CN103472511A - 一种高挺度反射膜及其制备方法 - Google Patents

一种高挺度反射膜及其制备方法 Download PDF

Info

Publication number
CN103472511A
CN103472511A CN2013104383484A CN201310438348A CN103472511A CN 103472511 A CN103472511 A CN 103472511A CN 2013104383484 A CN2013104383484 A CN 2013104383484A CN 201310438348 A CN201310438348 A CN 201310438348A CN 103472511 A CN103472511 A CN 103472511A
Authority
CN
China
Prior art keywords
reflectance coating
reflecting film
stiffness
basic unit
mass parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013104383484A
Other languages
English (en)
Other versions
CN103472511B (zh
Inventor
罗培栋
樊华伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NINGBO DXC NEW MATERIAL TECHNOLOGY Co Ltd
Original Assignee
NINGBO DXC NEW MATERIAL TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NINGBO DXC NEW MATERIAL TECHNOLOGY Co Ltd filed Critical NINGBO DXC NEW MATERIAL TECHNOLOGY Co Ltd
Priority to CN201310438348.4A priority Critical patent/CN103472511B/zh
Publication of CN103472511A publication Critical patent/CN103472511A/zh
Application granted granted Critical
Publication of CN103472511B publication Critical patent/CN103472511B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种高挺度反射膜，包括反射膜基层，反射膜基层内具有微泡，反射膜基层的材料为PET；反射膜基层上设有一层扩散膜，扩散膜由下列组分组成：聚甲基丙烯酸甲酯：20质量份，多异氰酸酯：15质量份，扩散粒子：1～3质量份。其制备方法为首先准备反射膜基层，再制备涂布液，制备涂布液时按照下列比例将物料混合均匀：聚甲基丙烯酸甲酯20质量份、多异氰酸酯15质量份、扩散粒子1～3质量份；涂布液制备完成后将其涂布在反射膜基层上，置于烘箱中在130℃的温度下加热干燥1分钟即可。本发明的反射膜反射出的光线更均匀、柔和。由于把反射性能和扩散性能整合在一张膜上，可降低生产成本。

