WO2012133910A1 - 耐応力腐食割れ性に優れた耐磨耗鋼板およびその製造方法 - Google Patents

耐応力腐食割れ性に優れた耐磨耗鋼板およびその製造方法 Download PDF

Info

Publication number
WO2012133910A1
WO2012133910A1 PCT/JP2012/059126 JP2012059126W WO2012133910A1 WO 2012133910 A1 WO2012133910 A1 WO 2012133910A1 JP 2012059126 W JP2012059126 W JP 2012059126W WO 2012133910 A1 WO2012133910 A1 WO 2012133910A1
Authority
WO
WIPO (PCT)
Prior art keywords
less
steel sheet
wear
steel
resistant steel
Prior art date
Application number
PCT/JP2012/059126
Other languages
English (en)
French (fr)
Inventor
植田　圭治
室田　康宏
石川　信行
Original Assignee
Ｊｆｅスチール株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ｊｆｅスチール株式会社 filed Critical Ｊｆｅスチール株式会社
Priority to EP12765557.9A priority Critical patent/EP2692890B1/en
Priority to AU2012233197A priority patent/AU2012233197B8/en
Priority to BR112013025002-0A priority patent/BR112013025002B1/pt
Priority to KR1020137026383A priority patent/KR20130133036A/ko
Priority to MX2013011154A priority patent/MX348365B/es
Priority to CN201280015444.1A priority patent/CN103459635B/zh
Priority to US14/008,104 priority patent/US9879334B2/en
Publication of WO2012133910A1 publication Critical patent/WO2012133910A1/ja

Abstract

建設機械、産業機械等に供して好適な耐応力腐食割れ性に優れる耐磨耗鋼板およびその製造方法を提供する。具体的には、質量％で、Ｃ：０．２０～０．２７％、Ｓｉ：０．０５～１．０％、Ｍｎ：０．３０～０．９０％、Ｐ、Ｓ、Ｎｂ：０．００５～０．０２５％、Ｔｉ：０．００８～０．０２０％、Ａｌ：０．１％以下、Ｎ：０．００１０～０．００６０％、さらに、Ｃｒ、Ｍｏ、Ｗ、Ｂの１種または２種以上を含有し、必要に応じてＣｕ、Ｎｉ、Ｖ、ＲＥＭ、Ｃａ、Ｍｇの１種または２種以上を含有し、ＤＩ＊が４５以上で、残部Ｆｅおよび不可避的不純物からなる組成を有し、ミクロ組織が焼戻しマルテンサイトを基地相とし、粒径が円相当直径で０．０１～０．５μｍ以下のＮｂ、Ｔｉ系析出物が２×１０２個／ｍｍ２以上存在する鋼板。また、上記記載の鋼組成を有する鋼片を加熱後、熱間圧延を行い、再加熱焼入れまたは直接焼入れを行う。

Description

耐応力腐食割れ性に優れた耐磨耗鋼板およびその製造方法
　本発明は、建設機械（ｃｏｎｓｔｒｕｃｔｉｏｎ　ｍａｃｈｉｎｅ）、産業機械（ｉｎｄｕｓｔｒｉａｌ　ｍａｃｈｉｎｅ）、造船（ｓｈｉｐｂｕｉｄｉｎｇ）、鋼管（ｓｔｅｅｌ　ｐｉｐｅ）、土木（ｃｉｖｉｌ　ｅｎｇｉｎｅｅｒｉｎｇ）、建築等に供して好適な板厚４ｍｍ以上の耐磨耗鋼板（ａｂｒａｓｉｏｎ　ｒｅｓｉｓｔａｎｔ　ｓｔｅｅｌ　ｐｌａｔｅ　ｏｒ　ｓｔｅｅｌ　ｓｈｅｅｔ）に係り、特に、耐応力腐食割れ性（ｒｅｓｉｓｔａｎｃｅ　ｏｆ　ｓｔｒｅｓｓ　ｃｏｒｒｏｓｉｏｎ　ｃｒａｃｋ）が優れたものに関する。
　建設機械、産業機械、造船、鋼管、土木、建築等の鉄鋼構造物や機械、装置等に熱間圧延鋼板が用いられる際には、鋼板の磨耗特性（ａｂｒａｓｉｏｎ　ｒｅｓｉｓｔａｎｔ　ｐｒｏｐｅｒｔｙ）が要求されることがある。磨耗は、機械、装置等、稼動する部位において、鋼材同士、あるいは土砂、岩石など異種材料との継続的な接触により発生し、鋼材の表層部が削り取られる現象である。
