CN105419655B - 一种全息电化铝烫印胶及其制备方法 - Google Patents
一种全息电化铝烫印胶及其制备方法 Download PDFInfo
- Publication number
- CN105419655B CN105419655B CN201510965780.8A CN201510965780A CN105419655B CN 105419655 B CN105419655 B CN 105419655B CN 201510965780 A CN201510965780 A CN 201510965780A CN 105419655 B CN105419655 B CN 105419655B
- Authority
- CN
- China
- Prior art keywords
- kilograms
- resin
- glue
- stirring
- container
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种全息电化铝烫印胶及其制备方法，该发明的烫印胶的配方由聚丙烯酸树脂、甲基丙烯酸乙酯、聚酯树脂、EVA树脂、松香树脂、填充剂、助剂与溶剂组成，利用体系中各种树脂的不同特点，能满足多种基材表面的实现良好的上烫性，对基膜和被烫印基材具有双重强附着力，脆性适中，分切性较好，不易产生“飞金”、缺笔断划和糊板等问题，而且适用范围广、生产成本低，在普通纸片及多种油墨处理的盒片表面均有较好的烫印性，适用于细线条和精密图案烫印。
Description
技术领域
本发明属于电化铝烫印工艺，尤其是涉及一种全息电化铝烫印胶及制备方法。
背景技术
电化铝结构一般由胶黏层(烫印胶层)、镀铝层、全息图案层、离型层(隔离层)与基膜层组成。电化铝烫印，是借助于加热加压条件，使电化铝薄膜的烫印胶层和离型层熔融成粘流态，镀铝层及全息图像层从PET基膜上剥离，将烫印胶层粘在基材(如烟包、酒包、证卡、布匹、皮革等)上，由于烫印胶迅速冷却固化，带有全息图案的镀铝层则牢牢烫印在承印品的表面。电化铝产品以其优良的视觉效果和独特的艺术性而备受人们青睐，尤其在印刷与防伪包装领域应用广泛。
但是，国产烫印胶因附着力不好，易发生飞金、糊板等，尤其在许多表面涂覆了硅油或蜡等难粘性涂层的材料表面，烫印胶的烫印性受到较大局限，这就迫使多数厂商不得采购价格昂贵的进口胶，增加了生产成本，因此，自主研制一种性能优异、使用广泛的高性能烫印胶势在必行。
发明内容
为了克服现有烫印胶的不足，本发明旨在提供一种粘黏力强、用途广泛且性能优异的全息电化铝烫印胶以及制备该烫印胶的方法。
本发明采用的技术方案是：
一种全息电化铝烫印胶，由以下重量份的成分组成：聚丙烯酸甲酯3～10份，甲基丙烯酸乙酯3～10份，聚酯树脂5～15份，EVA树脂0.5～3份，松香树脂1～5份，填充剂1～10份，助剂0.5～1份，溶剂50～80份。
所述填充剂为气相二氧化硅；助剂为邻苯二甲酸二丁酯；溶剂为甲苯、丁酮、乙酸乙酯，且三者占烫印胶总重量的百分比分别为20％～30％、25％～35％、10％～20％。
所述聚酯树脂是一种微黄透明片状物质，分子量为17000，玻璃化温度为56℃，表面密度1.26g/cm2。
所述的EVA树脂是一种白色粉末状物质，VA含量为28％，熔融指数为150。
所述的松香树脂是原脂松香，软化点为75℃～80℃。
一种制备上述全息电化铝烫印胶的方法，其具体步骤为：
①将细小粉末状聚丙烯酸甲酯与甲基丙烯酸乙酯以及乙酸乙酯、丁酮加入搅拌容器内，加热至25℃～35℃，进行搅拌溶解，搅拌速度为300～500r/min，搅拌时间30～40min至丙烯酸树脂完全溶解分散，制成丙烯酸溶液于容器中密封备用；
②将颗粒状EVA树脂及甲苯、丁酮加入搅拌容器内，加热至40℃～50℃进行搅拌溶解，搅拌速度600～700r/min，搅拌时间50～60min至EVA树脂完全溶解分散，制成EVA溶液于容器中密封备用；
③将片状聚酯树脂及丁酮加入搅拌容器内，加热至25℃～35℃进行搅拌溶解，搅拌速度300～400r/min，搅拌时间30～40min至聚酯树脂完全溶解分散，制成聚酯树脂溶液于容器中密封备用；
④将块状松香树脂及丁酮、乙酸乙酯加入搅拌容器内，常温搅拌溶解，搅拌速度300～400r/min，搅拌时间20～30min至松香树脂完全溶解分散，制成松香树脂溶液于容器中密封备用；
⑤将上述制备的丙烯酸溶液、EVA溶液、聚酯树脂溶液、松香树脂溶液加入容器中并搅拌混合均匀，加入气相二氧化硅、邻苯二甲酸二丁酯及甲苯，加热至40℃～50℃并进行搅拌分散，至邻苯二甲酸二丁酯与气相二氧化硅分散均匀后冷却至室温，即可制得全息电化铝烫印胶。
