CN104277620A - Environment-friendly wall coating - Google Patents
Environment-friendly wall coating Download PDFInfo
- Publication number
- CN104277620A CN104277620A CN201410449251.8A CN201410449251A CN104277620A CN 104277620 A CN104277620 A CN 104277620A CN 201410449251 A CN201410449251 A CN 201410449251A CN 104277620 A CN104277620 A CN 104277620A
- Authority
- CN
- China
- Prior art keywords
- parts
- minute
- add
- deionized water
- obtains
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environment-friendly wall coating which is prepared from the following raw materials in parts by weight: 2-3 parts of polypropylene oxide glycol, 1-2 parts of propylgallate, 0.8-1 part of seed oil of camellia oleifera abel, 0.7-1 part of n-salicylanilide, 1-2 parts of calcium lactate, 2-3 parts of palm wax, 3-4 parts of polypropylene glycol adipate, 2-3 parts of polytetrafluoroethylene, 0.7-2 parts of polybenzimidazole, 5-7 parts of attapulgite, 10-13 parts of feldspar powder, 100-140 parts of butyl acrylate, 160-200 parts of vinyl acetate, 4-6 parts of polyvinyl alcohol, 0.5-2 parts of potassium persulfate, 500-700 parts of deionized water, 2-4 parts of sodium dodecyl sulfate and 4-6 parts of a bonding auxiliary. The coating disclosed by the invention is good in environment-friendliness and free of volatile toxic substances, can be widely applied to brushing indoor and outdoor exterior walls, further has killing and inhibiting effects on some microorganisms and is strong in weather resistance and good in bonding strength and resistance.
Description
?
Technical field
The present invention relates generally to paint field, particularly relates to a kind of environmental protection wall surface coating.
Background technology
Be applied to body surface can be formed there is protection, the class I liquid I of solid-state film of decoration or property (as insulation, anticorrosion, mark etc.) or the general name of solid material, comprise oil (property) paint, water-miscible paint, powder coating.Paint is flowable liquid coating, comprises oil (property) paint and water-miscible paint.Paint take organic solvent as medium or high solid, solvent-free oil-base paint.Water-miscible paint is used water dissolving or the coating with water-dispersion.Coating is as one of the main material of house decoration, and the large percentage accounted in decorations, buys the whether qualified environment directly having influence on overall finishing effect and room of coating, sometimes even can produce harm greatly to the health of human body.At present along with the generation of various coating, the quality requirements of coating is also improved constantly, and improve constantly coating quality and can play very large help for building, life.
Summary of the invention
The object of the invention is just to provide a kind of environmental protection wall surface coating.
The present invention is achieved by the following technical solutions:
A kind of environmental protection wall surface coating, is characterized in that what it was made up of the raw material of following weight parts:
Polyoxypropyleneglycol 2-3, Tenox PG 1-2, Chinese vegetable tallow 0.8-1, n-Salicylanlide 0.7-1, calcium lactate 1-2, palm wax 2-3, hexanodioic acid propanediol polyester 3-4, tetrafluoroethylene 2-3, polybenzimidazole 0.7-2, attapulgite 5-7, feldspar in powder 10-13, butyl acrylate 100-140, vinyl acetate 160-200, polyvinyl alcohol 4-6, Potassium Persulphate 0.5-2, deionized water 500-700, sodium laurylsulfonate 2-4, adhesive aid 4-6;
Described adhesive aid is made up of each raw material of following weight parts:
Organosilicon crylic acid latex 30-35, methyl methacrylate 2-4, exsiccated ammonium alum 1-2, emulsifier op-10 0.5-1, ammonium persulphate 0.7-1, Triethylene glycol dimethacrylate 2-3, triolein 1-2, titania powder 2-4, deionized water 10-14;
By titania powder, Triethylene glycol dimethacrylate, triolein mixing, 3-4 minute is uniformly mixed at 70-75 DEG C, add 40-50%, the ammonium persulphate of above-mentioned deionized water weight, 100-150 rev/min of dispersed with stirring 10-13 minute, obtains dispersion liquid;
Emulsifier op-10 and exsiccated ammonium alum are mixed to join in remaining deionized water, at 60-70 DEG C, are uniformly mixed 3-5 minute, add methyl methacrylate, dispersion liquid, be stirred to normal temperature, add each raw material of residue, obtain described adhesive aid.
