CN101189752A - 质子传导性聚合物膜及其制造方法、以及使用该聚合物膜的燃料电池 - Google Patents
质子传导性聚合物膜及其制造方法、以及使用该聚合物膜的燃料电池 Download PDFInfo
- Publication number
- CN101189752A CN101189752A CNA2006800195959A CN200680019595A CN101189752A CN 101189752 A CN101189752 A CN 101189752A CN A2006800195959 A CNA2006800195959 A CN A2006800195959A CN 200680019595 A CN200680019595 A CN 200680019595A CN 101189752 A CN101189752 A CN 101189752A
- Authority
- CN
- China
- Prior art keywords
- polymer film
- group
- proton
- acid
- conducting polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | |||
聚合物膜 | 聚合物膜1 | 聚合物膜2 | 聚合物膜3 | 聚合物膜1 | 聚合物膜1 | ||
浸渗酸种类 | 乙烯基膦酸 | 乙烯基膦酸 | 乙烯基膦酸 | 乙烯基膦酸 | 乙烯基膦酸 | ||
酸浸渗量(质量%) | 240 | 250 | 210 | 180 | 310 | ||
离子传导度(150℃)(×10-2S/cm) | 1.4 | 1.5 | 1.1 | 1.0 | 1.8 | ||
发电特性 | 初期 | 开路电压(V) | 0.984 | 0.995 | 0.975 | 0.985 | 0.971 |
电压(V)(0.3A/cm2) | 0.573 | 0.570 | 0.566 | 0.565 | 0.581 | ||
500小时后 | 开路电压(V) | 0.980 | 0.988 | 0.974 | 0.983 | 0.968 | |
降低率(%) | 0.4 | 0.7 | 0.1 | 0.2 | 0.3 | ||
电压(V)(0.3A/cm2) | 0.571 | 0.566 | 0.564 | 0.564 | 0.576 | ||
降低率(%) | 0.4 | 0.7 | 0.4 | 0.2 | 0.9 |
比较例1 | 比较例2 | 比较例3 | |||
聚合物膜 | 聚合物膜4 | 聚合物膜4 | 聚合物膜1 | ||
浸渗酸种类 | 正磷酸 | 乙烯基膦酸 | 正磷酸 | ||
酸浸渗量(质量%) | 350 | 390 | 不能通过聚合物膜溶解进行测定 | ||
离子传导度(150℃)(×10-2S/cm) | 1.4 | 1.4 | |||
发电特性 | 初期 | 开路电压(V) | 0.951 | 0.965 | |
电压(V)(0.3A/cm2) | 0.546 | 0.568 | |||
500小时后 | 开路电压(V) | 0.882 | 0.930 | ||
降低率(%) | 7.3 | 3.6 | |||
电压(V)(0.3A/cm2) | 0.481 | 0.545 | |||
降低率(%) | 13.5 | 4.2 |
Claims (8)