CN102838277A - Production process of honey peach CZ diamond - Google Patents
Production process of honey peach CZ diamond Download PDFInfo
- Publication number
- CN102838277A CN102838277A CN2012103433566A CN201210343356A CN102838277A CN 102838277 A CN102838277 A CN 102838277A CN 2012103433566 A CN2012103433566 A CN 2012103433566A CN 201210343356 A CN201210343356 A CN 201210343356A CN 102838277 A CN102838277 A CN 102838277A
- Authority
- CN
- China
- Prior art keywords
- water
- bores
- parts
- pearl base
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a production process of a honey peach CZ diamond. The honey peach CZ diamond comprises the following raw materials in parts by weight: 60-70 parts of SiO2, 0.5-1.5 parts of Al2O3, 0.5-2.5 parts of BaO, 1.5-5 parts of ZnO, 1.0-2.5 parts of B2O3, 3-8 parts of K2O3, 8-15 parts of Na2O, 0.5-1.5 parts of CaO, 0.3-1.5 parts of Se and 0.03-0.3 parts of S. The production process comprises the following steps of: smelting by a hot smelting kiln and classifying; discharging to obtain a CZ diamond bead blank; sequentially carrying out fire polishing by a fire polishing furnace, and grinding by a grinding machine; and grinding a plurality of cutting surfaces of the CZ diamond by a multi-faced grinding machine tool and chemically plating to obtain a CZ diamond finished product.
Description
Technical field
The present invention relates to water and bore the production technique field, mainly is that a kind of water of honey peach color bores production technique.
Background technology
Water bores as a kind of novel decorative article, because of material economy, the similar diamond of visual effect, receives very much people's welcome, is widely used in the ornaments designs such as clothes of fine quality, belt, satchel, wrist-watch, mobile phone.
Honey peach color water bores because of its color noble, plain, is loved by the people.But in the conventional production methods, generally be in plumbiferous basestocks side, to add tinting material cerium oxide, titanium oxide, Erbium trioxide, utilize cerium oxide, titanium oxide is painted that product yellowly; It is pink to utilize Erbium trioxide into, and two kinds of color stacks are coloured to the honey peach look with product, and the while is for ease of the eliminating of bubble in melting process; Also to add finings weisspiessglanz etc.; The finished product contain poisonous, noxiouss such as lead, antimony, easily use human body and environment are polluted injury, and contain cerium in the raw material; REEs such as erbium, raw materials cost is expensive.
Summary of the invention
The objective of the invention is that to bore raw materials for production poisonous, harmful in order to overcome in the prior art honey peach color water; Use pollution damage bigger; The high deficiency of cost of manufacture, and a kind of step that provides is simple, production technique is bored in environmental protection, production cost honey peach water low, quality of finished product good.
The technical scheme that the present invention adopted is: the production technique that a kind of honey peach water bores, and key step is following:
A, raw material are by following weight proportion: SiO
260-70 part, Al
2O
30.5-1.5 part, BaO 0.5-2.5 part, ZnO 1.5-5 part, B
2O
31.0-2.5 part, K
2O 3-8 part, Na
2O 8-15 part, CaO 0.5-1.5 part, Se 0.3-1.5 part, S 0.03-0.3 part;
B, slow preheating heat melting furnaces 5-7 days, hot melt kiln temperature progressively is increased to 1350-1500 ℃;
C, raw material proportionally required to mix process admixtion, admixtion is added in the hot melt kiln after the preheating, continue heating, after fusing under the 1350-1500 ℃ of high temperature, clarification, homogenizing 7-10 hour, form feed liquid;
D, feed liquid are by the 1000-1200 ℃ of insulation discharging of discharging road; Discharging is simultaneously to the charging of hot melt kiln equivalent; Discharging becomes water to bore pearl base band through mould compacting, naturally cooling, and water bores pearl base band and sends into crusher in crushing, sieves and remove the burr that water bores pearl base band, obtains water and bores the pearl base;
E, according to following weight ratio: water bores pearl base 90-110 part, carbon dust 2-5 part, Graphite Powder 99 5-10 part, water is bored pearl base and carbon dust, Graphite Powder 99 uniform mixing after, add fire by batch charger and throw ingle and throw 750-900 ℃ of fire throwing temperature, 20-30 minute fiery throwing time;
Water after f, fire are thrown bores the pearl base and adds in the sander, and adds recirculated water, and the 15-25 minute removal water of polishing bores pearl base surface-fire and throws bur; Water bores pearl base diameter when requiring size, prolongs the polishing time, extracts and measures water in real time and bore pearl base diameter, reach dimensional requirement after, stop polishing;
Water brill pearl base after g, the polishing is delivered to multiaspect grinding machine grinding water and is bored a plurality of tangent planes, and the warpization plating obtains water and is drilled to article again.
