CN104250488A - Stable weatherable waterproof paint - Google Patents
Stable weatherable waterproof paint Download PDFInfo
- Publication number
- CN104250488A CN104250488A CN201410445759.0A CN201410445759A CN104250488A CN 104250488 A CN104250488 A CN 104250488A CN 201410445759 A CN201410445759 A CN 201410445759A CN 104250488 A CN104250488 A CN 104250488A
- Authority
- CN
- China
- Prior art keywords
- parts
- stirring
- minute
- dispersed
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Disclosed stable weatherable waterproof paint is composed of the following raw materials in parts by weight: 71-80 parts of aqueous acrylic emulsion, 2-3 parts of calcium aluminate, 2-4 parts of triallyl isocyanurate, 1-2 parts of polystyrene sulfonic acid, 0.1-0.2 part of gluconolactone, 1-2 parts of 2,6-di-tert-butyl-4-methylphenol, 2-3 parts of magnesium silicate, 10-14 parts of fumed silica, 1-2 parts of alum powder, 2-4 parts of polytetrafluoroethylene wax, 1-2 parts of calcium hydrogenphosphate, 1-2 parts of diphenylsilanediol, 13-20 parts of deionized water, and 6-7 parts of a bonding auxiliary agent. The bonding auxiliary agent added into the waterproof paint is capable of effectively promoting compatibility of all materials, improving the boding effect of the paint with a base material, enhancing adhesive force, improving anti-stripping property and improving the stability of the paint. The paint is good in weatherability and waterproofness and lasting in protection effect.
Description
Technical field
The present invention relates generally to a kind of coating, particularly relates to one and stablizes weather-proof waterproof paint.
Background technology
So-called coating refers to that coating body surface can form film under certain conditions and play protection, the class I liquid I of decoration or other specific functions (insulation, antirust, mildew-resistant, heat-resisting etc.) or solid material.Be main raw material mainly with vegetables oil greatly because of early stage coating, therefore also known as painting.Present synthetic resins is most of or all instead of vegetables oil, therefore is called coating.Application of paints is all respects in life, and coating not only requires that cohesiveness is strong, good weatherability, and resistance is high, also wants nontoxic pollution-free, therefore improves constantly the overall quality of coating for improving people's living standard, and accelerating urban development has very great meaning.
Summary of the invention
The object of the invention is just to provide one and stablizes weather-proof waterproof paint.
The present invention is achieved by the following technical solutions:
One stablizes weather-proof waterproof paint, and it is made up of the raw material of following weight parts:
Aqueous acrylic emulsion 71-80, calcium aluminate 2-3, cyanacrylate 2-4, polyvinylbenzenesulfonic acid 1-2, glucono-lactone 0.1-0.2,2,6 ditertiary butyl p cresol 1-2, Magnesium Silicate q-agent 2-3, aerosil 10-14, alum powder 1-2, tetrafluoroethylene wax 2-4, secondary calcium phosphate 1-2, Diphenylsilanediol 1-2, deionized water 13-20, adhesive aid 6-7;
Described adhesive aid is made up of the raw material of following weight parts:
Eva emulsion 40-46, lauryl glucosyl 1-2, methyl methacrylate 2-4, ammonium persulphate 1-2, allyl polyglycol 3-4, potassium zirconium carbonate 1-2, nano-carbon powder 2-3, tetrafluoroethylene wax 2-3, nano titanium oxide 0.1-1, deionized water 6-8;
By potassium zirconium carbonate, nano-carbon powder mixing, add tetrafluoroethylene wax after stirring, at 60-70 DEG C, be uniformly mixed 10-16 minute, add allyl polyglycol, be stirred to normal temperature, join in Eva emulsion, 200-300 rev/min of dispersed with stirring 10-12 minute;
Lauryl glucosyl is joined in deionized water, after stirring, add ammonium persulphate, methyl methacrylate, 60-80 rev/min of dispersed with stirring 3-5 minute;
Mixed with each raw material of residue by each raw material after above-mentioned process, 800-1000 rev/min of dispersed with stirring 2-4 minute, obtains described adhesive aid.
Stablize a preparation method for weather-proof waterproof paint, it is characterized in that comprising the following steps:
By aerosil, alum powder, Magnesium Silicate q-agent, tetrafluoroethylene wax, secondary calcium phosphate, calcium aluminate mixing, 10-20 minute is uniformly mixed at 50-70 DEG C, join in aqueous acrylic emulsion, 400-500 rev/min of dispersed with stirring 10-15 minute, mix with each raw material of residue, 600-800 rev/min of dispersed with stirring 20-30 minute, obtains and describedly stablizes weather-proof waterproof paint.
