WO2012053831A2 - 터치 패널용 점착제 조성물 - Google Patents
터치 패널용 점착제 조성물 Download PDFInfo
- Publication number
- WO2012053831A2 WO2012053831A2 PCT/KR2011/007814 KR2011007814W WO2012053831A2 WO 2012053831 A2 WO2012053831 A2 WO 2012053831A2 KR 2011007814 W KR2011007814 W KR 2011007814W WO 2012053831 A2 WO2012053831 A2 WO 2012053831A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- pressure
- sensitive adhesive
- adhesive composition
- substrate
- touch panel
- Prior art date
Abstract
Description
실시예 | 비교예 | |||||||
1 | 2 | 3 | 4 | 1 | 2 | 3 | ||
기포발생 억제성 | 내열 조건 | O | O | O | O | O | O | O |
들뜸/박리 억제성 | 내열 조건 | O | O | O | O | O | O | O |
휨 정도 (단위: mm) | 내열 조건 | 0.7 | 0.6 | 0.6 | 0.7 | 0.6 | 0.6 | 0.8 |
저항변화율 | 8% | 5% | 4% | 9% | 18% | 18% | 20% |
Claims (18)
- 아크릴 중합체 및 티올 화합물을 포함하는 터치 패널용 점착제 조성물.
- 제 1 항에 있어서, 아크릴 중합체는 (메타)아크릴산 에스테르 단량체 및 가교성 관능기를 가지는 공중합성 단량체를 중합된 형태로 포함하는 터치 패널용 점착제 조성물.
- 제 2 항에 있어서, (메타)아크릴산 에스테르 단량체는, 탄소수 1 내지 20의 알킬기를 가지는 알킬 (메타)아크릴레이트인 터치 패널용 점착제 조성물.
- 제 2 항에 있어서, 가교성 관능기가 히드록시기, 카복실기, 질소 함유기, 에폭시기 또는 이소시아네이트기인 터치 패널용 점착제 조성물.
- 제 1 항에 있어서, 아크릴 중합체는 중량평균분자량이 35만 내지 250만인 터치 패널용 점착제 조성물.
- 제 6 항에 있어서, R2는, 탄소수 4 내지 20의 알킬기인 터치 패널용 점착제 조성물.
- 제 1 항에 있어서, 점착제 조성물은 아크릴 중합체 100 중량부에 대하여 0.001 중량부 내지 5 중량부의 티올 화합물을 포함하는 터치 패널용 점착제 조성물.
- 제 1 항에 있어서, 점착제 조성물은 아크릴 중합체를 가교시키는 다관능성 가교제를 추가로 포함하는 터치 패널용 점착제 조성물.
- 제 9 항에 있어서, 다관능성 가교제는 이소시아네이트 가교제, 에폭시 가교제, 아지리딘 가교제 또는 금속 킬레이트 가교제인 터치 패널용 점착제 조성물.
- 제 1 항에 있어서, 하기 일반식 1의 조건을 만족하는 터치 패널용 점착제 조성물:[일반식 1]△R = [(R-Ri)/Ri]×100≤15%상기 일반식 1에서, △R은 저항변화율이고, Ri는, 상기 점착제 조성물의 경화물인 점착제층을 ITO 전극에 부착한 후에 측정한 상기 ITO 전극의 초기 저항이며, R은, 상기 점착제층이 부착된 ITO 전극을 60℃ 및 90% 상대 습도에서 240 시간 동안 유지한 후에 측정한 상기 ITO 전극의 저항이다.
- 제 1 항에 따른 점착제 조성물을 경화된 상태로 포함하는 점착제층을 가지는 터치 패널용 점착 필름.
- 기재: 및 상기 기재의 일면 또는 양면에 형성되고, 제 1 항에 따른, 점착제 조성물을 경화된 상태로 포함하는 점착제층을 가지는 도전성 필름.
- 제 13 항에 있어서, 기재는 플라스틱 기재인 도전성 필름.
- 제 13 항에 있어서, 기재의 적어도 일면에는 도전층이 추가로 형성되어 있고, 점착제층이 상기 도전층에 부착되어 있는 도전성 필름.
- 제 13 항에 있어서, 일면에 도전층이 형성되어 있는 기판을 추가로 포함하고, 상기 기판의 도전층에 점착제층이 부착되어 있는 도전성 필름.
- 제 16 항에 있어서, 기재상에 형성된 도전층을 추가로 포함하고, 기판상에 형성된 도전층과 기재상에 형성된 도전층이 점착제층에 의해 서로 부착되어 있는 도전성 필름.
- 제 13 항에 따른 도전성 필름을 포함하는 터치 패널.