CN104312343A - Elastic water-proof coating used for automobiles - Google Patents
Elastic water-proof coating used for automobiles Download PDFInfo
- Publication number
- CN104312343A CN104312343A CN201410502425.2A CN201410502425A CN104312343A CN 104312343 A CN104312343 A CN 104312343A CN 201410502425 A CN201410502425 A CN 201410502425A CN 104312343 A CN104312343 A CN 104312343A
- Authority
- CN
- China
- Prior art keywords
- parts
- stirring
- minute
- raw material
- rev
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Elastic water-proof coating used for automobiles is disclosed. The coating comprises following raw materials by weight: 70-80 parts of silicone acrylic emulsion, 10-20 parts of XL-800 elastic pure acrylic emulsion, 3-4 parts of glycerol ester of rosin, 0.1-0.2 part of potassium peroxodisulfate, 1-2 parts of fenugreek gum, 2-4 parts of ethylparaben, 0.7-2 parts of alkenyl succinic anhydride, 1-2 parts of sodium pyrophosphate, 1-2 parts of polyvinylpyrrolidone, 1-2 parts of ammonium alcohol ether sulphate, 10-14 parts of titanium dioxide, 2-3 parts of zinc stearate, 1-2 parts of polyethylene glycol adipate, 0.7-1 part of 8-hydroxyquinoline, 18-25 parts of deionized water and 5-8 parts of an adhesion auxiliary agent. The water-proof coating can be subjected to direct construction on base surfaces of a plurality of materials which are wet or dry, and has advantages of good extensibility, high surface strength, high coefficient of elongation, good adhesiveness, good freezing resistance, high weather fastness, good quality feeling and wide application.
Description
?
Technical field
The present invention relates generally to a kind of coating, particularly relates to a kind of automobile elastic water proofing paint.
Background technology
So-called coating refers to that coating body surface can form film under certain conditions and play protection, the class I liquid I of decoration or other specific functions (insulation, antirust, mildew-resistant, heat-resisting etc.) or solid material.Be main raw material mainly with vegetables oil greatly because of early stage coating, therefore also known as painting.Present synthetic resins is most of or all instead of vegetables oil, therefore is called coating.Application of paints is all respects in life, and coating not only requires that cohesiveness is strong, good weatherability, and resistance is high, also wants nontoxic pollution-free, therefore improves constantly the overall quality of coating for improving people's living standard, and accelerating urban development has very great meaning.
Summary of the invention
The object of the invention is just to provide a kind of automobile elastic water proofing paint.
The present invention is achieved by the following technical solutions:
A kind of automobile elastic water proofing paint, it is made up of the raw material of following weight parts:
Organosilicon crylic acid latex 70-80, XL-800 elasticity pure-acrylic emulsion 10-20, ester gum 3-4, Potassium Persulphate 0.1-0.2, fenugreek gum 1-2, ethyl p-hydroxybenzoate 2-4, alkenyl succinic anhydride 0.7-2, trisodium phosphate 1-2, polyvinylpyrrolidone 1-2, ethoxylated alkylphenol ammonium sulfate 1-2, titanium dioxide 10-14, Zinic stearas 2-3, poly-adipate glycol 1-2, oxine 0.7-1, deionized water 18-25, adhesive aid 5-8;
Described adhesive aid is made up of the raw material of following weight parts:
Eva emulsion 40-46, lauryl glucosyl 1-2, methyl methacrylate 2-4, vulcabond 1-2, allyl polyglycol 3-4, potassium zirconium carbonate 1-2, nano-carbon powder 2-3, tetrafluoroethylene wax 2-3, nano titanium oxide 0.1-1, deionized water 6-8;
By potassium zirconium carbonate, nano-carbon powder mixing, add tetrafluoroethylene wax after stirring, at 60-70 DEG C, be uniformly mixed 10-16 minute, add allyl polyglycol, be stirred to normal temperature, join in Eva emulsion, 200-300 rev/min of dispersed with stirring 10-12 minute;
Lauryl glucosyl is joined in deionized water, after stirring, add vulcabond, methyl methacrylate, 60-80 rev/min of dispersed with stirring 3-5 minute;
Mixed with each raw material of residue by each raw material after above-mentioned process, 800-1000 rev/min of dispersed with stirring 2-4 minute, obtains described adhesive aid.
A preparation method for automobile elastic water proofing paint, is characterized in that comprising the following steps:
Joined by ester gum in XL-800 elasticity pure-acrylic emulsion, be heated to 50-60 DEG C, add titanium dioxide, Zinic stearas, 200-300 rev/min is stirred 5-10 minute;
Join in deionized water by ethoxylated alkylphenol ammonium sulfate, add ethyl p-hydroxybenzoate, trisodium phosphate, polyvinylpyrrolidone after stirring, 200-300 rev/min is stirred a point 7-10 minute;
Mixed with each raw material of residue by each raw material after above-mentioned process, 600-800 rev/min of dispersed with stirring 20-30 minute, obtains described automobile elastic water proofing paint.