　鋼材の耐磨耗特性が劣ると、機械、装置の故障の原因となるだけでなく、構造物としての強度を維持できなくなる危険性があるため、高頻度での磨耗部位の補修、交換が不可避である。このため、磨耗する部位に適用される鋼材に対する耐磨耗特性の向上に対する要求は強い。
　従来、鋼材として優れた耐磨耗性を保有するためには、硬度を高めることが一般的であり、マルテンサイト単相組織（ｍａｒｔｅｎｓｉｔｅ　ｓｉｎｇｌｅ　ｐｈａｓｅ　ｍｉｃｒｏｓｔｒｕｃｔｕｒｅ）とすることにより飛躍的に高めることが可能である。また、マルテンサイト組織自体の硬さを上昇させるために、固溶Ｃ量（ａｍｏｕｎｔ　ｏｆ　ｓｏｌｉｄ　ｓｏｌｕｔｉｏｎ　ｃａｒｂｏｎ）を増加することが有効であり、種々の耐摩耗鋼板が開発されてきた（例えば、特許文献１~５）。
一方、鋼板に対して磨耗特性が要求される部位は、地鉄表面が露出する場合が多く、鋼材表面が腐食性の物質を含む水蒸気（ｍｏｉｓｔｕｒｅ　ｖａｐｏｒ）や、水分（ｍｏｉｓｔｕｒｅ）や油分（ｏｉｌ）などと接触し、鋼材の腐食が発生する。
　例えば、鉱石運搬用のコンベヤ（ｏｒｅ　ｃｏｎｖｅｙｅｒ）など鉱山機械（ｍｉｎｉｎｇ　ｍａｃｈｉｎｅｒｙ）に耐磨耗鋼が使用される場合には、土壌中の水分（ｍｏｉｓｔｕｒｅ　ｉｎ　ｓｏｉｌ）とともに、硫化水素（ｈｙｄｒｏｇｅｎ　ｓｕｌｆｉｄｅ）などの腐食性物質（ｃｏｒｒｏｓｉｖｅ　ｍａｔｅｒｉａｌ）が存在し、また、建設機械などに耐磨耗鋼が使用される場合には、ディーゼルエンジン（ｄｉｅｓｅｌ　ｅｎｇｉｎｅ）中に含まれる水分および酸化硫黄（ｓｕｌｆｕｒｉｃ　ｏｘｉｄｅ）などが存在し、何れも非常に厳しい腐食環境（ｃｏｒｒｏｓｉｏｎ　ｅｎｖｉｒｏｎｍｅｎｔ）となる場合がある。この際、鋼材表面での腐食反応（ｃｏｒｒｏｓｉｏｎ　ｒｅａｃｔｉｏｎ）においては、鉄がアノード反応（ａｎｏｄｅ　ｒｅａｃｔｉｏｎ）により酸化物（さび）を生成する一方で、水分のカソード反応（ｃａｔｈｏｄｅ　ｒｅａｃｔｉｏｎ）により水素が発生する。
　耐磨耗鋼のような高硬度なマルテンサイト組織の鋼材中に、腐食反応で生成した水素が侵入した場合には、鋼材が極端に脆化し、曲げ加工（ｂｅｎｄｉｎｇ　ｗｏｒｋ）や溶接などでの残留応力（ｗｅｌｄｉｎｇ　ｒｅｓｉｄｕａｌ　ｓｔｒｅｓｓ）や、使用環境（ｅｎｖｉｒｏｎｍｅｎｔ　ｏｆ　ｕｓａｇｅ）での負荷応力（ａｐｐｌｉｅｄ　ｓｔｒｅｓｓ）の存在化において、割れ（ｃｒａｃｋ）が発生する。これが応力腐食割れ（ｓｔｒｅｓｓ　ｃｏｒｒｏｓｉｏｎ　ｃｒａｃｋ）であり、機械、装置等に使用される鋼材には、稼動する安全性の観点から、耐磨耗性は勿論のこと、耐応力腐食割れ性に優れることが重要である。
特開平５−５１６９１号公報 特開平８−２９５９９０号公報 特開２００２−１１５０２４号公報 特開２００２−８０９３０号公報 特開２００４−１６２１２０号公報
日本学術振興会大１２９委員会（日本材料強度学会、１９８５）基準の応力腐食割れ標準試験法
　しかしながら、特許文献１~５等で提案されている耐磨耗鋼は、母材靭性、耐遅れ破壊特性（以上、特許文献１、３、４）、溶接性、溶接部の耐磨耗性、結露腐食環境における耐食性（以上、特許文献５）を備えることを目的とするもので、非特許文献１記載の応力腐食割れ標準試験法で優れる耐応力腐食割れ性と耐磨耗性を両立するには至っていない。
　そこで、本発明では、生産性（ｐｒｏｄｕｃｔｉｖｉｔｙ）の低下および製造コスト（ｐｒｏｄｕｃｔｉｏｎ　ｃｏｓｔ）の増大を引き起こすことなく、経済性（ｅｃｏｎｏｍｉｃ　ｅｆｆｉｃｉｅｎｃｙ）に優れ、耐応力腐食割れ性に優れる耐磨耗鋼板およびその製造方法を提供することを目的とする。
　本発明者らは、上記課題を達成するため、耐磨耗鋼板を対象に、優れた耐応力腐食割れ性能を確保するため、鋼板の化学成分、製造方法およびミクロ組織（ｍｉｃｒｏｓｔｒｕｃｔｕｒｅ）を決定する各種要因に関して鋭意研究を行い、以下の知見を得た。
　１．優れた耐磨耗特性を確保するためには、高硬度（ｈｉｇｈ　ｈａｒｄｎｅｓｓ）を確保することが必須であるが、過度の高硬度化は耐応力腐食割れ性を著しく低下させるため、硬度範囲を厳格に管理することが重要である。さらに、耐応力腐食割れ性を向上するためには、鋼板中に拡散性水素（ｄｉｆｆｕｓｉｂｌｅ　ｈｙｄｒｏｇｅｎ）のトラップサイト（ｔｒａｐ　ｓｉｔｅ）としてセメンタイト（ｃｅｍｅｎｔｉｔｅ）を分散することが有効である。このためには、Ｃをはじめとする鋼板の化学組成を厳格に管理して、鋼板の基地組織を焼戻しマルテンサイトとすることが重要である。
