CN101497519A - 磷石膏基粉刷石膏 - Google Patents
磷石膏基粉刷石膏 Download PDFInfo
- Publication number
- CN101497519A CN101497519A CNA2009101030728A CN200910103072A CN101497519A CN 101497519 A CN101497519 A CN 101497519A CN A2009101030728 A CNA2009101030728 A CN A2009101030728A CN 200910103072 A CN200910103072 A CN 200910103072A CN 101497519 A CN101497519 A CN 101497519A
- Authority
- CN
- China
- Prior art keywords
- phosphogypsum
- gypsum
- powder
- plastering gypsum
- based plastering
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种磷石膏基粉刷石膏，涉及建筑物墙体抹灰材料。该磷石膏基粉刷石膏主要包括磷石膏基建筑石膏75～95％、灰钙粉1～3％、缓凝剂0.1～0.5％、复合保水剂1.1～5.5％、乙烯-醋酸乙烯共聚乳胶粉0.3～1、填料0～20。采用纤维素醚类保水剂和膨润土相结合，既有效改善粉刷石膏的保水性，又降低了成本；采用缓凝剂有效地调节粉刷石膏的凝结时间，延长粉刷石膏的可操作时间；掺加填料和乳胶粉改善磷石膏基粉刷石膏的施工性、粘结性和抗裂性；添加灰钙粉降低杂质对粉刷石膏强度的不利影响。该磷石膏基粉刷石膏和易性与施工性好，可操作时间长，抗折、抗压、粘结强度高，体积稳定性好，抗裂性优异，成本较低，可用于建筑物墙体粉刷抹灰层。
Description
技术领域
本发明涉及建筑物墙体用抹灰材料的磷石膏基粉刷石膏。
背景技术
磷石膏是湿法生产磷酸时排放的工业废渣，主要成分为二水硫酸钙，含有少量的磷、氟以及有机物等杂质。由于磷石膏中有害杂质的影响，使其不能直接用于生产石膏建材。粉刷石膏是近年来国内外大力提倡的低能耗墙体抹灰材料。与石灰砂浆和水泥砂浆相比，粉刷石膏对人体亲和，能耗低，保水性好，粘结力强，不会出现开裂、起鼓、脱落的问题。但传统天然石膏配制的单相粉刷石膏性能易变，不易控制；混合相粉刷石膏生产复杂，而且价格昂贵，成本较高。利用磷石膏配制粉刷石膏，不仅变废为宝，节能减排，而且产品成本较低，市场竞争力强。
在2005年的《新型建筑材料》第10期上刊登了“磷石膏基粉刷石膏的绿色工艺设计”。该文献研究了用磷石膏基建筑石膏的制备工艺，配制了磷石膏基粉刷石膏，提出了磷石膏利用的绿色工艺设计原则。其粉刷石膏组分为磷石膏基建筑石膏：柠檬酸三钠缓凝剂：无机矿物保水剂＝100：1：3。该文献中研究了加入缓凝剂和保水剂，对磷石膏基建筑石膏加以改性配制粉刷石膏，但由于只选用了单掺柠檬酸三钠缓凝剂和无机矿物保水剂，未采用其他改性措施，因而配制的粉刷石膏的强度较低，粘结较差，成本较高。
本发明采用的生产工艺为常规工艺。
发明内容
本发明的目的在于针对上述出现的技术的不足，提供一种磷石膏基粉刷石膏，该粉刷石膏和易性好，可操作时间长，抗折、抗压强度高，具有更好的抗裂性和粘结性，成本较低。
为了实现上述发明目的，其技术方案是：
磷石膏基粉刷石膏包括以下组分和质量百分比：
磷石膏基建筑石膏 75～95
灰钙粉 1～3
缓凝剂 0.1～0.5
复合保水剂 1.1～5.5
乙烯—醋酸乙烯共聚乳胶粉 0.3～1
填料 0～20
其中：
磷石膏基建筑石膏：用磷石膏制备的建筑石膏，性能须满足GB9776-1988《建筑石膏》的要求；