Description

一种高挺度反射膜及其制备方法
(一)技术领域
本发明涉及一种反射膜，以及反射膜的制备方法。
(二)背景技术
随着数字时代的来临，液晶显示器(LCD)已经成为了当今最普遍的显示技术。因为LCD具有绿色环保，耗能低，低辐射，画面柔和等优点，所以LCD将会是未来几十年内主流的显示技术。LCD为非发光性的显示装置，须要借助背光源才能达到显示的功能。背光源性能的好坏除了会直接影响LCD显像质量外，背光源的成本占LCD模块的3-5％，所消耗的电力更占模块的75％，是LCD模块中相当重要的零组件。高精细、大尺寸的LCD，必须有高性能的背光技术与之配合，因此当LCD产业努力开拓新应用领域的同时，背光技术的高性能化亦扮演着幕后功臣的角色。
背光源体系的主要构件包括：光源、导光板、各类光学膜片。目前光源主要有EL、CCFL以及LED三种类型，依照光源分布位置不同可分为侧光式和直下式两种。随着LCD模组不断向更亮、更轻、更薄方向发展，侧光式CCFL式背光源成为目前背光源发展的主流。
背光源体系中光学膜片主要包括反射膜、扩散膜和增亮膜三种。反射膜的主要作用是提高光学表面的反射率，将漏出导光板底部的光线高效率且无耗损地反射，从而降低光耗损，减少用电量，提高液晶显示面的光饱和度。目前，为提高反射膜的反射率，广泛采用以下方法，在聚酯中添加大量的无机粒子或不相容树脂，在双向拉伸过程中，形成大量的微泡(如申请号为201010591111.6、201010589181.8、201010589164.4的中国发明专利等所提供的反射膜都具有微泡)，每一个微泡可作为一个全反射单元，高密度排布的全反射单元对光线形成全反射。通过这种方法得到的反射膜，具有反射率高的特点。然而具有微泡的反射膜内充满了空隙，因而导致反射膜的密度下降，膜的挺度降低，具体在使用时，就会发生膜片弯曲的现象，尤其是在电视机、液晶显示器、广告灯箱等需要膜片竖直放置的领域更为严重。
(三)发明内容
为了克服现有反射膜的上述不足，本发明提供一种高挺度反射膜，并提供制备方法。
本发明解决其技术问题的技术方案是：一种高挺度反射膜，包括反射膜基层，所述的反射膜基层内具有微泡，所述反射膜基层的材料为PET；
所述的反射膜基层上设有一层扩散膜，所述的扩散膜由下列组分组成：
聚甲基丙烯酸甲酯：20质量份
多异氰酸酯：15质量份
扩散粒子：1～3质量份。
优选的，所述的扩散粒子为二氧化钛粒子。
更优选的，所述的二氧化钛粒子为金红石型二氧化钛。
更优选的，所述金红石型二氧化钛粒子的粒径为0.1～15μm。
一种高挺度反射膜的制备方法，首先准备反射膜基层，再制备涂布液，制备涂布液时按照下列比例将物料混合均匀：聚甲基丙烯酸甲酯20质量份、多异氰酸酯15质量份、扩散粒子1～3质量份；
涂布液制备完成后将其涂布在反射膜基层上，置于烘箱中在130℃的温度下加热干燥1分钟即可。
所述的扩散粒子优先选用二氧化钛粒子。更优先选用金红石型二氧化钛。所述金红石型二氧化钛粒子的最优粒径为0.1～15μm。
本发明的有益效果在于：1.在反射膜基层上涂布一层扩散膜，该层扩散膜硬化后具有较高的硬度，从而提高了反射膜整体的挺度，同时在涂层内添加了一定量的扩散粒子，使该涂层可以在不破坏反射效果的基础上增加对入射光的扩散，从而出反射出的光线更均匀、柔和。2.由于把反射性能和扩散性能整合在一张膜上，可以减少或去掉扩散膜，使光线的损耗减少，并使得下游加工流程大为简化，提高生产效率，提高了成品率，有利于生产成本的降低，并起到节能降耗的作用。
(四)附图说明
图1是本发明的结构示意图。
(五)具体实施方式
下面结合附图和具体实施方式对本发明作进一步详细说明。
参照图1，一种高挺度反射膜，包括反射膜基层1，所述的反射膜基层1内具有微泡2，所述反射膜基层1的材料为PET；
所述的反射膜基层1上设有一层扩散膜3，所述的扩散膜3由下列组分组成：
聚甲基丙烯酸甲酯：20质量份
多异氰酸酯：15质量份
扩散粒子：1～3质量份。扩散粒子优选为二氧化钛粒子。二氧化钛有金红石型和锐钛型两种，由于金红石型二氧化钛结晶构造致密，折射率高，与聚酯树脂折射率差大，可以得到高反射的界面，因此更优选金红石型二氧化钛，本实施例中，扩散粒子就选用金红石型二氧化钛粒子，金红石型二氧化钛粒子的粒径为0.1～15μm，优选为0.5-10um，如果小于0.1um，则不会有明显的扩散作用，如果大于15um，则涂布比较困难，且粒子脱落不可避免。
上述高挺度反射膜的制备方法，首先准备反射膜基层，再制备涂布液，制备涂布液时按照下列比例将物料混合均匀：聚甲基丙烯酸甲酯20质量份、多异氰酸酯15质量份、扩散粒子1～3质量份；
涂布液制备完成后将其涂布在反射膜基层上，置于烘箱中在130℃的温度下加热干燥1分钟即可。

Claims (8)

1.一种高挺度反射膜，包括反射膜基层，所述的反射膜基层内具有微泡，其特征在于：所述反射膜基层的材料为PET；
所述的反射膜基层上设有一层扩散膜，所述的扩散膜由下列组分组成：
聚甲基丙烯酸甲酯：20质量份。
多异氰酸酯：15质量份。
扩散粒子：1～3质量份。
2.如权利要求1所述的高挺度反射膜，其特征在于：所述的扩散粒子为二氧化钛粒子。
3.如权利要去2所述的高挺度反射膜，其特征在于：所述的二氧化钛粒子为金红石型二氧化钛。
4.如权利要求3所述的高挺度反射膜，其特征在于：所述金红石型二氧化钛粒子的粒径为0.1～15μm。
5.一种高挺度反射膜的制备方法，首先准备反射膜基层，其特征在于：
再制备涂布液，制备涂布液时按照下列比例将物料混合均匀：聚甲基丙烯酸甲酯20质量份、多异氰酸酯15质量份、扩散粒子1～3质量份；
涂布液制备完成后将其涂布在反射膜基层上，置于烘箱中在130℃的温度下加热干燥1分钟即可。
6.如权利要求5所述的高挺度反射膜的制备方法，其特征在于：所述的扩散粒子选用二氧化钛粒子。
7.如权利要去6所述的高挺度反射膜，其特征在于：所述的二氧化钛粒子选用金红石型二氧化钛。
8.如权利要求7所述的高挺度反射膜，其特征在于：所述金红石型二氧化钛粒子的粒径为0.1～15μm。
CN201310438348.4A 2013-09-16 2013-09-16 一种高挺度反射膜及其制备方法 Active CN103472511B (zh)