　焼戻しマルテンサイト組織中のＮｂ、Ｔｉの炭化物、窒化物および複合炭窒化物（ｃｏｍｐｌｅｘ　ｃａｒｂｏｎｉｔｒｉｄｅ）はその分散状態（ｄｉｓｐｅｒｓｉｏｎ　ｓｔａｔｅ）を適正に管理することにより、鋼材の腐食反応により生成した拡散性水素のトラップサイトとして作用し、水素脆化割れ（ｈｙｄｒｏｇｅｎ　ｅｍｂｒｉｔｔｌｅｍｅｎｔ　ｃｒａｃｋｉｎｇ）を抑制する効果を有する。
　焼戻しマルテンサイト組織中のＮｂ、Ｔｉの炭化物、窒化物および複合炭窒化物の分散状態には、圧延、熱処理および冷却条件などが影響を及ぼし、これら製造条件を管理することが重要である。これにより、腐食環境下における結晶粒界破壊を抑制し、応力腐食割れを効果的に防止できる。
　２．さらに、焼戻しマルテンサイト組織（ｔｅｍｐｅｒｅｄ　ｍａｒｔｅｎｓｉｔｅ　ｍｉｃｒｏｓｔｒｕｃｔｕｒｅ）の結晶粒界破壊（ｇｒａｉｎ　ｂｏｕｎｄａｒｙ　ｆｒａｃｔｕｒｅ）を効果的に抑制するには、結晶粒界強度（ｇｒａｉｎ　ｂｏｕｎｄａｒｙ　ｓｔｒｅｎｇｔｈ）を高める対策が有効であり、Ｐなど不純物元素の低減とともに、Ｍｎの成分範囲を管理する必要がある。Ｍｎは、焼入れ性（ｈａｒｄｅ　ｎａｂｉｌｉｔｙ）を向上する効果を有し耐磨耗性向上に寄与する一方、鋼片の凝固過程（ｓｏｌｉｄｉｆｉｃａｔｉｏｎ　ｐｒｏｃｅｓｓ）において、Ｐとともに共偏析（ｃｏ‐ｓｅｇｒｅｇａｔｉｏｎ）しやすい元素であり、ミクロ偏析部における結晶粒界強度を低下させる。
　また、結晶粒界破壊を効果的に抑制するには、結晶粒を微細化することが有効であり、結晶粒の成長を抑えるピンニング効果（ｐｉｎｎｉｎｇ　ｅｆｆｅｃｔ）を有する微細な介在物（ｉｎｃｌｕｓｉｏｎ）の分散が効果的である。このためには、ＮｂおよびＴｉを添加し、鋼中に炭窒化物を分散させることが有効である。
　本発明は、得られた知見に、さらに検討を加えてなされたもので、すなわち、
１．質量％で、
Ｃ：０．２０~０．２７％、
Ｓｉ：０．０５~１．０％、
Ｍｎ：０．３０~０．９０％
Ｐ：０．０１０％以下、
Ｓ：０．００５％以下、
Ｎｂ：０．００５~０．０２５％、
Ｔｉ：０．００８~０．０２０％、
Ａｌ：０．１％以下、
Ｎ：０．００１０~０．００６０％、
さらに、
Ｃｒ：０．０５~１．５％、
Ｍｏ：０．０５~１．０％、
Ｗ：０．０５~１．０％、
Ｂ：０．０００３~０．００３０％、
の１種または２種以上を含有し、（１）式で示される焼入れ性指数（ｈａｒｄｅｎａｂｉｌｉｔｙ　ｉｎｄｅｘ）ＤＩ＊が４５以上で、残部Ｆｅおよび不可避的不純物からなる組成を有し、ミクロ組織が焼戻しマルテンサイトを基地相とし、粒径が円相当直径で０．０１~０．５μｍのＮｂおよびＴｉの１種または２種を含有する炭化物、窒化物あるいは炭窒化物が２×１０２個／ｍｍ２以上存在することを特徴とする耐応力腐食割れ性に優れた耐磨耗鋼板。
ＤＩ＊＝３３．８５×（０．１×Ｃ）０．５　×（０．７×Ｓｉ＋１）×（３．３３×Ｍｎ＋１）×（０．３５×Ｃｕ＋１）×（０．３６×Ｎｉ＋１）×（２．１６×Ｃｒ＋１）×（３×Ｍｏ＋１）×（１．７５×Ｖ＋１）×（１．５×Ｗ＋１）・・・・・（１）
但し、各合金元素は含有量（質量％）を示し、含有しない場合は０とする。
２．鋼組成に、質量％でさらに、
Ｃｕ：１．５％以下、
Ｎｉ：２．０％以下、
Ｖ：０．１％以下、
の１種または２種以上を含有することを特徴とする１記載の耐応力腐食割れ性に優れた耐磨耗鋼板。
３．鋼組成に、質量％でさらに、
ＲＥＭ：０．００８％以下、
Ｃａ：０．００５％以下、
Ｍｇ：０．００５％以下、
の１種または２種以上を含有することを特徴とする１または２に記載の耐応力腐食割れ性に優れた耐磨耗鋼板。
４．更に、焼戻しマルテンサイトの平均結晶粒径が円相当直径で１５μｍ以下であることを特徴とする１乃至３のいずれか一つに記載の耐応力腐食割れ性に優れた耐磨耗鋼板。
５．更に、表面硬度がブリネル硬さで４００~５２０ＨＢＷ１０／３０００であることを特徴とする１乃至４のいずれか一つに記載の耐応力腐食割れ性に優れた耐磨耗鋼板。
６．１乃至３のいずれか一つに記載の鋼組成を有する鋼片を１０００℃~１２００℃に加熱後、熱間圧延を行い、冷却後、Ａｃ３~９５０℃に再加熱して焼入れを行うことを特徴とする耐応力腐食割れ性に優れた耐磨耗鋼板の製造方法。
７．１乃至３のいずれか一つに記載の鋼組成を有する鋼片を１０００℃~１２００℃に加熱後、８５０℃以上の温度域で熱間圧延を行い、熱間圧延終了後、直ちにＡｒ３~９５０℃の温度から焼入れを行う耐応力腐食割れ性に優れた耐磨耗鋼板。
