifically completes according to the following steps: one, first adopt full manual method that boccaro is played slice process, obtain purple clay bar; Two, volcanic slurry and boccaro are mixed, obtain boccaro-volcanic slurry mixture; Three, boccaro-volcanic slurry mixture is coated on purple clay bar, thickness is 1.5mm, employing is beaten body cylinder method and is connected into cylinder with boccaro-volcanic slurry mixture in interior, boccaro form outside, then continue full manual method and be prepared into boccaro-volcanic slurry teapot green compact, at temperature is 1100 DEG C ~ 1200 DEG C, boccaro-volcanic slurry teapot green compact are fired, namely obtain boccaro-volcanic slurry teapot; In boccaro described in step 2-volcanic slurry mixture, the massfraction of volcanic slurry is 50%.
Boiling water is poured in boccaro-volcanic slurry teapot prepared by test two, place 30min, detect, hardly containing potassium and sodium in initial boiling water, in initial boiling water, calcium concn is 12.5mg/L, place after 30min, in boiling water, potassium concn is 10.2mg/L, na concn is 8.1mg/L, calcium concn is 25.6mg/L.
Test three: the preparation method of boccaro-volcanic slurry teapot, specifically completes according to the following steps: one, adopt full manual method that boccaro is prepared boccaro green compact; Two, volcanic slurry and boccaro are mixed, obtain boccaro-volcanic slurry mixture; Three, boccaro-volcanic slurry mixture is dipped, boccaro-volcanic slurry mixture is coated to boccaro green compact inner, applies 3 times, obtain boccaro-volcanic slurry teapot green compact, at temperature is 1100 DEG C ~ 1200 DEG C, boccaro-volcanic slurry teapot green compact are fired, namely obtain boccaro-volcanic slurry teapot; In boccaro described in step 2-volcanic slurry mixture, the massfraction of volcanic slurry is 50%.
Boiling water is poured in boccaro-volcanic slurry teapot prepared by test three, place 30min, detect, hardly containing potassium and sodium in initial boiling water, in initial boiling water, calcium concn is 12.5mg/L, place after 30min, in boiling water, potassium concn is 9.4mg/L, na concn is 7.8mg/L, calcium concn is 22.3mg/L.
Claims (9)
1. the preparation method of boccaro-volcanic slurry teapot, it is characterized in that the preparation method of boccaro-volcanic slurry teapot completes according to the following steps: first volcanic slurry and boccaro are mixed, obtain boccaro-volcanic slurry mixture, with boccaro-volcanic slurry mixture for raw material, adopt full manual method, semi-hand method, grouting kettle method or pull embryo method and boccaro-volcanic slurry mixture is prepared boccaro-volcanic slurry teapot green compact, at temperature is 1100 DEG C ~ 1200 DEG C, boccaro-volcanic slurry teapot green compact are fired, namely obtain boccaro-volcanic slurry teapot; In described boccaro-volcanic slurry mixture, the massfraction of volcanic slurry is 30% ~ 50%.
2. the preparation method of boccaro according to claim 1-volcanic slurry teapot, is characterized in that described volcanic slurry is Wudalianchi Volcanic sludge or Wudalianchi Volcanic ore powder.
3. the preparation method of boccaro according to claim 1-volcanic slurry teapot, is characterized in that described boccaro is yixing purple sand.
4. the preparation method of boccaro-volcanic slurry teapot, is characterized in that the preparation method of boccaro-volcanic slurry teapot completes according to the following steps: one, first adopt full manual method or semi-hand method that boccaro is played slice process, obtain purple clay bar; Two, volcanic slurry and boccaro are mixed, obtain boccaro-volcanic slurry mixture; Three, boccaro-volcanic slurry mixture is coated on purple clay bar, thickness is 1mm ~ 2mm, employing is beaten body cylinder method and is connected into cylinder with boccaro-volcanic slurry mixture in interior, boccaro form outside, then full manual method is continued or semi-hand method is prepared into boccaro-volcanic slurry teapot green compact, at temperature is 1100 DEG C ~ 1200 DEG C, boccaro-volcanic slurry teapot green compact are fired, namely obtain boccaro-volcanic slurry teapot; In boccaro described in step 2-volcanic slurry mixture, the massfraction of volcanic slurry is 45% ~ 55%.
5. the preparation method of boccaro according to claim 4-volcanic slurry teapot, is characterized in that the boccaro described in step one is yixing purple sand.
6. the preparation method of boccaro according to claim 4-volcanic slurry teapot, is characterized in that the boccaro described in step 2 is yixing purple sand; Volcanic slurry described in step 2 is Wudalianchi Volcanic sludge or Wudalianchi Volcanic ore powder.
7. the preparation method of boccaro-volcanic slurry teapot, is characterized in that the preparation method of boccaro-volcanic slurry teapot completes according to the following steps: one, adopt full manual method, semi-hand method, grouting kettle method or pull embryo method and boccaro is prepared boccaro green compact; Two, volcanic slurry and boccaro are mixed, obtain boccaro-volcanic slurry mixture; Three, boccaro-volcanic slurry mixture is dipped, boccaro-volcanic slurry mixture is coated to boccaro green compact inner, apply 2 ~ 3 times, obtain boccaro-volcanic slurry teapot green compact, at temperature is 1100 DEG C ~ 1200 DEG C, boccaro-volcanic slurry teapot green compact are fired, namely obtain boccaro-volcanic slurry teapot; In boccaro described in step 2-volcanic slurry mixture, the massfraction of volcanic slurry is 45% ~ 55%.
8. the preparation method of boccaro according to claim 7-volcanic slurry teapot, is characterized in that the boccaro described in step one is yixing purple sand.
9. the preparation method of boccaro according to claim 7-volcanic slurry teapot, is characterized in that the boccaro described in step 2 is yixing purple sand; Volcanic slurry described in step 2 is Wudalianchi Volcanic sludge or Wudalianchi Volcanic ore powder.