CN103993720A - 一种真石漆面层装饰板的制备方法 - Google Patents
一种真石漆面层装饰板的制备方法 Download PDFInfo
- Publication number
- CN103993720A CN103993720A CN201410179800.4A CN201410179800A CN103993720A CN 103993720 A CN103993720 A CN 103993720A CN 201410179800 A CN201410179800 A CN 201410179800A CN 103993720 A CN103993720 A CN 103993720A
- Authority
- CN
- China
- Prior art keywords
- raw material
- preparation
- surface layer
- layer decorative
- natural stone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种真石漆面层装饰板的制备方法,涉及装饰板材领域,包括真石漆、无纺布和水包水涂料,真石漆原料按以下重量份计的各组分制成:天然彩砂65-70,苯丙乳液16-20, 水10-15,乙二醇1-2,成膜助剂0.6-0.8,消泡剂0.2,烃乙基纤维素0.2-0.4,按照真石漆原料顺序加入到搅拌机中搅拌均匀,通过布料机和绘制车间的绘制和压制使原料初步呈板状结构,并将绘制好的原料通过传送带输送至烘烤箱内进行烘烤,烘烤成型的板经过切割机切割成块即可;本发明实用性强,使用起来比较方便,不但提高了工作效率,而且节省了成本,加快了施工进度,避免了质量问题。
Description
【技术领域】
本发明涉及装饰板材领域,尤其是涉及一种真石漆面层装饰板的制备方法。
【背景技术】
公知的,真石漆主要由高分子聚合物、天然彩石砂及相关的助剂如分散剂、消泡剂等制成,其在干结固化后坚硬如石,装饰效果酷似大理石或花岗石。真石漆属于艺术涂料中的质感涂料,经其装饰后的建筑物具有天然真实的自然色泽,给人以高雅、庄重的美感,适合于各类建筑物的室内外装饰,由于它可以相对较好地模仿石材的质感,并且具有防火、防水、耐酸碱、耐污染、无毒、无味、粘结力强和永不褪色等特点,近年来在建筑装饰领域得到了较多的使用,特别是随着人们对内外墙涂料装饰性要求的提高,真石漆以其独特的外观及性能越来越受到人们的喜爱,但是,目前多数真石漆存在喷涂时掉砂较多、施工性较差的问题,不仅造成施工周期延长、成本上升、影响施工,而且增加了质量问题的出现机会。
【发明内容】
为了克服背景技术中的不足,本发明公开了一种真石漆面层装饰板的制备方法,本发明通过将原料按照重量份混合搅拌支撑板状结构,并经过绘图和烘干,以此来达到商品生产化与快速施工的目的。
为了实现所述发明目的,本发明采用如下技术方案:
一种真石漆面层装饰板的制备方法,包括真石漆、无纺布和水包水涂料,真石漆原料按以下重量份计的各组分制成:
天然彩砂 65-70, 苯丙乳液 16-20, 水 10-15, 乙二醇 1-2,
成膜助剂 0.6-0.8, 消泡剂 0.2, 烃乙基纤维素 0.2-0.4,
进一步,将天然彩砂研磨成40-120目;
更进一步,按照真石漆原料顺序加入到搅拌机中搅拌均匀;
更进一步,通过布料机将搅拌好的原料投放在传送带上,并在原料和传送带之间铺设无纺布,传送带将原料输送至绘制车间,通过绘制车间的绘制和压制使原料初步呈板状结构;
更进一步,绘制好的原料通过传送带输送至烘烤箱内进行烘烤;
更进一步,烘烤成型的板经过切割机切割成块即可。
所述原料在搅拌机的搅拌时间为40-50分钟。
所述烘烤箱的温度为70-80℃。
