CN102628234A - 一种大豆纤维和真丝交织织物的染整工艺 - Google Patents
一种大豆纤维和真丝交织织物的染整工艺 Download PDFInfo
- Publication number
- CN102628234A CN102628234A CN2012100946688A CN201210094668A CN102628234A CN 102628234 A CN102628234 A CN 102628234A CN 2012100946688 A CN2012100946688 A CN 2012100946688A CN 201210094668 A CN201210094668 A CN 201210094668A CN 102628234 A CN102628234 A CN 102628234A
- Authority
- CN
- China
- Prior art keywords
- dyeing
- fabric
- fibre
- soya
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了大豆纤维和真丝交织织物的染整工艺，包括有以下步骤：坯布缝头、预定型、前处理、染色、脱水、后整理工艺，染色工艺为先采用70%酒***浸泡30-40分钟，再对大豆纤维采用低温型分散染料进行染色，染色温度为110℃以下，染浴的pH值为5～6，染色后的大豆纤维进行还原清洗，还原清洗后再进行染真丝；本发明所述的预定型保证了良好的外观平整性、手感和色泽；所述的前处理既起到退浆煮练的效果，又保证了大豆纤维的强力不受较大损失；所述的染色工艺保证了良好的染色效果和染色牢度，采用酒精进行杀菌，可以起到预防大豆纤维霉变等情况，熏衣草精油可以使得织物更为柔软、光滑。
Description
背景技术
本发明涉及纺织领域，具体是一种大豆纤维和真丝交织织物的染整工艺。
背景技术
真丝是人们喜爱的衣料，在中国有几千年历史；大豆纤维是一种植物纤维，具有凉爽、环保特别，特别适合用于夏天衣服面料，在织物上应用不断增加，但是现有织物工艺中尚没有将大豆纤维与真丝混纺，本发明在大豆纤维与真丝混纺织物的染整上进行了探索。
发明内容
本发明提供了一种大豆纤维和真丝交织织物的染整工艺，具有良好的上色率，结合了真丝与大豆纤维的优点，凉爽、手感好。
本发明的技术方案为：
一种大豆纤维和真丝交织织物的染整工艺，包括有以下步骤：坯布缝头、预定型、前处理、染色、脱水、后整理工艺，其特征在于：所述的预定型工艺的温度为130-150℃，时间为3-5分钟；所述的前处理工艺为将预定型后的织物进行退浆，退浆液中含有2-4g/L的碳酸氢钠、3-7g/L的双氧水、1-2g/L淀粉酶，退浆液温度为70℃以下；所述的染色工艺为先采用70%酒***浸泡30-40分钟，再对大豆纤维采用低温型分散染料进行染色，染色温度为110℃以下，染浴的pH值为5～6，染色后的大豆纤维进行还原清洗，还原清洗后再进行染真丝；还原清洗液中：保险粉0.5-1.5g/L，非离子洗涤剂1.5-2.5g/L，碳酸氢钠0.5-1.5g/L， 此清洗温度为58-63℃，时间为15-20分钟；所述的后整理工艺为将染色后的织物放入6-8 g/L的亲水性氨基硅柔软剂进行浸轧，浸轧后的织物于80-90℃烘干及拉幅定型。
所述的70%酒***中添加0.2-0.3%重量百分比的熏衣草精油、2-3%的竹醋液。
本发明所述的大豆纤维具有如下优点：
本发明所述的预定型保证了良好的外观平整性、手感和色泽；所述的前处理既起到退浆煮练的效果，又保证了大豆纤维的强力不受较大损失；所述的染色工艺保证了良好的染色效果和染色牢度，又降低了染色成本；所述的后整理工艺保证了纱线的强力。采用酒精进行杀菌，可以起到预防大豆纤维霉变等情况，熏衣草精油可以使得织物更为柔软、光滑。
具体实施方式
例1：
大豆纤维和真丝交织织物的染整工艺，包括有以下步骤：
依次进行坯布缝头、预定型、前处理、染色、脱水、后整理工艺，预定型工艺的温度为130-150℃，时间为3-5分钟；所述的前处理工艺为将预定型后的织物进行退浆，退浆液中含有2-4g/L的碳酸氢钠、3-7g/L的双氧水、1-2g/L淀粉酶，退浆液温度为70℃以下；所述的染色工艺为先采用70%酒***浸泡30-40分钟，再对大豆纤维采用低温型分散染料进行染色，染色温度为110℃以下，染浴的pH值为5～6，染色后的大豆纤维进行还原清洗，还原清洗后再进行染真丝；还原清洗液中：保险粉0.5-1.5g/L，阴离子洗涤剂1.5-2.5g/L，碳酸氢钠0.5-1.5g/L，清洗温度为58-63℃，时间为15-20分钟；所述的后整理工艺为将染色后的织物放入6-8 g/L的亲水性氨基硅柔软剂进行浸轧，浸轧后的织物于80-90℃烘干及拉幅定型。
例2：
大豆纤维和真丝交织织物的染整工艺，包括有以下步骤：
依次进行坯布缝头、预定型、前处理、染色、脱水、后整理工艺，预定型工艺的温度为130-150℃，时间为3-5分钟；所述的前处理工艺为将预定型后的织物进行退浆，退浆液中含有2-4g/L的碳酸氢钠、3-7g/L的双氧水、1-2g/L淀粉酶，退浆液温度为70℃以下；所述的染色工艺为先采用70%酒***浸泡30-40分钟，70%酒***中添加0.2-0.3%重量百分比的熏衣草精油，再对大豆纤维采用低温型分散染料进行染色，染色温度为110℃以下，染浴的pH值为5～6，染色后的大豆纤维进行还原清洗，还原清洗后再进行染真丝；还原清洗液中：保险粉0.5-1.5g/L，阴离子洗涤剂1.5-2.5g/L，碳酸氢钠0.5-1.5g/L， 清洗温度为58-63℃，时间为15-20分钟；所述的后整理工艺为将染色后的织物放入6-8 g/L的亲水性氨基硅柔软剂进行浸轧，浸轧后的织物于80-90℃烘干及拉幅定型。得到的织物色牢度好，柔软、光滑。
Claims (2)
1.一种大豆纤维和真丝交织织物的染整工艺，包括有以下步骤：坯布缝头、预定型、前处理、染色、脱水、后整理工艺，其特征在于：所述的预定型工艺的温度为130-150℃，时间为3-5分钟；所述的前处理工艺为将预定型后的织物进行退浆，退浆液中含有2-4g/L的碳酸氢钠、3-7g/L的双氧水、1-2g/L淀粉酶，退浆液温度为70℃以下；所述的染色工艺为先采用70%酒***浸泡30-40分钟，再对大豆纤维采用低温型分散染料进行染色，染色温度为110℃以下，染浴的pH值为5～6，染色后的大豆纤维进行还原清洗，还原清洗后再进行染真丝；还原清洗液中：保险粉0.5-1.5g/L，非离子洗涤剂1.5-2.5g/L，碳酸氢钠0.5-1.5g/L，清洗温度为58-63℃，时间为15-20分钟；所述的后整理工艺为将染色后的织物放入6-8 g/L的亲水性氨基硅柔软剂进行浸轧，浸轧后的织物于80-90℃烘干及拉幅定型。
2.根据权利要求1所述的大豆纤维和真丝交织织物的染整工艺，其特征在于所述的70%酒***中添加0.2-0.3%重量百分比的熏衣草精油。