CN102718542A - 一种防火外墙保温材料及其制备方法 - Google Patents

一种防火外墙保温材料及其制备方法 Download PDF

Info

Publication number
CN102718542A
CN102718542A CN2012100593296A CN201210059329A CN102718542A CN 102718542 A CN102718542 A CN 102718542A CN 2012100593296 A CN2012100593296 A CN 2012100593296A CN 201210059329 A CN201210059329 A CN 201210059329A CN 102718542 A CN102718542 A CN 102718542A
Authority
CN
China
Prior art keywords
insulation material
fire prevention
preparation
nano
wall heat
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012100593296A
Other languages
English (en)
Other versions
CN102718542B (zh
Inventor
白庆法
于欣
白宝刚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 201210059329 priority Critical patent/CN102718542B/zh
Publication of CN102718542A publication Critical patent/CN102718542A/zh
Application granted granted Critical
Publication of CN102718542B publication Critical patent/CN102718542B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种防火外墙保温材料，包括高锰酸钾、硬脂酸钙、聚丙烯纤维、硫铝酸盐水泥、粉煤灰、纳米水泥添加剂、水以及双氧水；能达到A级的防火性能，能够降低导热系数达到国家节能要求。

Description

一种防火外墙保温材料及其制备方法
技术领域
本发明涉及一种保温材料，特别是一种防火外墙保温材料及其制备方法。
背景技术
2009年10月公安部与住房和城乡***联合下发了《民用建筑外保温***及外墙装饰防火暂行规定》，对保温材料的防火性能进行了要求。2011年3月15日公安消防总局发文明确规定，在今后民用建筑外墙保温必须使用不燃的A级材料。
现有技术中一直没有发现既防火又轻且导热系数低的好配方。目前市场上很多无机保温材料虽然防火但是密度大、导热系数高、防水性差，远远达不到节能指标，而有机保温板虽然具有密度小、可加工性好、保温隔热效果好，但是产品本身易燃，安全性能低。像岩棉、矿棉和玻璃棉的无机材料，保温性能好、防火性能高可以达到A级标准，但价格高、吸水率高、施工不方便。因此需要一种配方简单、制备方便、防火及保温性能优良的建筑外墙材料。
发明内容
本发明的目的是提供一种配方简单、制备方便的防火外墙保温材料，具有优良的防火及保温性能。
本发明提供了一种防火外墙保温材料，包括：硫铝酸盐水泥、粉煤灰以及水，还包括高锰酸钾、硬脂酸钙、聚丙烯纤维、纳米水泥添加剂以及双氧水。
进一步优选，其组分按重量份组成为：硫铝酸盐水泥500-600份、粉煤灰250-350份、水200-300份、高锰酸钾1-2份、硬脂酸钙10-20份、聚丙烯纤维5-10份、纳米水泥添加剂200-220份以及双氧水30-50份。
进一步优选，所述双氧水的质量百分含量为15-30％。
进一步优选，所述纳米水泥添加剂为纳米硅、甲基丙烯酸甲酯和苯乙烯的混合物，所述纳米硅、甲基丙烯酸甲酯和苯乙烯的质量比为1∶10∶10。
本发明还提供了一种防火外墙保温材料的制备方法，将按比例配置的硫铝酸盐水泥、粉煤灰、水、高锰酸钾、硬脂酸钙、聚丙烯纤维和纳米水泥添加剂混合进行第一搅拌均匀后，加入双氧水继续第二搅拌后浇注于模具中，室温静置及脱模后形成产品。
进一步优选，第一搅拌时间为3-5分钟；第二搅拌时间为3-5分钟；所述静置时间为35-45分钟；所述第一搅拌和第二搅拌的操作温度为45℃。
本发明还提供了一种防火外墙保温板，使用上述防火外墙保温材料制得。
使用本发明所述防火外墙保温材料，具有如下优点：配方简单，易操作、发泡均匀、产品密度小、导热系数低，既能达到节能标准，又能达到A级防火要求。
附图说明
图1是本发明所述一种防火外墙保温板的制备流程图。
具体实施方式
根据图1所述本发明一种防火外墙保温材料的制备方法，将按比例配置的硫铝酸盐水泥、粉煤灰、水、高锰酸钾、硬脂酸钙、聚丙烯纤维和纳米水泥添加剂混合进行第一搅拌均匀后，加入双氧水继续第二搅拌后浇注于模具中，所述第一搅拌和第二搅拌的操作温度为45℃。室温静置及脱模后形成产品。所述纳米水泥添加剂为纳米硅、甲基丙烯酸甲酯和苯乙烯的混合物，所述纳米硅、甲基丙烯酸甲酯和苯乙烯的质量比为1∶10∶10。
实施例1：
按重量份，将500份硫铝酸盐水泥、350份粉煤灰、200份水、1份高锰酸钾、20份硬脂酸钙、5份聚丙烯纤维和220份纳米水泥添加剂混合进行第一搅拌5分钟，搅拌均匀后，加入50份15％(质量百分含量)的双氧水继续第二搅拌5分钟后，浇注于模具中，室温静置35分钟，脱模后进行切割，养护和检验后形成防火外墙保温板。
实施例2：
按重量份，将550份硫铝酸盐水泥、300份粉煤灰、250份水、1.5份高锰酸钾、10份硬脂酸钙、10份聚丙烯纤维和200份纳米水泥添加剂混合进行第一搅拌5分钟，搅拌均匀后，加入40份30％(质量百分含量)的双氧水继续第二搅拌3分钟后，浇注于模具中，室温静置40分钟，脱模后进行切割，养护和检验后形成防火外墙保温板。
实施例3：
按重量份，将600份硫铝酸盐水泥、250份粉煤灰、200份水、2份高锰酸钾、10份硬脂酸钙、5份聚丙烯纤维和200份纳米水泥添加剂混合进行第一搅拌3分钟，搅拌均匀后，加入50份30％(质量百分含量)的双氧水继续第二搅拌3分钟后，浇注于模具中，室温静置45分钟，脱模后进行切割，养护和检验后形成防火外墙保温板。
实施例1-3制得的保温板，发泡均匀、产品密度小、导热系数低，防火性能高可以达到A级标准，且制备简单快捷。

