CN107935542A - A kind of boccaro rock mud health water tank and preparation method thereof - Google Patents
A kind of boccaro rock mud health water tank and preparation method thereof Download PDFInfo
- Publication number
- CN107935542A CN107935542A CN201711211881.1A CN201711211881A CN107935542A CN 107935542 A CN107935542 A CN 107935542A CN 201711211881 A CN201711211881 A CN 201711211881A CN 107935542 A CN107935542 A CN 107935542A
- Authority
- CN
- China
- Prior art keywords
- parts
- mud
- boccaro
- water tank
- stone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of boccaro rock mud health water tank, including, each raw material of following parts by weight：85 99.5 parts of mixing raw ore base-material and 0.5 15 parts of health additive；The mixing raw ore base-material includes：Calm down volcanic rock mud and boccaro group mud of calming down, the health additive include blue or green spoil, orpiment stone, tourmaline, opal, serpentine, medical stone, Strange ice stone, hokutolite and Doctor king stone.The present invention also provides a kind of preparation method of boccaro rock mud health water tank.The mixing raw ore of the present invention, which originates from, calms down pure natural mineral aggregate, and volcanic rock mud density is relatively low, contains human body several mineral materials, there is demineralized water, be particularly suitable for making tea, at the same time, also sustainable release multiple beneficial element greatly promotes the effect of health into water during making tea；In addition, volcanic rock mud with honeycomb air hole structure not only wall is with more preferable gas permeability, but also device body particle is plentiful, glossiness is uniform, and feel exquisiteness is gentle.
Description
Technical field
The invention belongs to boccaro production field, and in particular to a kind of to utilize the boccaro rock mud health water storage for mixing raw ore preparation
Tank and preparation method thereof.
Background technology
During dark-red enameled pottery is made, pug is most important factor, is the important mark for determining a dark-red enameled pottery taste
Ruler.The pug of dark-red enameled pottery is made, species there are many kinds, is broadly divided into three major types：Purple mud, red soil, green mud.
At present, the mud material for dark-red enameled pottery made by the market is typically all to be formed using proportionings such as purple mud, section mud, red soil.Have
When, the original color and luster of pigment alteration sand can be also added in the formula of pug, produces the dark-red enameled pottery and tea set of various color and lusters.But
At present, the dark-red enameled pottery generally existing pug made of above-mentioned pug is not coarse, exquisite, is generally made compared with adaptive model, at the same time
The pug also brings the inconvenience made by hand, is mainly shown as that the thickness of slice cannot be guaranteed uniformly, to be easy to cause deformation,
And easily crack when burning till, the decline of yield rate is brought, the waste of pug is larger.In addition the purple made of such a pug
Sand pot can also influence the gas permeability and quality of pot, during with this purple sand tea set to make tea, also without will have in drinking water to human body
Harmful heavy metal, such as cadmium, lead, arsenic remove.Especially for the consummate technique of some requirement workmanships, due to the original of pug in itself
The value of dark-red enameled pottery is thus influenced, while has also seriously affected the popularization of purple sand process culture.
The content of the invention
In consideration of it, it is an object of the present invention to provide it is a kind of using mix raw ore preparation boccaro rock mud health water tank,
It is intended to overcome existing mud material for dark-red enameled pottery is unfavorable to be in the production process molded and be easily deformed by hand, causes the dark-red enameled pottery being fired into
The defects of generally existing pug is coarse, not exquisite and then influence dark-red enameled pottery gas permeability.
Another object of the present invention is to, there is provided a kind of utilize mixes the making that raw ore prepares boccaro rock mud health water tank
Method, it is intended to solve the problems, such as using easy cracking during existing pug fired dark-red enameled pottery.
In order to reach foregoing invention purpose, the technical solution taken is as follows：
A kind of boccaro rock mud health water tank, including, each raw material of following parts by weight：
85-99.5 parts of mixing raw ore base-material and 0.5-15 parts of health additive；
The mixing raw ore base-material includes：Calm down volcanic rock mud and calm down boccaro group mud, wherein, the volcanic rock mud of calming down
With calm down boccaro group mud weight proportion be 65:35；
The health additive includes following ingredients in parts by weight：Blue or green 45~70 parts of spoil, 4-7 parts of orpiment stone；
30~50 parts of tourmaline；10~20 parts of opal；15~20 parts of serpentine；5~10 parts of medical stone；10~15 parts of Strange ice stone；North
2~4 parts of lapidation；2~4 parts of Doctor king stone.