A preparation method for environmental protection wall surface coating, comprises the following steps:
(1) mixed by the 10-15% of Potassium Persulphate with above-mentioned deionized water weight, stirring and dissolving, obtains initiator solution;
(2) by sodium laurylsulfonate, polyoxypropyleneglycol, Tenox PG, polyvinyl alcohol mixing, add the 70-80% of residue deionized water weight, insulated and stirred 30-40 minute at 80-90 DEG C, is cooled to normal temperature, obtains pre-emulsion;
(3) the 40-50% mixing of the 30-40% of aforesaid propylene acid butyl ester weight, vinyl acetate weight is got, add above-mentioned pre-emulsion, 30-35 minute is uniformly mixed at 60-65 DEG C, raised temperature is 70-75 DEG C, add above-mentioned initiator solution, treat that emulsion is blue phase, insulation 60-70 minute, obtains seed emulsion;
(4) by remaining butyl acrylate, vinyl acetate mixing, add palm wax, hexanodioic acid propanediol polyester, insulated and stirred 20-30 minute at 70-80 DEG C, obtains mix monomer;
(5) in above-mentioned seed emulsion, add dropping mix monomer, time for adding is 90-120 minute, after dropwising, at 80-90 DEG C, is incubated 50-60 minute, cooling, filters discharging with 200-250 eye mesh screen;
(6) material above-mentioned steps (5) obtained mixes with each raw material of residue, and 800-1200 rev/min of dispersed with stirring 20-30 minute, obtains described environmental protection wall surface coating.
Advantage of the present invention is:
The coating feature of environmental protection of the present invention is good, not containing volatile toxic substance, can be widely used in indoor and outdoor body of wall brushing, and for the effect that some microorganisms also have killing and suppress, durability of coating is strong, cohesive strength, better resistance.The titania powder added in adhesive aid of the present invention can improve resistivity against fire and surface resistive, methyl methacrylate, exsiccated ammonium alum, emulsifier op-10, triolein mix with organosilicon crylic acid latex and effectively can improve cohesive strength, ammonium persulphate can promote the consistency between each raw material, improves the surface stability of finished product.
Embodiment
Embodiment 1
A kind of environmental protection wall surface coating, is characterized in that what it was made up of the raw material of following weight parts:
Polyoxypropyleneglycol 3, Tenox PG 2, Chinese vegetable tallow 0.8, n-Salicylanlide 0.7-, calcium lactate 2, palm wax 2, hexanodioic acid propanediol polyester 4, tetrafluoroethylene 3, polybenzimidazole 0.7, attapulgite 7, feldspar in powder 13, butyl acrylate 140, vinyl acetate 200, polyvinyl alcohol 4, Potassium Persulphate 0.5, deionized water 500, sodium laurylsulfonate 2-4, adhesive aid 4;
Described adhesive aid is made up of each raw material of following weight parts:
Organosilicon crylic acid latex 35, methyl methacrylate 2, exsiccated ammonium alum 2, emulsifier op-10 0.5, ammonium persulphate 0.7, Triethylene glycol dimethacrylate 2, triolein 2, titania powder 2, deionized water 14;
By titania powder, Triethylene glycol dimethacrylate, triolein mixing, at 75 DEG C, be uniformly mixed 4 minutes, add 40-50%, the ammonium persulphate of above-mentioned deionized water weight, 150 revs/min of dispersed with stirring 13 minutes, obtain dispersion liquid;
Emulsifier op-10 and exsiccated ammonium alum are mixed to join in remaining deionized water, at 70 DEG C, are uniformly mixed 3 minutes, add methyl methacrylate, dispersion liquid, be stirred to normal temperature, add each raw material of residue, obtain described adhesive aid.