Advantage of the present invention is:
The adhesive aid added in waterproof paint of the present invention effectively can promote the consistency of each storeroom, improves the bond effect of coating and base material, strengthens sticking power; improve stripper-resistance; improve the stability of coating, weathering resistance, good waterproof performance, protected effect is lasting.
Embodiment
Embodiment 1
One stablizes weather-proof waterproof paint, and it is made up of the raw material of following weight parts (kilogram):
Aqueous acrylic emulsion 80, calcium aluminate 3, cyanacrylate 4, polyvinylbenzenesulfonic acid 1, glucono-lactone 0.2,2,6 ditertiary butyl p cresol 2, Magnesium Silicate q-agent 3, aerosil 14, alum powder 1, tetrafluoroethylene wax 4, secondary calcium phosphate 1, Diphenylsilanediol 2, deionized water 20, adhesive aid 7;
Described adhesive aid is made up of the raw material of following weight parts:
Eva emulsion 46, lauryl glucosyl 2, methyl methacrylate 2, ammonium persulphate 2, allyl polyglycol 3, potassium zirconium carbonate 1, nano-carbon powder 2, tetrafluoroethylene wax 2, nano titanium oxide 0.1, deionized water 8;
By potassium zirconium carbonate, nano-carbon powder mixing, add tetrafluoroethylene wax after stirring, at 60 DEG C, be uniformly mixed 16 minutes, add allyl polyglycol, be stirred to normal temperature, join in Eva emulsion, 300 revs/min of dispersed with stirring 12 minutes;
Lauryl glucosyl is joined in deionized water, after stirring, add ammonium persulphate, methyl methacrylate, 80 revs/min of dispersed with stirring 3 minutes;
Mixed with each raw material of residue by each raw material after above-mentioned process, 1000 revs/min of dispersed with stirring 4 minutes, obtain described adhesive aid.
Stablize a preparation method for weather-proof waterproof paint, it is characterized in that comprising the following steps:
By aerosil, alum powder, Magnesium Silicate q-agent, tetrafluoroethylene wax, secondary calcium phosphate, calcium aluminate mixing, 20 minutes are uniformly mixed at 70 DEG C, join in aqueous acrylic emulsion, 500 revs/min of dispersed with stirring 10 minutes, mix with each raw material of residue, 800 revs/min of dispersed with stirring 30 minutes, obtain and describedly stablize weather-proof waterproof paint.
Performance test:
Unit elongation: >=300%;
Watertightness: 0.3MPa (one hour waterproof).
Claims (2)
1. stablize a weather-proof waterproof paint, it is characterized in that what it was made up of the raw material of following weight parts:
Aqueous acrylic emulsion 71-80, calcium aluminate 2-3, cyanacrylate 2-4, polyvinylbenzenesulfonic acid 1-2, glucono-lactone 0.1-0.2,2,6 ditertiary butyl p cresol 1-2, Magnesium Silicate q-agent 2-3, aerosil 10-14, alum powder 1-2, tetrafluoroethylene wax 2-4, secondary calcium phosphate 1-2, Diphenylsilanediol 1-2, deionized water 13-20, adhesive aid 6-7;
Described adhesive aid is made up of the raw material of following weight parts:
Eva emulsion 40-46, lauryl glucosyl 1-2, methyl methacrylate 2-4, ammonium persulphate 1-2, allyl polyglycol 3-4, potassium zirconium carbonate 1-2, nano-carbon powder 2-3, tetrafluoroethylene wax 2-3, nano titanium oxide 0.1-1, deionized water 6-8;
By potassium zirconium carbonate, nano-carbon powder mixing, add tetrafluoroethylene wax after stirring, at 60-70 DEG C, be uniformly mixed 10-16 minute, add allyl polyglycol, be stirred to normal temperature, join in Eva emulsion, 200-300 rev/min of dispersed with stirring 10-12 minute;
Lauryl glucosyl is joined in deionized water, after stirring, add ammonium persulphate, methyl methacrylate, 60-80 rev/min of dispersed with stirring 3-5 minute;
Mixed with each raw material of residue by each raw material after above-mentioned process, 800-1000 rev/min of dispersed with stirring 2-4 minute, obtains described adhesive aid.
2. stablize a preparation method for weather-proof waterproof paint as claimed in claim 1, it is characterized in that comprising the following steps:
By aerosil, alum powder, Magnesium Silicate q-agent, tetrafluoroethylene wax, secondary calcium phosphate, calcium aluminate mixing, 10-20 minute is uniformly mixed at 50-70 DEG C, join in aqueous acrylic emulsion, 400-500 rev/min of dispersed with stirring 10-15 minute, mix with each raw material of residue, 600-800 rev/min of dispersed with stirring 20-30 minute, obtains and describedly stablizes weather-proof waterproof paint.