Above-mentioned raw materials comprises quartz sand powder, aluminum oxide powder, barium carbonate, oxide powder and zinc, Borax pentahydrate, salt of wormwood, soda ash, lime carbonate, selenium powder, sulphur.
Above-mentioned raw materials comprises quartz sand powder, aluminum oxide powder, barium carbonate, oxide powder and zinc, boric acid, salt of wormwood, soda ash, lime carbonate, selenium powder, sulphur.
Above-mentioned raw materials comprises quartz sand powder, aluminum oxide powder, barium carbonate, oxide powder and zinc, Borax pentahydrate, salt of wormwood, soda ash, lime carbonate, Sodium Selenite, sulphur.
Above-mentioned raw materials comprises quartz sand powder, aluminum oxide powder, barium carbonate, oxide powder and zinc, boric acid, salt of wormwood, soda ash, lime carbonate, Sodium Selenite, sulphur.
Compared with prior art, advantage of the present invention is:
1, SiO in the material composition
2Play skeleton function, and stablize the effect of other components; Al
2O
3Play skeleton function and prevent phase-splitting, crystallization effect; BaO plays and improves specific refractory power, improves proportion and smooth finish effect; ZnO improves specific refractory power and smooth finish; B
2O
3Play fluxing action, improve thermostability and chemicalstability; K
2O, Na
2O plays fluxing action, and utilizes its " two alkali effect " to improve smooth finish and transparency; CaO helps adjusting shaping speed; It is faint yellow to utilize cheap S that product into; Se red; Both stacks are coloured to the honey peach look, have replaced rare earth cerium oxide, Erbium trioxide and the titanium oxide of expensive painted, and production cost reduces greatly; And need not add poisonous, the noxiouss of heavy metal such as lead, arsenic, antimony in the production process, to using the injury of human body and environmental nonpollution;
2, the slow preheating of hot melt kiln high temperature helps the indeformable of kiln structure, increases the service life; The discharging road is incubated discharging by well heater, and feed liquid is incubated heating, and temperature decrease causes feed liquid cold excessively when avoiding feed liquid to be flowed out by the high temperature molten bath, influences quality product, helps the quality of improving the quality of products; Water bores the pearl base and in fire is thrown stove, by action of gravity upset and displacement takes place, and the pearl base becomes circle under surface tension effects, improves pearl base circularity, can satisfy the following process mill and highly necessary ask, and the pearl base of having avoided causing because of the circularity problem is scrapped, and reduces learies, improves yield rate; Sander polishing is removed pearl base epidermis fire and is thrown bur, and sanding operation saves time, laborsaving, and efficient is high, polishes simultaneously to pearl base dimensional requirement, helps improving the product size quality.
Embodiment
Below in conjunction with embodiment the present invention is done to further describe, but the present invention is not limited only to following embodiment.