Further, the boccaro of calming down rolls into a ball each component that mud drum includes following parts by weight:Purple mud and white clay, wherein purple mud with
The ratio of white clay is 70-85:5-15.
A kind of utilize provided by the invention mixes the method that raw ore prepares boccaro rock mud health water tank, including following step
Suddenly：
S1：Grinding, by exploitation it is pure natural calm down volcanic rock mud and calm down boccaro group cement mineral material carry out spread harvested grain on a threshing floor weathering, drying
After pulverize, be screened to 70 mesh, it is spare；
S2：System material, calms down volcanic rock mud and boccaro group's mud of calming down according to weight proportion is 65 by ground:35 ratio
Mixing raw ore base-material is mixed to form, it is spare；
S3：Pugging, chooses 0.5-15 parts of mixing of 85-99.5 parts of mixing raw ore base-material and health additive in parts by weight
Mixing pug is formed, and addition mountain spring water is placed in pugging and is mixed in pug mix；
Wherein, the mixing pug and the weight ratio for adding mountain spring water are 5:1, the health additive is included with parts by weight
The following ingredients of meter：Blue or green 45~70 parts of spoil, 4-7 parts of orpiment stone；30~50 parts of tourmaline；10~20 parts of opal；Snake
15~20 parts of stone；5~10 parts of medical stone；10~15 parts of Strange ice stone；2~4 parts of hokutolite；2~4 parts of Doctor king stone；
S4：Mixing pug equal portions that are aging, will having refined, are placed in cylinder interior sealing with oilpaper encapsulation, cylinder are placed in closed
1-5 is stood in environment；
S5：Embryo processed, will be aging after mixing pug, pat be moulded into type into being labelled to mould left-hand seat after the slice of 3-5mm by hand
Form mold base；
S6：Calcine for the first time, the mold base is put into progress first time calcining in gas kiln, calcination time 24-36h, is forged
It is 1230-1370 DEG C to burn temperature, calcining terminate insulation 12-24 it is small when after kiln discharge, automatic cooling；
S7：Embryo is repaiied, after carrying out geometric standard measurement to the above-mentioned water tank burnt till, is repaiied using trimming device
It is whole, reach geometrically regular with physical method；
S8：Second of calcining, the mold base of finishing is put into gas kiln and carries out second of calcining, calcination time 24-36h,
Calcining heat is 1230-1370 DEG C, calcining terminate insulation 12-24 it is small when after kiln discharge, automatic cooling；
S9：Third firing, the water tank after second is calcined are put into smokeless coal pit and carry out third firing, during calcining
Between be 45-60min, calcining heat is 1350-1450 DEG C, is immediately placed on its water tank in closed reduction kiln after calcination
Kiln discharge forms boccaro rock mud health water tank after automatic cooling.
Further, the boccaro of calming down rolls into a ball each component that mud drum includes following parts by weight:Purple mud and white clay, wherein purple mud with
The ratio of white clay is 70-85:5-15.
Beneficial effects of the present invention：The boccaro rock mud health water tank of the present invention is prepared using raw ore is mixed, it is mixed
Raw ore, which originates from, calms down produced pollution-free pure natural mineral aggregate, and the volcanic rock mud density of one of them is relatively low, containing pole beneficial to people
The several mineral materials of body, can play the role of demineralized water, be particularly suitable for steeping different types of tea, and the pH value of adjustable water quality
The entrances such as millet paste, herbal cuisine are natural, return sweet long, larynx rhythm multiplication between 7.1-8.2, making, meanwhile, it can also be held during making tea
Continuous release multiple beneficial element greatly promotes the effect of health into water；In addition, the honeycomb stomata that volcanic rock mud has itself
Structure makes the gas permeability of the boccaro rock mud health water tank of preparation be much better than other tanks, and not only wall has preferably thoroughly
Gas, and device body particle is plentiful, glossiness is uniform, and feel exquisiteness is gentle；In addition, utilize the boccaro rock mud for mixing raw ore preparation
Health water tank can keep nuisance zero to separate out at a high temperature of 1200 degree so that and diet is safer, while under hot environment
It will not make pottery porcelain, can also allow its gas permeability and saturating fragrance more excellent；Finally, the present invention is added using mixing raw ore base-material and health
Add the combination of agent, and optimize composition proportion so that air hole structure maximizes, while also overcomes not glazing i.e. meeting in traditional technique
Slowly the defects of leakage.