缓凝剂：柠檬酸或三聚磷酸钠；
复合保水剂：
甲基纤维素醚或羟丙基甲基纤维素醚 0.1～0.5
膨润土 1～5；
填料：滑石粉或石英砂。
本发明与现有技术相比具有如下技术效果：
(1)和易性好，可操作时间长，不粘抹子；
(2)抗折、抗压强度较高，成本较低；
(3)粉刷层无裂纹，不起灰，不空鼓，粘结牢固，稳定性好。
要利用磷石膏制备的建筑石膏配制粉刷石膏首要解决的问题是建筑石膏的缓凝问题，选择合适的缓凝剂，能保证粉刷石膏具有较好的可操作时间和最低的强度降幅。建筑石膏的初凝时间一般在10min以内，而粉刷石膏的可操作时间不应低于60min，采用缓凝剂是唯一的选择。本发明采用柠檬酸、三聚磷酸钠石膏专用缓凝剂，不仅有效地调节了粉刷石膏的凝结时间，保证有足够的时间进行施工操作，并且对强度的影响较小。采用0.3％的柠檬酸作为缓凝剂时，初凝时间可以延长到90min以上，可操作时间大大延长。
保水性是粉刷石膏的重要技术指标，良好的保水性可避免粉刷石膏塑性开裂和表面粉化。通常采用单一的保水剂技术，纤维素醚是常用的商品保水剂。不同的保水剂种类和掺量，改善粉刷石膏的保水性不同，其中甲基纤维素醚保水效果最好，但其掺量较大，成本较高。本发明采用复合保水技术，在较低成本下大大改善了磷石膏基粉刷石膏的保水性。新加入的无机保水剂组分膨润土为层状结构，有强烈的吸水性，具有保水作用，与甲基纤维素醚复合使用可有效降低后者掺量，降低粉刷石膏配制的材料成本。采用0.5％羟丙基甲基纤维素醚和5％膨润土相复合的粉刷石膏，保水率较未掺保水剂的粉刷石膏提高了256％，并且大大降低了粉刷石膏的成本。
为了改善粉刷石膏的施工性，可掺入一定比例的无机惰性填料。随填料掺量增加，粉刷石膏的凝结时间延长，刮涂性、打磨性趋好，但强度、粘结性降低。滑石粉、石英砂等可有效改善粉刷石膏的施工性能，增强抗裂效果和耐候性，而且降低了粉刷石膏的成本。
为了改善粉刷石膏的粘结性能，本发明还在配制过程中加入了乙烯—醋酸乙烯共聚乳胶粉，很好地提高了粉刷石膏的粘结性能和施工性能。掺加0.8％乙烯—醋酸乙烯共聚乳胶粉的磷石膏基粉刷石膏，其剪切粘结强度达0.68MPa，较未掺乳胶粉的提高57％。
另外，为了中和磷石膏基建筑石膏中残留的磷酸杂质，本发明还加入了少量的碱组分—灰钙粉，有效地降低了杂质对粉刷石膏性能的影响，可使磷石膏基粉刷石膏抗折、抗压强度较未掺碱组分的粉刷石膏分别提高26％、32％。
试验表明：当磷石膏基粉刷石膏配比(重量百分比)为：磷石膏基建筑石膏82、灰钙粉2、柠檬酸0.3、甲基纤维素醚0.3、膨润土3、乙烯—醋酸乙烯共聚乳胶粉0.4、滑石粉12，该粉刷石膏性能为：初凝时间146min、终凝时间208min、可操作时间2h、保水率95％、抗折强度4.5MPa、抗压强度12.4MPa、剪切粘结强度0.82MPa，满足JC/T517-2004粉刷石膏》标准中对面层和底层粉刷石膏的要求。
具体实施方式
磷石膏基粉刷石膏按以下组分和重量百分比一次称足同时搅拌而成：
实施例1：
磷石膏基建筑石膏 82
灰钙粉 2
柠檬酸 0.3
甲基纤维素醚 0.3
膨润土 3
乙烯—醋酸乙烯共聚乳胶粉 0.4
滑石粉 12。
实施例2：
磷石膏基建筑石膏 95
灰钙粉 2
柠檬酸 0.2
羟丙基甲基纤维素醚 0.35
膨润土 1.8
乙烯—醋酸乙烯共聚乳胶粉 0.65。
实施例3：
磷石膏基建筑石膏 85
灰钙粉 1.5
三聚磷酸钠 0.25
甲基纤维素醚 0.25
膨润土 1
乙烯—醋酸乙烯共聚乳胶粉 0.3
滑石粉 11.7。
实施例4：
磷石膏基建筑石膏 75
灰钙粉 1
三聚磷酸钠 0.4
羟丙基甲基纤维素醚 0.1
膨润土 2.5
乙烯—醋酸乙烯共聚乳胶粉 1
滑石粉 20。
实施例5：
磷石膏基建筑石膏 86
灰钙粉 2
柠檬酸 0.2
羟丙基甲基纤维素醚 0.4
