CN103013292A - 一种耐腐蚀环氧树脂漆 - Google Patents
一种耐腐蚀环氧树脂漆 Download PDFInfo
- Publication number
- CN103013292A CN103013292A CN2012105344092A CN201210534409A CN103013292A CN 103013292 A CN103013292 A CN 103013292A CN 2012105344092 A CN2012105344092 A CN 2012105344092A CN 201210534409 A CN201210534409 A CN 201210534409A CN 103013292 A CN103013292 A CN 103013292A
- Authority
- CN
- China
- Prior art keywords
- epoxy resin
- transformer
- corrosion
- parts
- resistant epoxy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种耐腐蚀环氧树脂漆,它是由下述重量份的原料组成:E-20环氧树脂132-145、改性酚醛树脂21-25、1,2,3-苯骈三氮唑18-24、聚丙烯酸2-3、乙二醇1-3、季戊四醇三丙烯酸酯2-4、N-2-(氨乙基)-3-氨丙基三甲氧基硅烷0.8-1、聚丙烯酸乙酯1-1.2、过氧化苯甲酸叔丁酯0.2-0.4、乳化剂OP-100.6-1、消泡剂聚二甲基硅氧烷0.1-0.2、十二烷基二甲基叔胺0.5-0.8;本发明采用了改性环氧树脂制备的水性乳液成品作为主成膜物质,使得整个生产过程平稳易控,成品一致性大幅提高,批次稳定性好;选用乙二醇和季戊四醇三丙烯酸酯作为溶剂,制成品气味大幅改良,对生产使用减少了环境污染。
Description
技术领域
本发明主要涉及一种耐腐蚀环氧树脂漆,属于化工领域。
背景技术
环氧树脂漆由于具有优异的耐湿抗变形性能,被广泛应用于特殊线圈( 如DY 线圈、电动工具线圈、各种变压器线圈) 线材的制造。采用传统方法生产的环氧树脂漆存在以下缺陷:采用普通工业酚、二甲苯作溶剂,气味大,刺激性强,污染环境;合成过程难以控制分子量,致使漆质批次不均,影响批次稳定性;工艺幅度小,应用涂制线材时,炉温/ 转速影响很大,对涂覆应用要求高,难以形成光洁表面;粘结力偏小,耐热性差。
发明内容
本发明目的就是为了弥补已有技术的缺陷,提供一种耐腐蚀环氧树脂漆。
本发明是通过以下技术方案实现的:
一种耐腐蚀环氧树脂漆,它是由下述重量份的原料组成:
E-20环氧树脂132-145、改性酚醛树脂21-25、1,2,3-苯骈三氮唑1-2、聚丙烯酸2-3、乙二醇10-13、季戊四醇三丙烯酸酯2-4、N-2-(氨乙基)-3-氨丙基三甲氧基硅烷0.8-1、聚丙烯酸乙酯1-1.2、过氧化苯甲酸叔丁酯 0.2-0.4、乳化剂OP-10 0.6-1、消泡剂聚二甲基硅氧烷0.1-0.2、十二烷基二甲基叔胺0.5-0.8;
所述的改性酚醛树脂的制备方法为:将5-7份酚醛树脂加入到18-20份苯乙烯、4-7份甲醇中,加热75-85℃至酚醛树脂全部溶解,再向其中加入4,4′-二苯基甲烷二异氰酸酯2-4份、聚丙烯酸酯2-4份、丙烯酸2-4份、乙烯基三甲氧基硅烷1-3份、癸二酸二辛酯1-3份、十二烷基苯磺酸钠0.5-1份、过硫酸钠0.2-0.3份,搅拌均匀反应0.9-1.2小时,得到改性酚醛树脂。
