CN104250459A - High-temperature-resistant anticorrosion waterproof paint - Google Patents
High-temperature-resistant anticorrosion waterproof paint Download PDFInfo
- Publication number
- CN104250459A CN104250459A CN201410445770.7A CN201410445770A CN104250459A CN 104250459 A CN104250459 A CN 104250459A CN 201410445770 A CN201410445770 A CN 201410445770A CN 104250459 A CN104250459 A CN 104250459A
- Authority
- CN
- China
- Prior art keywords
- parts
- stirring
- minute
- raw material
- waterproof paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Disclosed high-temperature-resistant anticorrosion waterproof paint is composed of the following raw materials in parts by weight: 80-90 parts of styrene-acrylic emulsion, 0.1-0.2 parts of furametpyr, 2-3 parts of beeswax, 10-14 parts of nanometer carbon powder, 1-2 parts of azodiisobutyronitrile, 1-2 parts of sodium pyrosulfite, 2-3 parts of triglycidyl isocyanurate, 10002-3 parts of polyethylene glycol, 1-2 parts of N-methylolacrylamide, 2-3 parts of bisphenol A epoxy resin, 1-2 parts of methyltin mercaptide, 20-25 parts of deionized water, and 4-6 parts of a bonding auxiliary agent. The waterproof paint has excellent adhesive force, a paint film is excellent in elasticity and hydrophobicity, and relatively high in tensile strength and elongation at break, the added bisphenol A epoxy resin is capable of effectively improving the heat resistance, improving the hot-environment adaptability, and the paint is good in weatherability and corrosion resistance.
Description
Technical field
The present invention relates generally to a kind of coating, particularly relates to a kind of fire resistant anticorrosive waterproof paint.
Background technology
So-called coating refers to that coating body surface can form film under certain conditions and play protection, the class I liquid I of decoration or other specific functions (insulation, antirust, mildew-resistant, heat-resisting etc.) or solid material.Be main raw material mainly with vegetables oil greatly because of early stage coating, therefore also known as painting.Present synthetic resins is most of or all instead of vegetables oil, therefore is called coating.Application of paints is all respects in life, and coating not only requires that cohesiveness is strong, good weatherability, and resistance is high, also wants nontoxic pollution-free, therefore improves constantly the overall quality of coating for improving people's living standard, and accelerating urban development has very great meaning.
Summary of the invention
The object of the invention is just to provide a kind of fire resistant anticorrosive waterproof paint.
The present invention is achieved by the following technical solutions:
A kind of fire resistant anticorrosive waterproof paint, it is made up of the raw material of following weight parts:
Benzene emulsion 80-90, fluopicolide 0.1-0.2, beeswax 2-3, nano-carbon powder 10-14, Diisopropyl azodicarboxylate 1-2, Sodium Pyrosulfite 1-2, isocyanuric acid three-glycidyl ester 2-3, cetomacrogol 1000 2-3, N hydroxymethyl acrylamide 1-2, dihydroxyphenyl propane type epoxy resin 2-3, dimethyl dimercapto 2-ethyl hexyl ethanoate tin 1-2, deionized water 20-25, adhesive aid 4-6;
Described adhesive aid is made up of the raw material of following weight parts:
Organosilicon crylic acid latex 31-40, hydroxyethyl methylacrylate 4-7, calcium ascorbate 0.7-2, Sodium dodecylbenzene sulfonate 1-2, diatomite 3-4, dibutyl maleinate 2-3, polybenzimidazole 1-2, TriMethylolPropane(TMP) 1-2, Potassium Persulphate 1-2, deionized water 5-8;
Diatomite is mixed with calcium ascorbate, adds dibutyl maleinate, insulated and stirred 3-5 minute at 40-50 DEG C after ball milling is even, join in hydroxyethyl methylacrylate, stir;
Sodium dodecylbenzene sulfonate is joined in deionized water, after stirring, add Potassium Persulphate, TriMethylolPropane(TMP), 100-200 rev/min of dispersed with stirring 6-10 minute;
By the mixing of materials after above-mentioned process, mix with each raw material of residue after stirring, 300-400 rev/min of dispersed with stirring 20-30 minute, obtains described adhesive aid.
A preparation method for fire resistant anticorrosive waterproof paint, is characterized in that comprising the following steps:
By nano-carbon powder, Sodium Pyrosulfite mixing, add dihydroxyphenyl propane type epoxy resin, Diisopropyl azodicarboxylate after stirring, at 60-70 DEG C, be uniformly mixed 15-20 minute, be cooled to normal temperature;
By cetomacrogol 1000, beeswax mixing, join after stirring in deionized water, add dimethyl dimercapto 2-ethyl hexyl ethanoate tin, 40-60 rev/min of dispersed with stirring 5-8 minute;
Mixed with each raw material of residue by raw material after above-mentioned process, 700-800 rev/min of dispersed with stirring 30-40 minute, obtains described fire resistant anticorrosive waterproof paint.
Advantage of the present invention is:
Waterproof paint of the present invention has outstanding sticking power, and paint film elasticity, hydrophobic nature are excellent, and tensile strength, elongation at break are higher, the dihydroxyphenyl propane type epoxy resin added effectively can improve resistance toheat, improve the adaptability to thermal environment, weathering resistance, good corrosion resistance.