Embodiment
In order to make those skilled in the art more fully understand application scheme, below in conjunction with the implementation in the application
Example, is clearly and completely described the technical solution of the application, it is clear that described embodiment is only the application one
The embodiment divided, instead of all the embodiments.Based on the embodiment in the application, those of ordinary skill in the art are not doing
Go out all other embodiments obtained under the premise of creative work, should all belong to the scope of the application protection.
Embodiment 1
A kind of boccaro rock mud health water tank, including, each raw material of following parts by weight：
85 parts of mixing raw ore base-material and 15 parts of health additive；The mixing raw ore base-material includes：Calm down volcanic rock
Mud and calm down boccaro group mud, wherein, it is described calm down volcanic rock mud and calm down boccaro group mud weight proportion be 65:35；It is described flat
Determine each component that boccaro group mud drum includes following parts by weight:Purple mud and white clay, wherein the ratio of purple mud and white clay is 70:5；Institute
Stating health additive includes following ingredients in parts by weight：Blue or green 45 parts of spoil, 4 parts of orpiment stone；30 parts of tourmaline；Opal
10 parts；15 parts of serpentine；5 parts of medical stone；10 parts of Strange ice stone；2 parts of hokutolite；2 parts of Doctor king stone.
A kind of utilize provided by the invention mixes the method that raw ore prepares boccaro rock mud health water tank, including following step
Suddenly：
S1：Grinding, by exploitation it is pure natural calm down volcanic rock mud and calm down boccaro group cement mineral material carry out spread harvested grain on a threshing floor weathering, drying
After pulverize, be screened to 70 mesh, it is spare；
S2：System material, calms down volcanic rock mud and boccaro group's mud of calming down according to weight proportion is 65 by ground:35 ratio
Mixing raw ore base-material is mixed to form, it is spare；
S3：Pugging, 85 parts of the mixing raw ore base-material chosen in parts by weight are mixed to form mixing with 15 parts of health additive
Pug, and add mountain spring water in pug is mixed and be placed in pugging and be mixed；
Wherein, the mixing pug and the weight ratio for adding mountain spring water are 5:1, the health additive is included with parts by weight
The following ingredients of meter：Blue or green 45 parts of spoil, 4 parts of orpiment stone；30 parts of tourmaline；10 parts of opal；15 parts of serpentine；Medical stone 5
Part；10 parts of Strange ice stone；2 parts of hokutolite；2 parts of Doctor king stone；
S4：Mixing pug equal portions that are aging, will having refined, are placed in cylinder interior sealing with oilpaper encapsulation, cylinder are placed in closed
1 year is stood in environment；
S5：Embryo processed, will be aging after mixing pug, pat be moulded into type shape into being labelled to mould left-hand seat after the slice of 3mm by hand
Into mold base；
S6：Calcine for the first time, the mold base is put into progress first time calcining in gas kiln, calcination time 24h, calcining temperature
Spend for 1230 DEG C, calcining terminate insulation 12 it is small when after kiln discharge, automatic cooling；
S7：Embryo is repaiied, after carrying out geometric standard measurement to the above-mentioned water tank burnt till, is repaiied using trimming device
It is whole, reach geometrically regular with physical method；
S8：Second of calcining, the mold base of finishing is put into gas kiln and carries out second of calcining, calcination time 24h, calcining
Temperature is 1230 DEG C, calcining terminate insulation 12 it is small when after kiln discharge, after automatic cooling；
S9：Third firing, the water tank after second is calcined are put into smokeless coal pit and carry out third firing, during calcining
Between be 45min, calcining heat is 1350 DEG C, is immediately placed on its water tank in closed reduction kiln cools down automatically after calcination
Kiln discharge forms boccaro rock mud health water tank afterwards.
