CN105062235A - Organic-inorganic roofing composite multi-functional waterproof coating - Google Patents
Organic-inorganic roofing composite multi-functional waterproof coating Download PDFInfo
- Publication number
- CN105062235A CN105062235A CN201510475350.8A CN201510475350A CN105062235A CN 105062235 A CN105062235 A CN 105062235A CN 201510475350 A CN201510475350 A CN 201510475350A CN 105062235 A CN105062235 A CN 105062235A
- Authority
- CN
- China
- Prior art keywords
- parts
- organic
- add
- raw material
- roofing composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an organic-inorganic roofing composite multi-functional waterproof coating composed of the following raw materials in parts by weight: 50-60 parts of a styrene acrylic emulsion BC991, 2-3 parts of fatty alcohol-polyoxyethylene ether, 1-2 parts of hexadecanoic acid, 0.7-1 part of isopropyl p-hydroxy-benzoate, 1-2 parts of octadecanoic acid, 4-7 parts of polyethylene wax, 1-2 parts of titanium dioxide, 10-15 parts of Suzhou soil, 0.1-0.2 parts of potassium pyrophosphate, 3-4 parts of hollow glass micro-beads, 3-5 parts of fly ash floating beads, 0.5-1 part of glyceryl tristearate, 5-7 parts of a bonding auxiliary agent, and 6-20 parts of deionized water. The waterproof coating has the advantages of convenient construction, low cost, good elasticity of a coating film, acid and alkali resistance, aging resistance, good waterproofness, heat-preservation and heat-insulation properties, and green environmental protection.
Description
Technical field
The present invention relates generally to a kind of coating, particularly relates to a kind of organic and inorganic roofing composite multifunction waterproof paint.
Background technology
Waterproof paint has a variety of in the market, and some hardness is higher, easily ftractures along with the strain cracking of basic unit, the easy bulge infiltration had; Some environment protectings are poor, therefore produce the strong waterproof paint of a kind of over-all properties for nation-building and people life improvement have good promoter action.
Summary of the invention
The object of the invention is just to provide a kind of organic and inorganic roofing composite multifunction waterproof paint.
The present invention is achieved by the following technical solutions:
A kind of organic and inorganic roofing composite multifunction waterproof paint, it is made up of the raw material of following weight parts:
Benzene emulsion BC99150-60, fatty alcohol-polyoxyethylene ether 2-3, hexadecanoic acid 1-2, p-hydroxybenzoic acid isopropyl ester 0.7-1, octadecanoic acid 1-2, polyethylene wax 4-7, titanium dioxide 1-2, Suzhou soil 10-15, potassium pyrophosphate 0.1-0.2, hollow glass micropearl 3-4, fly ash float 3-5, Tristearoylglycerol 0.5-1, adhesive aid 5-7, deionized water 6-20;
Described adhesive aid is made up of the raw material of following weight parts:
Vinyl acetate-ethylene copolymerization emulsions 20-35, Viscogum BE 4-6, chitosan 1-2, stearyl methacrylate 3-5, Chinese Angelica Root 1-2, gibbsite 3-4, water are appropriate;
By above-mentioned stearyl methacrylate heat fused, add chitosan, stir, add gibbsite, Chinese Angelica Root, abundant mixing, joined in 6-8 times of water by above-mentioned mixed material, ball milling 1-2 hour, adds Viscogum BE, insulated and stirred reaction 15-20 minute at 60-85 DEG C, add each raw material of residue, abundant ball milling, obtains described adhesive aid.
A preparation method for organic and inorganic roofing composite multifunction waterproof paint, comprises the following steps:
By above-mentioned polyethylene wax, Suzhou soil mixing, be heated to 70-80 DEG C, stir, reduction temperature is 30-35 DEG C, add each raw material except benzene emulsion BC991,600-800 rev/min of dispersed with stirring 5-10 minute, add each raw material of residue, high-speed stirring, to mixing, obtains described organic and inorganic roofing composite multifunction waterproof paint.
