CN103205068B - 一种抗静电浸塑制品及其制备方法 - Google Patents
一种抗静电浸塑制品及其制备方法 Download PDFInfo
- Publication number
- CN103205068B CN103205068B CN201310043427.5A CN201310043427A CN103205068B CN 103205068 B CN103205068 B CN 103205068B CN 201310043427 A CN201310043427 A CN 201310043427A CN 103205068 B CN103205068 B CN 103205068B
- Authority
- CN
- China
- Prior art keywords
- leaching
- mould
- retardant
- fire
- antistatic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种具有阻燃、抗静电性能的浸塑制品及其制备方法。其成分包括PVC树脂50-100份、增塑剂20-100份、抗静电剂1-15份、分散剂0.5-15份,稳定剂0.2-10份,将上述成分配成浸塑液;将模具预热到120-250℃后浸入浸塑液,1-120秒后取出;将附着有塑胶的模具在200-550℃下塑化2-80秒后取出冷却5-60秒,脱模后制得具有阻燃、抗静电性能的浸塑制品。通过这种方法制备的浸塑制品表面电阻率为105-109Ω,垂直燃烧达到UL94-V0级标准,具有较好的抗静电性和阻燃性。
Description
技术领域
本发明涉及一种聚氯乙烯成型制品及制备方法,特别是一种具有阻燃、抗静电聚氯乙烯浸塑制品及其制备方法。此类制品可广泛应用于各类需要阻燃、消除静电的器具和需要静电保护的各种制品,如航天光纤模块、电路装置、导静电装置、高速连接器、通信光纤行业、激光器插芯、微同轴、光缆器件的保护等。
背景技术
PVC是一种应用非常广泛的通用塑料,被用来制成各种制品。但PVC是一种绝缘性很好的材料,也较易产生静电,不适合在抗静电要求高的场合使用。同时,PVC在燃烧时会分解产生HCl,从而产生大量烟雾,因而对PVC进行阻燃抑烟也非常重要。关于PVC阻燃和抗静电方面的相关专利也比较多,如CN102786754A公开了一种沼气用阻燃抗静电增韧PVC管材,CN1699462A公开了一种抗静电、耐候灯饰用PVC亚光片材及其制备方法,CN102127275A公开了一种阻燃PVC泡沫塑料板用组合物及其制品与制备方法,CN1583869A公开了一种PVC阻燃抑烟剂、由其制备的PVC及其制备方法,。
浸塑是一种塑料涂覆工艺,就是将塑料涂装在基体上。根据是否需要加热分为热浸塑和冷浸塑,按照浸塑的原材料可分为液体浸塑和粉体浸塑。浸塑工艺具有设备简单、加工成本低、成型容易、可加工各种外形等特点而被广泛使用。但利用浸塑方法来制备PVC制品的专利并不多,如CN1709963A公开了聚氯乙烯热浸塑配制品及其生产方法和应用。至今未见使用浸塑的方法来制备阻燃、抗静电制品的专利。
发明内容
本发明的目的是为了提供一种阻燃、抗静电PVC制品及其制备方法。使用本专利提供的方法可以简单、快速的制备阻燃、抗静电PVC制品。
本发明的目的是通过以下技术方案来实现的:
本发明涉及一种具有阻燃、抗静电性能的浸塑制品,其特征在于包括以下组分及重量份数:
优选的,所述的PVC树脂为PVC糊树脂,也可以是PVC糊树脂与掺混树脂组成的混合体系,掺混树脂所占的比例为0-50%。
进一步优选的,所述的增塑剂包括:邻苯二甲酸酯类、对苯二甲酸酯类、脂肪酸酯类、磷酸酯类、环氧酯类、聚酯类、偏苯三酸酯类、均苯四酸酯类、含氯增塑剂、烷基磺酸蜡类、多元醇酯类、离子液体等的一种或多种。