Embodiment 2
A kind of boccaro rock mud health water tank, including, each raw material of following parts by weight：99.5 parts of mixing raw ore base-material and
0.5 part of health additive；The mixing raw ore base-material includes：Calm down volcanic rock mud and boccaro group mud of calming down, wherein, it is described flat
Determine volcanic rock mud and calm down boccaro group mud weight proportion be 65:35；The boccaro group mud drum of calming down includes each of following parts by weight
Component:Purple mud and white clay, wherein the ratio of purple mud and white clay is 85:15；The health additive is included in parts by weight
Following ingredients：Blue or green 70 parts of spoil, 7 parts of orpiment stone；50 parts of tourmaline；20 parts of opal；20 parts of serpentine；Medical stone 10
Part；15 parts of Strange ice stone；4 parts of hokutolite；4 parts of Doctor king stone.
A kind of utilize provided by the invention mixes the method that raw ore prepares boccaro rock mud health water tank, including following step
Suddenly：
S1：Grinding, by exploitation it is pure natural calm down volcanic rock mud and calm down boccaro group cement mineral material carry out spread harvested grain on a threshing floor weathering, drying
After pulverize, be screened to 70 mesh, it is spare；
S2：System material, calms down volcanic rock mud and boccaro group's mud of calming down according to weight proportion is 65 by ground:35 ratio
Mixing raw ore base-material is mixed to form, it is spare；
S3：Pugging, 99.5 parts of the mixing raw ore base-material chosen in parts by weight are mixed to form mixed with 0.5 part of health additive
Pug is closed, and addition mountain spring water is placed in pugging and is mixed in pug mix；
Wherein, the mixing pug and the weight ratio for adding mountain spring water are 5:1, the health additive is included with parts by weight
The following ingredients of meter：Blue or green 70 parts of spoil, 7 parts of orpiment stone；50 parts of tourmaline；20 parts of opal；20 parts of serpentine；Medical stone 10
Part；15 parts of Strange ice stone；4 parts of hokutolite；4 parts of Doctor king stone；
S4：Mixing pug equal portions that are aging, will having refined, are placed in cylinder interior sealing with oilpaper encapsulation, cylinder are placed in closed
5 years are stood in environment；
S5：Embryo processed, will be aging after mixing pug, pat be moulded into type shape into being labelled to mould left-hand seat after the slice of 5mm by hand
Into mold base；
S6：Calcine for the first time, the mold base is put into progress first time calcining in gas kiln, calcination time 36h, calcining temperature
Spend for 1370 DEG C, calcining terminate insulation 24 it is small when after kiln discharge, automatic cooling；
S7：Embryo is repaiied, after carrying out geometric standard measurement to the above-mentioned water tank burnt till, is repaiied using trimming device
It is whole, reach geometrically regular with physical method；
S8：Second of calcining, the mold base of finishing is put into gas kiln and carries out second of calcining, calcination time 36h, calcining
Temperature is 1370 DEG C, calcining terminate insulation 24 it is small when after kiln discharge, after automatic cooling；
S9：Third firing, the water tank after second is calcined are put into smokeless coal pit and carry out third firing, during calcining
Between be 60min, calcining heat is 1450 DEG C, is immediately placed on its water tank in closed reduction kiln cools down automatically after calcination
Kiln discharge forms boccaro rock mud health water tank afterwards.
Embodiment 3
A kind of boccaro rock mud health water tank, including, each raw material of following parts by weight：90 parts of mixing raw ore base-material and 10
The health additive of part；The mixing raw ore base-material includes：Calm down volcanic rock mud and calm down boccaro group mud, wherein, it is described to calm down
The weight proportion that volcanic rock mud and boccaro of calming down roll into a ball mud is 65:35；The boccaro of calming down rolls into a ball each group that mud drum includes following parts by weight
Point:Purple mud and white clay, wherein the ratio of purple mud and white clay is 80:10；The health additive is included in parts by weight
Following ingredients：Blue or green 55 parts of spoil, 6 parts of orpiment stone；35 parts of tourmaline；14 parts of opal；18 parts of serpentine；7 parts of medical stone；Very
11 parts of ice stone；3 parts of hokutolite；3.5 parts of Doctor king stone.