　なお、本発明では、焼戻しマルテンサイトの平均結晶粒径は、焼戻しマルテンサイトが旧オーステナイト粒であるとして、旧オーステナイト粒径の円相当径にて平均結晶粒径を求めた。
　本発明によれば、生産性の低下および製造コストの増大を引き起こすことなく、優れた耐応力腐食割れ性を有する耐磨耗鋼板が得られ、鋼構造物の安全性や寿命の向上に大きく寄与し、産業上格段の効果を奏する。
Ｐ含有量が０．００７~０．００９％である耐摩耗鋼（ブリネル硬さで４５０~５００ＨＢＷ１０／３０００のもの）での耐応力腐食割れ特性（ＫＩＳＣＣ）とＭｎ量との関係を示す図である。 Ｍｎ含有量が０．５~０．７％である耐摩耗鋼（ブリネル硬さで４５０~５００ＨＢＷ１０／３０００のもの）での耐応力腐食割れ特性（ＫＩＳＣＣ）とＰ量との関係を示す図である。 応力腐食割れ標準試験に用いる試験片形状を示す図。 図３に示す試験片を用いる試験機の構成を示す図。
［ミクロ組織］
　本発明では、鋼板のミクロ組織の基地相を焼戻しマルテンサイトとし、さらに、ミクロ組織中のＮｂおよびＴｉの１種または２種を含有する炭化物、窒化物あるいは炭窒化物（以下、Ｎｂ、Ｔｉ系析出物）の存在状態を規定する。
　Ｎｂ、Ｔｉ系析出物の粒径は円相当径で０．０１~０．５μｍとする。０．０１μｍ未満では、拡散性水素のトラップサイトとして水素脆化割れを抑制する効果が飽和するだけでなく、実製造で０．０１μｍ未満に管理するには、製造負荷が極度に増大し、製造コストが上昇する。一方、０．５μｍを越えると熱間圧延および熱処理時の結晶粒の粗大化を抑制する効果、および拡散性水素のトラップサイトとして水素脆化割れを抑制する効果が得られない。
　上記粒径のＮｂ、Ｔｉ系析出物がミクロ組織中で２×１０２個／ｍｍ２未満であると、熱間圧延および熱処理時の結晶粒の粗大化を抑制する効果、および拡散性水素のトラップサイトとして水素脆化割れを抑制する効果が得られないため、２×１０２個／ｍｍ２以上とする。
　本発明では、更に耐応力腐食割れ性を向上させる場合、上記に加えて、鋼板のミクロ組織の基地相（ｂａｓｅ　ｐｈａｓｅ　ｏｒ　ｍａｉｎ　ｐｈａｓｅ）を平均結晶粒径が円相当直径で１５μｍ以下の焼戻しマルテンサイトにする。鋼板の耐磨耗特性を有するためには、焼戻しマルテンサイト組織とすることが必要である。ただし、焼戻しマルテンサイトの平均結晶粒径が円相当直径で１５μｍを超えると耐応力腐食割れ性が劣化する。このため、焼戻しマルテンサイトの平均結晶粒径は１５μｍ以下とすることが好ましい。
　なお、母相中に焼戻しマルテンサイトの他に、ベイナイト（ｂａｉｎｉｔｅ）、パーライト（ｐｅａｒｌｉｔｅ）およびフェライト（ｆｅｒｒｉｔｅ）等の組織が混在すると、硬度が低下し、耐摩耗性が低下するため、これらの組織の面積分率（ａｒｅａ　ｒａｔｉｏ）は少ない方が良く、混在する場合は面積分率で５％以下とすることが望ましい。
　一方、マルテンサイトが混在すると、耐応力腐食割れ性が低下するため少ないほうが良く、面積分率で１０％以下の場合には影響が無視できるため含有してもよい。
また、表面硬度がブリネル硬さ（Ｂｒｉｎｅｌｌ　ｈａｒｄｎｅｓｓ）で４００ＨＢＷ１０／３０００未満の場合には、耐磨耗鋼としての寿命が短くなり、一方、５２０ＨＢＷ１０／３０００を超えると耐応力腐食割れ性が顕著に劣化するようになるため、表面硬度をブリネル硬さで４００~５２０ＨＢＷ１０／３０００の範囲とすることが好ましい。
　［成分組成］
　本発明では、優れた耐応力腐食割れ性を確保するため、鋼板の成分組成を規定する。なお、説明において％は質量％とする。
Ｃ：０．２０~０．２７％
　Ｃは、マルテンサイトの硬度を高め、優れた耐磨耗性を確保するために重要な元素でその効果を得るため、０．２０％以上の含有を必要とする。一方、０．２７％を越えて含有すると、マルテンサイトの硬さが過度に上昇し、耐応力腐食割れ性が低下する。このため、０．２０~０．２７％の範囲に限定する。好ましくは、０．２１~０．２６％である。
Ｓｉ：０．０５~１．０％
　Ｓｉは、脱酸材（ｄｅｏｘｉｄｉｚｉｎｇ　ａｇｅｎｔ）として作用し、製鋼上、必要であるだけでなく、鋼に固溶して固溶強化（ｓｏｌｉｄ　ｓｏｌｕｔｉｏｎ　ｓｔｒｅｎｇｔｈｅｎｉｎｇ）により鋼板を高硬度化する効果を有する。このような効果を得るためには、０．０５％以上の含有を必要とする。一方、１．０％を超えて含有すると、溶接性（ｗｅｌｄａｂｉｌｉｔｙ）が劣化するため、０．０５~１．０％の範囲に限定する。好ましくは、０．０７~０．５％である。
Ｍｎ：０．３０~０．９０％
