CN104312418A - Crylic acid polyurethane powder coating for ceramic - Google Patents
Crylic acid polyurethane powder coating for ceramic Download PDFInfo
- Publication number
- CN104312418A CN104312418A CN201410542842.XA CN201410542842A CN104312418A CN 104312418 A CN104312418 A CN 104312418A CN 201410542842 A CN201410542842 A CN 201410542842A CN 104312418 A CN104312418 A CN 104312418A
- Authority
- CN
- China
- Prior art keywords
- parts
- product
- powder coating
- polyurethane powder
- pottery
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a crylic acid polyurethane powder coating for ceramic. The crylic acid polyurethane powder coating comprises the following raw materials: methacrylic acid, isobutyl ester, mercapto propane, cyclohexanone, dimethylbenzene, butyl cellosolve, pigment, toluene, dodecanedioic acid, pentaerythritol, a plasticizer, methylbenzene diisocyanate, methylisobutylketone, rutile titanium dioxide and methyl methacrylate. The melting point of a product is 145-155 DEG C, the gloss degree of the product is 135-155%, the gloss retention rate is 93-97% after the product is artificially aged for 500 hours, the tensile strength of the product is 20-30MPa, the elongation of the product is 250-350%, the shore hardness of the product is 50-60H, the product is normal when being soaked for 30-40 days in a hydrochloric acid solution, the adhesion property of the product is 1-2 grade, the impact resistance of the product is 550-650N/cm, the product is free of bubbling or wrinkle when being soaked in saturated calcium hydroxide for 25-35 days, and the product is resistant to washing and scratching for 1200-1400 times.
Description
Technical field
The application belongs to paint field, particularly relates to a kind of pottery acroleic acid polyurethane powder coating.
Background technology
The various goods that pottery is is the material that main raw material is mixing, shaping through pulverizing and calcining is obtained with natural clay and various natural mineral.People were called pottery the article of high-temperature firing in special kiln be made into potter's clay in the past, and pottery is the general name of pottery and porcelain.The traditional concept of pottery refers to all artificial Industrial products being raw material with Inorganic nonmetal mineral such as clays.It comprises by clay or containing the mixture of clay through mixing, be shaped, calcining and the various goods made.All belonged to its scope to the meticulousst fine pottery and porcelain by the most coarse earthenware.Main raw material for it takes from natural silicate minerals (as clay, quartz etc.), therefore with industry such as glass, cement, enamel, refractory materialss, belongs to the category of " silicate industry ".Ceramic industry is very fast in China's development, and selling market turns to rise gradually.China is a Production of Ceramics big country, also increasing to the demand of pottery.From domestic market situation, in recent years have a gratifying situation, supply falls short of demand for new, special products of famous brands, of extra fine quality ceramic product, high-grade ceramic and medium-to-high grade snitaryware very in great demand, the measured traditional product of matter continues to be in great demand, unsalable just ropy product.
Coating, is be applied to body surface can be formed and have protection, the class I liquid I of solid-state film of decoration or property (as insulation, anticorrosion, mark etc.) or the general name of solid material, comprises oil (property) paint, water-miscible paint, powder coating.Paint is flowable liquid coating, comprises oil (property) paint and water-miscible paint.Paint take organic solvent as medium or high solid, solvent-free oil-base paint.Water-miscible paint is used water dissolving or the coating with water-dispersion.Coating is as one of the main material of house decoration, and the large percentage accounted in decorations, buys the whether qualified environment directly having influence on overall finishing effect and room of coating, sometimes even can produce harm greatly to the health of human body.Founding of New, over 60 years, along with the development of national economy every profession and trade, progressively develops into the requisite important industry of all fields of national economy as its supporting coatings industry from an extremely unobtrusive little industry.Through the struggling hard of several generations, pioneer and keep forging ahead, China has become second-biggest-in-the-world coating material production state and country of consumption, enters into the main flow of world's coating industry development.
Ceramic coating weathering resistance and processing characteristics excellence, bear dirty and resistant to damage.Although ceramic coating resistant to damage in the past, if carry out bending machining to the parts after application, easily cracks, and fluorine resin paints and organic coating, easily by the damage such as sandstone, dust.Therefore, the appearance of ceramic coating, receives the favor of ceramic industry, and the infiltration of forward other industry, promise well.Ceramic coating is that one can make organism and inorganics react, thus has had both the novel ceramic coating of both advantages.The hardness of the ceramic coating of a new generation can reach more than 6H.High temperature resistant 400 degree, not sticky effect, color is multiple.And dimethylbenzene ceramic coating can be made.And universal along with humanity concept, and the formation of novel harmonious society, designs that a kind of glossiness is high, shock-resistance strong, strong adhesion and the pottery acroleic acid polyurethane powder coating of the good excellence of solvent resistance is very important.
