WO2020013515A1 - 사이클로헥산 폴리에스터계 물질을 포함하는 가소제 조성물 및 이를 포함하는 수지 조성물 - Google Patents
사이클로헥산 폴리에스터계 물질을 포함하는 가소제 조성물 및 이를 포함하는 수지 조성물 Download PDFInfo
- Publication number
- WO2020013515A1 WO2020013515A1 PCT/KR2019/008139 KR2019008139W WO2020013515A1 WO 2020013515 A1 WO2020013515 A1 WO 2020013515A1 KR 2019008139 W KR2019008139 W KR 2019008139W WO 2020013515 A1 WO2020013515 A1 WO 2020013515A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- group
- formula
- cyclohexane
- acid
- integer
- Prior art date
Abstract
Description
목적 생성물1) | 과수소화물2-2) | |
실시예 1-1 | 86.1 | 1.631 |
실시예 1-2 | 85.8 | 3.741 |
실시예 1-3 | 87.2 | 0.583 |
실시예 1-4 | 82.3 | 9.588 |
비교예 1-1 | - | - |
비교예 1-2 | 78.6 | 12.646 |
비교예 1-3 | 89.5 | 11.596 |
비교예 1-4 | 99.7 | 0.027 |
구분 | 경도 | 이행손실(%) | 가열감량(%) | 인장강도(kgf/㎠) | 신율(%) | 내광성(ΔE) | |
Shore 'A' | Shore 'D' | ||||||
실시예 1-1 | 90.9 | 45.3 | 3.37 | 0.73 | 243.5 | 342.1 | 1.4 |
실시예 1-2 | 90.7 | 45.2 | 3.40 | 0.92 | 241.7 | 337.0 | 1.4 |
실시예 1-3 | 90.7 | 45.3 | 3.02 | 0.58 | 245.1 | 349.1 | 1.3 |
실시예 1-4 | 90.8 | 45.4 | 3.56 | 1.84 | 244.0 | 338.1 | 1.6 |
비교예 1-1 | 94.2 | 50.3 | 4.78 | 0.70 | 238.6 | 320.4 | 7.6 |
비교예 1-2 | 90.8 | 45.4 | 4.69 | 3.22 | 228.0 | 319.5 | 2.0 |
비교예 1-3 | 90.7 | 45.5 | 4.32 | 3.08 | 237.9 | 326.9 | 2.1 |
비교예 1-4 | 90.8 | 45.2 | 3.52 | 0.98 | 242.5 | 324.5 | 1.3 |
목적 생성물1) | 과수소화물2) | |
실시예 2-1 | 87.3 | 1.45 |
실시예 2-2 | 82.8 | 5.56 |
실시예 2-3 | 79.2 | 9.23 |
비교예 2-1 | - | - |
비교예 2-2 | 77.5 | 13.50 |
비교예 2-3 | 99.8 | 0.01 |
구분 | 경도 | 이행손실(%) | 가열감량(%) | 인장강도(kgf/㎠) | 신율(%) | 스트레스 테스트 | |
Shore 'A' | Shore 'D' | ||||||
실시예 2-1 | 91.2 | 45.6 | 3.28 | 1.32 | 221.6 | 281.3 | 0.5 |
실시예 2-2 | 91.3 | 45.7 | 3.26 | 1.52 | 224.4 | 282.8 | 0.5 |
실시예 2-3 | 91.0 | 45.2 | 3.24 | 2.01 | 223.0 | 286.5 | 0.5 |
비교예 2-1 | 94.4 | 50.4 | 4.25 | 1.02 | 220.6 | 278.4 | 3.0 |
비교예 2-2 | 91.0 | 45.1 | 3.42 | 3.21 | 204.6 | 283.0 | 1.0 |
비교예 2-3 | 92.0 | 45.9 | 4.20 | 1.34 | 218.7 | 268.4 | 3.0 |
목적 생성물1) | 과수소화물2) | |
실시예 3-1 | 86.0 | 2.23 |
실시예 3-2 | 81.2 | 7.52 |
실시예 3-3 | 80.5 | 9.10 |
비교예 3-1 | - | - |
비교예 3-2 | 78.4 | 12.02 |
비교예 3-3 | 99.6 | 0.03 |
구분 | 경도 | 이행손실(%) | 가열감량(%) | 인장강도(kgf/㎠) | 신율(%) | 스트레스 테스트 | 내광성(△E) | |
Shore 'A' | Shore 'D' | |||||||
실시예 3-1 | 96.1 | 53.9 | 1.69 | 0.47 | 223.7 | 294.6 | 0 | 1.6 |
실시예 3-2 | 96.0 | 53.4 | 1.60 | 0.60 | 224.5 | 295.6 | 0 | 1.8 |
실시예 3-3 | 95.9 | 53.4 | 1.55 | 0.65 | 223.0 | 301.2 | 0 | 1.8 |
비교예 3-1 | 98.7 | 55.4 | 2.13 | 0.42 | 222.7 | 294.5 | 1 | 6.5 |
비교예 3-2 | 95.9 | 53.3 | 1.98 | 1.12 | 217.3 | 281.4 | 0 | 2.2 |
비교예 3-3 | 96.8 | 54.5 | 1.56 | 0.45 | 223.1 | 280.6 | 0.5 | 1.6 |
Claims (11)
- 하기 화학식 1로 표시되는 화합물인 사이클로헥산 폴리에스터계 물질; 및하기 화학식 2로 표시되는 화합물 과수소화물;을 포함하며,상기 과수소화물은 사이클로헥산 폴리에스터계 물질 100 중량부 대비 0.1내지 10 중량부로 포함되는 것인 가소제 조성물:[화학식 1][화학식 2]상기 화학식 1 및 화학식 2에 있어서,R1 및 R2는 각각 독립적으로 탄소수 4 내지 10의 알킬기이고,R3는 메틸기이며,n은 2 또는 3이고, m은 0 내지 2의 정수이며, p는 0 내지 3의 정수이고, m+p는 0 내지 3의 정수이며, n-m은 1 내지 3의 정수이다.