　Ｍｎは、鋼の焼入れ性（ｈａｒｄｅｎａｂｉｌｉｔｙ）を増加させる効果を有し、母材の硬度を確保するために０．３０％以上は必要である。一方、０．９０％を超えて含有すると、母材の靭性（ｔｏｕｇｈｎｅｓｓ）、延性（ｄｕｃｔｉｌｉｔｙ）および溶接性が劣化するだけでなく、Ｐの粒界偏析（ｉｎｔｅｒｇｒａｎｕｌａｒ　ｓｅｇｒｅｇａｔｉｏｎ）を助長し、耐応力腐食割れの発生を助長する。図１はＰ含有量が０．００７~０．００９％である耐摩耗鋼（ブリネル硬さで４５０~５００ＨＢＷ１０／３０００のもの）での耐応力腐食割れ特性（ＫＩＳＣＣ）とＭｎ量との関係である。実験方法は後述する実施例と同じであるが、Ｍｎ量が増えるほどＫＩＳＣＣ値が低下、すなわち耐応力腐食割れ特性が低下している。このため、Ｍｎ含有量は０．３０~０．９０％の範囲に限定する。好ましくは、０．３５~０．８５％である。
Ｐ：０．０１０％以下
　Ｐが０．０１０％を超えて含有すると、粒界に偏析し、耐応力腐食割れの発生起点となる。図２はＭｎ含有量が０．５~０．７％である耐摩耗鋼（ブリネル硬さで４５０~５００ＨＢＷ１０／３０００のもの）での耐応力腐食割れ特性（ＫＩＳＣＣ）とＰ量との関係である。Ｐ量が増えるほどＫＩＳＣＣ値が低下することが明白である。このため、Ｐ含有量は０．０１０％を上限とし、可能なかぎり低減することが望ましい。望ましくは０．０８５％以下とする。
　Ｓ：０．００５％以下
　Ｓは母材の低温靭性や延性を劣化させるため、０．００５％を上限として低減することが望ましい。好ましくは０．００３％以下、より好ましくは０．００２％以下とする。
　Ｎｂ：０．００５~０．０２５％
　Ｎｂは、炭窒化物として析出し、母材および溶接熱影響部（ｗｅｌｄ　ｈｅａｔ−ａｆｆｅｃｔｅｄ　ｚｏｎｅ）のミクロ組織を微細化するとともに、固溶Ｎ（ｓｏｌｕｔｅ　Ｎ）を固定して靱性を改善するだけでなく、生成した炭窒化物が拡散性水素のトラップサイトに有効であり、応力腐食割れ抑制の効果を兼備する重要な元素である。このような効果を得るためには、０．００５％以上の含有が必要である。一方、０．０２５％を越えて含有すると、粗大な炭窒化物が析出し、破壊の起点（ｏｒｉｇｉｎ　ｏｆ　ｔｈｅ　ｆｒａｃｔｕｒｅ）となることがある。このため、０．００５~０．０２５％の範囲に限定する。
　Ｔｉ：０．００８~０．０２０％
　Ｔｉは、窒化物もしくはＮｂとともに炭窒化物を形成し、結晶粒の粗大化を抑制する効果を有するとともに、固溶Ｎの低減による靱性の劣化を抑制する効果を有する。さらに、生成した炭窒化物が拡散性水素のトラップサイトに有効であり、応力腐食割れ抑制の効果を兼備する重要な元素である。このような効果を得るためには、０．００８％以上の含有が必要である。一方、０．０２０％を越えて含有すると、析出物が粗大化し母材の靱性を劣化する。このため、０．００５~０．０２０％の範囲に限定する。
　Ａｌ：０．１％以下
　Ａｌは、脱酸剤として作用し、鋼板の溶鋼の脱酸プロセス（ｄｅｏｘｉｄｉｚｉｎｇ　ｐｒｏｃｅｓｓ）に於いて、もっとも汎用的に使われる。また、鋼中の固溶Ｎを固定してＡｌＮを形成することにより、結晶粒の粗大化を抑制する効果を有するとともに、固溶Ｎの低減による靱性の劣化を抑制する効果を有する。一方、０．１％を超えて含有すると、溶接時に溶接金属部（ｗｅｌｄ　ｍｅｔａｌ）に混入して、溶接金属の靭性を劣化させるため、０．１％以下に限定する。好ましくは０．０８％以下とする。
　Ｎ：０．００１０~０．００６０％
　ＮはＴｉおよびＮｂと結合して窒化物、あるいは炭窒化物として析出して、熱間圧延および熱処理時の結晶粒の粗大化を抑制する効果、および拡散性水素のトラップサイトとして水素脆化割れを抑制する効果を有する。このような効果を有するために、０．００１０％以上のＮを含有する必要がある．一方、０．００６０％を超えて含有すると、固溶Ｎ量が増加し、靭性が著しく低下する．このため、Ｎは０．００１０~０．００６０％に限定する。
　Ｃｒ、Ｍｏ、ＷおよびＢの１種または２種以上
　Ｃｒ：０．０５~１．５％
　Ｃｒは、鋼の焼入れ性を増加させ、母材の高硬度化に有効な元素である。このような効果を有するためには、０．０５％以上の添加が必要である。一方、１．５％を越えて含有すると、母材靭性および耐溶接割れ性（ｗｅｌｄ　ｃｒａｃｋ　ｒｅｓｉｓｔａｎｃｅ）が低下する。このため、０．０５~１．５％の範囲に限定する。
　Ｍｏ：０．０５~１．０％
Ｍｏは、焼入れ性を顕著に増加させ、母材の高硬度化に有効な元素である。このような効果を得るためには、０．０５％以上とすることが好ましいが、１．０％を超えると、母材靭性、延性および耐溶接割れ性に悪影響を及ぼすため、１．０％以下とする。