优选的,所述的抗静电剂包括:导电炭黑、石墨、碳纳米管、纳米碳纤维、石墨烯、金属粉末、金属氧化物、镀有金属的导电填料、导电云母等的一种或多种。
进一步优选的,所述的抗静电剂是微米、纳米或者微米与纳米混合的材料。
优选的,所述的分散剂主要包括含酸性基团聚合物、含酸性基团聚合物盐、具有颜料亲和基团的共聚酯、含颜料亲和基团高分子共聚物、羟基官能羧酸酯、丙烯酸共聚物、含颜料亲和基团的磷酸盐、含颜料亲和基团的烷醇胺、特殊结构的丙烯酸共聚物、多元羧酸的羟基铵盐、多元胺酰胺的磷酸盐、高分子聚胺酸与烷胺等的一种或多种。
优选的,所述的稳定剂主要包括有机锡、羧酸镉、羧酸锌、羧酸钙、羧酸钡、钙锌稳定剂、钡锌稳定剂、钡镉稳定剂、钡镉锌稳定剂等的一种或多种。
本发明所涉及的一种制备具有阻燃、抗静电性能的浸塑制品的方法,其特征在于包括如下步骤:
将PVC树脂、增塑剂、分散剂、稳定剂混合,再加入抗静电剂,混合均匀配成浸塑液,将模具预热到120-250℃后浸入浸塑液,1-120秒后取出;将附着有塑胶的模具在200-550℃下塑化2-80秒后取出冷却5-60秒,脱模后制得具有阻燃、抗静电性能的浸塑制品。
与现有技术相比,本发明具有如下创新之处:
1、将导电效率高的无机抗静电剂引入到浸塑工艺中,有利于制品电阻的降低,从而实现较好的抗静电效果;
2、分散剂的加入使抗静电剂分散更加均匀,同时也降低了粘度,因而可以加入更多的静电剂,更大程度地降低制品的电阻率;
3、本发明中使用的抗静电剂既能起到降低电阻的作用,同时还起到了阻燃抑烟的作用。
具体实施方式
下面结合具体实施例对本发明进行详细说明。以下实施例将有助于本领域的技术人员进一步理解本发明,但不以任何形式限制本发明。应当指出的是,对本领域的普通技术人员来说,在不脱离本发明构思的前提下,还可以做出若干变形和改进。这些都属于本发明的保护范围。
实施例1
本实施例涉及一种具有阻燃、抗静电性能的浸塑制品,包括表1所示的组分和重量份数。
1、把上述原料(除抗静电剂外)混合,再加入抗静电剂,混合均匀制得阻燃、抗静电浸塑液,在25℃下粘度为2600cps;所述的碳纳米管为纳米材料;
2、先将所需外型的模具,加热至120℃,然后把模具浸入浸塑液中,120秒后将模具取出;
3、把覆有塑胶层的模具放入200℃的烘箱中,塑化成型80秒;
4、把塑化成型完毕后的制品,从烘箱取出冷却5秒,脱模得到阻燃、抗静电浸塑制品。
所得浸塑制品表面电阻率为4×108Ω2,垂直燃烧达到UL94-V0级标准。
实施例2
本实施例涉及一种具有阻燃、抗静电性能的浸塑制品,包括表1所示的组分和重量份数。
1、把上述原料(除抗静电剂外)混合,再加入抗静电剂,混合均匀制得阻燃、抗静电浸塑液,在25℃下粘度为3100cps;所述的导电云母为微米材料,导电银粉为纳米材料;
2、先将所需外型的模具,加热至190℃,然后把模具浸入浸塑液中,80秒后将模具取出;
3、把覆有塑胶层的模具放入300℃的烘箱中,塑化成型10秒;
4、把塑化成型完毕后的制品,从烘箱取出冷却20秒,脱模得到阻燃、抗静电浸塑制品。
所得浸塑制品表面电阻率为6×107Ω,垂直燃烧达到UL94-V0级标准。
实施例3
本实施例涉及一种具有阻燃、抗静电性能的浸塑制品,包括表1所示的组分和重量份数。
1、把上述原料(除抗静电剂外)混合,再加入抗静电剂,混合均匀制得阻燃、抗静电浸塑液,在25℃下粘度为4350cps;所述的导电炭黑为纳米与微米按照1∶1的混合材料;
2、先将所需外型的模具,加热至250℃,然后把模具浸入浸塑液中,1秒后将模具取出;
3、把覆有塑胶层的模具放入550℃的烘箱中,塑化成型2秒;
4、把塑化成型完毕后的制品,从烘箱取出冷却45秒,脱模得到阻燃、抗静电浸塑制品。