所述在烘烤箱内设有喷涂装置,喷涂装置内设有水包水涂料。
由于采用了上述技术方案,本发明具有如下有益效果:
本发明所述的一种真石漆面层装饰板的制备方法,包括真石漆和水包水涂料,通过将原料按照重量份混合搅拌支撑板状结构,并经过绘图和烘干,以此来达到商品生产化与快速施工的目的;本发明实用性强,使用起来比较方便,不但提高了工作效率,而且节省了成本,加快了施工进度,避免了质量问题。
【具体实施方式】
通过下面的实施例可以详细的解释本发明,公开本发明的目的旨在保护本发明范围内的一切技术改进。
实施例1 所述的一种真石漆面层装饰板的制备方法,包括真石漆、无纺布和水包水涂料,真石漆原料按以下重量份计的各组分制成:
天然彩砂 65, 苯丙乳液 16, 水 10, 乙二醇 1,
成膜助剂 0.6, 消泡剂 0.2, 烃乙基纤维素 0.2,
进一步,将天然彩砂研磨成40-120目;
更进一步,按照真石漆原料顺序加入到搅拌机中搅拌均匀;
更进一步,通过布料机将搅拌好的原料投放在传送带上,并在原料和传送带之间铺设无纺布,传送带将原料输送至绘制车间,通过绘制车间的绘制和压制使原料初步呈板状结构;
更进一步,绘制好的原料通过传送带输送至烘烤箱内进行烘烤;
更进一步,烘烤成型的板经过切割机切割成块即可。
所述原料在搅拌机的搅拌时间为40-50分钟。
所述烘烤箱的温度为70-80℃。
所述在烘烤箱内设有喷涂装置,喷涂装置内设有水包水涂料。
表1为本发明实施例1提供的真石漆面层装饰板的检验结果
由表1可知,所述的一种真石漆面层装饰板符合行业使用要求,具有较好的施工性。
实施例2 所述的一种真石漆面层装饰板的制备方法,包括真石漆、无纺布和水包水涂料,真石漆原料按以下重量份计的各组分制成:
天然彩砂 70 , 苯丙乳液 20, 水 15, 乙二醇 2,
成膜助剂 0.8, 消泡剂 0.2, 烃乙基纤维素 0.4,
进一步,将天然彩砂研磨成40-120目;
更进一步,按照真石漆原料顺序加入到搅拌机中搅拌均匀;
更进一步,通过布料机将搅拌好的原料投放在传送带上,并在原料和传送带之间铺设无纺布,传送带将原料输送至绘制车间,通过绘制车间的绘制和压制使原料初步呈板状结构;
更进一步,绘制好的原料通过传送带输送至烘烤箱内进行烘烤;
更进一步,烘烤成型的板经过切割机切割成块即可。
所述原料在搅拌机的搅拌时间为40-50分钟。
所述烘烤箱的温度为70-80℃。
所述在烘烤箱内设有喷涂装置,喷涂装置内设有水包水涂料。
表2为本发明实施例2提供的真石漆面层装饰板的检验结果
由表2可知,所述的一种真石漆面层装饰板符合行业使用要求,具有较好的施工性。
本发明未详述部分为现有技术。
Claims (4)
1.一种真石漆面层装饰板的制备方法,包括真石漆、无纺布和水包水涂料,其特征是:真石漆原料按以下重量份计的各组分制成:
天然彩砂 65-70, 苯丙乳液 16-20, 水 10-15, 乙二醇 1-2,
成膜助剂 0.6-0.8, 消泡剂 0.2, 烃乙基纤维素 0.2-0.4,
进一步,将天然彩砂研磨成40-120目;
更进一步,按照真石漆原料顺序加入到搅拌机中搅拌均匀;
更进一步,通过布料机将搅拌好的原料投放在传送带上,并在原料和传送带之间铺设无纺布,传送带将原料输送至绘制车间,通过绘制车间的绘制和压制使原料初步呈板状结构;
更进一步,绘制好的原料通过传送带输送至烘烤箱内进行烘烤;
更进一步,烘烤成型的板经过切割机切割成块即可。
2.根据权利要求1所述的一种真石漆面层装饰板的制备方法,其特征是:所述原料在搅拌机的搅拌时间为40-50分钟。
3.根据权利要求1所述的一种真石漆面层装饰板的制备方法,其特征是:所述烘烤箱的温度为70-80℃。
4.根据权利要求1所述的一种真石漆面层装饰板的制备方法,其特征是:所述在烘烤箱内设有喷涂装置,喷涂装置内设有水包水涂料。