　Ｗ：０．０５~１．０％
Ｗは、焼入れ性を顕著に増加させ、母材の高硬度化に有効な元素である。このような効果を得るためには、０．０５％以上とすることが好ましいが、１．０％を超えると、母材靭性、延性および耐溶接割れ性に悪影響を及ぼすため、１．０％以下とする。
　Ｂ：０．０００３~０．００３０％
Ｂは、微量の添加で焼入れ性を顕著に増加させ、母材の高硬度化に有効な元素である。このような効果を得るためには、０．０００３％以上とすることが好ましいが、０．００３０％を超えると、母材靭性、延性および耐溶接割れ性に悪影響を及ぼすため、０．００３０％以下とする。
　ＤＩ＊＝３３．８５×（０．１×Ｃ）０．５　×（０．７×Ｓｉ＋１）×（３．３３×Ｍｎ＋１）×（０．３５×Ｃｕ＋１）×（０．３６×Ｎｉ＋１）×（２．１６×Ｃｒ＋１）×（３×Ｍｏ＋１）×（１．７５×Ｖ＋１）×（１．５×Ｗ＋１）
　但し、各合金元素は含有量（質量％）を示し、含有しない場合は０とする。
母材の基地組織を焼戻しマルテンサイトとして、耐磨耗性を向上させるためには、上式で規定されるＤＩ＊が４５以上を満足させることが重要である。ＤＩ＊が４５未満の場合、板厚表層からの焼入れ深さが１０ｍｍを下回り、耐磨耗鋼としての寿命が短くなるため、４５以上とする。
　以上が本発明の基本成分組成で残部は、Ｆｅおよび不可避的不純物とするが、本発明では、さらに、強度特性を向上させる場合、Ｃｕ、Ｎｉ、Ｖの１種または２種以上を含有することができる。Ｃｕ、Ｎｉ、Ｖは、いずれも鋼の強度向上に寄与する元素であり、所望する強度に応じて適宜含有する。
　Ｃｕを含有する場合は、１．５％を超えると熱間脆性（ｈｏｔ　ｂｒｉｔｔｌｅｎｅｓｓ）を生じて鋼板の表面性状（ｓｕｒｆａｃｅ　ｐｒｏｐｅｒｔｙ）を劣化させるため、１．５％以下とする。
　Ｎｉを含有する場合は、２．０％を超えると効果が飽和し、経済的に不利になるため、２．０％以下とする。Ｖを含有する場合は、０．１％を超えると、母材靭性および延性を劣化させるため、０．１％以下とする。
　本発明では、さらに、靭性を向上させる場合、ＲＥＭ、Ｃａ、Ｍｇの１種または２種以上を含有することができる。ＲＥＭ、ＣａおよびＭｇは、いずれも靭性向上に寄与し、所望する特性に応じて選択して含有させる。
　ＲＥＭを含有する場合は、０．００２％以上とすることが好ましいが、０．００８％を超えても効果が飽和するため、０．００８％を上限とする。Ｃａを含有する場合は、０．０００５％以上とすることが好ましいが、０．００５％を超えても効果が飽和するため、０．００５％を上限とする。Ｍｇを含有する場合は、０．００１％以上とすることが好ましいが、０．００５％を超えても効果が飽和するため、０．００５％を上限とする。
［製造条件］
　説明において、温度に関する「℃」表示は、板厚の１／２位置における温度を意味するものとする。
　本発明に係る耐磨耗鋼板は、上記した組成の溶鋼（ｍｏｌｔｅｎ　ｓｔｅｅｌ）を、公知の溶製方法（ｓｔｅｅｌｍａｉｋｉｎｇ　ｐｒｏｃｅｓｓ）で溶製し、連続鋳造法（ｃｏｎｔｉｎｕｏｕｓ　ｃａｓｔｉｎｇ）あるいは造塊（ｉｎｇｏｔ　ｃａｓｔｉｎｇ）−分塊圧延法（ｂｌｏｏｍｉｎｇ　ｍｅｔｈｏｄ）により、所定寸法のスラブ（ｓｌａｂ）等の鋼素材とすることが好ましい。
　次いで、得られた鋼素材を１０００~１２００℃に再加熱後、熱間圧延し、所望の板厚の鋼板とする。再加熱温度が１０００℃未満では、熱間圧延での変形抵抗（ｄｅｆｏｒｍａｔｉｏｎ　ｒｅｓｉｓｔａｎｃｅ）が高くなり、１パス当たりの圧下率量（ｒｏｌｌｉｎｇ　ｒｅｄｕｃｔｉｏｎ）が大きく取れなくなることから、圧延パス数が増加し、圧延能率（ｒｏｌｌｉｎｇ　ｅｆｆｉｃｉｅｎｃｙ）の低下を招くとともに、鋼素材（スラブ）中の鋳造欠陥（ｃａｓｔ　ｄｅｆｅｃｔ）を圧着することができない場合がある。
　一方、再加熱温度が１２００℃を超えると、加熱時のスケール（ｓｃａｌｅ）によって表面疵（ｓｕｒｆａｃｅ　ｓｃｒａｔｃｈ）が生じやすく、圧延後の手入れ（ｒｅｐａｉｒ）の負荷が増大する。このため、鋼素材の再加熱温度は１０００~１２００℃の範囲とする。直送圧延する場合は、鋼素材が１０００~１２００℃で熱間圧延を開始する。熱間圧延における圧延条件は特に規定しない。