Embodiment
Embodiment 1
A kind of fire resistant anticorrosive waterproof paint, it is made up of the raw material of following weight parts (kilogram):
Benzene emulsion 90, fluopicolide 0.2, beeswax 2, nano-carbon powder 14, Diisopropyl azodicarboxylate 2, Sodium Pyrosulfite 2, isocyanuric acid three-glycidyl ester 3, cetomacrogol 1000 3, N hydroxymethyl acrylamide 1, dihydroxyphenyl propane type epoxy resin 2, dimethyl dimercapto 2-ethyl hexyl ethanoate tin 1, deionized water 25, adhesive aid 4;
Described adhesive aid is made up of the raw material of following weight parts:
Organosilicon crylic acid latex 40, hydroxyethyl methylacrylate 7, calcium ascorbate 0.7, Sodium dodecylbenzene sulfonate 1, diatomite 3, dibutyl maleinate 3, polybenzimidazole 1, TriMethylolPropane(TMP) 1, Potassium Persulphate 2, deionized water 8;
Mixed with calcium ascorbate by diatomite, add dibutyl maleinate after ball milling is even, at 50 DEG C, insulated and stirred 3 minutes, joins in hydroxyethyl methylacrylate, stirs;
Sodium dodecylbenzene sulfonate is joined in deionized water, after stirring, add Potassium Persulphate, TriMethylolPropane(TMP), 200 revs/min of dispersed with stirring 6 minutes;
By the mixing of materials after above-mentioned process, mix with each raw material of residue after stirring, 400 revs/min of dispersed with stirring 30 minutes, obtain described adhesive aid.
A preparation method for fire resistant anticorrosive waterproof paint, is characterized in that comprising the following steps:
By nano-carbon powder, Sodium Pyrosulfite mixing, add dihydroxyphenyl propane type epoxy resin, Diisopropyl azodicarboxylate after stirring, at 70 DEG C, be uniformly mixed 20 minutes, be cooled to normal temperature;
By cetomacrogol 1000, beeswax mixing, join after stirring in deionized water, add dimethyl dimercapto 2-ethyl hexyl ethanoate tin, 40 revs/min of dispersed with stirring 5 minutes;
Mixed with each raw material of residue by raw material after above-mentioned process, 800 revs/min of dispersed with stirring 40 minutes, obtain described fire resistant anticorrosive waterproof paint.
Performance test:
Unit elongation: >=300%;
Watertightness: 0.3MPa (one hour waterproof).
Claims (2)
1. a fire resistant anticorrosive waterproof paint, is characterized in that what it was made up of the raw material of following weight parts:
Benzene emulsion 80-90, fluopicolide 0.1-0.2, beeswax 2-3, nano-carbon powder 10-14, Diisopropyl azodicarboxylate 1-2, Sodium Pyrosulfite 1-2, isocyanuric acid three-glycidyl ester 2-3, cetomacrogol 1000 2-3, N hydroxymethyl acrylamide 1-2, dihydroxyphenyl propane type epoxy resin 2-3, dimethyl dimercapto 2-ethyl hexyl ethanoate tin 1-2, deionized water 20-25, adhesive aid 4-6;
Described adhesive aid is made up of the raw material of following weight parts:
Organosilicon crylic acid latex 31-40, hydroxyethyl methylacrylate 4-7, calcium ascorbate 0.7-2, Sodium dodecylbenzene sulfonate 1-2, diatomite 3-4, dibutyl maleinate 2-3, polybenzimidazole 1-2, TriMethylolPropane(TMP) 1-2, Potassium Persulphate 1-2, deionized water 5-8;
Diatomite is mixed with calcium ascorbate, adds dibutyl maleinate, insulated and stirred 3-5 minute at 40-50 DEG C after ball milling is even, join in hydroxyethyl methylacrylate, stir;
Sodium dodecylbenzene sulfonate is joined in deionized water, after stirring, add Potassium Persulphate, TriMethylolPropane(TMP), 100-200 rev/min of dispersed with stirring 6-10 minute;
By the mixing of materials after above-mentioned process, mix with each raw material of residue after stirring, 300-400 rev/min of dispersed with stirring 20-30 minute, obtains described adhesive aid.
2. a preparation method for fire resistant anticorrosive waterproof paint as claimed in claim 1, is characterized in that comprising the following steps:
By nano-carbon powder, Sodium Pyrosulfite mixing, add dihydroxyphenyl propane type epoxy resin, Diisopropyl azodicarboxylate after stirring, at 60-70 DEG C, be uniformly mixed 15-20 minute, be cooled to normal temperature;
By cetomacrogol 1000, beeswax mixing, join after stirring in deionized water, add dimethyl dimercapto 2-ethyl hexyl ethanoate tin, 40-60 rev/min of dispersed with stirring 5-8 minute;
Mixed with each raw material of residue by raw material after above-mentioned process, 700-800 rev/min of dispersed with stirring 30-40 minute, obtains described fire resistant anticorrosive waterproof paint.