按照上述步骤制得的全息电化铝烫印胶，具有以下有益效果：
1、聚丙烯酸甲酯：硬度适中，具有很强的表面初粘性，适用范围广，对于油墨、铝层、塑料表面均有较好的附着力，而且韧性、耐磨性和光泽度佳，与其他组分相溶性好。
2、甲基丙烯酸乙酯：硬度适中，韧性好，也具有较好的表面初粘性和持粘性，对各种表面尤其是UV油墨表面附着力较好。
3、EVA树脂：有较好的柔韧性，耐候性和粘附力，用于调节配方的柔韧性。
4、聚酯树脂：有较好的熔融粘度、挠曲性和柔韧性，优良的耐候性、耐水性和弹性，使用温度范围宽，可用于多种表面，用于调节粘度和稳定性。
5、松香树脂：价格便宜，软化点低，粘性大，溶解性好，用于增加初粘，改进润湿和塑性。
6、邻苯二甲酸丁酯：用于增加配方树脂的韧性、延伸率，降低其内聚强度和弹性模量，改善胶层脆性，增进熔融流动，降低熔融温度。
7、气相二氧化硅用于改善胶水内聚力，增加胶黏剂强度和涂层排气性。
总之，该全息电化铝烫印胶附着力好、应用广泛且性能优异，有利于降低电化铝烫印工艺的生产成本。
具体实施方式
下面结合实例对本发明做进一步说明：
原料：
聚丙烯酸甲酯4.6公斤，甲基丙烯酸乙酯4.6公斤，聚酯树脂5.3公斤，EVA树脂0.7公斤，脂松香3.6公斤，气相二氧化硅4.6公斤，邻苯二甲酸丁酯2.1公斤，甲苯26公斤，丁酮30公斤，乙酸乙酯16公斤。
制备：
①将4.6公斤聚丙烯酸甲酯、4.6公斤甲基丙烯酸乙酯及乙酸乙酯10公斤、丁酮10公斤加入搅拌容器内，加热至25℃～35℃进行搅拌溶解，搅拌速度300～500r/min，搅拌时间30～40min至丙烯酸树脂完全溶解分散，制成丙烯酸溶液于容器中密封备用；
②将0.7公斤EVA树脂及10公斤甲苯、5公斤丁酮加入搅拌容器内，加热至40℃～50℃进行搅拌溶解，搅拌速度600～700r/min，搅拌时间50～60min至EVA树脂完全溶解分散，制成EVA溶液于容器中密封备用；
③将5.3公斤聚酯树脂及10公斤丁酮加入搅拌容器内，加热至25℃～35℃进行搅拌溶解，搅拌速度300～400r/min，搅拌时间30～40min至聚酯树脂完全溶解分散，制成聚酯树脂溶液于容器中密封备用；
④将3.6公斤原脂松香及5公斤丁酮、6公斤乙酸乙酯加入搅拌容器内，常温搅拌溶解，搅拌速度300～400r/min，搅拌时间20～30min至松香树脂完全溶解分散，制成松香树脂溶液于容器中密封备用；
⑤将上述丙烯酸溶液、EVA溶液、聚酯溶液、松香树脂溶液加入搅拌容器中混合均匀，加入助剂2.1公斤、气相二氧化硅4.6公斤和甲苯16公斤，加热至40℃～50℃进行搅拌分散，搅拌至气相二氧化硅和邻苯二甲酸丁酯分散均匀后冷却至室温，得全息电化铝烫印胶。
Claims (3)
1.一种全息电化铝烫印胶，由以下重量份的成分组成：聚丙烯酸甲酯4.6公斤，甲基丙烯酸乙酯4.6公斤，聚酯树脂5.3公斤，EVA树脂0.7公斤，原脂松香3.6公斤，气相二氧化硅4.6公斤，邻苯二甲酸丁酯2.1公斤，甲苯26公斤，丁酮30公斤，乙酸乙酯16公斤。
2.根据权利要求1所述的全息电化铝烫印胶，其特征在于：所述的EVA树脂的VA含量为28％，熔融指数为150。
3.制备如权利要求1所述一种全息电化铝烫印胶的方法，其特征在于：包括以下工艺步骤和工艺参数：
①将4.6公斤聚丙烯酸甲酯、4.6公斤甲基丙烯酸乙酯及乙酸乙酯10公斤、丁酮10公斤加入搅拌容器内，加热至25℃～35℃进行搅拌溶解，搅拌速度300～500r/min，搅拌时间30～40min至丙烯酸树脂完全溶解分散，制成丙烯酸溶液于容器中密封备用；
②将0.7公斤EVA树脂及10公斤甲苯、5公斤丁酮加入搅拌容器内，加热至40℃～50℃进行搅拌溶解，搅拌速度600～700r/min，搅拌时间50～60min至EVA树脂完全溶解分散，制成EVA溶液于容器中密封备用；
③将5.3公斤聚酯树脂及10公斤丁酮加入搅拌容器内，加热至25℃～35℃进行搅拌溶解，搅拌速度300～400r/min，搅拌时间30～40min至聚酯树脂完全溶解分散，制成聚酯树脂溶液于容器中密封备用；
④将3.6公斤原脂松香及5公斤丁酮、6公斤乙酸乙酯加入搅拌容器内，常温搅拌溶解，搅拌速度300～400r/min，搅拌时间20～30min至松香树脂完全溶解分散，制成松香树脂溶液于容器中密封备用；
⑤将上述丙烯酸溶液、EVA溶液、聚酯溶液、松香树脂溶液加入搅拌容器中混合均匀，加入邻苯二甲酸丁酯2.1公斤、气相二氧化硅4.6公斤和甲苯16公斤，加热至40℃～50℃进行搅拌分散，搅拌至气相二氧化硅和邻苯二甲酸丁酯分散均匀后冷却至室温，得全息电化铝烫印胶。