CN104250500A - Environment-friendly anti-seepage waterproof paint - Google Patents
Environment-friendly anti-seepage waterproof paint Download PDFInfo
- Publication number
- CN104250500A CN104250500A CN201410445734.0A CN201410445734A CN104250500A CN 104250500 A CN104250500 A CN 104250500A CN 201410445734 A CN201410445734 A CN 201410445734A CN 104250500 A CN104250500 A CN 104250500A
- Authority
- CN
- China
- Prior art keywords
- parts
- stirring
- minute
- dispersed
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Disclosed environment-friendly anti-seepage waterproof paint is composed of the following raw materials in parts by weight: 70-80 parts of silicone-acrylic emulsion, 1-2 parts of tea seed powder, 1-2 parts of ammonium tungstate, 0.6-1 part of pyromellitic dianhydride, 0.2-0.3 parts of polyvinyl acid, 2.4-3 parts of oxidized polyethylene wax, 1-2 parts of magnesium fluoride, 1-2 parts of 4-hydroxy-4-methyl-2-pentanone, 2-3 parts of hexabromocyclododecane, 2-4 parts of octyl epoxy stearate, 5-8 parts of montmorillonite powder, 2-3 parts of polyoxyethylene oleate, 6-10 parts of calcined kaolin, 16-20 parts of deionized water, and 6-8 parts of a bonding auxiliary agent. The waterproof paint is applicable to indoor water prevention, is convenient to construct aiming at complex-shaped fields, is good in seepage prevention, does not need repairing for a long time, and is good in water resistance, strong in seepage resistance, not easy to fall off and strong in weatherability.
Description
Technical field
The present invention relates generally to a kind of coating, particularly relates to a kind of environmental protection anti-leakage waterproof paint.
Background technology
So-called coating refers to that coating body surface can form film under certain conditions and play protection, the class I liquid I of decoration or other specific functions (insulation, antirust, mildew-resistant, heat-resisting etc.) or solid material.Be main raw material mainly with vegetables oil greatly because of early stage coating, therefore also known as painting.Present synthetic resins is most of or all instead of vegetables oil, therefore is called coating.Application of paints is all respects in life, and coating not only requires that cohesiveness is strong, good weatherability, and resistance is high, also wants nontoxic pollution-free, therefore improves constantly the overall quality of coating for improving people's living standard, and accelerating urban development has very great meaning.
Summary of the invention
The object of the invention is just to provide a kind of environmental protection anti-leakage waterproof paint.
The present invention is achieved by the following technical solutions:
A kind of environmental protection anti-leakage waterproof paint, it is made up of the raw material of following weight parts:
Organosilicon crylic acid latex 70-80, tea seed powder 1-2, ammonium tungstate 1-2, pyromellitic acid dianhydride 0.6-1, acid polyethylene 0.2-0.3, oxidized polyethlene wax 2.4-3, magnesium fluoride 1-2, diacetone alcohol 1-2, hexabromocyclododecane 2-3, octyl epoxy stearate 2-4, montmorillonite powder 5-8, polyoxyethylene oleic acid ester 2-3, calcined kaolin 6-10, deionized water 16-20, adhesive aid 6-8;
Described adhesive aid is made up of the raw material of following weight parts:
Eva emulsion 40-46, lauryl glucosyl 1-2, methyl methacrylate 2-4, ammonium persulphate 1-2, allyl polyglycol 3-4, potassium zirconium carbonate 1-2, nano-carbon powder 2-3, tetrafluoroethylene wax 2-3, nano titanium oxide 0.1-1, deionized water 6-8;
By potassium zirconium carbonate, nano-carbon powder mixing, add tetrafluoroethylene wax after stirring, at 60-70 DEG C, be uniformly mixed 10-16 minute, add allyl polyglycol, be stirred to normal temperature, join in Eva emulsion, 200-300 rev/min of dispersed with stirring 10-12 minute;
Lauryl glucosyl is joined in deionized water, after stirring, add ammonium persulphate, methyl methacrylate, 60-80 rev/min of dispersed with stirring 3-5 minute;
Mixed with each raw material of residue by each raw material after above-mentioned process, 800-1000 rev/min of dispersed with stirring 2-4 minute, obtains described adhesive aid.
A preparation method for environmental protection anti-leakage waterproof paint, is characterized in that comprising the following steps:
By montmorillonite powder, calcined kaolin mixing, add polyoxyethylene oleic acid ester, acid polyethylene after ball milling is even, at 50-70 DEG C, be uniformly mixed 6-9 minute, join in deionized water, 100-200 rev/min of dispersed with stirring 6-10 minute;
By tea seed powder, oxidized polyethlene wax, magnesium fluoride mixing, join after stirring in organosilicon crylic acid latex, 100-160 rev/min of dispersed with stirring 10-15 minute;
Mixed with each raw material of residue by each raw material after above-mentioned process, 600-800 rev/min of dispersed with stirring 20-30 minute, obtains described environmental protection anti-leakage waterproof paint.