Embodiment one:
The production technique that a kind of honey peach water bores, key step is following:
A, raw material are joined choosing by following weight ratio: SiO
2: 65 parts; Al
2O
3: 1 part; BaO:2 part; ZnO:3 part; B
2O
3: 2 parts; K
2O:6 part; Na
2O:10 part; CaO:1 part; Se:0.7 part; S:0.09 part;
B, with various raw material pulverizing, proportionally require to mix, process admixtion;
C, admixtion is added in the hot melt kiln, fusing under 1400 ℃ of high temperature, and through forming feed liquid after clarification, the homogenizing;
D, feed liquid become water to bore blank by the insulation discharging of discharging road through mould compacting, naturally cooling;
E, according to following weight ratio: water bores 100 parts of pearl bases, 8 parts of carbon dusts, 8 parts of Graphite Powder 99s, water is bored blank and carbon dust, Graphite Powder 99 uniform mixing after, add fire by batch charger and throw the ingle throwing;
Water after f, fire are thrown bores in the pearl base adding sander, and adds recirculated water, and the sander polishing is removed water and bored pearl base surface-fire throwing bur;
Water brill pearl base after g, the polishing is delivered to multiaspect grinding machine grinding water and is bored a plurality of tangent planes, obtains water and is drilled to article.
Embodiment two:
The production technique that a kind of honey peach water bores, key step is following:
A, raw material are joined choosing by following weight ratio: SiO
260 parts, Al
2O
30.5 part, 0.5 part of BaO, 1.5 parts of ZnO, B
2O
31.0 part, K
23 parts of O, Na
28 parts of O, 0.5 part of CaO, 0.3 part of Se, 0.03 part of S;
B, with various raw material pulverizing, proportionally require to mix, process admixtion;
C, admixtion is added in the hot melt kiln, fusing under 1380 ℃ of high temperature, and through forming feed liquid after clarification, the homogenizing;
D, feed liquid become water to bore blank by the insulation discharging of discharging road through mould compacting, naturally cooling;
E, according to following weight ratio: water bores 90 parts of pearl bases, 5 parts of carbon dusts, 5 parts of Graphite Powder 99s, water is bored blank and carbon dust, Graphite Powder 99 uniform mixing after, add fire by batch charger and throw the ingle throwing;
Water after f, fire are thrown bores in the pearl base adding sander, and adds recirculated water, and the sander polishing is removed water and bored pearl base surface-fire throwing bur;
Water brill pearl base after g, the polishing is delivered to multiaspect grinding machine grinding water and is bored a plurality of tangent planes, obtains water and is drilled to article.
Embodiment three:
The production technique that a kind of honey peach water bores, key step is following:
A, raw material are joined choosing by following weight ratio: SiO
270 parts, Al
2O
31.5 part, 2.5 parts of BaO, 5 parts of ZnO, B
2O
32.5 part, K
28 parts of O, Na
215 parts of O, 01.5 part of CaO, 1.5 parts of Se, 0.3 part of S;
B, with various raw material pulverizing, proportionally require to mix, process admixtion;
C, admixtion is added in the hot melt kiln, fusing under 1450 ℃ of high temperature, and through forming feed liquid after clarification, the homogenizing;
D, feed liquid become water to bore blank by the insulation discharging of discharging road through mould compacting, naturally cooling;
E, according to following weight ratio: water bores 110 parts of pearl bases, 10 parts of carbon dusts, 10 parts of Graphite Powder 99s, water is bored blank and carbon dust, Graphite Powder 99 uniform mixing after, add fire by batch charger and throw the ingle throwing;
Water after f, fire are thrown bores in the pearl base adding sander, and adds recirculated water, and the sander polishing is removed water and bored pearl base surface-fire throwing bur;
Water brill pearl base after g, the polishing is delivered to multiaspect grinding machine grinding water and is bored a plurality of tangent planes, obtains water and is drilled to article.