A preparation method for environmental protection wall surface coating, is characterized in that comprising the following steps:
(1) mixed with 15% of above-mentioned deionized water weight by Potassium Persulphate, stirring and dissolving, obtains initiator solution;
(2) by sodium laurylsulfonate, polyoxypropyleneglycol, Tenox PG, polyvinyl alcohol mixing, add 80% of residue deionized water weight, at 90 DEG C, insulated and stirred 40 minutes, is cooled to normal temperature, obtains pre-emulsion;
(3) get 40% of aforesaid propylene acid butyl ester weight, 50% mixing of vinyl acetate weight, add above-mentioned pre-emulsion, at 65 DEG C, be uniformly mixed 35 minutes, raised temperature is 75 DEG C, adds above-mentioned initiator solution, treats that emulsion is blue phase, be incubated 70 minutes, obtain seed emulsion;
(4) by remaining butyl acrylate, vinyl acetate mixing, add palm wax, hexanodioic acid propanediol polyester, at 80 DEG C, insulated and stirred 30 minutes, obtains mix monomer;
(5) in above-mentioned seed emulsion, add dropping mix monomer, time for adding is 120 minutes, after dropwising, at 90 DEG C, be incubated 60 minutes, and cooling filters discharging with 250 eye mesh screens;
(6) material above-mentioned steps (5) obtained mixes with each raw material of residue, and 1200 revs/min of dispersed with stirring 30 minutes, obtain described environmental protection wall surface coating.
Performance test:
Unit elongation: >=300%;
Watertightness: 0.3MPa (one hour waterproof).
Claims (2)
1. an environmental protection wall surface coating, is characterized in that what it was made up of the raw material of following weight parts:
Polyoxypropyleneglycol 2-3, Tenox PG 1-2, Chinese vegetable tallow 0.8-1, n-Salicylanlide 0.7-1, calcium lactate 1-2, palm wax 2-3, hexanodioic acid propanediol polyester 3-4, tetrafluoroethylene 2-3, polybenzimidazole 0.7-2, attapulgite 5-7, feldspar in powder 10-13, butyl acrylate 100-140, vinyl acetate 160-200, polyvinyl alcohol 4-6, Potassium Persulphate 0.5-2, deionized water 500-700, sodium laurylsulfonate 2-4, adhesive aid 4-6;
Described adhesive aid is made up of each raw material of following weight parts:
Organosilicon crylic acid latex 30-35, methyl methacrylate 2-4, exsiccated ammonium alum 1-2, emulsifier op-10 0.5-1, ammonium persulphate 0.7-1, Triethylene glycol dimethacrylate 2-3, triolein 1-2, titania powder 2-4, deionized water 10-14;
By titania powder, Triethylene glycol dimethacrylate, triolein mixing, 3-4 minute is uniformly mixed at 70-75 DEG C, add 40-50%, the ammonium persulphate of above-mentioned deionized water weight, 100-150 rev/min of dispersed with stirring 10-13 minute, obtains dispersion liquid;
Emulsifier op-10 and exsiccated ammonium alum are mixed to join in remaining deionized water, at 60-70 DEG C, are uniformly mixed 3-5 minute, add methyl methacrylate, dispersion liquid, be stirred to normal temperature, add each raw material of residue, obtain described adhesive aid.
2. a preparation method for environmental protection wall surface coating as claimed in claim 1, is characterized in that comprising the following steps:
(1) mixed by the 10-15% of Potassium Persulphate with above-mentioned deionized water weight, stirring and dissolving, obtains initiator solution;
(2) by sodium laurylsulfonate, polyoxypropyleneglycol, Tenox PG, polyvinyl alcohol mixing, add the 70-80% of residue deionized water weight, insulated and stirred 30-40 minute at 80-90 DEG C, is cooled to normal temperature, obtains pre-emulsion;
(3) the 40-50% mixing of the 30-40% of aforesaid propylene acid butyl ester weight, vinyl acetate weight is got, add above-mentioned pre-emulsion, 30-35 minute is uniformly mixed at 60-65 DEG C, raised temperature is 70-75 DEG C, add above-mentioned initiator solution, treat that emulsion is blue phase, insulation 60-70 minute, obtains seed emulsion;
(4) by remaining butyl acrylate, vinyl acetate mixing, add palm wax, hexanodioic acid propanediol polyester, insulated and stirred 20-30 minute at 70-80 DEG C, obtains mix monomer;
(5) in above-mentioned seed emulsion, add dropping mix monomer, time for adding is 90-120 minute, after dropwising, at 80-90 DEG C, is incubated 50-60 minute, cooling, filters discharging with 200-250 eye mesh screen;
(6) material above-mentioned steps (5) obtained mixes with each raw material of residue, and 800-1200 rev/min of dispersed with stirring 20-30 minute, obtains described environmental protection wall surface coating.