CN103213363A - 一种农业用薄膜 - Google Patents

一种农业用薄膜 Download PDF

Info

Publication number
CN103213363A
CN103213363A CN2013100875507A CN201310087550A CN103213363A CN 103213363 A CN103213363 A CN 103213363A CN 2013100875507 A CN2013100875507 A CN 2013100875507A CN 201310087550 A CN201310087550 A CN 201310087550A CN 103213363 A CN103213363 A CN 103213363A
Authority
CN
China
Prior art keywords
parts
film
low density
average molecular
density polyethylene
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013100875507A
Other languages
English (en)
Inventor
朱义珍
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2013100875507A priority Critical patent/CN103213363A/zh
Publication of CN103213363A publication Critical patent/CN103213363A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种农业用薄膜，包括多层膜，其特征在于：至少一层的外层膜由以下重量份数组分组成：聚乳酸10-20份，聚己内酯10-20份，直链低密度聚乙烯20-30份，聚丙烯40-50份，遮光剂1-5份；内层膜由以下重量份数组分组成：聚丙烯50-60份，乙烯-乙酸乙烯酯共聚物15-25份，低密度聚乙烯30-40份。本发明提供的农业用薄膜，可以有效的遮光，使得农作物避免被太阳光太强透射，同时，添加了可降解的材料，提高了薄膜的降解性能，减少了土壤中的残膜与碎片。

Description

一种农业用薄膜
技术领域
本发明属于农业技术领域，主要涉及农业用薄膜。 
背景技术
农业用地膜的主要成分为聚乙烯或聚丙烯，是目前世界上生产量最大的塑料制品。农膜的使用有利于作物的生长发育，提高作物产量。然而，农膜使用量的增加及其难降解性使土壤中残膜及其碎片增多，引起土壤板结、通透性变差，造成农作物减产，其难回收性导致其废弃在自然界中，对生态环境危害很大。对于在农业用薄膜大棚内栽培的作物而言，存在若透射的太阳光线过强，会对作物产生灼伤等不良影响的情形。 
发明内容
为解决现有技术的不足，本发明的目的在于提供一种农业用薄膜，可以起到对农作物遮光的作用，同时具有良好的降解性能。 
为了实现上述目标，本发明采用如下的技术方案： 
一种农业用薄膜，包括多层膜，其特征在于：至少一层的外层膜由以下重量份数组分组成：聚乳酸10-20份，聚己内酯10-20份，直链低密度聚乙烯20-30份，聚丙烯40-50份，遮光剂1-5份；内层膜由以下重量份数组分组成：聚丙烯50-60份，乙烯-乙酸乙烯酯共聚物15-25份，低密度聚乙烯30-40份。 
前述外层膜还可以由以下重量份数组成：聚乳酸-聚己内酯共聚物25-35份，直链低密度聚乙烯30-40份，聚丙烯55-65份，遮光剂1-5份。 
前述遮光剂为二氧化钛或炭黑中的一种。 
前述聚乳酸的数均分子量为50000-80000；前述聚己内酯的数均分子量为50000-80000；前述直链低密度聚乙烯的数均分子量为10000-20000；前述聚丙烯 的数均分子量为8500-10000；前述低密度聚乙烯的数均分子量为10000-20000。 
前述乙烯-乙酸乙烯酯共聚物中乙酸乙烯酯的质量含量为25～35%，乙烯-乙酸乙烯酯共聚物的数均分子量为30000-50000。 
前述聚乳酸-聚己内酯共聚物为无规共聚物，数均分子量为80000-100000。 
本发明的有益之处在于：本发明提供的农业用薄膜，可以有效的遮光，使得农作物避免被太阳光太强透射，同时，添加了可降解的材料，提高了薄膜的降解性能，减少了土壤中的残膜与碎片。 
具体实施方式
以下结合具体实施例对本发明作具体的介绍。 
实施例1-5和对比例1-2中，聚乳酸的数均分子量为50000-80000；聚己内酯的数均分子量为50000-80000；直链低密度聚乙烯的数均分子量为10000-20000；聚丙烯的数均分子量为8500-10000；乙烯-乙酸乙烯酯共聚物中乙酸乙烯酯的质量含量为25～35%，乙烯-乙酸乙烯酯共聚物的数均分子量为30000-50000；低密度聚乙烯的数均分子量为10000-20000；聚乳酸-聚己内酯共聚物为无规共聚物，数均分子量为80000-100000。 
实施例1： 
一种农业用薄膜，至少一层的外层膜由以下重量份数组分组成：聚乳酸10份，聚己内酯10份，直链低密度聚乙烯20份，聚丙烯40份，二氧化钛2份；内层膜由以下重量份数组分组成：聚丙烯50份，乙烯-乙酸乙烯酯共聚物15份，低密度聚乙烯30份。将外层膜与内层膜分别按配比投料，经挤出，吹胀，牵引后得到各分层膜，再将内外层膜通过热密封机，在受压0.15MPa条件下加热120℃一段时间后粘结成多层农业用薄膜。 
实施例2： 
一种农业用薄膜，至少一层的外层膜由以下重量份数组分组成：聚乳酸15份，聚己内酯15份，直链低密度聚乙烯25份，聚丙烯45份，二氧化钛5份；内层膜由以下重量份数组分组成：聚丙烯55份，乙烯-乙酸乙烯酯共聚物20份，低密度聚乙烯35份。将外层膜与内层膜分别按配比投料，经挤出，吹胀，牵引后得到各分层膜，再将内外层膜通过热密封机，在受压0.15MPa条件下加热120℃一段时间后粘结成多层农业用薄膜。 
实施例3： 
一种农业用薄膜，至少一层的外层膜由以下重量份数组分组成：聚乳酸20份，聚己内酯20份，直链低密度聚乙烯30份，聚丙烯50份，炭黑3份；内层膜由以下重量份数组分组成：聚丙烯60份，乙烯-乙酸乙烯酯共聚物25份，低密度聚乙烯40份。将外层膜与内层膜分别按配比投料，经挤出，吹胀，牵引后得到各分层膜，再将内外层膜通过热密封机，在受压0.15MPa条件下加热120℃一段时间后粘结成多层农业用薄膜。 
实施例4： 
一种农业用薄膜，至少一层的外层膜由以下重量份数组分组成：聚乳酸-聚己内酯共聚物25份，直链低密度聚乙烯30份，聚丙烯55份，二氧化钛4份；内层膜由以下重量份数组分组成：聚丙烯56份，乙烯-乙酸乙烯酯共聚物22份，低密度聚乙烯37份。将外层膜与内层膜分别按配比投料，经挤出，吹胀，牵引后得到各分层膜，再将内外层膜通过热密封机，在受压0.15MPa条件下加热120℃一段时间后粘结成多层农业用薄膜。 
实施例5： 
一种农业用薄膜，至少一层的外层膜由以下重量份数组分组成：聚乳酸-聚 己内酯共聚物35份，直链低密度聚乙烯40份，聚丙烯65份，炭黑1份；内层膜由以下重量份数组分组成：聚丙烯52份，乙烯-乙酸乙烯酯共聚物16份，低密度聚乙烯33份。将外层膜与内层膜分别按配比投料，经挤出，吹胀，牵引后得到各分层膜，再将内外层膜通过热密封机，在受压0.15MPa条件下加热120℃一段时间后粘结成多层农业用薄膜。 
对比例1： 
一种农业用薄膜，至少一层的外层膜由以下重量份数组分组成：直链低密度聚乙烯45份，聚丙烯55份，二氧化钛3份；内层膜由以下重量份数组分组成：聚丙烯52份，乙烯-乙酸乙烯酯共聚物18份，低密度聚乙烯35份。将外层膜与内层膜分别按配比投料，经挤出，吹胀，牵引后得到各分层膜，再将内外层膜通过热密封机，在受压0.15MPa条件下加热120℃一段时间后粘结成多层农业用薄膜。 
对比例2： 
一种农业用薄膜，至少一层的外层膜由以下重量份数组分组成：聚乳酸18份，聚己内酯18份，直链低密度聚乙烯26份，聚丙烯44份；内层膜由以下重量份数组分组成：聚丙烯58份，乙烯-乙酸乙烯酯共聚物25份，低密度聚乙烯40份。将外层膜与内层膜分别按配比投料，经挤出，吹胀，牵引后得到各分层膜，再将内外层膜通过热密封机，在受压0.15MPa条件下加热120℃一段时间后粘结成多层农业用薄膜。 
实施例1-5和对比例1-2进行以下测试： 
降解实验：将初始薄膜质量记为m1，薄膜埋于土壤中90天后取出称量，质量记为m2，质量损失率（%）为(m1-m2)/m1； 
拉伸强度，断裂伸长率：按照ASTMD-882标准测试； 
遮光率：按照透射箱法进行测试。 
表1中列出了实施例1-5和对比例1-2的测试结果。 
表1实施例1-5和对比例1-2的测试结果 
Figure BDA00002936521300051
由表1中可以得知，实施例1-5保留了良好的力学性能的同时，相对于普通薄膜对比例1，具有了良好的降解性能，有效的降低了残膜量。另外，实施例1-5与对比例2相比还具有较好的遮光性能。 
以上显示和描述了本发明的基本原理、主要特征和优点。本行业的技术人员应该了解，上述实施例不以任何形式限制本发明，凡采用等同替换或等效变换的方式所获得的技术方案，均落在本发明的保护范围内。 