Advantage of the present invention is:
Waterproof paint of the present invention may be used for indoor waterproof, and for complex-shaped place, easy construction, manifests protection well to seepage, need not reprocess for a long time, water-tolerant, and leakage resistance is strong, and difficult drop-off, weathering resistance is strong.
Embodiment
Embodiment 1
A kind of environmental protection anti-leakage waterproof paint, it is made up of the raw material of following weight parts (kilogram):
Organosilicon crylic acid latex 70, tea seed powder 2, ammonium tungstate 1, pyromellitic acid dianhydride 0.6, acid polyethylene 0.3, oxidized polyethlene wax 2.4, magnesium fluoride 2, diacetone alcohol 1, hexabromocyclododecane 3, octyl epoxy stearate 2, montmorillonite powder 8, polyoxyethylene oleic acid ester 2-3, calcined kaolin 10, deionized water 20, adhesive aid 6;
Described adhesive aid is made up of the raw material of following weight parts:
Eva emulsion 46, lauryl glucosyl 2, methyl methacrylate 4, ammonium persulphate 2, allyl polyglycol 3, potassium zirconium carbonate 1, nano-carbon powder 3, tetrafluoroethylene wax 2, nano titanium oxide 0.1, deionized water 6;
By potassium zirconium carbonate, nano-carbon powder mixing, add tetrafluoroethylene wax after stirring, at 60 DEG C, be uniformly mixed 16 minutes, add allyl polyglycol, be stirred to normal temperature, join in Eva emulsion, 300 revs/min of dispersed with stirring 12 minutes;
Lauryl glucosyl is joined in deionized water, after stirring, add ammonium persulphate, methyl methacrylate, 80 revs/min of dispersed with stirring 5 minutes;
Mixed with each raw material of residue by each raw material after above-mentioned process, 1000 revs/min of dispersed with stirring 4 minutes, obtain described adhesive aid.
A preparation method for environmental protection anti-leakage waterproof paint, is characterized in that comprising the following steps:
By montmorillonite powder, calcined kaolin mixing, ball milling evenly after add polyoxyethylene oleic acid ester, acid polyethylene, at 70 DEG C, be uniformly mixed 9 minutes, join in deionized water, 100 revs/min of dispersed with stirring 10 minutes;
By tea seed powder, oxidized polyethlene wax, magnesium fluoride mixing, join after stirring in organosilicon crylic acid latex, 160 revs/min of dispersed with stirring 15 minutes;
Mixed with each raw material of residue by each raw material after above-mentioned process, 800 revs/min of dispersed with stirring 30 minutes, obtain described environmental protection anti-leakage waterproof paint.
Performance test:
Unit elongation: >=300%;
Watertightness: 0.3MPa (one hour waterproof).
Claims (2)
1. an environmental protection anti-leakage waterproof paint, is characterized in that what it was made up of the raw material of following weight parts:
Organosilicon crylic acid latex 70-80, tea seed powder 1-2, ammonium tungstate 1-2, pyromellitic acid dianhydride 0.6-1, acid polyethylene 0.2-0.3, oxidized polyethlene wax 2.4-3, magnesium fluoride 1-2, diacetone alcohol 1-2, hexabromocyclododecane 2-3, octyl epoxy stearate 2-4, montmorillonite powder 5-8, polyoxyethylene oleic acid ester 2-3, calcined kaolin 6-10, deionized water 16-20, adhesive aid 6-8;
Described adhesive aid is made up of the raw material of following weight parts:
Eva emulsion 40-46, lauryl glucosyl 1-2, methyl methacrylate 2-4, ammonium persulphate 1-2, allyl polyglycol 3-4, potassium zirconium carbonate 1-2, nano-carbon powder 2-3, tetrafluoroethylene wax 2-3, nano titanium oxide 0.1-1, deionized water 6-8;
By potassium zirconium carbonate, nano-carbon powder mixing, add tetrafluoroethylene wax after stirring, at 60-70 DEG C, be uniformly mixed 10-16 minute, add allyl polyglycol, be stirred to normal temperature, join in Eva emulsion, 200-300 rev/min of dispersed with stirring 10-12 minute;
Lauryl glucosyl is joined in deionized water, after stirring, add ammonium persulphate, methyl methacrylate, 60-80 rev/min of dispersed with stirring 3-5 minute;
Mixed with each raw material of residue by each raw material after above-mentioned process, 800-1000 rev/min of dispersed with stirring 2-4 minute, obtains described adhesive aid.
2. a preparation method for environmental protection anti-leakage waterproof paint as claimed in claim 1, is characterized in that comprising the following steps:
By montmorillonite powder, calcined kaolin mixing, add polyoxyethylene oleic acid ester, acid polyethylene after ball milling is even, at 50-70 DEG C, be uniformly mixed 6-9 minute, join in deionized water, 100-200 rev/min of dispersed with stirring 6-10 minute;
By tea seed powder, oxidized polyethlene wax, magnesium fluoride mixing, join after stirring in organosilicon crylic acid latex, 100-160 rev/min of dispersed with stirring 10-15 minute;
Mixed with each raw material of residue by each raw material after above-mentioned process, 600-800 rev/min of dispersed with stirring 20-30 minute, obtains described environmental protection anti-leakage waterproof paint.