CN101570826A - 一种多级真空蒸馏分离铅锡合金的方法 - Google Patents
一种多级真空蒸馏分离铅锡合金的方法 Download PDFInfo
- Publication number
- CN101570826A CN101570826A CNA2009100945518A CN200910094551A CN101570826A CN 101570826 A CN101570826 A CN 101570826A CN A2009100945518 A CNA2009100945518 A CN A2009100945518A CN 200910094551 A CN200910094551 A CN 200910094551A CN 101570826 A CN101570826 A CN 101570826A
- Authority
- CN
- China
- Prior art keywords
- tin
- vacuum
- lead
- vacuum distilling
- output
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种多级真空蒸馏分离铅锡合金的方法,原料铅锡合金在真空炉中进行三级真空蒸馏,控制一级蒸馏温度为900℃-1050℃,真空度0.1Pa-0.5Pa,蒸馏10-20分钟;二级蒸馏温度为1100℃-1250℃;三级蒸馏温度为1100℃-1250℃。得到的产品精锡中含铅量小于0.005%,金属锡和铅的直收率均大于等于98%,同时对原料中铅的含量要求扩大为7%-95%的范围,增加了工艺设备对原料的适应范围。
Description
一、技术领域
本发明涉及一种多级真空蒸馏分离铅锡合金的方法,是一种将铅锡合金分离除铅,得到的金属锡产品中含铅量小于0.005%的方法,属于火法冶金技术领域。
二、背景技术
公知的铅锡合金分离锡、铅的生产工艺中,结晶法能将锡中铅分离到含铅量小于0.03%,但它要求原料的含铅量要小于等于10%,金属锡的直收率在96%-97%间;其它方式中电解法对原料的要求更克苛,要求含铅量小于等于2%,含金属铋小于等于0.5%,金属锡的直收率效低,为76%-80%;原真空蒸馏工艺方式下,产品金属锡中含铅量仍含有2%-4%,锡的直收率为97%,对原料的要求为含铅量78%-89%,这些方法中存在对原料的要求高,或存在处理量和处理效果的局限性;还存在锡的直收率相对较低,或工艺环境差的缺点;本方法是在一种真空蒸馏工艺条件下(真空度为0.1Pa-0.5Pa),对铅锡合金原料的铅含量要求放宽到7%-95%范围内,可获得产品金属锡中含铅量小于0.005%。各方法取得的技术指标如下表1:
表1各种铅锡合金处理方法比较
三、发明内容:
本发明的目的是提供一种多级真空蒸馏分离铅锡合金的方法,原料铅锡合金在真空炉中进行分离铅、锡,使产品精锡中含铅量小于0.005%,金属锡和铅的直收率均大于等于98%,同时对原料中铅的含量要求为7%-95%的范围,增加了工艺设备对原料的适应范围。
本发明按以下步骤完成:其工艺路线入图1,
1.原料为含Pb 95%-7质量%,Sn 5%--93质量%的铅锡合金,入熔化锅熔化;
2.熔融后的铅锡合金加入真空炉内进行一级真空蒸馏,控制温度为900℃-1050℃,真空度0.1Pa-0.5Pa,蒸馏10-20分钟,产出一级粗锡(Sn≥90%,Pb≤7%)和粗铅(Sn≤2%,Pb≥98%);粗铅铸锭为成品。根据需要另作处理;
3.一级粗锡进入二级真空蒸馏,控制温度为1100℃-1250℃,真空度0.1Pa-0.5Pa,蒸馏时间为10-20分钟,产出二级粗锡(Sn≥98%,Pb≤0.05%),同时产出Sn≤42%,Pb≥50%的铅锡合金。铅锡合金可作为原料转入一级真空蒸馏继续提炼;