Advantage of the present invention is:
Waterproof paint easy construction of the present invention, with low cost, film good springiness, acid and alkali-resistance, anti-aging, existing good water-repellancy, possesses heat insulation property again, environmental protection.。
Embodiment
Embodiment 1
A kind of organic and inorganic roofing composite multifunction waterproof paint, it is made up of the raw material of following weight parts (kilogram):
Benzene emulsion BC99160, fatty alcohol-polyoxyethylene ether 3, hexadecanoic acid 1, p-hydroxybenzoic acid isopropyl ester 0.7, octadecanoic acid 1, polyethylene wax 4-7, titanium dioxide 2, Suzhou soil 15, potassium pyrophosphate 0.2, hollow glass micropearl 4, fly ash float 3-5, Tristearoylglycerol 0.5, adhesive aid 5, deionized water 20;
Described adhesive aid is made up of the raw material of following weight parts:
Vinyl acetate-ethylene copolymerization emulsions 35, Viscogum BE 4, chitosan 1, stearyl methacrylate 5, Chinese Angelica Root 1, gibbsite 3, water are appropriate;
By above-mentioned stearyl methacrylate heat fused, add chitosan, stir, add gibbsite, Chinese Angelica Root, abundant mixing, joined by above-mentioned mixed material in 8 times of water, ball milling 2 hours, adds Viscogum BE, at 85 DEG C, insulated and stirred reacts 20 minutes, add each raw material of residue, abundant ball milling, obtains described adhesive aid.
A preparation method for organic and inorganic roofing composite multifunction waterproof paint, comprises the following steps:
By above-mentioned polyethylene wax, Suzhou soil mixing, be heated to 80 DEG C, stir, reducing temperature is 35 DEG C, add each raw material except benzene emulsion BC991,800 revs/min of dispersed with stirring 10 minutes, add each raw material of residue, high-speed stirring, to mixing, obtains described organic and inorganic roofing composite multifunction waterproof paint.
Performance test:
Unit elongation: >=300%;
Watertightness: 0.3MPa (one hour waterproof).
Claims (2)
1. an organic and inorganic roofing composite multifunction waterproof paint, is characterized in that what it was made up of the raw material of following weight parts:
Benzene emulsion BC99150-60, fatty alcohol-polyoxyethylene ether 2-3, hexadecanoic acid 1-2, p-hydroxybenzoic acid isopropyl ester 0.7-1, octadecanoic acid 1-2, polyethylene wax 4-7, titanium dioxide 1-2, Suzhou soil 10-15, potassium pyrophosphate 0.1-0.2, hollow glass micropearl 3-4, fly ash float 3-5, Tristearoylglycerol 0.5-1, adhesive aid 5-7, deionized water 6-20;
Described adhesive aid is made up of the raw material of following weight parts:
Vinyl acetate-ethylene copolymerization emulsions 20-35, Viscogum BE 4-6, chitosan 1-2, stearyl methacrylate 3-5, Chinese Angelica Root 1-2, gibbsite 3-4, water are appropriate;
By above-mentioned stearyl methacrylate heat fused, add chitosan, stir, add gibbsite, Chinese Angelica Root, abundant mixing, joined in 6-8 times of water by above-mentioned mixed material, ball milling 1-2 hour, adds Viscogum BE, insulated and stirred reaction 15-20 minute at 60-85 DEG C, add each raw material of residue, abundant ball milling, obtains described adhesive aid.
2. a preparation method for organic and inorganic roofing composite multifunction waterproof paint as claimed in claim 1, is characterized in that comprising the following steps:
By above-mentioned polyethylene wax, Suzhou soil mixing, be heated to 70-80 DEG C, stir, reduction temperature is 30-35 DEG C, add each raw material except benzene emulsion BC991,600-800 rev/min of dispersed with stirring 5-10 minute, add each raw material of residue, high-speed stirring, to mixing, obtains described organic and inorganic roofing composite multifunction waterproof paint.