所述的耐腐蚀环氧树脂漆及其制备方法,其特征在于包括以下步骤:
(1)按配方称取各原料成分,混合加热至8 5-90℃,搅拌反应40-50分钟;
(2)冷却、研磨、过滤,即得耐腐蚀环氧树脂漆。
一种耐腐蚀环氧树脂漆,它用在变压器上的浸漆方法为:
(1)将本发明的耐腐蚀环氧树脂漆倒入配料容器内,缓缓加入季戊四醇三丙烯酸酯稀释,用BZ-4杯测量粘度,满足所需的粘度后,停止稀释,将配好的漆倒入浸槽内;
(2)将变压器整齐的摆放在浸渍筛上;
(3)将排好的变压器浸渍筛吊入浸槽内浸泡4-6分钟,然后吊出滴漆8-10分钟;
(4)将滴漆完毕的插针式变压器摆放在带有铁板的铁筛子上,然后将铁筛子一层一层叠起于手推车上,然后推置于烘箱中烘,在温度为75-95℃下烘2-2.5小时;滴漆完毕的端子线式变压器挂到架子上在通风处风干1.5-2小时,然后推置于烘箱中烘,在温度为65-85℃下,烘2-2.5小时;
(5)出箱清理:将烘干后的变压器趁热出箱,清楚变压器各处的余漆和漆瘤,同时趁热铁铭牌和标签。
变压器烘干后对有端子线引出的变压器应趁热将线理顺,对于插针式引出的变压器接线柱若浸到漆,需入锡炉中沾锡,吃锡面应全面、光滑、无毛刺、无虚焊、骨架无烫伤、损坏现象。
本发明的优点是:
本发明采用了改性环氧树脂制备的水性乳液成品作为主成膜物质,使得整个生产过程平稳易控,成品一致性大幅提高,批次稳定性好;选用乙二醇和季戊四醇三丙烯酸酯作为溶剂,制成品气味大幅改良,对生产使用减少了环境污染;耐热性的改性酚醛树脂加入,大幅提升了漆膜固化后的耐热等级,提高了最终成品的使用寿命;偶联剂N-2-(氨乙基)-3-氨丙基三甲氧基硅烷的加入,提高了与基材的粘结强度及线材涂覆的表面光洁度,再加上其余各种助剂的配合,最终赋予成品良好的表面质量,理想的抗湿变形性,优异的耐油、抗湿特性及粘结强度。
具体实施方式
实施例1
一种耐腐蚀环氧树脂漆,它是由下述重量份(公斤)的原料组成:
E-20环氧树脂132、改性酚醛树脂25、1,2,3-苯骈三氮唑1、聚丙烯酸2、乙二醇12、季戊四醇三丙烯酸酯4、N-2-(氨乙基)-3-氨丙基三甲氧基硅烷0.8、聚丙烯酸乙酯1.2、过氧化苯甲酸叔丁酯 0.4、乳化剂OP-10 0.6、消泡剂聚二甲基硅氧烷0.1、十二烷基二甲基叔胺0.8;
所述的改性酚醛树脂的制备方法为:将5公斤酚醛树脂加入到18公斤苯乙烯、4公斤甲醇中,加热75-85℃至酚醛树脂全部溶解,再向其中加入4,4′-二苯基甲烷二异氰酸酯2公斤、聚丙烯酸酯2公斤、丙烯酸2公斤、乙烯基三甲氧基硅烷1公斤、癸二酸二辛酯1公斤、十二烷基苯磺酸钠0.5公斤、过硫酸钠0.2公斤,搅拌均匀反应0.9-1.2小时,得到改性酚醛树脂。
耐腐蚀环氧树脂漆及其制备方法,其特征在于包括以下步骤:
(1)按配方称取各原料成分,混合加热至8 5-90℃,搅拌反应40-50分钟;
(2)冷却、研磨、过滤,即得耐腐蚀环氧树脂漆。
一种耐腐蚀环氧树脂漆,它用在变压器上的浸漆方法为:
(1)将本发明的耐腐蚀环氧树脂漆倒入配料容器内,缓缓加入季戊四醇三丙烯酸酯稀释,用BZ-4杯测量粘度,满足所需的粘度后,停止稀释,将配好的漆倒入浸槽内;
(2)将变压器整齐的摆放在浸渍筛上;