4.产出的二级粗锡进入三级真空蒸馏,控制温度为1100℃-1250℃,真空度0.1Pa0.5Pa,蒸馏时间为10-20分钟,产出精锡(Pb≤0.005%),同时产出Sn≤42%,Pb≥50%的铅锡合金,可作为原料进入第一级真空蒸馏。
与公知技术相比的优点及积极效果
1)、本发明对铅锡合金分离铅和锡,达到产品精锡中铅含量小于0.005%;
2)、金属铅、锡的直收率均大于等于98%,回收率均大于等于99%;
3)、对于铅锡合金中含铅量从7%到95%的物料均可实现铅与锡分离,达到金属精锡中含铅量小于0.005%;
4)、本发明处理铅锡合金的能力达5-8吨/台.日。
四、附图说明:
图1是本发明工艺路线图。
五、具体实施方式
实施例1:
物料成分:Sn=85.68质量%,Pb=12.21质量%,其它为2.11质量%。熔融物料入真空炉进行一级蒸馏,控制真空度为0.1Pa,蒸馏温度为900℃,蒸馏时间为20分钟,处理量240Kg/h,共计处理9650Kg。产出一级粗锡8455Kg,占总处理量的87.6%,含铅量0.96%,其它2.32%;产出粗铅1104Kg,占总处理量的11.4%,含锡量1.94%,其它0.52%;产出浮渣79.8Kg,占总处理量的0.83%,损失11.2Kg,占总处理量的0.12%。平均电耗342KWh/h。
一级粗锡进入二级真空蒸馏,控制真空度0.3Pa,蒸馏温度1200℃,蒸馏时间为15分钟,处理量:150Kg/h,共计处理8455Kg。产出二级粗锡8290Kg,占总处理量的98%,含铅量0.02%,其它2.21%;产出铅锡合金140.5Kg,占总处理量的1.7%,含锡量41.32%;产出浮渣13.5Kg,占总处理量的0.16%;损失11Kg,占总处理量的0.13%。平均电耗400KWh/h。
二级粗锡进入三级真空蒸馏,控制真空度0.5Pa;蒸馏温度1250℃,蒸馏时间为10分钟,处理量150Kg/h,共计处理8290Kg。产出精锡8260Kg,占总处理量的99.6%,含铅量0.003%;产出铅锡合金10Kg,占总处理量的0.1%,含锡量41.12%;产出浮渣16.8Kg,占总处理量的0.2%,损失3.2Kg,损失量占总处理量的0.03%;平均电耗412KWh/h。
实施例2:
物料成分:Sn=21.84质量%,Pb=77.99质量%,其它为0.17质量%。物料入真空炉进行一级蒸馏,控制真空度0.1Pa;蒸馏温度1050℃,蒸馏时间为20分钟,处理量为260Kg/h,共计处理9500Kg。产出一级粗锡2185Kg;一级粗锡进入二级真空蒸馏,控制真空度0.1Pa,蒸馏温度1150℃,蒸馏时间为15分钟,处理量:150Kg/h,共计处理8455Kg。产出二级粗锡8290Kg;二级粗锡进入三级真空蒸馏,控制真空度0.5Pa;蒸馏温度1250℃,馏时间为10分钟,处理量150Kg/h,共计处理8290Kg。产出精锡8260Kg,精锡含铅量0.0048%。
Claims (2)
1、一种多级真空蒸馏分离铅锡合金的方法,其特征在于:其按以下步骤完成,
1).熔融后的铅锡合金加入真空炉内进行一级真空蒸馏,控制温度为900℃-1050℃,真空度0.1Pa-0.5Pa,蒸馏10-20分钟,产出一级粗锡和粗铅,粗铅铸锭为成品,再根据需要另作处理;
2).一级粗锡进入二级真空蒸馏,控制温度为1100℃-1250℃,真空度0.1Pa-0.5Pa,蒸馏时间为10-20分钟,产出二级粗锡和铅锡合金,铅锡合金作为原料转入一级真空蒸馏继续提炼;
3).产出的二级粗锡进入三级真空蒸馏,控制温度为1100℃-1250℃,真空度0.1Pa-0.5Pa,蒸馏时间为10-20分钟,产出精锡和铅锡合金,作为原料进入一级真空蒸馏。
2、根据权利要求1所述的多级真空蒸馏分离铅锡合金的方法,其特征在于:所述原料为含Pb 95%-7质量%,含Sn 5%-93质量%的铅锡合金。