CN103058704B - 一种防火芯板及其生产方法 - Google Patents

一种防火芯板及其生产方法 Download PDF

Info

Publication number
CN103058704B
CN103058704B CN201210593152.8A CN201210593152A CN103058704B CN 103058704 B CN103058704 B CN 103058704B CN 201210593152 A CN201210593152 A CN 201210593152A CN 103058704 B CN103058704 B CN 103058704B
Authority
CN
China
Prior art keywords
core board
magnesium chloride
fireproof core
clear water
fire protection
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201210593152.8A
Other languages
English (en)
Other versions
CN103058704A (zh
Inventor
刘福权
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU ZHONGTIAN FIRE FIGHTING EQUIPMENT CO Ltd
Original Assignee
JIANGSU ZHONGTIAN FIRE FIGHTING EQUIPMENT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU ZHONGTIAN FIRE FIGHTING EQUIPMENT CO Ltd filed Critical JIANGSU ZHONGTIAN FIRE FIGHTING EQUIPMENT CO Ltd
Priority to CN201210593152.8A priority Critical patent/CN103058704B/zh
Publication of CN103058704A publication Critical patent/CN103058704A/zh
Application granted granted Critical
Publication of CN103058704B publication Critical patent/CN103058704B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种防火芯板，其特征是：防火芯板的组成份：耐火水泥、无水氯化镁、轻烧粉、闭孔玻化微珠、工程纤维、早强剂、网格布、发泡剂、清水、石膏、无纺布，其重量％比：4∶16.3∶33∶2.5∶0.25∶0.62∶0.25∶0.32∶40∶2.5∶0.2。具有不燃、防火、防潮、耐腐蚀；环保、无毒、无味；轻质高强、隔热、保温；使用方便、可切、可刨、可锯。

Description

一种防火芯板及其生产方法
技术领域
本发明涉及一种防火材料，特别是一种防火芯板。
背景技术
目前，防火门产品大量采用“硅酸铝纤维材料”，由于硅酸铝产品在生产、使用过程中会产生纤维，有一定的刺激性，对人体的健康产生危害；在失火之后，还会产生大量的烟毒，致使人员塞息。
发明内容
为克服现有技术的不足，本发明提供一种新的环保型“轻质无机防火芯板”，具有不燃、防火、防潮、耐腐蚀；环保、无毒、无味；轻质高强、隔热、保温；使用方便、可切、可刨、可锯。
本发明解决问题的技术方案是：一种防火芯板，其特征是：防火芯板的组成份：耐火水泥、无水氯化镁、轻烧粉、闭孔玻化微珠、工程纤维、早强剂、网格布、发泡剂、清水、石膏、无纺布，其重量％比：525级耐火水泥∶99％无水氯化镁∶85％轻烧粉∶50-70目闭孔玻化微珠∶高强工程纤维∶早强剂∶耐碱网格布∶发泡剂∶pH值小于7的清水∶模型石膏∶无纺布==4∶16.3∶33∶2.5∶0.25∶0.62∶0.25∶0.32∶40∶2.5∶0.2。
其生产方法：
①首先将无水氯化镁溶解在准备好的清水中，把溶解的氯化镁水溶液、轻烧粉、耐火水泥按比例放入搅拌机中搅拌1分钟，加入闭孔玻化微珠、工程纤维、发泡剂、早强剂继续搅拌2分钟，再放入模型石膏搅拌1分钟，所得浆料备用。
②将上述浆料注入自带网格布和无纺布的带挤压装置的设备中，生产出带模的板材。
③将上述的带模板材放置一段时间，夏天4小时，冬天6小时，进行脱模，脱模后用压机压平，堆码、放平、养护3-5天后切边，进入烘干房烘干，待含水率降至8％以下即为成品，取出入成品库。
耐火水泥标号采用525级。
闭孔玻化微珠，其过筛目数为50-70目。
无水氯化镁为99％氯化镁。
轻烧粉为85％轻烧粉。
所用清水的pH值小于7。
本发明的有益的效果是，具有不燃、防火、防潮、耐腐蚀；环保、无毒、无味；轻质高强、隔热、保温；使用方便、可切、可刨、可锯。
具体实施方式
实施例：
取无水氯化镁19.8Kg置于49.5Kg清水中制成氯化镁水溶液，把制得的氯化镁水溶液和轻烧粉40Kg、耐火水泥4.8Kg放入搅拌机中搅拌1分钟，加入闭孔玻化微珠3Kg、工程纤维0.3Kg、发泡剂0.4Kg、早强剂0.78Kg继续搅拌2分钟，再放入模型石膏3Kg搅拌1分钟备用；将上述备好的浆料注入自带网格布0.3Kg和无纺布0.24Kg的带挤压装置的模型中，在模型中形成板块，将带模的板块放置一段时间，夏天放置4小时冬天放置6小时脱模，并用压机压平，再堆码、放平养护3-5天后切边，进入烘干房烘干，标准控制在含水率低于8％以下。
批量生产时可采用辊桶挤压式自动流水线设备生产出带模的板材，再将带模板材放置4-6小时，脱模，压平、堆码放平养护3-5天切边，进入烘干房烘干，达到含水率低于8％以下即为成品，进入成品库。
产品用途：
该防火芯板主要用于木质防火门、钢质防火门、防盗门中的填充材料，还广泛适用于家庭、消防隔音隔热要求高的宾馆、写字楼、商业购物中心、楼层隔间、学校、实验室、医院、火车站、机场、剧院、舞厅、娱乐城、工厂、活动房等多种内部装修隔墙、防火、隔热、隔音等。

Claims (7)

1.一种防火芯板，其特征是：防火芯板的组成份：耐火水泥、无水氯化镁、轻烧粉、闭孔玻化微珠、工程纤维、早强剂、网格布、发泡剂、清水、石膏、无纺布，其重量％比：
525级耐火水泥∶99％无水氯化镁∶85％轻烧粉∶50-70目闭孔玻化微珠∶高强工程纤维∶早强剂∶耐碱网格布∶发泡剂∶pH值小于7的清水∶模型石膏∶无纺布==4∶16.3∶33∶2.5∶0.25∶0.62∶0.25∶0.32∶40∶2.5∶0.2
2.按照权利要求1所述的防火芯板，其特征是：其生产方法：
①首先将无水氯化镁溶解在准备好的清水中，把溶解的氯化镁水溶液、轻烧粉、耐火水泥按比例放入搅拌机中搅拌1分钟，加入闭孔玻化微珠、工程纤维、发泡剂、早强剂继续搅拌2分钟，再放入模型石膏搅拌1分钟，所得浆料备用。
②将上述浆料注入自带网格布和无纺布的带挤压装置的设备中，生产出带模的板材。
③将上述的带模板材放置一段时间，夏天4小时，冬天6小时，进行脱模，脱模后用压机压平，堆码、放平、养护3-5天后切边，进入烘干房烘干，待含水率降至8％以下即为成品，取出入成品库。
3.按照权利要求1或2所述的防火芯板，其特征是：耐火水泥标号采用525级。
4.按照权利要求1或2所述的防火芯板，其特征是：闭孔玻化微珠，其过筛目数为50-70目。
5.按照权利要求1或2所述的防火芯板，其特征是：无水氯化镁为99％氯化镁。
6.按照权利要求1或2所述的防火芯板，其特征是：轻烧粉为85％轻烧粉。
7.按照权利要求1或2所述的防火芯板，其特征是：所用清水的pH值小于7。
CN201210593152.8A 2012-12-26 2012-12-26 一种防火芯板及其生产方法 Expired - Fee Related CN103058704B (zh)