WO2015199461A1 - 전도성 실리콘 수지 조성물 및 이로부터 제조된 전자파 차폐용 가스켓 - Google Patents
전도성 실리콘 수지 조성물 및 이로부터 제조된 전자파 차폐용 가스켓 Download PDFInfo
- Publication number
- WO2015199461A1 WO2015199461A1 PCT/KR2015/006487 KR2015006487W WO2015199461A1 WO 2015199461 A1 WO2015199461 A1 WO 2015199461A1 KR 2015006487 W KR2015006487 W KR 2015006487W WO 2015199461 A1 WO2015199461 A1 WO 2015199461A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- silicone resin
- resin composition
- conductive
- conductive silicone
- gasket
- Prior art date
Abstract
Description
단위 | 비교예1 | 비교예2 | 실시예1 | 비교예3 | ||
내부식성 | 전 | Ω | 19 | 10 | 100 | 125 |
후 | Ω(%) | 170(895%) | 22(220%) | 132(32%) | 3050(2440%) | |
열충격 | 전 | Ω | 19 | 10 | 100 | 125 |
후 | Ω(%) | 71(370%) | 19(90%) | 119(19%) | 128(3%) | |
열팽창계수 | 106m/℃ | Cu_166.6 | SiC_- | Graphite_7.9 | ||
인장찬성계수 | Gpa | Cu_108 | SiC_- | Graphite_5~15 |
최고 차폐효과 | 최저 차폐효과 | ||
실시예1 | Ag/SiC | 80dB 이상(250.50MHz~1500.00MHz) | 65.5dB(30.00MHz) |
run | 단위 | 실시예1(열경화형) | 비교예4(수분경화) | |
연신율 | 1 | % | 140 | 70 |
2 | 138 | 65 | ||
3 | 135 | 66 | ||
평균 | 137 | 67 | ||
영구압축줄음율 | 1 | % | 30 | 55 |
2 | 28 | 50 | ||
3 | 30 | 50 | ||
평균 | 29 | 51 |
Claims (9)
- (a) 금속으로 코팅된 실리콘카바이드(SiC) 도전성 입자;(b) 열경화형 실리콘 수지; 및(c) 용매;를포함하는 것을 특징으로 하는 전도성 실리콘 수지 조성물.
- 제1항에 있어서,상기 (a) 도전성 입자 100중량부에 대하여 상기 (b) 성분은 30 내지 150중량부이며, 상기 (c) 성분은 5 내지 35중량부인 것을 특징으로 하는 전도성 실리콘 수지 조성물.
- 제1항에 있어서,상기 (a) 도전성 입자의 입도가 10 내지 300㎛인 것을 특징으로 하는 전도성 실리콘 수지 조성물.
- 제1항에 있어서,상기 (a) 도전성 입자의 금속은 은(Ag), 니켈(Ni), 구리(Cu) 및 알루미늄(Al)으로 구성된 군에서 선택되는 1종 이상인 것을 특징으로 하는 전도성 실리콘 수지 조성물.
- 제1항에 있어서,상기 (a) 도전성 입자의 금속은 2 내지 40중량%인 것을 특징으로 하는 전도성 실리콘 수지 조성물.
- 제1항에 있어서,상기 (b) 열경화형 실리콘 수지는 열경화형 일액형 또는 이액형 실리콘 수지인 것을 특징으로 하는 전도성 실리콘 수지 조성물.
- 제1항에 있어서,상기 (b) 열경화형 실리콘 수지의 점도가 비흐름성 내지 3000cps인 것을 특징으로 하는 전도성 실리콘 수지 조성물.
- 제1항에 있어서,상기 (c) 용매는 실리콘 오일, 탄화수소, 할로겐화 탄화수소, 에스테르 및 실록산으로 구성된 군에서 선택되는 1종 이상인 것을 특징으로 하는 전도성 실리콘 수지 조성물.
- 제1항의 전도성 실리콘 수지 조성물을 사용하여 제조된 전자파 차폐용 가스켓.