CN107382269A - A kind of health pottery pot with slow-release function - Google Patents
A kind of health pottery pot with slow-release function Download PDFInfo
- Publication number
- CN107382269A CN107382269A CN201710783139.1A CN201710783139A CN107382269A CN 107382269 A CN107382269 A CN 107382269A CN 201710783139 A CN201710783139 A CN 201710783139A CN 107382269 A CN107382269 A CN 107382269A
- Authority
- CN
- China
- Prior art keywords
- parts
- slow
- volcanic rock
- release function
- medical stone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of health pottery pot with slow-release function, belongs to special pottery field, and it is fired by the clay improved and formed, and described improvement clay consists of composition and formed by certain mass fraction：30 40 parts of kaolinite, 40 50 parts of hydromuscovite, 10 20 parts of montmorillonite, 30 40 parts of quartz, 35 parts of aluminum oxide, 28 parts of 16 part, nanometer volcanic rock of nano medical stone, 35 parts of zirconium oxide, nano medical stone and nanometer volcanic rock are carried in constituent, there is the trace element of a large amount of needed by human body in medical stone and volcanic rock, and it can be released slowly into water, persistently improve water quality.
Description
Technical field
The invention belongs to special pottery field, more particularly to a kind of health pottery pot with slow-release function.
Background technology
With expanding economy, the living standard of people improves constantly, and the requirement to quality of life also improves constantly, to strong
The life of health is also increasingly focused on, but while economic development, the trade effluent, rural sewage, the sanitary sewage that largely discharge
Water resource pollution can be caused Deng pollutant, forms the serious nervous situation of drinking water sources, while also result in the quality of drinking water
Decline, the health of the mankind is adversely affected.Improvement to water quality is advantageous to lift quality of life, passes through the container to being filled with water
It is improved, allows it persistently to improve the research emphasis that water quality turns into current.
Pottery, it is the utensil fired with clay or clay after kneading shapes.Pottery is with a long history, in the Neolithic Age
The generation just pottery of first meeting simple coarse.Pottery is used as a kind of daily necessities in ancient times, is typically now being used as handicraft to collect,
Because composition is various, manufacture craft is simply ripe, is highly suitable as improving the container of water quality.
The content of the invention
The above situation is had based on prior art, the present invention provides a kind of health pottery pot with slow-release function, and it is formed
Nano medical stone and nanometer volcanic rock are carried in composition, the trace element in medical stone and volcanic rock with a large amount of needed by human body,
And it can be released slowly into water, persistently improve water quality.
The present invention achieves the goal by the following technical programs：
A kind of health pottery pot with slow-release function, it is fired by the clay improved and formed, and described improvement clay is by with the following group
Formed into composition by certain mass fraction：Kaolinite 30-40 parts, hydromuscovite 40-50 parts, montmorillonite 10-20 parts, quartz
30-40 parts, aluminum oxide 3-5 parts, nano medical stone 1-6 parts, nanometer volcanic rock 2-8 parts, zirconium oxide 3-5 parts.
Preferably, described improvement clay consists of composition and formed by certain mass fraction：Kaolinite 34-36
Part, hydromuscovite 42-48 parts, montmorillonite 12-14 parts, quartzy 34-36 parts, aluminum oxide 3.5-4.5 parts, nano medical stone 2-4 parts,
Nanometer volcanic rock 4-6 parts, zirconium oxide 3.5-4.5 parts.
Preferably, the improvement clay described in it consists of composition and formed by certain mass fraction：35 parts of kaolinite,
46 parts of hydromuscovite, 13 parts of montmorillonite, 35 parts of quartz, 4 parts of aluminum oxide, 5 parts of 3 part, nanometer volcanic rock of nano medical stone, zirconium oxide
4 parts.
Wherein, the temperature of its firing is 1300-1400 DEG C, hour time 18-20.
The device have the advantages that：Medical stone and volcanic rock, wheat meal are with the addition of in the clay that traditional pottery uses
There is the trace element of a large amount of needed by human body in stone and volcanic rock, Nanometer Maifan Stone and volcanic rock are dispersed in pottery matrix,
Trace element therein is released slowly into water, can be neutralized in water and be sterilized remaining chlorine-containing compound, and is retained or increased
Needed by human body trace element in water, improves water quality；Aluminum oxide is with the addition of in clay, toughness in pottery is improved, improves
The service life of pottery.
Embodiment
With reference to specific embodiment, the invention will be further described.
Embodiment one：
A kind of health pottery pot with slow-release function, it is fired by the clay improved and formed, and described improvement clay is by with the following group
Formed into composition by certain mass fraction：30 parts of kaolinite, 40 parts of hydromuscovite, 10 parts of montmorillonite, quartzy 30 parts, aluminum oxide
3 parts, 2 parts of 1 part, nanometer volcanic rock of nano medical stone, 3 parts of zirconium oxide.
Above-mentioned material is pulverized and mixed in proportion, running water is added and is mixed, then by conventional pottery Making programme system
Into pottery pot, the temperature of its firing is 1300 DEG C, 18 hours time.