Claims (6)

1.一种农业用薄膜，包括多层膜，其特征在于：至少一层的外层膜由以下重量份数组分组成：聚乳酸10-20份，聚己内酯10-20份，直链低密度聚乙烯20-30份，聚丙烯40-50份，遮光剂1-5份；内层膜由以下重量份数组分组成：聚丙烯50-60份，乙烯-乙酸乙烯酯共聚物15-25份，低密度聚乙烯30-40份。
2.根据权利要求1所述的一种农业用薄膜，其特征在于：所述外层膜还可以由以下重量份数组成：聚乳酸-聚己内酯共聚物25-35份，直链低密度聚乙烯30-40份，聚丙烯55-65份，遮光剂1-5份。
3.根据权利要求1或2所述的一种农业用薄膜，其特征在于：所述遮光剂为二氧化钛或炭黑中的一种。
4.根据权利要求1或2所述的一种农业用薄膜，其特征在于：所述聚乳酸的数均分子量为50000-80000；所述聚己内酯的数均分子量为50000-80000；所述直链低密度聚乙烯的数均分子量为10000-20000；所述聚丙烯的数均分子量为8500-10000；所述低密度聚乙烯的数均分子量为10000-20000。
5.根据权利要求1所述的一种农业用薄膜，其特征在于：所述乙烯-乙酸乙烯酯共聚物中乙酸乙烯酯的质量含量为25~35%，乙烯-乙酸乙烯酯共聚物的数均分子量为30000-50000。
6.根据权利要求2所述的一种农业用薄膜，其特征在于：所述聚乳酸-聚己内酯共聚物为无规共聚物，数均分子量为80000-100000。
CN2013100875507A 2013-03-19 2013-03-19 一种农业用薄膜 Pending CN103213363A (zh)