Summary of the invention
The technical problem solved:
The application, for above-mentioned technical problem, provides a kind of pottery acroleic acid polyurethane powder coating, solves that existing pottery acroleic acid polyurethane powder coating glossiness is low, not shock-resistant, sticking power is low and the technical problems such as poor solvent resistance.
Technical scheme:
Acroleic acid polyurethane powder coating used by a kind of pottery, and the raw materials by weight portion proportioning of described pottery acroleic acid polyurethane powder coating is as follows: methacrylic acid 20-30 part; Isobutyl ester 8-10 part; Dredge base propane 10-20 part; Pimelinketone 4-10 part; Dimethylbenzene 60-80 part; Butyl glycol ether 4-8 part; Pigment 5-15 part; Toluene 6-8 part; Dodecanedioic acid 80-90 part; Tetramethylolmethane 1-5 part; Softening agent 1-10 part; Tolylene diisocyanate 9-11 part; Mibk 40-50 part; Rutile type Titanium Dioxide 35-45 part; Methyl methacrylate 100 parts.
As a preferred technical solution of the present invention: the raw materials by weight portion proportioning of described pottery acroleic acid polyurethane powder coating is as follows: methacrylic acid 100 parts; Isobutyl ester 4 parts; Dredge 25 parts, base propane; Pimelinketone 3 parts; Dimethylbenzene 8 parts; Butyl glycol ether 4 parts; Pigment 10 parts; Toluene 7 parts; Dodecanedioic acid 85 parts; Tetramethylolmethane 9 parts; 5 parts, softening agent; Tolylene diisocyanate 5 parts; Mibk 2 parts; Rutile type Titanium Dioxide 35 parts; Methyl methacrylate 30 parts.
As a preferred technical solution of the present invention: described pigment adopts ultramarine or deep chrome yellow.
As a preferred technical solution of the present invention: described softening agent adopts DOP or DBP.
Beneficial effect: a kind of pottery acroleic acid polyurethane powder coating of the present invention adopts above technical scheme compared with prior art, there is following technique effect: 1, product fusing point 145-155 DEG C, glossiness 135%-155%, after artificial accelerated aging 500h, protects light rate 93-97%; 2, tensile strength 20-30MPa, elongation 250-350%, shore hardness 50-60H, soak 30-40d without exception in 5% hydrochloric acid soln; 3, sticking power 1-2 level, shock strength 550-650N/cm, soaks in saturated calcium hydroxide that 25-35d is non-foaming, elephant skin; 4, scrub resistance 1200-1400 time, the widespread production not division of history into periods can replace current material.
Embodiment
Embodiment 1:
Acroleic acid polyurethane powder coating used by a kind of pottery, and its raw materials by weight portion proportioning is as follows: methacrylic acid 20 parts; Isobutyl ester 8 parts; Dredge 10 parts, base propane; Pimelinketone 4 parts; Dimethylbenzene 60 parts; Butyl glycol ether 4 parts; Deep chrome yellow 5 parts; Toluene 6 parts; Dodecanedioic acid 80 parts; Tetramethylolmethane 1 part; DBP1 part; Tolylene diisocyanate 9 parts; Mibk 40 parts; Rutile type Titanium Dioxide 35 parts; Methyl methacrylate 100 parts.
Added by above-mentioned raw materials in reactor, be warmed up to 130 DEG C, insulation reaction 2h mixes, and pulverizes after cooling with pulverizer, with the sieved sieve of 130mg, and obtained coating.
Product fusing point 145 DEG C, glossiness 135%, after artificial accelerated aging 500h, protects light rate 93%; Tensile strength 20MPa, elongation 250%, shore hardness 50H, soaks 30d without exception in 5% hydrochloric acid soln; Sticking power 2 grades, shock strength 550N/cm, soaks in saturated calcium hydroxide that 25d is non-foaming, elephant skin, scrub resistance 1200 times.
