WO2017007005A1 - Matière imprimée rétro-réfléchissante anti-contrefaçon, son procédé de fabrication et procédé de détermination d'authenticité l'utilisant - Google Patents

Matière imprimée rétro-réfléchissante anti-contrefaçon, son procédé de fabrication et procédé de détermination d'authenticité l'utilisant Download PDF

Info

Publication number
WO2017007005A1
WO2017007005A1 PCT/JP2016/070183 JP2016070183W WO2017007005A1 WO 2017007005 A1 WO2017007005 A1 WO 2017007005A1 JP 2016070183 W JP2016070183 W JP 2016070183W WO 2017007005 A1 WO2017007005 A1 WO 2017007005A1
Authority
WO
WIPO (PCT)
Prior art keywords
retroreflective
printed matter
printing
layer
spherical transparent
Prior art date
Application number
PCT/JP2016/070183
Other languages
English (en)
Japanese (ja)
Inventor
博昭 島根
文人 小林
優徳 秋元
Original Assignee
共同印刷株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 共同印刷株式会社 filed Critical 共同印刷株式会社
Publication of WO2017007005A1 publication Critical patent/WO2017007005A1/fr

Abstract

La présente invention concerne une matière imprimée rétro-réfléchissante anti-contrefaçon qui peut être obtenue à un faible coût. Cette matière imprimée rétro-réfléchissante (10) anti-contrefaçon comprend un substrat d'impression (1), une couche de matériau réfléchissant imprimée (2) comprenant un matériau réfléchissant (2a), et une couche de corps sphérique transparent imprimée (3) comprenant des corps sphériques transparents (3a), dans ledit ordre, et le diamètre de particule moyen des corps sphériques transparents (3a) est de 10 µm à moins de 50 µm.
PCT/JP2016/070183 2015-07-08 2016-07-07 Matière imprimée rétro-réfléchissante anti-contrefaçon, son procédé de fabrication et procédé de détermination d'authenticité l'utilisant WO2017007005A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2015-137082 2015-07-08
JP2015137082A JP2017019144A (ja) 2015-07-08 2015-07-08 偽造防止用の再帰反射性印刷物、その製造方法及びそれを用いた真贋判定方法

Publications (1)

Publication Number Publication Date
WO2017007005A1 true WO2017007005A1 (fr) 2017-01-12

Family

ID=57685092

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2016/070183 WO2017007005A1 (fr) 2015-07-08 2016-07-07 Matière imprimée rétro-réfléchissante anti-contrefaçon, son procédé de fabrication et procédé de détermination d'authenticité l'utilisant

Country Status (2)

Country Link
JP (1) JP2017019144A (fr)
WO (1) WO2017007005A1 (fr)

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP7453802B2 (ja) 2020-02-25 2024-03-21 三菱鉛筆株式会社 筆記具

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH10193887A (ja) * 1997-01-16 1998-07-28 Japan Polymer-Ku Kk 再帰反射性の転写シート
JP2002019259A (ja) * 2000-07-10 2002-01-23 Shiseido Co Ltd 偽変造防止用素材
JP2008037096A (ja) * 2001-12-20 2008-02-21 Seiko Epson Corp 偽造対策を施した記録物
JP2014079994A (ja) * 2012-10-18 2014-05-08 Izumi Kogyo Kk 紐部材における光輝装飾構造およびその製造方法

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH10193887A (ja) * 1997-01-16 1998-07-28 Japan Polymer-Ku Kk 再帰反射性の転写シート
JP2002019259A (ja) * 2000-07-10 2002-01-23 Shiseido Co Ltd 偽変造防止用素材
JP2008037096A (ja) * 2001-12-20 2008-02-21 Seiko Epson Corp 偽造対策を施した記録物
JP2014079994A (ja) * 2012-10-18 2014-05-08 Izumi Kogyo Kk 紐部材における光輝装飾構造およびその製造方法

Also Published As

Publication number Publication date
JP2017019144A (ja) 2017-01-26

Similar Documents

Publication Publication Date Title
TWI641660B (zh) 磁性或可磁化色料顆粒及光學效應層
RU2681767C2 (ru) Способы отверждения на месте слоев с оптическим эффектом, полученных устройствами, генерирующими магнитное поле, генерируя вогнутые линии поля
CN103476596B (zh) 具有光学可变色层的光学可变防伪元件
EP1819525A1 (fr) Element de securite a aspect dependant de l'angle de vision
JP2008188973A (ja) 真偽判別可能な情報担持体
JP3398758B2 (ja) 偽造防止用情報担持体
JP5281773B2 (ja) インキ組成物
JP2017119404A (ja) 偽造防止用の再帰反射性物品、その製造方法及びそれを用いた真贋判定方法
WO2017007005A1 (fr) Matière imprimée rétro-réfléchissante anti-contrefaçon, son procédé de fabrication et procédé de détermination d'authenticité l'utilisant
JP2009269309A (ja) 真偽判別可能な情報担持体
JP2003182202A (ja) 潜像表示媒体
JP2016155903A (ja) フォトクロミック光輝性インキ及びその印刷物
CA3193623A1 (fr) Documents ou articles de securite comportant des couches a effet optique comprenant des particules de pigments magnetiques ou magnetisables et procedes de production desdites couc hes a effet optique
JP5533484B2 (ja) 潜像画像を有する印刷物
JP6686347B2 (ja) ホログラム積層体、情報記録媒体およびホログラム積層体の製造方法
JP6686346B2 (ja) ホログラム積層体、情報記録媒体およびホログラム積層体の製造方法
JP2002127649A (ja) 隠蔽情報形成体
JP2021076748A (ja) 再帰反射性積層体及びその製造方法、並びに真贋性判定方法
JP2004230783A (ja) 印刷物

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16821473

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 16821473

Country of ref document: EP

Kind code of ref document: A1