- 제1항에 있어서,상기 화학식 1 및 화학식 2에 있어서,R1 및 R2는 각각 독립적으로 탄소수 5 내지 10의 알킬기이고,R3는 메틸기이며,n이 2인 경우, m은 0 또는 1이며, p는 0 내지 2의 정수이고, m+p는 0 내지 2의 정수이며, n-m은 1 또는 2이고,n이 3인 경우, m은 0 내지 2의 정수이며, p는 0 내지 3의 정수이고, m+p는 0 내지 3의 정수이며, n-m은 1 내지 3의 정수이다.
- 제1항에 있어서,상기 사이클로헥산 폴리에스터계 물질은 하기 화학식 1-3으로 표시되는 화합물이고,상기 과수소화물은 하기 화학식 2-5 내지 2-10로 표시되는 화합물 중에서 선택되는 화합물을 1종 이상 포함하는 것인 가소제 조성물:[화학식 1-3]상기 화학식 1-3에서,R13 내지 R15는 각각 독립적으로 탄소수 4 내지 10의 알킬기이다.[화학식 2-5][화학식 2-6][화학식 2-7][화학식 2-8][화학식 2-9][화학식 2-10]상기 화학식 2-5 내지 2-10에서,R23 및 R26은 각각 독립적으로 탄소수 4 내지 10의 알킬기이고,R24 및 R25는 각각 독립적으로 수소 또는 메틸기이다.
- 제1항에 있어서,상기 화학식 1 및 2에서, R1 및 R2는 각각 독립적으로 n-부틸기, 이소부틸기, n-펜틸기, 이소펜틸기, n-헥실기, 이소헥실기, n-헵틸기, 이소헵틸기, n-옥틸기, 이소옥틸기, 2-에틸헥실기, n-노닐기, 이소노닐기, n-데실기, 이소데실기 및 2-프로필헵틸기로 이루어진 군에서 선택되는 것인 가소제 조성물.
- 제1항에 있어서,상기 화학식 1 및 2에서, R1 및 R2는 각각 독립적으로 이소헵틸기, 2-에틸헥실기, n-노닐기, 이소노닐기 및 2-프로필헵틸기로 이루어진 군에서 선택되는 것인 가소제 조성물.
- 이소프탈산, 테레프탈산 및 트리멜리트산으로 이루어진 군에서 선택된 어느 하나의 방향족 카르복실산을 수소화 하여 사이클로헥산 폴리카르복실산을 포함하는 수소화물을 얻는 단계; 및상기 수소화물 및 1차 알킬 알코올을 에스터화 반응시키는 단계;를 포함하고,상기 1차 알킬 알코올의 알킬 탄소수는 4 내지 10이고,상기 사이클로헥산 폴리카르복실산은 사이클로헥산 1,3-디카르복실산, 사이클로헥산 1,4-디카르복실산 또는 사이클로헥산 1,2,4-트리카르복실산인 것인 제1항의 가소제 조성물의 제조방법.
- 수지 100 중량부; 및 제1항의 가소제 조성물 5 내지 150 중량부;를 포함하는 수지 조성물.
- 제10항에 있어서,상기 수지는 에틸렌 초산 비닐, 폴리에틸렌, 폴리프로필렌, 폴리케톤, 폴리염화비닐, 폴리스타이렌, 폴리우레탄, 천연고무, 합성고무 및 열가소성 엘라스토머로 이루어진 군에서 선택된 1 종 이상인 것인 수지 조성물.