膨润土 2.9
乙烯—醋酸乙烯共聚乳胶粉 0.5
石英砂 8。
实施例6：
磷石膏基建筑石膏 82
灰钙粉 3
柠檬酸 0.1
甲基纤维素醚 0.3
膨润土 3.8
乙烯—醋酸乙烯共聚乳胶粉 0.8
石英砂 10。
实施例7：
磷石膏基建筑石膏 90
灰钙粉 1.9
三聚磷酸钠 0.5
羟丙基甲基纤维素醚 0.2
膨润土 1.5
乙烯—醋酸乙烯共聚乳胶粉 0.9
石英砂 5。
实施例8：
磷石膏基建筑石膏 91
灰钙粉 2.5
柠檬酸 0.15
羟丙基甲基纤维素醚 0.15
膨润土 4
乙烯—醋酸乙烯共聚乳胶粉 0.6
石英砂 1.6。
实施例9：
磷石膏基建筑石膏 76
灰钙粉 2.5
三聚磷酸钠 0.3
甲基纤维素醚 0.5
膨润土 5
乙烯—醋酸乙烯共聚乳胶粉 0.7
滑石粉 15。
Claims (10)
1.一种磷石膏基粉刷石膏，其特征在于该磷石膏基粉刷石膏的组分及重量百分比为：
磷石膏基建筑石膏 75～95
灰钙粉 1～3
缓凝剂 0.1～0.5
复合保水剂 1.1～5.5
乙烯—醋酸乙烯共聚乳胶粉 0.3～1
填料 0～20
其中：
缓凝剂：柠檬酸或三聚磷酸钠；
复合保水剂：
甲基纤维素醚或羟丙基甲基纤维素醚 0.1～0.5
膨润土 1～5；
填料：滑石粉或石英砂。
2.根据权利要求1所述的磷石膏基粉刷石膏，其特征在于该磷石膏基粉刷石膏的具体组分及重量百分比：
磷石膏基建筑石膏 82
灰钙粉 2
柠檬酸 0.3
甲基纤维素醚 0.3
膨润土 3
乙烯—醋酸乙烯共聚乳胶粉 0.4
滑石粉 12。
3.根据权利要求1所述的磷石膏基粉刷石膏，其特征在于该磷石膏基粉刷石膏的具体组分及重量百分比：
磷石膏基建筑石膏 95
灰钙粉 2
柠檬酸 0.2
羟丙基甲基纤维素醚 0.35
膨润土 1.8
乙烯—醋酸乙烯共聚乳胶粉 0.65。
4.根据权利要求1所述的磷石膏基粉刷石膏，其特征在于该磷石膏基粉刷石膏的具体组分及重量百分比：
磷石膏基建筑石膏 85
灰钙粉 1.5
三聚磷酸钠 0.25
甲基纤维素醚 0.25
膨润土 1
乙烯—醋酸乙烯共聚乳胶粉 0.3
滑石粉 11.7。
5.根据权利要求1所述的磷石膏基粉刷石膏，其特征在于该磷石膏基粉刷石膏的具体组分及重量百分比：
磷石膏基建筑石膏 75
灰钙粉 1
三聚磷酸钠 0.4
羟丙基甲基纤维素醚 0.1
膨润土 2.5
乙烯—醋酸乙烯共聚乳胶粉 1
滑石粉 20。
6.根据权利要求1所述的磷石膏基粉刷石膏，其特征在于该磷石膏基粉刷石膏的具体组分及重量百分比：
磷石膏基建筑石膏 86
灰钙粉 2
柠檬酸 0.2
羟丙基甲基纤维素醚 0.4
膨润土 2.9
乙烯—醋酸乙烯共聚乳胶粉 0.5
石英砂 8。
7.根据权利要求1所述的磷石膏基粉刷石膏，其特征在于该磷石膏基粉刷石膏的具体组分及重量百分比：
磷石膏基建筑石膏 82
灰钙粉 3
柠檬酸 0.1
甲基纤维素醚 0.3
膨润土 3.8
乙烯—醋酸乙烯共聚乳胶粉 0.8
石英砂 10。
8.根据权利要求1所述的磷石膏基粉刷石膏，其特征在于该磷石膏基粉刷石膏的具体组分及重量百分比：
磷石膏基建筑石膏 90
灰钙粉 1.9
三聚磷酸钠 0.5
羟丙基甲基纤维素醚 0.2
膨润土 1.5
乙烯—醋酸乙烯共聚乳胶粉 0.9
石英砂 5。
9.根据权利要求1所述的磷石膏基粉刷石膏，其特征在于该磷石膏基粉刷石膏的具体组分及重量百分比：
磷石膏基建筑石膏 91
灰钙粉 2.5
柠檬酸 0.15
羟丙基甲基纤维素醚 0.15
膨润土 4
乙烯—醋酸乙烯共聚乳胶粉 0.6
石英砂 1.6。
10.根据权利要求1所述的磷石膏基粉刷石膏，其特征在于该磷石膏基粉刷石膏的具体组分及重量百分比：
磷石膏基建筑石膏 76
灰钙粉 2.5
三聚磷酸钠 0.3
甲基纤维素醚 0.5
膨润土 5
乙烯—醋酸乙烯共聚乳胶粉 0.7
滑石粉 15。