A kind of utilize provided by the invention mixes the method that raw ore prepares boccaro rock mud health water tank, including following step
Suddenly：
S1：Grinding, by exploitation it is pure natural calm down volcanic rock mud and calm down boccaro group cement mineral material carry out spread harvested grain on a threshing floor weathering, drying
After pulverize, be screened to 70 mesh, it is spare；
S2：System material, calms down volcanic rock mud and boccaro group's mud of calming down according to weight proportion is 65 by ground:35 ratio
Mixing raw ore base-material is mixed to form, it is spare；
S3：Pugging, 90 parts of the mixing raw ore base-material chosen in parts by weight are mixed to form mixing with 10 parts of health additive
Pug, and add mountain spring water in pug is mixed and be placed in pugging and be mixed；
Wherein, the mixing pug and the weight ratio for adding mountain spring water are 5:1, the health additive is included with parts by weight
The following ingredients of meter：Blue or green 55 parts of spoil, 6 parts of orpiment stone；35 parts of tourmaline；14 parts of opal；18 parts of serpentine；Medical stone 7
Part；11 parts of Strange ice stone；3 parts of hokutolite；3.5 parts of Doctor king stone.
S4：Mixing pug equal portions that are aging, will having refined, are placed in cylinder interior sealing with oilpaper encapsulation, cylinder are placed in closed
3.5 years are stood in environment；
S5：Embryo processed, will be aging after mixing pug, pat be moulded into type shape into being labelled to mould left-hand seat after the slice of 4mm by hand
Into mold base；
S6：Calcine for the first time, the mold base is put into progress first time calcining in gas kiln, calcination time 30h, calcining temperature
Spend for 1300 DEG C, calcining terminate insulation 20 it is small when after kiln discharge, automatic cooling；
S7：Embryo is repaiied, after carrying out geometric standard measurement to the above-mentioned water tank burnt till, is repaiied using trimming device
It is whole, reach geometrically regular with physical method；
S8：Second of calcining, the mold base of finishing is put into gas kiln and carries out second of calcining, calcination time 28h, calcining
Temperature is 1350 DEG C, calcining terminate insulation 22 it is small when after kiln discharge, after automatic cooling；
S9：Third firing, the water tank after second is calcined are put into smokeless coal pit and carry out third firing, during calcining
Between be 50min, calcining heat is 1400 DEG C, is immediately placed on its water tank in closed reduction kiln cools down automatically after calcination
Kiln discharge forms boccaro rock mud health water tank afterwards.
The boccaro rock mud health water tank of the present invention is prepared using raw ore is mixed, its mixing raw ore, which originates to calm down, to be produced
Pollution-free pure natural mineral aggregate, the volcanic rock mud density of one of them is relatively low, and the several mineral materials containing pole beneficial to human body, can rise
To the effect of demineralized water, it is particularly suitable for steeping different types of tea, and the pH value of adjustable water quality makes tea between 7.1-8.2
The entrances such as soup, herbal cuisine are natural, return sweet long, larynx rhythm multiplication, meanwhile, also sustainable release multiple beneficial element during making tea
Into water, the effect of health is greatly promoted；In addition, the honeycomb air hole structure that volcanic rock mud has itself makes the boccaro rock of preparation
The gas permeability of mud health water tank is much better than other tanks, and not only wall has more preferable gas permeability, but also device body particle
It is plentiful, glossiness is uniform, feel exquisiteness is gentle；In addition, can be using the boccaro rock mud health water tank for mixing raw ore preparation
Nuisance zero is kept to separate out at a high temperature of 1200 degree so that diet is safer, while will not make pottery porcelain under hot environment,
It can also allow its gas permeability and saturating fragrance more excellent；Finally, the present invention uses the combination of mixing raw ore base-material and health additive, and excellent
It is melted into distribution ratio so that air hole structure maximizes, while also overcomes the defects of not glazing can be leaked slowly in traditional technique.