所得浸塑制品表面电阻率为8×105Ω,垂直燃烧达到UL94-V0级标准。
实施例4
本实施例涉及一种具有阻燃、抗静电性能的浸塑制品,包括表1所示的组分和重量份数。
1、把上述原料(除抗静电剂外)混合,再加入抗静电剂,混合均匀制得阻燃、抗静电浸塑液,在25℃下粘度为3580cps;所述的导电炭黑为纳米与微米按照1∶1的混合材料;
2、先将所需外型的模具,加热至180℃,然后把模具浸入浸塑液中,50秒后将模具取出;
3、把覆有塑胶层的模具放入250℃的烘箱中,塑化成型10秒;
4、把塑化成型完毕后的制品,从烘箱取出冷却15秒,脱模得到阻燃、抗静电浸塑制品。
所得浸塑制品表面电阻率为9×106Ω2,垂直燃烧达到UL94-V0级标准。
实施例5
本实施例涉及一种具有阻燃、抗静电性能的浸塑制品,包括表1所示的组分和重量份数。
1、把上述原料(除抗静电剂外)混合,再加入抗静电剂,混合均匀制得阻燃、抗静电浸塑液,在25℃下粘度为2860cps;所述的导电炭黑为毫米与微米按照1∶1的混合材料;
2、先将所需外型的模具,加热至180℃,然后把模具浸入浸塑液中,50秒后将模具取出;
3、把覆有塑胶层的模具放入250℃的烘箱中,塑化成型10秒;
4、把塑化成型完毕后的制品,从烘箱取出冷却15秒,脱模得到阻燃、抗静电浸塑制品。
所得浸塑制品表面电阻率为1.5×109Ω,垂直燃烧达到UL94-V0级标准。
对照例1
本对照例1包括表1所示的组分和重量份数。
1、把上述原料混合均匀制得浸塑液,在25℃下粘度为740cps;
2、先将所需外型的模具,加热至250℃,然后把模具浸入浸塑液中,1秒后将模具取出;
3、把覆有塑胶层的模具放入550℃的烘箱中,塑化成型2秒;
4、把塑化成型完毕后的制品,从烘箱取出冷却45秒,脱模得到浸塑制品。
所得浸塑制品表面电阻率为2.3×1011Ω,无阻燃效果。
对照例2
本对照例2包括表1所示的组分和重量份数。
1、把上述原料(除抗静电剂外)混合,再加入抗静电剂,混合均匀制得阻燃、抗静电浸塑液,在25℃下粘度远大于20000cps,接近凝胶状;所述的导电炭黑为纳米与微米按照1∶1的混合材料;
2、此粘度下无法采用浸塑工艺制备浸塑制品。
通过对照例1、对照例2与实施例3的对照说明,抗静电剂的加入可以明显的降低制品的电阻率,并起到阻燃作用,但抗静电剂的加入会使浸塑液粘度急剧增加,只有加入适当的分散剂才能使体系满足浸塑工艺条件,进而制备出阻燃、抗静电制品。
表1实施例、对照例中各组分及其重量份数
Claims (4)
1.一种具有阻燃、抗静电性能的浸塑制品,其特征在于包括以下组分及重量份数:
PVC树脂50-100
增塑剂20-100
抗静电剂1-15
分散剂0.5-15
稳定剂0.2-10,
其中,所述的抗静电剂包括导电炭黑、石墨、碳纳米管、纳米碳纤维、石墨烯、导电云母的一种或多种;所述的分散剂包括含酸性基团聚合物盐、含颜料亲和基团的磷酸盐、含颜料亲和基团的烷醇胺、多元羧酸的羟基铵盐、高分子聚胺酸的一种或多种;并且所述浸塑制品表面电阻率为105-109Ω,垂直燃烧达到UL94-V0级标准。
2.根据权利要求1所述的一种具有阻燃、抗静电性能的浸塑制品,其特征在于所述的PVC树脂为PVC糊树脂,也可以是PVC糊树脂与掺混树脂组成的混合体系,掺混树脂所占的比例为0-50%。
3.根据权利要求1所述的一种具有阻燃、抗静电性能的浸塑制品,其特征在于所述的增塑剂包括:邻苯二甲酸酯类、对苯二甲酸酯类、脂肪酸酯类、磷酸酯类、环氧酯类、聚酯类、偏苯三酸酯类、均苯四酸酯类、含氯增塑剂、烷基磺酸蜡类、多元醇酯类、离子液体的一种或多种。
4.根据权利要求1所述的一种具有阻燃、抗静电性能的浸塑制品,其特征在于所述的抗静电剂是微米、纳米或者微米与纳米混合的材料。