Embodiment 2:
Acroleic acid polyurethane powder coating used by a kind of pottery, and its raw materials by weight portion proportioning is as follows: methacrylic acid 30 parts; Isobutyl ester 10 parts; Dredge 20 parts, base propane; Pimelinketone 10 parts; Dimethylbenzene 80 parts; Butyl glycol ether 8 parts; Deep chrome yellow 15 parts; Toluene 8 parts; Dodecanedioic acid 90 parts; Tetramethylolmethane 5 parts; DOP10 part; Tolylene diisocyanate 11 parts; Mibk 50 parts; Rutile type Titanium Dioxide 45 parts; Methyl methacrylate 100 parts.
Added by above-mentioned raw materials in reactor, be warmed up to 150 DEG C, insulation reaction 4h mixes, and pulverizes after cooling with pulverizer, with the sieved sieve of 150mg, and obtained coating.
Product fusing point 150 DEG C, glossiness 145%, after artificial accelerated aging 500h, protects light rate 95%; Tensile strength 25MPa, elongation 300%, shore hardness 55H, soaks 35d without exception in 5% hydrochloric acid soln; Adhesion 1 grade, shock strength 600N/cm, soaks in saturated calcium hydroxide that 30d is non-foaming, elephant skin, scrub resistance 1300 times.
Embodiment 3:
Acroleic acid polyurethane powder coating used by a kind of pottery, and its raw materials by weight portion proportioning is as follows: methacrylic acid 100 parts; Isobutyl ester 4 parts; Dredge 25 parts, base propane; Pimelinketone 3 parts; Dimethylbenzene 8 parts; Butyl glycol ether 4 parts; 10 parts, ultramarine; Toluene 7 parts; Dodecanedioic acid 85 parts; Tetramethylolmethane 9 parts; DOP5 part; Tolylene diisocyanate 5 parts; Mibk 2 parts; Rutile type Titanium Dioxide 35 parts; Methyl methacrylate 30 parts.
Added by above-mentioned raw materials in reactor, be warmed up to 140 DEG C, insulation reaction 3h mixes, and pulverizes after cooling with pulverizer, with the sieved sieve of 140mg, and obtained coating.
Product fusing point 155 DEG C, glossiness 155%, after artificial accelerated aging 500h, protects light rate 97%; Tensile strength 30MPa, elongation 350%, shore hardness 60H, soaks 40d without exception in 5% hydrochloric acid soln; Adhesion 1 grade, shock strength 650N/cm, soaks in saturated calcium hydroxide that 35d is non-foaming, elephant skin, scrub resistance 1400 times.
Composition all components in above embodiment all can business be bought.
Above-described embodiment is just for setting forth content of the present invention, instead of restriction, and any change therefore in the implication suitable with claims of the present invention and scope, all should think to be included in the scope of claims.
Claims (4)
1. an acroleic acid polyurethane powder coating used by pottery, it is characterized in that the raw materials by weight portion proportioning of described pottery acroleic acid polyurethane powder coating is as follows: methacrylic acid 20-30 part; Isobutyl ester 8-10 part; Dredge base propane 10-20 part; Pimelinketone 4-10 part; Dimethylbenzene 60-80 part; Butyl glycol ether 4-8 part; Pigment 5-15 part; Toluene 6-8 part; Dodecanedioic acid 80-90 part; Tetramethylolmethane 1-5 part; Softening agent 1-10 part; Tolylene diisocyanate 9-11 part; Mibk 40-50 part; Rutile type Titanium Dioxide 35-45 part; Methyl methacrylate 100 parts.
2. a kind of pottery acroleic acid polyurethane powder coating according to claim 1, is characterized in that the raw materials by weight portion proportioning of described pottery acroleic acid polyurethane powder coating is as follows: methacrylic acid 100 parts; Isobutyl ester 4 parts; Dredge 25 parts, base propane; Pimelinketone 3 parts; Dimethylbenzene 8 parts; Butyl glycol ether 4 parts; Pigment 10 parts; Toluene 7 parts; Dodecanedioic acid 85 parts; Tetramethylolmethane 9 parts; 5 parts, softening agent; Tolylene diisocyanate 5 parts; Mibk 2 parts; Rutile type Titanium Dioxide 35 parts; Methyl methacrylate 30 parts.
3. a kind of pottery acroleic acid polyurethane powder coating according to claim 1, is characterized in that: described pigment adopts ultramarine or deep chrome yellow.
4. a kind of pottery acroleic acid polyurethane powder coating according to claim 1, is characterized in that: described softening agent adopts DOP or DBP.