Advantage of the present invention is:
Waterproof paint of the present invention directly can be constructed on moist or dry multiple material basal plane, and good-extensibility, surface strength are high, unit elongation is high, and cohesiveness is good, and frost resistance is good, and weathering resistance is strong, and texture is good, is widely used.
Embodiment
Embodiment 1
A kind of automobile elastic water proofing paint, it is made up of the raw material of following weight parts (kilogram):
Organosilicon crylic acid latex 80, XL-800 elasticity pure-acrylic emulsion 20, ester gum 3, Potassium Persulphate 0.2, fenugreek gum 2, ethyl p-hydroxybenzoate 2, alkenyl succinic anhydride 0.7, trisodium phosphate 2, polyvinylpyrrolidone 1-2, ethoxylated alkylphenol ammonium sulfate 2, titanium dioxide 14, Zinic stearas 3, poly-adipate glycol 2, oxine 0.7, deionized water 25, adhesive aid 5;
Described adhesive aid is made up of the raw material of following weight parts:
Eva emulsion 46, lauryl glucosyl 2, methyl methacrylate 4, vulcabond 1, allyl polyglycol 3, potassium zirconium carbonate 1, nano-carbon powder 2, tetrafluoroethylene wax 3, nano titanium oxide 0.1, deionized water 8;
By potassium zirconium carbonate, nano-carbon powder mixing, add tetrafluoroethylene wax after stirring, at 70 DEG C, be uniformly mixed 16 minutes, add allyl polyglycol, be stirred to normal temperature, join in Eva emulsion, 300 revs/min of dispersed with stirring 12 minutes;
Lauryl glucosyl is joined in deionized water, after stirring, add vulcabond, methyl methacrylate, 80 revs/min of dispersed with stirring 5 minutes;
Mixed with each raw material of residue by each raw material after above-mentioned process, 1000 revs/min of dispersed with stirring 4 minutes, obtain described adhesive aid.
A preparation method for automobile elastic water proofing paint, is characterized in that comprising the following steps:
Joined by ester gum in XL-800 elasticity pure-acrylic emulsion, be heated to 60 DEG C, add titanium dioxide, Zinic stearas, 300 revs/min are stirred 10 minutes;
Join in deionized water by ethoxylated alkylphenol ammonium sulfate, add ethyl p-hydroxybenzoate, trisodium phosphate, polyvinylpyrrolidone after stirring, 300 revs/min of stirrings divide 10 minutes;
Mixed with each raw material of residue by each raw material after above-mentioned process, 800 revs/min of dispersed with stirring 30 minutes, obtain described automobile elastic water proofing paint.
Performance test:
Unit elongation: >=300%;
Watertightness: 0.3MPa (one hour waterproof).
Claims (2)
1. an automobile elastic water proofing paint, is characterized in that what it was made up of the raw material of following weight parts:
Organosilicon crylic acid latex 70-80, XL-800 elasticity pure-acrylic emulsion 10-20, ester gum 3-4, Potassium Persulphate 0.1-0.2, fenugreek gum 1-2, ethyl p-hydroxybenzoate 2-4, alkenyl succinic anhydride 0.7-2, trisodium phosphate 1-2, polyvinylpyrrolidone 1-2, ethoxylated alkylphenol ammonium sulfate 1-2, titanium dioxide 10-14, Zinic stearas 2-3, poly-adipate glycol 1-2, oxine 0.7-1, deionized water 18-25, adhesive aid 5-8;
Described adhesive aid is made up of the raw material of following weight parts:
Eva emulsion 40-46, lauryl glucosyl 1-2, methyl methacrylate 2-4, vulcabond 1-2, allyl polyglycol 3-4, potassium zirconium carbonate 1-2, nano-carbon powder 2-3, tetrafluoroethylene wax 2-3, nano titanium oxide 0.1-1, deionized water 6-8;
By potassium zirconium carbonate, nano-carbon powder mixing, add tetrafluoroethylene wax after stirring, at 60-70 DEG C, be uniformly mixed 10-16 minute, add allyl polyglycol, be stirred to normal temperature, join in Eva emulsion, 200-300 rev/min of dispersed with stirring 10-12 minute;
Lauryl glucosyl is joined in deionized water, after stirring, add vulcabond, methyl methacrylate, 60-80 rev/min of dispersed with stirring 3-5 minute;
Mixed with each raw material of residue by each raw material after above-mentioned process, 800-1000 rev/min of dispersed with stirring 2-4 minute, obtains described adhesive aid.
2. a preparation method for automobile elastic water proofing paint as claimed in claim 1, is characterized in that comprising the following steps:
Joined by ester gum in XL-800 elasticity pure-acrylic emulsion, be heated to 50-60 DEG C, add titanium dioxide, Zinic stearas, 200-300 rev/min is stirred 5-10 minute;
Join in deionized water by ethoxylated alkylphenol ammonium sulfate, add ethyl p-hydroxybenzoate, trisodium phosphate, polyvinylpyrrolidone after stirring, 200-300 rev/min is stirred a point 7-10 minute;
Mixed with each raw material of residue by each raw material after above-mentioned process, 600-800 rev/min of dispersed with stirring 20-30 minute, obtains described automobile elastic water proofing paint.