WO2020009493A1 - 1,2-펜탄디올 제조용 촉매 및 이를 이용한 1,2-펜탄디올의 제조방법 - Google Patents
1,2-펜탄디올 제조용 촉매 및 이를 이용한 1,2-펜탄디올의 제조방법 Download PDFInfo
- Publication number
- WO2020009493A1 WO2020009493A1 PCT/KR2019/008195 KR2019008195W WO2020009493A1 WO 2020009493 A1 WO2020009493 A1 WO 2020009493A1 KR 2019008195 W KR2019008195 W KR 2019008195W WO 2020009493 A1 WO2020009493 A1 WO 2020009493A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- pentanediol
- catalyst
- starting material
- reaction
- hydrogenation
- Prior art date
Abstract
Description
제조예 | Catalyst | 온도 (oC) | 시간(h) | 압력(bar) | Furfural Conv.% | Product Yield (%) | ||||
Furfuryl alcohol | MTHF | 1,2-PDO | 1,5-PDO | Others | ||||||
1 | 5 wt% Ru/ZnO | 150 | 4 | 30 | 100 | 60.9 | 27 | - | - | 12.1 |
6 | 100 | 49.6 | 36 | - | - | 14.4 | ||||
2 | 4.1 wt% 1Ru-2Sn/ZnO | 150 | 4 | 30 | 100 | 9.4 | 7.1 | 43.6 | 28.3 | 11.6 |
6 | 100 | 5.2 | 6.3 | 42.2 | 29.6 | 16.7 | ||||
3 | 4.1 wt% 1Ru-5Sn/ZnO | 150 | 5 | 30 | 100 | 0 | 0.4 | 84.2 | 9.1 | 6.3 |
6 | 25 | 100 | 0 | 0 | 86.3 | 11.2 | 2.3 | |||
140 | 5 | 35 | 100 | 0 | 0 | 87.3 | 12.1 | 0.6 | ||
130 | 5 | 35 | 100 | 6.9 | 0 | 78.2 | 11.3 | 3.6 | ||
6 | 100 | 0 | 0 | 83.6 | 12.4 | 4.0 | ||||
100 | 6 | 35 | 100 | 81.4 | 0 | 9.3 | 5.8 | 3.5 | ||
6 | 25 | 100 | 88.2 | 0 | 5.9 | 2.6 | 3.3 | |||
6 | 15 | 100 | 96.2 | 0 | 1.1 | 0.3 | 2.4 | |||
6 | 5 | 81 | 76 | 0 | 0 | 0 | 5.0 | |||
4 | 4.1 wt% 1Ru-7Sn/ZnO | 150 | 6 | 30 | 100 | 0 | 0 | 81.3 | 14.2 | 4.5 |
140 | 6 | 30 | 100 | 0 | 0 | 84.9 | 11.3 | 3.8 | ||
5 | 5 wt% Pt/HT | 140 | 6 | 30 | 100 | 15.3 | 0 | 54.4 | 18.2 | 12.1 |
6 | 4.1 wt% 1Ru-5Sn/HT(Mg/Al=3) | 140 | 6 | 30 | 100 | 32.1 | 0 | 41.9 | 12.2 | 13.8 |
7 | 4.1 wt% 1Pt-5Sn/ZnO | 140 | 6 | 30 | 100 | 3.1 | 0 | 79.1 | 13.6 | 4.2 |
8 | 6.1 wt% 1Ni-1Sn/ZnO | 140 | 6 | 30 | 100 | 20.2 | 0 | 64.6 | 10.4 | 4.8 |
160 | 6 | 30 | 100 | 3.1 | 0 | 80.1 | 15.1 | 1.7 | ||
9 | 4.1 wt% 1Ru-5Sn/SiO2 | 140 | 6 | 30 | 100 | 75.2 | 0 | 8.3 | 12.9 | 3.6 |
10 | 4.1 wt% 1Ru-5Sn/Al2O3 | 140 | 6 | 30 | 100 | 80.2 | 0 | 7.6 | 8.8 | 3.4 |
11 | 5 wt% Ru/(8:2)SnO2-SiO2 | 140 | 6 | 30 | 100 | 9.3 | 25.6 | 32.3 | 20.1 | 12.7 |
12 | 5 wt% Cu/(8:2)SnO2-SiO2 | 140 | 6 | 30 | 100 | 83 | 0 | 6.4 | 1.7 | 8.9 |
13 | 4.1 wt% 1(Cu-Ni)-5Sn/SiO2 | 140 | 6 | 30 | 100 | 79.3 | 0 | 6.7 | 10.1 | 3.9 |
제조예 | Catalyst | Temp.(oC) | H2Press.(bar) | Furfuryl alcohol Conv.% | C Yield (%) | |||||
MTHF | 1,2-PDO | 1,5-PDO | THFA | 2MF | Others | |||||
14 | 10 wt.% 1Ni-1Sn/ZnO | 230 | 30 | 100 | 0 | 84.1 | 11.8 | 3.2 | 0.6 | 0.3 |
230 | 40 | 100 | 0 | 90.4 | 9.1 | 0.3 | 0.2 | 0 | ||
250 | 40 | 100 | 0 | 91.4 | 8.4 | 0.2 | 0 | 0 | ||
15 | 10 wt.% 1Cu-1Sn/ZnO | 250 | 40 | 100 | 0 | 70.8 | 23.2 | 4.3 | 1.4 | 0.3 |
16 | 10 wt.% 1Co-1Sn/ZnO | 250 | 40 | 100 | 0 | 73.2 | 21.6 | 3.2 | 1.5 | 0.5 |
17 | 4.1 wt.% 1Ru-7Sn/ZnO | 250 | 40 | 100 | 0 | 77.4 | 17.7 | 2.8 | 1.2 | 0.9 |
18 | 10 wt.% Ni/ZnO | 250 | 40 | 100 | 47.2 | 17.3 | 28.4 | 5.1 | 1.2 | 0.8 |
19 | 10 wt.% 1Ni-1Sn/γ-Al2O3 | 250 | 40 | 100 | 3.2 | 38 | 37.7 | 14.9 | 5.1 | 1.1 |
20 | 10 wt.% 1Ni-1Sn/CeO2 | 250 | 40 | 100 | 0 | 80.5 | 14.8 | 3.7 | 0.5 | 0.5 |
Claims (14)
- 푸르푸랄(furfural), 푸르푸릴 알코올(furfuryl alcohol) 중 하나 이상을 포함하는 출발물질과 수소의 반응으로부터 1,2-펜탄디올을 제조하는데 사용되는 촉매에 있어서,염기성 지지체에 촉매활성금속이 담지 되되, 상기 촉매활성금속은 주석을 포함하고, 또 다른 금속으로서 전이금속 중의 하나 이상의 금속을 포함하는 것을 특징으로 하는 상기 출발물질의 수소화 반응에 의한 1,2-펜탄디올 제조용 촉매.