(3)将排好的变压器浸渍筛吊入浸槽内浸泡6分钟,然后吊出滴漆10分钟;
(4)将滴漆完毕的插针式变压器摆放在带有铁板的铁筛子上,然后将铁筛子一层一层叠起于手推车上,然后推置于烘箱中烘,在温度为95℃下烘2.5小时;滴漆完毕的端子线式变压器挂到架子上在通风处风干1.5小时,然后推置于烘箱中烘,在温度为85℃下,烘2.5小时;
(5)出箱清理:将烘干后的变压器趁热出箱,清楚变压器各处的余漆和漆瘤,同时趁热铁铭牌和标签。
变压器烘干后对有端子线引出的变压器应趁热将线理顺,对于插针式引出的变压器接线柱若浸到漆,需入锡炉中沾锡,吃锡面应全面、光滑、无毛刺、无虚焊、骨架无烫伤、损坏现象。
性能测试:
1、外观:清澈透明,无杂质无气泡;
2、粘度:1130mpa.s( 旋转粘度计/30±1℃ ) ;
3、耐热性:再软化温度为187℃;
4、粘结强度(N/mm2):9.7;
5、抗湿变性(%):1.3
6、耐变压器油(1000h/105℃):漆膜无损坏。
Claims (4)
1.一种耐腐蚀环氧树脂漆,其特征在于它是由下述重量份的原料组成:
E-20环氧树脂132-145、改性酚醛树脂21-25、1,2,3-苯骈三氮唑1-2、聚丙烯酸2-3、乙二醇10-13、季戊四醇三丙烯酸酯2-4、N-2-(氨乙基)-3-氨丙基三甲氧基硅烷0.8-1、聚丙烯酸乙酯1-1.2、过氧化苯甲酸叔丁酯 0.2-0.4、乳化剂OP-10 0.6-1、消泡剂聚二甲基硅氧烷0.1-0.2、十二烷基二甲基叔胺0.5-0.8;
所述的改性酚醛树脂的制备方法为:将5-7份酚醛树脂加入到18-20份苯乙烯、4-7份甲醇中,加热75-85℃至酚醛树脂全部溶解,再向其中加入4,4′-二苯基甲烷二异氰酸酯2-4份、聚丙烯酸酯2-4份、丙烯酸2-4份、乙烯基三甲氧基硅烷1-3份、癸二酸二辛酯1-3份、十二烷基苯磺酸钠0.5-1份、过硫酸钠0.2-0.3份,搅拌均匀反应0.9-1.2小时,得到改性酚醛树脂。
2.一种如权利要求1所述的耐腐蚀环氧树脂漆及其制备方法,其特征在于包括以下步骤:
(1)按配方称取各原料成分,混合加热至8 5-90℃,搅拌反应40-50分钟;
(2)冷却、研磨、过滤,即得耐腐蚀环氧树脂漆。
3.根据权利要求1所述的一种耐腐蚀环氧树脂漆,其特征在于,它用在变压器上的浸漆方法为:
(1)将本发明的耐腐蚀环氧树脂漆倒入配料容器内,缓缓加入季戊四醇三丙烯酸酯稀释,用BZ-4杯测量粘度,满足所需的粘度后,停止稀释,将配好的漆倒入浸槽内;
(2)将变压器整齐的摆放在浸渍筛上;
(3)将排好的变压器浸渍筛吊入浸槽内浸泡4-6分钟,然后吊出滴漆8-10分钟;
(4)将滴漆完毕的插针式变压器摆放在带有铁板的铁筛子上,然后将铁筛子一层一层叠起于手推车上,然后推置于烘箱中烘,在温度为75-95℃下烘2-2.5小时;滴漆完毕的端子线式变压器挂到架子上在通风处风干1.5-2小时,然后推置于烘箱中烘,在温度为65-85℃下,烘2-2.5小时;
(5)出箱清理:将烘干后的变压器趁热出箱,清楚变压器各处的余漆和漆瘤,同时趁热铁铭牌和标签。
4.根据权利要求3所述的耐腐蚀环氧树脂漆用在变压器上的浸漆方法,其特征在于变压器烘干后对有端子线引出的变压器应趁热将线理顺,对于插针式引出的变压器接线柱若浸到漆,需入锡炉中沾锡,吃锡面应全面、光滑、无毛刺、无虚焊、骨架无烫伤、损坏现象。