It is filled with water using the pottery pot burnt out, the content of chlorine residue is lower relative to the content of control group in water after the time of one end,
And the trace element of many suitable absorption of human body is carried in water.
Embodiment two：
A kind of health pottery pot with slow-release function, it is fired by the clay improved and formed, and described improvement clay is by with the following group
Formed into composition by certain mass fraction：40 parts of kaolinite, 50 parts of hydromuscovite, 0 part of montmorillonite 2, quartzy 40 parts, aluminum oxide
5 parts, 8 parts of 6 part, nanometer volcanic rock of nano medical stone, 5 parts of zirconium oxide.
Above-mentioned material is pulverized and mixed in proportion, running water is added and is mixed, then by conventional pottery Making programme system
Into pottery pot, the temperature of its firing is 1400 DEG C, 20 hours time.
It is filled with water using the pottery pot burnt out, the content of chlorine residue is lower relative to the content of control group in water after the time of one end,
And the trace element of many suitable absorption of human body is carried in water.
Embodiment three：
A kind of health pottery pot with slow-release function, it is fired by the clay improved and formed, and described improvement clay is by with the following group
Formed into composition by certain mass fraction：34 parts of kaolinite, 42 parts of hydromuscovite, 12 parts of montmorillonite, quartzy 34 parts, aluminum oxide
3.5 parts, 4 parts of 2 part, nanometer volcanic rock of nano medical stone, 3.5 parts of zirconium oxide.
Above-mentioned material is pulverized and mixed in proportion, running water is added and is mixed, then by conventional pottery Making programme system
Into pottery pot, the temperature of its firing is 1300 DEG C, 19 hours time.
Example IV：
A kind of health pottery pot with slow-release function, it is fired by the clay improved and formed, and described improvement clay is by with the following group
Formed into composition by certain mass fraction：36 parts of kaolinite, 48 parts of hydromuscovite, 14 parts of montmorillonite, quartzy 36 parts, aluminum oxide
4.5 parts, 6 parts of 4 part, nanometer volcanic rock of nano medical stone, 4.5 parts of zirconium oxide.
Above-mentioned material is pulverized and mixed in proportion, running water is added and is mixed, then by conventional pottery Making programme system
Into pottery pot, the temperature of its firing is 1300 DEG C, 19 hours time.
It is filled with water using the pottery pot burnt out, the content of chlorine residue is lower relative to the content of control group in water after the time of one end,
And the trace element of many suitable absorption of human body is carried in water.
Embodiment five：
A kind of health pottery pot with slow-release function, it is fired by the clay improved and formed, and described improvement clay is by with the following group
Formed into composition by certain mass fraction：35 parts of kaolinite, 46 parts of hydromuscovite, 13 parts of montmorillonite, quartzy 35 parts, aluminum oxide
4 parts, 5 parts of 3 part, nanometer volcanic rock of nano medical stone, 4 parts of zirconium oxide.
Above-mentioned material is pulverized and mixed in proportion, running water is added and is mixed, then by conventional pottery Making programme system
Into pottery pot, the temperature of its firing is 1300 DEG C, 19 hours time.
It is filled with water using the pottery pot burnt out, the content of chlorine residue is lower relative to the content of control group in water after the time of one end,
And the trace element of many suitable absorption of human body is carried in water.
Embodiment described above only expresses the several embodiments of the present invention, and its description is more specific and detailed, but simultaneously
Therefore the limitation to the scope of the claims of the present invention can not be interpreted as.It should be pointed out that for one of ordinary skill in the art
For, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to the guarantor of the present invention
Protect scope.Therefore, the protection domain of patent of the present invention should be determined by the appended claims.
Claims (4)
1. a kind of health pottery pot with slow-release function, its spy is being, it is fired by the clay improved and formed, described improvement
Clay consists of composition and formed by certain mass fraction：Kaolinite 30-40 parts, hydromuscovite 40-50 parts, montmorillonite
10-20 parts, quartzy 30-40 parts, aluminum oxide 3-5 parts, nano medical stone 1-6 parts, nanometer volcanic rock 2-8 parts, zirconium oxide 3-5 parts.
A kind of 2. health pottery pot with slow-release function according to claim 1, it is characterised in that described improvement clay
Composition is consisted of to form by certain mass fraction：Kaolinite 34-36 parts, hydromuscovite 42-48 parts, montmorillonite 12-14
Part, quartzy 34-36 parts, aluminum oxide 3.5-4.5 parts, nano medical stone 2-4 parts, nanometer volcanic rock 4-6 parts, zirconium oxide 3.5-4.5
Part.
A kind of 3. health pottery pot with slow-release function according to claim 2, it is characterised in that the improvement pottery described in it
Soil consists of composition and formed by certain mass fraction：35 parts of kaolinite, 46 parts of hydromuscovite, 13 parts of montmorillonite, quartz
35 parts, 4 parts of aluminum oxide, 5 parts of 3 part, nanometer volcanic rock of nano medical stone, 4 parts of zirconium oxide.
4. according to a kind of any described health pottery pots with slow-release function of claim 1-3, it is characterised in that its firing
Temperature is 1300-1400 DEG C, hour time 18-20.