- 제 1항에 있어서,상기 염기성 지지체는 알칼리 산화물, 알칼리토류 산화물, 란탄족 산화물, 아연-산화물, 스피넬, 페로브스카이트, 하이드로탈사이트, 칼슘실리케이트, 염기성 제올라이트, 염기성 금속유기골격체 중에서 선택된 하나 이상인 것을 특징으로 하는 상기 출발물질의 수소화반응에 의한 1,2-펜탄디올 제조용 촉매.
- 제 1항에 있어서, 상기 염기성 지지체는 MgO, CaO, BaO-ZnO, MgO-Al2O3, ZnO, ZrO2, CeO2, 하이드록시아파타이트(hydroxyapatite), Mg2Al2O4, ZnAl2O4, BaTiO3, ZnTiO3, Cs2O, CsX(X = OH, Cl, Br, 또는 I), Zr계 MOFs, Mg계 MOFs, Ca계 MOFs, Sr계 MOFs, Ba계 MOFs, Mg2Al2O4, ZnAl2O4, BaTiO3, ZnTiO3 중에서 선택된 어느 하나 이상인 것을 특징으로 하는 상기 출발물질의 수소화반응에 의한 1,2-펜탄디올 제조용 촉매.
- 제 1항에 있어서,상기 촉매활성금속 중에서 주석의 함량은 20~99.5 몰% 인 것임을 특징으로 하는 상기 출발물질의 수소화반응에 의한 1,2-펜탄디올 제조용 촉매.
- 제 1항에 있어서,상기 전이금속은 8족, 9족, 10족, 11족에 속하는 전이금속 중의 하나 이상의 금속인 것을 특징으로 하는 상기 출발물질의 수소화반응에 의한 1,2-펜탄디올 제조용 촉매.
- 제 1항에 있어서,상기 전이금속은 Ru, Pt, Rh, Ir, Pd, Ni, Co, Cu 중에서 선택된 하나 이상인 것을 특징으로 하는 상기 출발물질의 수소화반응에 의한 1,2-펜탄디올 제조용 촉매.
- 제 1항에 있어서,상기 촉매는 산화성 분위기에서의 소성 없이 환원하여 사용되는 것임을 특징으로 하는 상기 출발물질의 수소화반응에 의한 1,2-펜탄디올 제조용 촉매.
- 제 1항 내지 제 7항 중 어느 한 항에 기재된 촉매의 존재 하에,푸르푸랄(furfural), 푸르푸릴 알코올(furfuryl alcohol) 중 하나 이상을 포함하는 출발물질의 수소화 반응으로부터 1,2-펜탄디올을 제조하는 방법.
- 제 8항에 있어서,상기 출발물질인 푸르푸랄(furfural), 푸르푸릴 알코올(furfuryl alcohol)은 바이오매스로부터 유래된 것임을 특징으로 하는 상기 출발물질의 수소화 반응으로부터 1,2-펜탄디올을 제조하는 방법.
- 제 8항에 있어서,상기 푸르푸랄은 자일란이 가수분해(hydrolysis)된 자일로스를 탈수반응하여 얻어진 것이며, 푸르푸릴 알코올은 상기 푸르푸랄이 수소화되어 생성된 것임을 특징으로 하는 상기 출발물질의 수소화 반응으로부터 1,2-펜탄디올을 제조하는 방법.
- 제 8항에 있어서,상기 반응온도는 100 ~ 200 ℃이고, 반응 압력은 5 ~ 50 bar이며, 상기 반응은 액상에서 진행되는 것을 특징으로 하는 상기 출발물질의 수소화 반응으로부터 1,2-펜탄디올을 제조하는 방법.
- 제 8항에 있어서,상기 반응온도는 200 ~ 300 ℃이고, 반응 압력은 5 ~ 100 bar이며, 상기 반응은 기상에서 진행되는 것을 특징으로 하는 상기 출발물질의 수소화 반응으로부터 1,2-펜탄디올을 제조하는 방법.
- 제 8항에 있어서,상기 출발물질을 1-프로판올, 이소프로판올, 1-부탄올, 2-부탄올 및 이의 혼합물 중에서 선택되는 어느 하나의 용매에 희석하여 액상에서 반응시키는 것을 특징으로 하는 상기 출발물질과 수소의 반응으로부터 1,2-펜탄디올을 제조하는 방법.
- 제 8항에 있어서,상기 촉매의 사용량은 상기 출발물질에 대하여 0.001 ~ 25 wt% 인 것을 특징으로 하는 상기 출발물질과 수소의 반응으로부터 1,2-펜탄디올을 제조하는 방법.