　熱間圧延後に鋼板内の温度の均一化を図り、特性のばらつき（ｃｈａｒａｃｔｅｒｉｓｔｉｃ　ｖａｒｉａｔｉｏｎ）を抑えるため再加熱処理を熱間圧延後、空冷した後に行う。再加熱処理の前に鋼板はフェライト、ベイナイト、またはマルテンサイトへの変態を完了している必要があり、再加熱熱処理前に、鋼板温度が３００℃以下、好ましくは２００℃以下、より好ましくは１００℃以下まで冷却する。冷却後に再加熱処理を行うが、再加熱温度がＡｃ３以下では組織中にフェライトが混在し、硬度が低下する。一方、９５０℃を超えると、結晶粒が粗大化し、靱性および耐応力腐食割れ性が低下するため、Ａｃ３~９５０℃とする。Ａｃ３（℃）は、例えば、次式で求めることが可能である。
Ａｃ３＝８５４−１８０Ｃ＋４４Ｓｉ−１４Ｍｎ−１７．８Ｎｉ−１．７Ｃｒ
（ただし、Ｃ、Ｓｉ、Ｍｎ、　Ｎｉ、Ｃｒ：各合金元素の含有量（ｍａｓｓ％））
　再加熱の保持時間（ｈｏｌｄｉｎｇ　ｔｉｍｅ）は鋼板内の温度が均一になれば短時間でもよい。一方、長時間になると、結晶粒が粗大化し、靭性および耐応力腐食割れ性が低下するので、１ｈｒ以内が望ましい。なお、熱間圧延後に再加熱する場合は熱間圧延の終了温度は特に規定しない。
　再加熱後、焼入れ（ＲＱ）を行う。焼入れ後、鋼板内の特性をより均一化するとともに、耐応力腐食割れ性を向上させる場合、１００~３００℃に再加熱して焼戻（ｔｅｍｐｅｒｉｎｇ）をしてもよい。焼戻し温度（ｔｅｍｐｅｒｉｎｇ　ｔｅｍｐｅｒａｔｕｒｅ）が３００℃を超えると、硬度の低下が大きくなり耐磨耗性が低下するとともに、生成するセメンタイトが粗大化し、拡散性水素のトラップサイトとしての効果が得られなくなる。
　一方、焼戻し温度が１００℃未満では、上記した効果が得られない。保持時間は鋼板内の温度が均一になれば短時間でもよい。一方、保持時間が長時間になると、生成するセメンタイトが粗大化し、拡散性水素のトラップサイトとしての効果が低下するので、１ｈｒ以内が望ましい。
　熱間圧延後、再加熱処理を施さない場合は、圧延終了温度をＡｒ３~９５０℃とし、圧延終了後、直ちに焼入れ（ＤＱ）を行ってもよい。焼入れの開始温度（圧延終了温度と略同じ）は、Ａｒ３未満では、組織中にフェライトが混入し、硬度が低下し、一方、９５０℃以上になると、結晶粒が粗大化し、靱性および耐応力腐食割れ性が低下するため、Ａｒ３~９５０℃とする。尚、Ａｒ３点は例えば、次式で求めることが可能である。
　Ａｒ３＝８６８−３９６Ｃ＋２５Ｓｉ−６８Ｍｎ−２１Ｃｕ−３６Ｎｉ−２５Ｃｒ−３０Ｍｏ（ただし、Ｃ、Ｓｉ、Ｍｎ、Ｃｕ、Ｎｉ、Ｃｒ、Ｍｏ：各合金元素の含有量（質量％））焼入れ後、焼戻し処理を行う場合は、熱間圧延後、再加熱する場合と同様とする。
　転炉（ｓｔｅｅｌ　ｃｏｎｖｅｒｔｅｒ）−取鍋精錬（ｌａｄｌｅ　ｒｅｆｉｎｉｎｇ）−連続鋳造法で、表１−１および表１−２に示す種々の成分組成に調製した鋼スラブ（ｓｔｅｅｌ　ｓｌａｂ）を、９５０~１２５０℃に加熱した後、熱間圧延を施し、一部の鋼板には圧延直後に焼入れ（ＤＱ）をし、その他の鋼板については、圧延後空冷し、再加熱後焼入れ（ＲＱ）を行った。
　得られた鋼板について、ミクロ組織調査、表面硬度測定、母材靭性、応力腐食割れ性試験を下記の要領で実施した。
　ミクロ組織の調査は、得られた各鋼板の板厚１／４ｔ部における圧延方向に平行な断面について、ミクロ組織観察用サンプルを採取し、ナイタール腐食（ｎｉｔａｌ　ｃｏｒｒｏｓｉｏｎ　ｔｒｅａｔｍｅｎｔ）の後、５００倍の光学顕微鏡（ｏｐｔｉｃａｌ　ｍｉｃｒｏｓｃｏｐｅ）で組織を撮影して評価した。
　また、焼戻しマルテンサイトの平均結晶粒径の評価は、各鋼板の板厚１／４ｔ部における圧延方向に平行な断面について、ピクリン酸腐食（ｐｉｃｒｉｃ　ａｃｉｄ　ｃｏｒｒｏｓｉｏｎ　ｔｒｅａｔｍｅｎｔ）の後、光学顕微鏡にて５００倍で５視野撮影した後、画像解析装置（ｉｍａｇｅ　ａｎａｌｙｚａｔｉｏｎ　ｅｑｕｉｐｍｅｎｔ）を用いた。なお、焼戻しマルテンサイトの平均結晶粒径は、焼戻しマルテンサイト結晶粒径が旧オーステナイト粒径と同じであるとして、旧オーステナイト粒径の円相当径にて平均結晶粒径を求めた。
　さらに、焼戻しマルテンサイト組織中のＮｂ、Ｔｉ系析出物の個数密度の調査は、各鋼板の板厚１／４ｔ部における圧延方向に平行な断面について、透過型電子顕微鏡（ｔｒａｎｓｍｉｓｓｉｏｎ　ｅｌｅｃｔｒｏｎ　ｍｉｃｒｏｓｃｏｐｅ）にて５００００倍の撮影を１０視野行い、Ｎｂ、Ｔｉ系析出物の個数を調べた。
　表面硬度の測定はＪＩＳ　Ｚ２２４３（１９９８）に準拠し、表層下の表面硬度（表層のスケールを除去した後に測定した表面の硬度）を測定した。測定は１０ｍｍのタングステン硬球（ｔｕｎｇｓｔｅｎ　ｈａｒｄ　ｂａｌｌ）を使用し、荷重は３０００ｋｇｆとした。