Each composition of the embodiment of the invention can obtain from suitable admixtion or raw material, and for example SiO2 obtains from quartz sand powder, and Al2O3 obtains from aluminum oxide powder; BaO obtains from barium carbonate, and ZnO obtains from oxide powder and zinc, and B2O3 obtains from Borax pentahydrate or boric acid; K2O obtains from salt of wormwood, and Na2O obtains from soda ash, and CaO obtains from lime carbonate; Se obtains from selenium powder or Sodium Selenite, and S obtains from sulphur.According to each composition content in admixtion or raw material, calculate corresponding admixtion or raw-meal ingredient, admixtion that corresponding selection is an amount of or raw material.
Claims (6)
1. the honey peach water production technique of boring, it is characterized in that: key step is following:
A, raw material are by following weight proportion: SiO
260-70 part, Al
2O
30.5-1.5 part, BaO 0.5-2.5 part, ZnO 1.5-5 part, B
2O
31.0-2.5 part, K
2O 3-8 part, Na
2O 8-15 part, CaO 0.5-1.5 part, Se 0.3-1.5 part, S 0.03-0.3 part;
B, slow preheating heat melting furnaces 5-7 days, hot melt kiln temperature progressively is increased to 1350-1500 ℃;
C, raw material proportionally required to mix process admixtion, admixtion is added in the hot melt kiln after the preheating, continue heating, after fusing under the 1350-1500 ℃ of high temperature, clarification, homogenizing 7-10 hour, form feed liquid;
D, feed liquid are by the 1000-1200 ℃ of insulation discharging of discharging road; Discharging is simultaneously to the charging of hot melt kiln equivalent; Discharging becomes water to bore pearl base band through mould compacting, naturally cooling, and water bores pearl base band and sends into crusher in crushing, sieves and remove the burr that water bores pearl base band, obtains water and bores the pearl base;
E, according to following weight ratio: water bores pearl base 90-110 part, carbon dust 2-5 part, Graphite Powder 99 5-10 part, water is bored pearl base and carbon dust, Graphite Powder 99 uniform mixing after, add fire by batch charger and throw ingle and throw 750-900 ℃ of fire throwing temperature, 20-30 minute fiery throwing time;
Water after f, fire are thrown bores the pearl base and adds in the sander, and adds recirculated water, and the 15-25 minute removal water of polishing bores pearl base surface-fire and throws bur;
Water brill pearl base after g, the polishing is delivered to multiaspect grinding machine grinding water and is bored a plurality of tangent planes, and the warpization plating obtains water and is drilled to article again.
2. the production technique that a kind of honey peach water according to claim 1 bores, it is characterized in that: raw material comprises quartz sand powder, aluminum oxide powder, barium carbonate, oxide powder and zinc, Borax pentahydrate, salt of wormwood, soda ash, lime carbonate, selenium powder, sulphur.
3. the production technique that a kind of honey peach water according to claim 1 bores, it is characterized in that: raw material comprises quartz sand powder, aluminum oxide powder, barium carbonate, oxide powder and zinc, boric acid, salt of wormwood, soda ash, lime carbonate, selenium powder, sulphur.
4. the production technique that a kind of honey peach water according to claim 1 bores, it is characterized in that: raw material comprises quartz sand powder, aluminum oxide powder, barium carbonate, oxide powder and zinc, Borax pentahydrate, salt of wormwood, soda ash, lime carbonate, Sodium Selenite, sulphur.
5. the production technique that a kind of honey peach water according to claim 1 bores, it is characterized in that: raw material comprises quartz sand powder, aluminum oxide powder, barium carbonate, oxide powder and zinc, boric acid, salt of wormwood, soda ash, lime carbonate, Sodium Selenite, sulphur.
6. the production technique that a kind of honey peach water according to claim 1 bores is characterized in that: among the said step f, extract in real time in the bruting process and measure water and bore pearl base diameter; Water bores pearl base diameter when requiring size; Prolong the polishing time, reach dimensional requirement after, stop polishing.