The foregoing is only a preferred embodiment of the present invention, is not intended to limit the invention, for the skill of this area
For art personnel, the invention may be variously modified and varied.Within the spirit and principles of the invention, that is made any repaiies
Change, equivalent substitution, improvement etc., should all be included in the protection scope of the present invention.
Claims (4)
1. a kind of boccaro rock mud health water tank, it is characterised in that including each raw material of following parts by weight：
85-99.5 parts of mixing raw ore base-material and 0.5-15 parts of health additive；
The mixing raw ore base-material includes：Calm down volcanic rock mud and calm down boccaro group mud, wherein, it is described calm down volcanic rock mud peace
The weight proportion for determining boccaro group mud is 65:35；
The health additive includes following ingredients in parts by weight：Blue or green 45~70 parts of spoil, 4-7 parts of orpiment stone；Electrically
30~50 parts of stone；10~20 parts of opal；15~20 parts of serpentine；5~10 parts of medical stone；10~15 parts of Strange ice stone；Hokutolite 2
~4 parts；2~4 parts of Doctor king stone.
A kind of 2. boccaro rock mud health water tank according to claim 1, it is characterised in that the boccaro group mud drum of calming down
Include each component of following parts by weight:Purple mud and white clay, wherein the ratio of purple mud and white clay is 70-85:5-15.
3. a kind of utilize mixes the method that raw ore prepares boccaro rock mud health water tank, it is characterised in that comprises the following steps：
S1：Grinding, by exploitation it is pure natural calm down volcanic rock mud and boccaro group cement mineral material of calming down spread harvested grain on a threshing floor weathering, it is dry after grind
Grinds, are screened to 70 mesh, spare；
S2：System material, calms down volcanic rock mud and boccaro group's mud of calming down according to weight proportion is 65 by ground:35 ratio mixing
Mixing raw ore base-material is formed, it is spare；
S3：Pugging, 85-99.5 parts of the mixing raw ore base-material chosen in parts by weight are mixed to form with 0.5-15 parts of health additive
Pug is mixed, and addition mountain spring water is placed in pugging and is mixed in pug mix；
Wherein, the mixing pug and the weight ratio for adding mountain spring water are 5:1, the health additive is included in parts by weight
Following ingredients：Blue or green 45~70 parts of spoil, 4-7 parts of orpiment stone；30~50 parts of tourmaline；10~20 parts of opal；Serpentine 15
~20 parts；5~10 parts of medical stone；10~15 parts of Strange ice stone；2~4 parts of hokutolite；2~4 parts of Doctor king stone；
S4：Mixing pug equal portions that are aging, will having refined, are placed in cylinder interior sealing with oilpaper encapsulation, cylinder are placed in closed environment
Middle standing 1-5；
S5：Embryo processed, will be aging after mixing pug, pat formed into being labelled to mould left-hand seat after the slice of 3-5mm and be moulded into type by hand
Mold base；
S6：Calcine for the first time, the mold base is put into progress first time calcining in gas kiln, calcination time 24-36h, calcining temperature
Spend for 1230-1370 DEG C, calcining terminate insulation 12-24 it is small when after kiln discharge, automatic cooling；
S7：Embryo is repaiied, after carrying out geometric standard measurement to the above-mentioned water tank burnt till, is repaired, used using trimming device
Physical method reaches geometrically regular；
S8：Second of calcining, the mold base of finishing is put into gas kiln and carries out second of calcining, calcination time 24-36h, calcining
Temperature is 1230-1370 DEG C, calcining terminate insulation 12-24 it is small when after kiln discharge, automatic cooling；
S9：Third firing, the water tank after second is calcined are put into smokeless coal pit and carry out third firing, and calcination time is
45-60mi n, calcining heat are 1350-1450 DEG C, are after calcination immediately placed on its water tank in closed reduction kiln certainly
Kiln discharge forms boccaro rock mud health water tank after dynamic cooling.
4. a kind of utilize according to claim 3 mixes the method that raw ore prepares boccaro rock mud health water tank, its feature
It is, the boccaro of calming down rolls into a ball each component that mud drum includes following parts by weight:Purple mud and white clay, wherein comparing purple mud and matching somebody with somebody for white clay
Example is 70-85:5-15.