　各鋼板の板厚１／４位置の圧延方向と垂直な方向から、ＪＩＳ　Ｚ　２２０２（１９９８年）の規定に準拠してシャルピーＶノッチ試験片（Ｖ　ｎｏｔｃｈ　ｔｅｓｔ　ｓｐｅｃｉｍｅｎ）を採取し、ＪＩＳ　Ｚ　２２４２（１９９８年）の規定に準拠して各鋼板について３本のシャルピー衝撃試験（Ｃｈａｒｐｙ　ｉｍｐａｃｔ　ｔｅｓｔ）を実施し、−２０℃での吸収エネルギーを求め、母材靭性を評価した。３本の吸収エネルギー（ｖＥ−２０）の平均値が３０Ｊ以上を母材靭性に優れるもの（本発明範囲内）とした。
　応力腐食割れ性試験は、日本学術振興会大１２９委員会（日本材料強度学会、１９８５）基準の応力腐食割れ標準試験法に準拠して実施した。試験片形状を図３、試験機形状を図４に示す。試験条件は、試験溶液：３．５％ＮａＣｌ、ｐＨ：６．７~７．０、試験温度：３０℃、最大試験時間：５００時間とし、応力腐食割れ性の下限界応力拡大係数（ｔｈｒｅｓｈｏｌｄ　ｓｔｒｅｓｓ　ｉｎｔｅｎｓｉｔｙ　ｆａｃｔｏｒ）ＫＩＳＣＣを求めた。表面硬度が４００~５２０ＨＢＷ１０／３０００、母材靭性が３０Ｊ以上、かつ、ＫＩＳＣＣが１００ｋｇｆ／ｍｍ−３／２以上を本発明の目標性能とした。
　表２−１~表２−４に供試鋼板の製造条件および上記試験結果を示す。本発明例（Ｎｏ．１，４~１２）は、上記目標性能を満足することが確認されたが、比較例（Ｎｏ１、２、１３~２８）は、表面硬度、母材靭性、および耐応力腐食割れ性のいずれか、あるいはそれらのうちの複数が目標性能を満足できない。
Figure JPOXMLDOC01-appb-T000001
Figure JPOXMLDOC01-appb-T000002
Figure JPOXMLDOC01-appb-T000003
Figure JPOXMLDOC01-appb-T000004
Figure JPOXMLDOC01-appb-T000005
Figure JPOXMLDOC01-appb-T000006

Claims (7)

  1. 　質量％で、
    Ｃ：０．２０~０．２７％、
    Ｓｉ：０．０５~１．０％、
    Ｍｎ：０．３０~０．９０％、
    Ｐ：０．０１０％以下、
    Ｓ：０．００５％以下、
    Ｎｂ：０．００５~０．０２５％、
    Ｔｉ：０．００８~０．０２０％、
    Ａｌ：０．１％以下、
    Ｎ：０．００１０~０．００６０％、
    さらに、
    Ｃｒ：０．０５~１．５％、
    Ｍｏ：０．０５~１．０％、
    Ｗ：０．０５~１．０％、
    Ｂ：０．０００３~０．００３０％、
    の１種または２種以上を含有し、（１）式で示されるＤＩ＊が４５以上で、残部Ｆｅおよび不可避的不純物からなる組成を有し、ミクロ組織が焼戻しマルテンサイトを基地相とし、粒径が円相当直径で０．０１~０．５μｍのＮｂおよびＴｉの１種または２種を含有する炭化物、窒化物あるいは炭窒化物が２×１０２個／ｍｍ２以上存在する耐磨耗鋼板。
    ＤＩ＊＝３３．８５×（０．１×Ｃ）０．５　×（０．７×Ｓｉ＋１）×（３．３３×Ｍｎ＋１）×（０．３５×Ｃｕ＋１）×（０．３６×Ｎｉ＋１）×（２．１６×Ｃｒ＋１）×（３×Ｍｏ＋１）×（１．７５×Ｖ＋１）×（１．５×Ｗ＋１）・・・・・（１）
    但し、各合金元素は含有量（質量％）を示し、含有しない場合は０とする。
  2. 　鋼組成に、質量％でさらに、
    Ｃｕ：１．５％以下、
    Ｎｉ：２．０％以下、
    Ｖ：０．１％以下、
    の１種または２種以上を含有する請求項１記載の耐磨耗鋼板。
  3. 　鋼組成に、質量％でさらに、
    ＲＥＭ：０．００８％以下、
    Ｃａ：０．００５％以下、
    Ｍｇ：０．００５％以下、
    の１種または２種以上を含有する請求項１または２に記載の耐磨耗鋼板。
  4. 　更に、焼戻しマルテンサイトの平均結晶粒径が円相当直径で１５μｍ以下である請求項１乃至３のいずれか一つに記載の耐磨耗鋼板。
  5. 　更に、表面硬度がブリネル硬さで４００~５２０ＨＢＷ１０／３０００である請求項１乃至４のいずれか一つに記載の耐磨耗鋼板。
  6. 　請求鋼１乃至３のいずれか一つに記載の鋼組成を有する鋼片を１０００℃~１２００℃に加熱後、熱間圧延を行い、冷却後、Ａｃ３~９５０℃に再加熱して焼入れを行う耐磨耗鋼板の製造方法。
  7. 　請求鋼１乃至３のいずれか一つに記載の鋼組成を有する鋼片を１０００℃~１２００℃に加熱後、８５０℃以上の温度域で熱間圧延を行い、熱間圧延終了後、直ちにＡｒ３~９５０℃の温度から焼入れを行う耐磨耗鋼板の製造方法。
PCT/JP2012/059126 2011-03-29 2012-03-28 耐応力腐食割れ性に優れた耐磨耗鋼板およびその製造方法 WO2012133910A1 (ja)