Claims (10)

1.一种防火外墙保温材料，包括：硫铝酸盐水泥、粉煤灰以及水，其特征在于，还包括高锰酸钾、硬脂酸钙、聚丙烯纤维、纳米水泥添加剂以及双氧水。
2.根据权利要求1所述的防火外墙保温材料，其特征在于，其组分按重量份组成为：硫铝酸盐水泥500-600份、粉煤灰250-350份、水200-300份、高锰酸钾1-2份、硬脂酸钙10-20份、聚丙烯纤维5-10份、纳米水泥添加剂200-220份以及双氧水30-50份。
3.根据权利要求1或2所述的防火外墙保温材料，其特征在于，所述双氧水的质量百分含量为15-30％。
4.根据权利要求1或2所述的防火外墙保温材料，其特征在于，所述纳米水泥添加剂为纳米硅、甲基丙烯酸甲酯和苯乙烯的混合物，所述纳米硅、甲基丙烯酸甲酯和苯乙烯的质量比为1∶10∶10。
5.一种如权利要求1-4任一所述的防火外墙保温材料的制备方法，其特征在于：将按比例配置的硫铝酸盐水泥、粉煤灰、水、高锰酸钾、硬脂酸钙、聚丙烯纤维和纳米水泥添加剂混合进行第一搅拌均匀后，加入双氧水继续第二搅拌后浇注于模具中，室温静置及脱模后形成产品。
6.根据权利要求5所述的制备方法，其特征在于，第一搅拌时间为3-5分钟。
7.根据权利要求6所述的制备方法，其特征在于，第二搅拌时间为3-5分钟。
8.根据权利要求7所述的制备方法，其特征在于，所述静置时间为35-45分钟。
9.根据权利要求8所述的制备方法，其特征在于，所述第一搅拌和第二搅拌的操作温度为45℃。
10.一种防火外墙保温板，其特征在于使用如权利要求1-4任一所述防火外墙保温材料制得。
CN 201210059329 2012-03-08 2012-03-08 一种防火外墙保温材料及其制备方法 Expired - Fee Related CN102718542B (zh)